• 대한화학회지
• /
• 제44권1호
• /
• pp.60-67
• /
• 2000

표면공명흡수는 매질의 유전상수값에 의존한다. 금 나노미립자가 함침된 $TiO_2/SiO_2$ 복합산화물 박막을 $Ti(OPr^i)_4$과 $Si(OEt)_4$, 그리고 $HAuCl_4{\cdot}7H_2O$를 사용하여 졸-겔 방법으로 제조하였다. $TiO_2/SiO_2$ 박막에 함침된 금 나노미립자의 최대 표면 공명 흡수는 $TiO_2/SiO_2$의 몰비에 따라 540 nm에서 615 nm 까지 선형적으로 변하였다. 이러한 박막에 함침된 금 나노미립자의 크기와 구조를 TEM과 XRD로 측정하였다. 그리고 $TiO_2/SiO_2$ 박막의 유전상수값을 실험 data로부터 이론적으로 계산하였다

• Transactions on Electrical and Electronic Materials
• /
• 제12권5호
• /
• pp.193-196
• /
• 2011

Lead zirconate titanate (PZT)/ bismuth ferrite (BFO) multilayer thin films have been fabricated by the spin-coating method on Pt(200 nm)/Ti(10 nm)/$SiO_2$(100 nm)/p-Si(100) substrates using $BiFeO_3$ and $Pb(Zr_{0.52}Ti_{0.48})O_3$ metal alkoxide solutions. The PZT/BFO multilayer thin films show a uniform and void-free grain structure, and the grain size is smaller than that of PZT single films. The reason for this is assumed to be that the lower BFO layers play an important role as a nucleation site or seed layer for the formation of homogeneous and uniform upper PZT layers. The dielectric constant and dielectric losses decreased with increasing number of coatings, and the six-layer PZT/BFO thin film has good properties of 162 (dielectric constant) and 0.017 (dielectric losses) at 1 kHz. The remnant polarization and coercive field of three-layer PZT/BFO thin films were 13.86 ${\mu}C/cm^2$ and 37 kV/cm respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.291.2-291.2
• /
• 2014

ZnO 박막(thin film)은 씨앗층(seed layer)의 종류, 두께, 증착 조건 등에 따라 그 특성이 달라지는 것으로 알려져 있다. 이에 본 연구에서는 씨앗층의 종류에 따른 박막의 특성변화를 알아 보기 위해, 졸겔 스핀코팅(sol-gel spin-coating) 방법으로 4가지 종류의 씨앗층(Al-ZnO, Co-ZnO, Cu-ZnO, In-ZnO) 위에 ZnO 박막을 성장 한 후 성장된 ZnO 박막의 구조적, 광학적 특성을 field emission scanning electron microscope, X-ray diffractometer, UV-visible spectrometer를 통해 조사하였다. ZnO 박막의 표면구조는 씨앗층의 종류에 따라 변하였으며, 씨앗층 위에 성장된 ZnO 박막들의 c축 배향성과 결정성이 씨앗층 없이 성장된 ZnO 박막보다 더 우수하게 나타났다. 투과도(transmittance) 측정값을 통해 계산된 광학적 밴드갭(optical bandgap)과 Urbach 에너지는 씨앗층에 따라 다른 값을 나타내었다. 광학적 밴드갭은 Al-ZnO 씨앗층 위에 성장된 ZnO 박막에서 가장 크게 나타났으며, Urbach 에너지는 Co-ZnO 씨앗층 위에 성장된 ZnO 박막에서 가장 낮았다. 따라서 ZnO박막 성장 시 용도에 맞게 적절한 씨앗층을 사용하는 것은 소자의 성능을 향상시키는데 매우 중요한 역할을 할 수 있다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2010년도 제39회 하계학술대회 초록집
• /
• pp.281-281
• /
• 2010

