$Pb(Zr_{0.3},Ti_{0.7})O_3$, $Pb(Zr_{0.3},Ti_{0.3})O_3$ powders were prepared by the sol-gel method and PZT heterolayered thick films were fabricated by the screen-printing method. The structural properties as a faction of the composition ration were studied. As a result of the differential thermal analysis (DTA), exothermic peak was observed at around $864^{\circ}C$ dne to the formation of the polycrystalline perovskite phase. The PZT heterolayered thick film sintered at $1050^{\circ}C$ for 10min showed the average grain size $1{\sim}1.4{\mu}m$. The average thickness of PZT heterolayered thick films, obained by $3{\sim}6times$ of screen-printing, was approximately $60{\sim}110{\mu}m$.
Journal of information and communication convergence engineering
/
제1권2호
/
pp.63-66
/
2003
High $T_c$ superconducting lines will be applied as key materials in the areas of power transmission line; magnetic levitation of vehicle; magnetic separation; magnetic energy storage and marine propulsion. A combination method of electrophoresis deposition and zone-melting for preparation of YBaCuO tape is proposed. The submicron particle powder of YBaCuO made by sol-gel method is used in the electrophoresis process. A 40∼50 ${\mu}\textrm{m}$ thickness of YBaCuO film on Ag plate could be deposited in about three minutes. After deposition the film is rolled and heat treated in order to increase the density and the adhesion of the film to the Ag plate. Silver(Ag) and lead oxide(PbO) were added in the YBaCuO powder in order to reduce its melting point. The YBaCuO coating with controlled Ag and PbO contents was preliminarily zone-melted at about $945^{\circ}C$.
Ferroelectric PZT heterolayered thin films were fabricated by spin coating method on the Pt/Ti/SiO$_2$/Si substrate using PZT(10/90) and PZT(90/10) metal alkoxide solutions. All PZT heterolayered films showed a homogeneous grain structure without presence of the rosette structure. It can be assumed that the lower PZT layers a role of nucleation site or seeding layer for the formation of the upper PZT layer. Zr and Ti diffusion into the Pt electrode were mainly distributed at the surface of Pt electrode beneath the PZT/Pt interface. The PZT/Pt interfacial layer showed a microstructure characterized by a grain phase surrounded by a Pb-deficient pyrochlore matrix phase. The relative dielectric constant and the dielectric loss of the PZT-6 film were 567 and 3.6, respectively.
티타늄과 스테인리스 기판위에 졸-겔 코팅법으로 무기질 보호막을 형성하였고 기계적 특성을 테스트 하였다. 무기질 보호막은 금속 표면위에 졸-겔 코팅용액을 스프레이 코팅하여 제작하였다. 티타늄과 스테인리스 기판위에 적용한 무기질 보호막은 현저한 내스크래치성 향상을 보였다. 또한 실리카 나노입자의 첨가에 따른 무기질 보호막의 경도 향상을 보였다. 그러나 실리카 나노입자가 2 wt% 이상 첨가됨에 따라 보호막의 경도가 감소함을 알 수 있었다.
극저 유전특성을 갖는 SiO2 에어로겔의 박막화의 층간 절연막으로써의 응용성이 연구되었다. 점도가 10~14cP인 SiO2 폴리머 졸을 이소프로판을 분위기 하에서 1000~7000m으로 p-Si(111) 웨이퍼 상에 스핀코팅한 습윤겔 박막을 25$0^{\circ}C$와 1160 psing 조건에서 초임계건조하여 0.5 g/㎤ 정도의 밀도(78% 기공율) 와 4000~21000$\AA$ 범위의 두께를 갖는 SiO2 에어로겔 박막을 제조하였다. 박막의 두께와 미세구조를 제어할 수 있는 주요 인자는 졸의 농도, 회전속도 및 습윤겔 숙성시간임을 알 수 있었다. SiO2 에어로겔 박막의 유전상수 값은 giga급 이상의 차세대 반도체 소자에 충분히 응용될 수 있을 정도로 낮은 2.0 정도이었다.
최근 환경오염에 관한 문제가 대두됨에 따라서 친환경 수처리 공법에 관한 다양한 방법들이 논의되고 있다. 현재 시장을 주도하고 있는 고분자 멤브레인은 저가이나, 내화학성 및 내구성 측면에서 많은 문제점을 안고 있다. 이에 따라 친환경적이며 내구성, 내화학성이 뛰어난 세라믹 멤브레인의 기공 구조, 크기 및 표면 처리를 통하여 고효율의 수처리용 세라믹 멤브레인을 제작하였다. $ZrO_2$ 및 $TiO_2$의 균일한 코팅막 형성을 통하여 멤브레인의 기공 크기를 조절 하였다. 테입케스팅, 졸겔 공정법을 활용하여 멤브레인 표면에 성공적으로 나노기공을 가지는 세라믹 코팅막을 형성하였다. 세라믹 멤브레인의 미세조직 분석, 코팅막의 기공의 크기 분석을 진행하였으며 이에 대한 수처리 특성 변화를 관측하였다.
