• Korean Journal of Materials Research
• /
• v.32 no.12
• /
• pp.515-521
• /
• 2022

Various types of optical materials and devices used in special environments must satisfy durability and optical properties. In order to improve the durability of zinc sulfide multispectral (MS ZnS) substrates with transmission wavelengths from visible to infrared, Ge-Sb-Se-based chalcogenide glass was used as a sealing material to bond the MS ZnS substrates. Wetting tests of the Ge-Sb-Se-based chalcogenide glass were conducted to analyze flowability as a function of temperature, by considering the glass transition temperature (T_g) and softening temperature (T_s). In the wetting test, the viscous flow of the chalcogenide glass sample was analyzed according to the temperature. After placing the chalcogenide glass disk between MS ZnS substrates (20 × 30 mm), the sealing test was performed at a temperature of 485 ℃ for 60 min. Notably, it was found that the Ge-Sb-Se-based chalcogenide glass sealed the MS ZnS substrates well. After the MS ZnS substrates were sealed with chalcogenide glass, they showed a transmission of 55 % over 3~12 ㎛. The tensile strength of the sealed MS ZnS substrates with Ge-Sb-Se-based chalcogenide glass was analyzed by applying a maximum load of about 240 N, confirming its suitability as a sealing material in the far infrared range.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.138-141
• /
• 2008

The effects of annealing temperature and time on mechanical properties and microstructures were investigated in cold drawn pearlitic steel wires. During annealing, the increment of the tensile strength at low temperatures found to be due to age hardening, while the decrease in the tensile strength at high temperatures was attributed to age softening, involving the spheroidization of lamellar cementite and recovery of lamellar ferrite. Since tensile strength and the occurrence of the delamination would be closely related to the dissolution of cementite, the lower annealing temperature and the increase of drawing strain caused the higher tensile strength and the easier occurrence of the delamination in cold drawn pearlitic steel wires.

• Journal of Mechanical Science and Technology
• /
• v.20 no.1
• /
• pp.13-18
• /
• 2006

Ti-8Ta-3Nb, as a new biomaterial, was prepared by cast and swaging process. Their deformation behavior of Ti-8Ta-3Nb alloy has been characterized on the basis of its flow stress variation obtained from the true strain rate compression testing in the temperature of $700-900^{\circ}C$ and strain rate of $0.001-10\;s^{-1}$. At the strain rates lower than $0.1\;s^{-1}$ and the all temperature ranges which consist of two phase ${\alpha}+{\beta}$ as well as single ${\beta}$ phase fields, the flow curves show a small degree of flow softening behavior. In contrast, the shapes of the flow curves at other strain rates indicate unstable behavior. The shapes of the flow curves were similar in both as-cast and swaged specimen as well as in both ${\alpha}+{\beta}$ phase and ${\beta}$ phase. The flow stress data did not obey the kinetic rate equation over the entire regime of testing but a good fit has been obtained in the intermediate range of temperatures ($750-850^{\circ}C$). In this range, a stress exponent value of about 7.7 in as-cast specimens and about 6.2 in swaged specimens with an apparent activation energy of about 300 kJ/mol and about 206 kJ/mol respectively have been evaluated.

• Journal of the Korean Ceramic Society
• /
• v.14 no.4
• /
• pp.230-235
• /
• 1977

In this paper the conditions of surface crystallization of glass were studied. The basic glass which is apt to crystallize, with $SiO_2$ 72.50, $Al_2O_3$ 5, 00, $Na_2O$ 8.00 $K_2O$ 3.50, CaO 5.00, MgO 3.00, $B_2O_3$ 3.00 Wt% is chosen. The strain point and softening point of this glass is 4$25^{\circ}C$ and 778$^{\circ}C$ each, and between the two temperatures we could get grystal on its surface by immersion in salt baths during some controlled hours. The kind of crystal on the surface of glass was confirmed by X-ray diffraction analysis and the change of the thickness of crystalline layers depending on temperature and time, was surveyed by using optical microscope. The results are as follows; 1. The chloride group is more suitable than sulfate group for the treating salt. 2. In the condition with 50 LiCl.50NaCl at 62$0^{\circ}C$ for 2 hrs and with 50 LiCL.20-30 NaCl.30-20 $CaCl_2$ at 72$0^{\circ}C$ for 15-20 min. we could get the best crystalline layers. 3. The crystal was silica-O and petalite with a little tridymite and nepheline. 4. The thickness of crystalline layers increased with increasement of temperature and time.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10b
• /
• pp.43-46
• /
• 2003

