• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.33 no.1
• /
• pp.7-14
• /
• 2023

Forty Viscosity data of glass bottles fabricated in a glass bottle manufacturing plant for 4 years were calculated using Lakatos model. The relationship between the glass bottle compositions and viscosities at log η of 3, 6.6, 10 and 12.3 Pa·s was analyzed. MgO that was a component of the glass bottle showed the maximum coefficient of variation of 0.89, but it gave a very small change in the viscosity. CaO that was another component of the glass bottle lowered the isokom temperature because it tended to reduce the number of non-bridging oxygen at temperature below a softening point.

• Journal of the Korean Vacuum Society
• /
• v.17 no.6
• /
• pp.481-486
• /
• 2008

The different degrees of blackening were observed at the inner surface of borosilicate, soda-lime, and aluminosilicate glass tubes having different sodium (Na) contents. The sodium contents ($Na_2O$) within the borosilicate, soda-lime, and aluminosilicate glass tubes were found to be 4%, 14%, and 0.06%, respectively. The degree of blackening was shown to increase as the sodium content within the glass of the fluorescent lamp containing Ne+Ar+Hg gas mixture. Higher degree of blackening was observed from the inner surface of the glass tube coated with $Y_2O_3$. The blackening was found to be originated from the amalgam of $NaHg_2$ generated by the chemical reaction between the mercury ions within the discharge gas and sodium within the glass tube during operation.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.5
• /
• pp.74-81
• /
• 2019

This study reports the CW $CO_2$ laser scribing of soda lime glass. In this study, scribing experiments are carried out at different laser powers, scan speeds, and focal positions to investigate the effect of the process parameters on the interaction characteristics between a laser beam and glass. In particular, the interaction characteristics are analyzed and described with the input laser energy per unit length. According to the experimental results, the damage threshold for the glass surface was found to exist between 0.072 and 0.08 J/mm. The input laser energy in this region induced partial melting of the surface and grain-shaped cracks. These cracks tended to increase as the input laser energy increased. At the laser input energy larger than 1 J/mm, a huge crack propagating along the scan direction was produced, and the volume below the scribed area was fully melted. The growth of this crack finally resulted in the complete cutting of the glass at the input laser energy above 8 J/mm. It was found that both the width and depth of the scribed line increased with increasing input laser energy. For the beam focusing at the rear surface, the width of the scribed line varied irregularly. This could be ascribed to the increased asymmetry of the beam intensity distribution when the laser beam was focused at the rear surface. Under this condition, a large burr was only produced on one side of the scribed line.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08a
• /
• pp.367-370
• /
• 2007

An EEFL with the sodium free alumino-silicate glass of high K and low $tan{\delta}$, has been investigated. As compared with borosilicate and the soda-lime EEFLs, the luminous efficiency as well as the pinhole stability of new EEFLs improves remarkably without blackening of $NaHg_2$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2000.01a
• /
• pp.181-182
• /
• 2000

The glass compositions of $PbO-SiO_2-B_2O_3$ system and $P_2O_5-PbO-ZnO$ system for the transparent dielectric materials for front panel and $P_2O_5-ZnO-BaO$ and $SiO_2-ZnO-B_2O_3$ for the reflective dielectric materials for back panel of PDP(Plasma Display Panel) were investigated. As a transparent dielectric materials for front panel, $PbO-SiO_2-B_2O_3$ glass showed good dielectric properties, high transparency and proper thermal expansion matching to soda-lime glass substrate. And the reflective dielectric materials for back panel were prepared from parent glass of $SiO_2-ZnO-B_2O_3$ system and oxide filler. It was found that these glass-ceramics are useful materials for reflective dielectric layers, as those have a similar thermal expansion to soda-lime glass plate, high reflectance, low sintering temperature.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1729-1731
• /
• 1999

The effect of Na on the structural and electrical properties of CIGS films were studied and their effects on the CIGS/Mo thin film solar cells were investigated. Soda-lime glass and Corning glass were used as substrates to compare the effect of Na diffusion into CIGS film. The resistivity of CIGS films was not changed in the Cu-poor region due to diffusion of Na from soda-lime glass but was mainly determined by the surface resitivity controlled by excess Na.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.16-18
• /
• 2009