Sol-gel 법으로 제조한 $Pb(Sc_{1/2}Nb_{1/2})O_3$(이하 PSN) sol을 이용하여 스핀 코팅법으로 Pt(111)/Ti/$SiO_2$/Si 기판위에 제조한 박막의 제조 공정에 따른 영향을 연구하였다. Pt 기판위에 PSN sol을 증착, 건조한 후에 $370^{\circ}C$에서 5분간 열처리를 행한 후 $10^{\circ}C/sec$의 급속 가열로 $600{\sim}700^{\circ}C$에서 최종 열처리한 경우에 박막은 (111)면으로 우선 배향하는 것으로 나타났다. 그러나 중간 열처리를 거치지 않고, 급속가열에 의한 최종 열처리만을 행한 경우에는 (100)면으로 우선 배향하는 것으로 나타났다. 한편, 중간 열처리 후 $4^{\circ}C/min$의 승온속도로 관상로에서 최종 열처리를 행한 경우에는 (111)면과 (100)면이 동시에 나타나는 것으로 나타났다. 동일한 조건하에서 박막의 두께는 모두 300로 중간 열처리 공정이 어떠한 영향도 미치지 않는 것으로 나타났다.
Tetraethylorthosilicate (TEOS)를 전구체로서 이용하여 제조된 기존의 반사방지(AR; anti-reflective) 코팅막은 대부분 수분을 쉽게 흡수할 뿐만 아니라 낮은 내마모성을 갖는다. 본 연구에서는 AR 코팅막의 투과율, 소수성 및 내마모성을 향상할 목적으로 전구체로서 methyltrimethoxysilane (MTMS)를 사용하고 불소 실란, 산 촉매, 염기 촉매 및 산-염기 2단계 촉매를 첨가하여 다양한 AR 코팅막을 제조하였다. 제조된 AR 코팅막은 UV-Vis, 접촉각 측정기, AFM, 연필경도 및 부착성 시험을 통해 특성을 분석하였다. 그 결과, 경화온도가 $300^{\circ}C$일 때 코팅되지 않은 유리 기판의 투과율은 90.5%인 반면, AR 코팅된 유리 기판의 투과율은 94.8%로 증가하였다. 불소 실란을 첨가한 경우, 소수성이 크게 향상되었음을 나타내듯이 AR 코팅막 표면에서의 접촉각은 $96.3^{\circ}$에서 $108^{\circ}$까지 증가하였다. AR 코팅막의 내마모성은 산 촉매에 의해 향상되었으며, 그것의 투과율은 염기 촉매에 의해 증가하였다. 산-염기 2단계 촉매 반응에 의해 제조한 AR 코팅막의 경우, 상승 효과에 의해 촉매의 도입 없이 제조된 AR 코팅막과 비교하여 투과율 및 내마모성이 향상되었다.
Studies on plants such as lotus leaf suggested that dual-scale structure could contribute to super-hydrophobicity. We introduced super-hydrophobicity onto poly(ethylene terephthalate)(PET) fabric with dual-scale structure by assembling $TiO_2$ nano sol. PET fabric was treated with $TiO_2$ sol, water-repellent agent using various parameters such as particle size, concentration. Morphological changes by particle size were observed using field emmission scanning electron microscopy(FE-SEM) and AFM measurement, contact angle measurement equipment. The contact angle of water was about 138.5$^{\circ}$, 125.8$^{\circ}$, 125.5$^{\circ}$ and 108.9$^{\circ}$ for PET fabric coated with 60.2nm, 120.1nm, 200nm and 410.5nm $TiO_2$ particles, compared with about 111.5$^{\circ}$ for PET fabric coated with water repellent. When we mixed particle sizes of 60.2nm and 120.1nm by 7:3 volume ratio, the contact angle of water was about 132.5$^{\circ}$. And we mixed particle sizes of 60.2nm and 200nm by 7:3 volume ratio, the contact angle of water was about 141.8$^{\circ}$. Also we mixed particle sizes of 60.2nm and 410.5nm by 7:3 volume ratio, the best super-hydrophobicity was obtained. In this paper, we fabricated various surface structures to the water-repellent surfaces by using four types of $TiO_2$ nano-particles, and we found that the nanoscale structure was very important for the super-hydrophobicity.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.