Very low refractive index (<1.4) materials have been proved to be the key factor improving the performance of various optical components, such as reflectors, filters, photonic crystals, LEDs, and solar cell. Highly porous SiO2 are logically designed for ultralow refractive index materials because of the direct relation between porosity and index of refraction. Among them, ordered macroporous SiO2 is of potential material since their theoretically low refractive index ~1.10. However, in the conventional synthesis of ordered macroporous SiO2, the time required for the crystallization of organic nanoparticles, such as polystyrene (PS), from colloidal solution into well ordered template is typical long (several days for 1 cm substrate) due to the low interaction between particles and particle - substrate. In this study, polystyrene - polyacrylic acid (PS-AA) nanoparticles synthesized by miniemulsion polymerization method have hydrophilic polyacrylic acid tails on the surface of particles which increase the interaction between particle and with substrate giving rise to the formation of PS-AA film by simply spin - coating method. Less ordered with controlled thickness films of PS-AA on silicon wafer were successfully fabricated by changing the spinning speed or concentration of colloidal solution, as confirmed by FE-SEM. Based on these template films, a series of macroporous SiO2 films whose thicknesses varied from 300nm to ~1000nm were fabricated either by conventional sol - gel infiltration or gas phase deposition followed by thermal removal of organic template. Formations of SiO2 films consist of interconnected air balls with size ~100 nm were confirmed by FE-SEM and TEM. These highly porous SiO2 show very low refractive indices (<1.18) over a wide range of wavelength (from 200 to 1000nm) as shown by SE measurement. Refraction indices of SiO2 films at 633nm reported here are of ~1.10 which, to our best knowledge, are among the lowest values having been announced.

• 한국재료학회지
• /
• 제20권8호
• /
• pp.401-407
• /
• 2010

We studied the influence of different types of metal electrodes on the performance of solution-processed zinc tin oxide (ZTO) thin-film transistors. The ZTO thin-film was obtained by spin-coating the sol-gel solution made from zinc acetate and tin acetate dissolved in 2-methoxyethanol. Various metals, Al, Au, Ag and Cu, were used to make contacts with the solution-deposited ZTO layers by selective deposition through a metal shadow mask. Contact resistance between the metal electrode and the semiconductor was obtained by a transmission line method (TLM). The device based on an Al electrode exhibited superior performance as compared to those based on other metals. Kelvin probe force microscopy (KPFM) allowed us to measure the work function of the oxide semiconductor to understand the variation of the device performance as a function of the types metal electrode. The solution-processed ZTO contained nanopores that resulted from the burnout of the organic species during the annealing. This different surface structure associated with the solution-processed ZTO gave a rise to a different work function value as compared to the vacuum-deposited counterpart. More oxygen could be adsorbed on the nanoporous solution-processed ZTO with large accessible surface areas, which increased its work function. This observation explained why the solution-processed ZTO makes an ohmic contact with the Al electrode.

• 한국전기전자재료학회논문지
• /
• 제12권1호
• /
• pp.62-68
• /
• 1999

Ferroelectric $Sr_{0.7}/B_{2.3}(Ta_{1-x}Nb_x)_2O_9$(x=0, 0.1, 0.2, 0.3) thin films were deposited on $Pt/SiO_2/Si$ substrate by MOD(Metalorganic Decomposition) process. Metal carboxylate and metal alkoxide were used as precursors, and 2-methoxyethanol, xylene as solvents. After spin coating, thin films were pre-annealed at $400^{\circ}C$, followed by RTA(Rapid Thermal Annealing) and final annealing at $800^{\circ}C$ in oxygen atmosphere. These procedures were repeated three times to obtain thin films with the thickness of $2000{\AA}$. To enhance the nucleation and growth of layered-perovskite phase, thin films were rapid-thermally annealed above $720^{\circ}C$ in oxygen atmosphere. As RTA temperature increased, fluorite phase was transformed to layered-perovskite phase. And the change of Nb contents affected dielectric / electrical properties and microstructure. The ferroelectric characteristics of $Sr_{0.7}/B_{2.3}(Ta_{1-x}Nb_x)_2O_9$ thin film were Pr=8.67 $\mu{C}/cm^2$, Ec=62.4kV/cm and $I_{L}=1.4\times10^{-7}A/cm^2$ at the applied voltage of 5V, respectively.

