• Journal of Advanced Marine Engineering and Technology
• /
• 제24권6호
• /
• pp.61-69
• /
• 2000

Indium-Tin Oxide (ITO) films were prepared on the commercial glass substrate by the Magnetron Sputtering method. The target was a 90wt.% $In_2O_3$-10wt.% $SnO_2$with 99.99% purity. The ITO films deposited by changing the partial pressure of oxygen gas ($O_2$/(Ar+$O_2$)) of 2, 3 and 5% as well as by changing the substrate temperature of $300^{\circ}C$ or $500^{\circ}C$. The influence of substrate pre-annealing and pre-cleaning on the quality of ITO film were examined, in which the substrate temperature was $500^{\circ}C$ and oxygen partial pressure was 3%. The characteristics of films were examined by the 4-point probe, Hall effect measurement system, SEM, AFM, Spectrophotometer, and X-ray diffraction. The optimum ITO films have been obtained when the substrate temperature is $500^{\circ}C$ and oxygen partial pressure is 3%. At optimum condition, the film showed transmittance of 81%, sheet resistivity of $226\Omegatextrm{cm}^2$, resistivity($\rho$) of $5.4\times10^{-3}\Omega$cm, carrier concentration of $1.0\times10^{19}cm^{-3}$, and carrier mobility of $150textrm{cm}^2$Vsec. From XRD spectrum, c(222) plane was dominant in the case of substrate temperature at $300^{\circ}C$, without regarding to oxygen partial pressure. However, in the case of substrate temperature at $500^{\circ}C$, c(400) plane was grown together with c(222) plane, only for oxygen partial pressure of 2 and 3%. In both case of chemical and ultrasonic cleaning without pre-annealing the substrate, it showed much almost same sheet resistivity, resistivity($\rho$), transmittance, carrier concentration, and carrier mobility. In case of $500^{\circ}C$/60min pre-annealing before ITO film deposited, both transimittance and carrier mobility are better than no pre-annealing, because pre-annealing is supposed to remove alkari ions diffusion from substrate. ITO film deposited on the Corning 0080 sybstrate showed a little bit better sheet resistivity, resistivity($\rho$), transimittance, carrier concentration than the film deposited on commercial glass. But no differences between Corning substrate and pre-annealed commercial glass substrate are found.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 춘계학술대회 논문집
• /
• pp.159-159
• /
• 2009

RF 스퍼터링법을 이용하여 유리기판위에 ZnO:Al 박막을 증착하고 다양한 조건 하에서 후 열처리를 실시하여 이에 따른 박막의 구조적, 전기적 및 광학적 특성과 HCl 습식 식각 후의 표면형상 변화를 조사하였다. ZnO:Al 투명전도막은 우수한 전기적, 광학적 특성, 수소 플라즈마 안정성 및 저 비용 등으로 실리콘 박막 태양전지 전면 전극용으로 많은 관심을 받고 있다. 기존의 비정질 실리콘 박막 태양전지용으로 많이 사용되고 있는 상용 Asahi-U형 ($SnO_2:F$) 투명전도막의 경우는 수소 플라즈마에 대한 안정성이 낮고 입사광의 장파장 대역에서의 낮은 산란특성으로 인하여 실리콘 박막 태양전지의 고효율화를 위한 적용에 한계를 나타내고 있다. 이를 개선하기 위하여 스퍼터링법으로 우수한 전기적 특성을 갖는 ZnO:Al 박막을 제조한 후 습식 식각을 통한 표면형상 변화를 통하여 입사광의 산란특성을 향상시키는 방법이 개발되어 많은 연구가 이루어지고 있다. 본 연구에서는 2.5 wt%의 $Al_2O_3$가 함유된 ZnO 타겟을 이용하여 ZnO:Al 박막을 RF 스퍼터링으로 증착한 후 $N_2$ 분위기와 진공 분위기 하에서 다양한 시간과 온도에 따라 후열처리를 하여 열처리 전 박막과의 물질 특성을 상호 비교하고 1%로 희석된 HCl로 습식 식각하여 열처리 전 박막의 구조적 특성이 습식 식각 후의 박막 표면형상 변화에 미치는 영향을 조사하였다. 이로부터 후열처리를 통한 ZnO:Al 투명전도막의 특성을 최적화하고 Asahi-U형 투명전도막과의 특성 비교를 통하여 실리콘 박막 태양전지용 전면전극으로의 적용 가능성을 조사하였다.