Prediction of final microstructures after high temperature forming of Ti-6Al-4V alloy was attempted in this study. Using two typical microstructures, i.e., equiaxed and $Widmanst\ddot{a}tten$ microstructures, compression test was carried out up to the strain level of 0.6 at various temperatures $(700\~1100^{\circ}C)$ and strain rates $(10^{-4}\~10^2/s)$. From the flow stress-strain data, parameters such as strain rate sensitivity (m) and activation energy (Q) were calculated and used to establish constitutive equations for both microstructures. Then, finite element analysis was performed to predict the final microstructure of the deformed body, which was well accorded with the experimental results.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2000.10a
• /
• pp.29-32
• /
• 2000

The static and metadynamic recrystallization of non-heat treated medium carbon steel(Fe - 0.45wt.$\%C\;-\;0.6wt.\%Si\;-\;1.2wt.\%Mn\;-\;-0.12wt.\%Cr \;-\;0.1wt.\%V \;-\;0.017wt\%$.Ti) were studied by the torsion test in the strain rate range of 0.05 - 5 $sec^{-1}$, and in the temperature range of $900\;-\;1100\;^{\circ}C$. Interrupted deformation was performed with 2 pass deformation in the pass strain range of $0.25 {\varepsilon}_p(peak strain)\;and\;{\varepsilon}_p$, and in the interpass time range or 0.5 - 100 sec. The dependence or pass strain(${\varepsilon}_i$), strain rate( $\dot{\varepsilon}$ ), temperature(T), and interpass time($t_i$) on static recrystallization (SRX) and metadynamic recrystallization (MDRX) were predicted from the modified Avrami's equations respectively. Comparison of the softening kinetics between SRX and MDRX was indicated that the rate of MDRX was more rapid than that of SRX under the same deformation variables.

• Journal of the Korean Ceramic Society
• /
• v.42 no.10 s.281
• /
• pp.691-697
• /
• 2005

Porous ceramics which have closes pore were fabricated by heat treatment at 100$\∼$ 600$^{\circ}C$ for 30 min using dried water glasses with 25, 35, and 45 wt$\%$ water contents. Size and distribution of the closed pore were varied depending on the water contents and heat treatment temperature. The expansion procedure could be distinguished by two stages. The frist stage occurred around loo$\%$ due to the evaporation of water and the second stage occurred at 200$\∼$400$^{\circ}C$ due to the decomposition of Si-OH compounds. The specimen was not expanded successfully because of the softening of the dried water glass at 500$\∼$600$^{\circ}C$.

• International Journal of Highway Engineering
• /
• v.11 no.3
• /
• pp.33-40
• /
• 2009

The use of the crumb rubber as an asphalt binder modifier may contribute to road maintenance and repair. The adhesion properties of the crumb rubber modified asphalt (CRMA) sealant have attracted interest due to brittle and adhesion failure of asphalt binders at low temperatures. In this study, the influence of a flexibilizer as a modifier for CRMA at low temperatures was investigated. Their properties were measured using the penetration, the softening point, the tensile and tensile adhesion tests at low temperature. The tensile adhesion strength and the strain of CRMAs were increased with increasing ductile deformation of the CR and the asphalt binder in the flexiblizer modified CRMAs. It was found that the flexibilizer concentration was an important factor for tensile and adhesion properties of CRMAs at low temperatures.

• Journal of Welding and Joining
• /
• v.26 no.6
• /
• pp.54-58
• /
• 2008

Laser welding with AZ61 filler wire was carried out to improve formability though reduction of porosity and formation of under fill bead. Optimum welding condition and mechanical properties of butt joint for $400{\times}500{\times}1.3mm$ magnesium sheets were studied. Optimal welding conditions of laser power, welding speed, and defocusing length are 1000W, 3m/min, and 2mm, respectively. Results of tensile test indicated that both tensile strength and elongation of specimens welded with filler wire were improved at room temperature because of reduction of porosity and under-filled bead formation in addition to the precipitation hardening and microstructure refinement by Al-Mn and Mg-Al-Zn precipitates. At elevated temperature of $200{\sim}350^{\circ}C$, fracture location of tensile specimen was shifted from weld metal to base metal, indicating less softening of weld metal than base metal.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.231-234
• /
• 2009

The effects of annealing temperature and time on mechanical properties and microstructures were already investigated in cold drawn pearlitic steel wires. During annealing, the increment of the tensile strength at low temperatures found to be due to age hardening, while the decrease in the tensile strength at high temperatures was attributed to age softening, involving the spheroidization of lamellar cementite and recovery of lamellar ferrite. Since Between increase of tensile strength and the occurrence of the delamination would be closely related to the dissolution of cementite, the increase of drawing strain by lower annealing temperature caused the between higher tensile strength and the easier occurrence of the delamination in cold drawn pearlitic steel wires.