• 한국자기학회지
• /
• 제17권2호
• /
• pp.51-54
• /
• 2007

역스피넬 산화물 $Fe_3O_4$에 Cr을 치환하여 얻어지는 $Cr_xFe_{3-x}O_4$ 박막 시료들을 졸-겔 스핀코팅 방법을 이용하여 제작하고 그 구조적, 전자기적 특성들에 대한 측정 및 분석을 수행하였다. X선 회절 측정 결과, Cr 성분비가 증가함에 따라 격자상수가 소폭 감소하는 것이 관측되었다. 이는 Fe 이온에 비해 이온반경이 상대적으로 작은 Cr 이온이 +3의 이온수를 가지고 8면체 자리를 치환하는 것으로 설명 가능하다. 시료들에 대한 진동시료자화를 측정한 결과, Cr 성분비 증가에 따라 포화자화량이 $Fe_3O_4$에 비하여 점차적으로 감소하였는데, 이는 8면체 자리의 $Fe^{3+}(d^5)$와 $Cr^{3+}(d^3)$ 나타내는 스핀 자기능률 값의 비교를 통하여 설명 가능하다. 또한, 자기저항 효과도 Cr 성분비 증가에 따라 포화자화량과 유사한 추세로 감소하였다. $Cr_xFe_{3-x}O_4$ 박막 시료들의 보자력은 Cr 성분비 증가에 따라 증가함을 보였는데, 이는 $Cr^{3+}$ 이온의 8면체 자리 치환에 따른 자기 이방성의 증가에 기인하는 것으로 해석된다.

• 한국재료학회지
• /
• 제9권8호
• /
• pp.804-809
• /
• 1999

테오스(TEOS)를 출발물질로 사용하여 건조조절제(DCCA;Dying Control Chemical Additives)를 첨가하지 않고, 솔-젤 법을 이용하여 Si(001) 단결정 기판 위에 실리카 박막을 제조하였다. 박막은 스핀 코팅 방법으로 테오스 =1 몰, 염산=0.05몰의 조건하에 메탄올, 증류수의 첨가량을 변화시키면서 젤화 완료시간, 박막의 두께, 균열 발생 여부, 박막의 결정성 등을 조사하였다. 그 결과 솔의 제화 완료시간은 메탄올 첨가량이 8몰일 때 가장 긴 640시간이었다. 코팅된 박막의 두께는 메탄올 첨가량이 많아질수록 감소하였다. 소결은 승온 속도$0.6^{\circ}C$/min으로 $500^{\circ}C$에서 1시간 행하였으며, 메탄올 첨가량이 0.8몰, 2몰일 때는 표면에서 균열이 발생하여 worm-like grain 구조를 가졌고, 메탄올 4몰인 경우에는 국부적으로 균열이 발생하였으나, 메탄올 양이 8몰 이상에서는 균열이 발생하지 않았다. 즉, 솔-젤 공정에서 균열 방지를 위해 첨가되는 건조조절제(DMF)를 첨가하지 않고도 용매인 메탄올과 증류수 혼합비를 조절, 표면장력을 제어함으로써 균열없는 박막을 제조하였다.

• 한국전기전자재료학회논문지
• /
• 제35권5호
• /
• pp.499-503
• /
• 2022

La_0.7Sr_0.3MnO₃ precursor solution were prepared by a sol-gel method. La_0.7Sr_0.3MnO₃ thin films were fabricated by a spin-coating method on a Pt/Ti/SiO₂/Si substrate. Structural and electrical properties with the variation of sintering temperature were measured. All specimens exhibited a polycrystalline orthorhombic crystal structure, and the average thickness of the specimens coated 6 times decreased from about 427 nm to 383 nm as the sintering temperature increased from 740℃ to 830℃. Electrical resistance decreased as the sintering temperature increased. In the La_0.7Sr_0.3MnO₃ thin films sintered at 830℃, electrical resistivity, TCR, B-value, and activation energy were 0.0374 mΩ·cm, 0.316%/℃, 296 K and 0.023 eV, respectively.