• E2M - 전기 전자와 첨단 소재
• /
• 제7권3호
• /
• pp.243-251
• /
• 1994

ITO(Indium Tin Oxide) film with thickness of 1500.angs. was prepared by an e-beam evaporator onto a glass and a p-type InP wafer (100) LEC grown Zn-doped p=2.3*10$\^$16/cm$\^$-3/), in which the components of ITO used for evaporation source were hot pressed pellets 1 mole% ln$\_$2/O$\_$3/+9 mole% SnO$\_$2/, and evaporated in O$\_$2/ ambient. The optimum conditions to preparation of ITO thin film were the substrate temperature of 350.deg. C, the injected oxygen pressure of 2*10$\^$-4/ torr, and the evaporation speed of 0.2-0.3.angs./sec, respectively. In these optimum conditions, the resistivity and the carrier concentration were 5.3*10$\^$-3/ .ohm.-cm, 6.5*10$\^$20/cm$\^$-3/, and the transmittance was over 80%. From the results of J-V measurements in ITO/p-InP structure solar cells, the higher pressure of injected oxygen, the more open circuit voltage. The efficiency of ITO/p-InP solar cell without the grid line contact, prepared by the optimum evaporation conditions, was 7.19%. By using the grid line contact, the efficiency, the open circuit voltage, the short circuit current density, the fill factor, the series resistance, and the shunt resistance were 8.5%, 0.47V, 29.48 mAcm$\^$-2/ , 61.35%, 3.ohm., and 26.6k.ohm., respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.400-400
• /
• 2012

산화물 반도체는 넓은 에너지갭을 가지고 높은 이동성과 높은 투명성을 가지기 때문에 초고 속 박막 트랜지스터(Thin film transistor; TFT)에 많이 응용되고 있다. 그러나 ZnO 및 $In_2O_3$ 산화물 반도체를 박막트랜지스터에 사용할 경우 소자가 불안정하여 전기적 성질이 저하되고 문턱전압의 이동이 일어난다. TFT에 사용되는 산화물 반도체로는 GaInZnO, ZrInZnO, HfInZnO 및 GaSnZnO의 전기적 특성에 관한 연구가 많이 되었다. 그러나 titanium-indium-zinc-oxide (TIZO) TFT에 대한 연구는 비교적 적게 수행 되었다. 본 연구에서는 TFTs의 안정성을 향상하기 위하여 TFT의 채널로 사용되는 TiInZnO를 형성하는데 간단한 제조 공정과 낮은 비용의 용액 증착방법을 사용하였다. 졸-겔 전해액은 Titanium (IV) isopropoxide $[Ti(OCH(CH_3)_2)_4]$, 0.1 M Zinc acetate dihydrate $[Zn(CH_3COO)_2{\cdot}2H_2O]$ 그리고 indium nitrate hydrate $[In(NO_3)_3{\cdot}xH_2O]$을 2-methoxyethanol의 용액에 합성하였다. $70^{\circ}C$에서 한 시간 동안 혼합 하였다. Ti의 몰 비율은 10%, 20% 및 40% 로 각각 달리하여 제작하였다. $SiO_2$층 위에 2,500 rpm 속도로 25초 동안 스핀 코팅하여 TFT를 제작하였다. TIZO 박막에 대한 X-선 광전자 스펙트럼 관측 결과는 Ti 몰 비율이 증가함에 따라 Ti 2p1/2피크의 세기가 증가함을 보여주었다. TiZO 박막에 Ti 원자를 첨가하면 $O^{2-}$ 이온이 감소하기 때문에 전하의 농도가 변화하였다. 전하 농도의 변화는 TiZO 채널을 사용하여 제작한 TFT의 문턱전압을 양 방향으로 이동 하였으며 off-전류를 감소하였다. TiZO 채널을 사용하여 제작한 TFT의 드레인 전류-게이트 전압 특성은 on/off비율이 $0.21{\times}107$ 만큼 크며 이것은 TFT 소자로서 우수한 성능을 보여주고 있다.

• 한국세라믹학회지
• /
• 제48권1호
• /
• pp.94-98
• /
• 2011

A Sn-doped $In_2O_3$ (ITO) nanowire photoelectrode was produced using a simple metal evaporation method at low synthesis temperature (< $540^{\circ}C$). The nanowire electrodes have large surface area compared with that of flat ITO thin film, and show low electrical resistivity of $5.6{\times}10^{-3}{\Omega}cm$ at room temperature. In order to apply ITO nanowires to the photoelectrodes of dye-sensitized solar cell (DSSC), those surfaces were modified by $TiO_2$ nanoparticles using a chemical bath deposition (CBD) method. The conversion efficiency of the fabricated $TiO_2$/ITO nanostructure-based DSSC was obtained at 1.4%, which was increased value by a factor of 6 than one without ITO nanowires photoelectrode. This result is attributed to the large surface area and superior electrical property of the ITO nanowires photoelectrode, as well as the structural advantages, including short diffusion length of photo-induced electrons, of the fabricated $TiO_2$/ITO nanostructure-based DSSC.