CIGS 박막태양전지는 박막태양전지 중 최고 효율(20%)을 보이는 태양전지로 각광받고 있다. 이러한 고효율 태양전지는 Soda-lime glass 를 기판으로 사용한 경우로 기판과 CIGS층의 열팽창계수가 비슷하고 또 나트륨이 CIGS 성장시 확산하여 광흡수층에 유익한 영향을 준다고 알려져 있다. 본 실험에서는 나트륨이 함유된 소다라임유리와 거의 포함하고 있지 않은 코닝유리를 기판으로 사용하여 CIGS 광흡수층의 차이를 분석하였다. SIMS, SEM분석결과 소다라임유리의 CIGS Mo 부근과 표면부위에 Na 농도가 높으며, grain 크기가 코닝에 비해 작음을 알 수 있었다. 전기적 특성은 소다라임유리기판의 경우 p-type 농도가 코닝유리기판에 비해 약 $10^5{\sim}10^6$천배가량 높음을 확인하였다. 셀특성또한 코닝 11%, SLG는 16%로 효율차이가 발생하였으며 이는 나트륨으로 p-type 전도도가 향상되어 효율이 개선되는 것으로 판단된다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.66-66
• /
• 2008

Most of the properties of ITO films depend on their substrate nature, deposition techniques and ITO film composition. For the display panel application, it is normally deposited on the glass substrate which has high strain point (>575 degree) and must be deposited at a temperature higher than $250^{\circ}C$ and then annealed at a temperature higher than $300^{\circ}C$ in order to high optical transmittance in the visible region, low reactivity and chemical duration. But the high strain point glass (HSPG) used as FPDs is blocking popularization of large sizes FPDs because it is more expensive than a soda lime glass (SLG). If the SLG could be used as substrate for FPDs, then diffusion of Na ion from the substrate occurs into the ITO films during annealing or heat treatment on manufacturing process and it affects the properties. Therefore proper care should be followed to minimize Na ion diffusion. In this study, we investigate the electrical, optical and structural properties of ITO films deposited on the SLG and the Asahi glass(PD200) substrate by rf magnetron sputtering using a ceramic target ($In_2O_3:SnO_2$, 90:10wt.%). These films were annealed in $N_2$ and air atmosphere at $400^{\circ}C$ for 20min, 1hr, and 2hrs. ITO films deposited on the SLG show a high electrical resistivity and structural defect as compared with those deposited on the PD200 due to the Na ion from the SLG on diffuse to the ITO film by annealing. However these properties can be improved by introducing a barrier layer of $SiO_2$ or $Al_2O_3$ between ITO film and the SLG substrate. The characteristics of films were examined by the 4-point probe, FE-SEM, UV-VIS spectrometer, and X-ray diffraction. SIMS analysis confirmed that barrier layer inhibited Na ion diffusion from the SLG.

• Composites Research
• /
• v.22 no.4
• /
• pp.33-40
• /
• 2009

Fiber orientation effects on the impact surface fracture of the glass plates coated with the glass fiber/epoxy lamina layer were investigated using a small-diameter steel-ball impact experiment. Four kinds of materials were used: soda-lime glass plates, unidirectional glass fiber/epoxy layer(one ply, two plies)-coated, crossed glass tiber/epoxy layer (two plies)-coated glass plates. The maximum stress and absorbed fracture energy were measured on the back surface of glass plates during the impact. With increasing impact velocity, various surface cracks such as ring, cone, radial and lateral cracks appeared near the impacted site of glass plates. Cracks in the plate drastically diminished by glass fiber coating. The tiber orientation guided the directions of delamination and plastic deformation zones between the tiber layer and the glass plate. Impact surface-fracture indices expressed in terms of the maximum stress and absorbed energy could be used as an effective evaluation parameter of the surface resistance.

• Journal of Conservation Science
• /
• v.32 no.1
• /
• pp.63-73
• /
• 2016

This study defined material and characteristics of 24 glass fragments and 26 whole glass beads. The feature of glass beads shape are divided into 5 types following color, size, weathering condition and manufacturing techniques. Through the chemical composition, the first and second type is soda glass, the third type is potash glass, the fourth and fifth type is lead barium glass. This site showed the aspect that the chemical composition is changed according to the feature of glass shape and was found that various chemical compositions. Looking at the flow of glass culture, the tomb that are lead barium glass IItype and potash glass I, IItype is relatively preceding period and the tomb that are soda glass and lead barium glass IIItype is following period.