• 전기학회논문지
• /
• 제60권2호
• /
• pp.344-348
• /
• 2011

A layer of $TiO_2$ thin film less than ~200nm in thickness, as a blocking layer, was deposited by 13.56 MHz radio frequency magnetron sputtering method directly onto the anode electrode to be isolated from the electrolyte in dye-sensitized solar cells (DSCs). This is to prevent the electrons from back-transferring from the electrode to the electrolyte ($I^-/{I_3}^-$). The presented DSCs were fabricated with working electrode of F:$SnO_2$(FTO) glass coated with blocking $TiO_2$ layer, dye-attached nanoporous $TiO_2$ layer, gel electrolyte and counter electrode of Pt-deposited FTO glass. The effects of blocking layer were studied with respect to impedance and conversion efficiency of the cells. The, electrochemical impedances of DSCs using this electrode were $R_1$: 13.9, $R_2$: 15.0, $R_3$: 10.9 and $R_h$: $82{\Omega}$. The $R_2$ impedance related by electron movement from nanoporous $TiO_2$ to TCO showed lower than that of normal DSCs. The photo-conversion efficiency of prepared DSCs was 5.97% ($V_{oc}$: 0.75V, $J_{sc}$: 10.5 mA/$cm^2$, ff: 0.75) and approximately 1% higher than general DSCs sample.

• 한국재료학회지
• /
• 제21권9호
• /
• pp.491-496
• /
• 2011

Transparent conducting oxides (TCOs) used in the antireflection layer and current spreading layer of heterojunction solar cells should have excellent optical and electrical properties. Furthermore, TCOs need a high work function over 5.2 eV to prevent the effect of emitter band-bending caused by the difference in work function between emitter and TCOs. Sn-doped $In_2O_3$ (ITO) film is a highly promising material as a TCO due to its excellent optical and electrical properties. However, ITO films have a low work function of about 4.8 eV. This low work function of ITO films leads to deterioration of the conversion efficiency of solar cells. In this work, ITO films with various Zn contents of 0, 6.9, 12.7, 28.8, and 36.6 at.% were fabricated by a co-sputtering method using ITO and AZO targets at room temperature. The optical and electrical properties of Zn-doped ITO thin films were analyzed. Then, silicon heterojunction solar cells with these films were fabricated. The 12.7 at% Zn-doped ITO films show the highest hall mobility of 35.71 $cm^2$/Vsec. With increasing Zn content over 12.7, the hall mobility decreases. Although a small addition of Zn content increased the work function, further addition of Zn content over 12.7 at.% led to decreasing electrical properties because of the decrease in the carrier concentration and hall mobility. Silicon heterojunction solar cells with 12.7 at% Zn-doped ITO thin films showed the highest conversion efficiency of 15.8%.

• 한국표면공학회지
• /
• 제47권5호
• /
• pp.239-243
• /
• 2014

The electrical and optical properties of amorphous In-Tin-Zinc-Oxide(ITZO) deposited at room temperature using rf-magnetron sputtering were investigated. The amorphous ITZO thin films were obtained at the composition of In:Sn:Zn = 6:2:2, 4:3:3, and 2:4:4, but the ITZO (8:1:1) showed a crystalline phase of bixbyite structure of In2O3. The resistivity of ITZO could be controlled by oxygen pressure in the sputtering ambient. The resistivity of post-annealed ITZO thin films exhibited the dependence on the amount of Indium. Optical energy band gap and transmittance increased as the amount of indium in ITZO increased. For the device application with ITZO, the bottom-gated thin-film transistor using ITZO as a active channel layer was fabricated. It showed a threshold voltage of 1.42V and an on/off ratio of $5.63{\times}10^7$ operated with saturation field-effect mobility of $14.2cm^2/V{\cdot}s$.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2015년도 제49회 하계 정기학술대회 초록집
• /
• pp.208.1-208.1
• /
• 2015

최근, 차세대 투명 디스플레이 구동소자로서 산화물 반도체를 이용한 Transparent Amorphous Oxide Semiconductor (TAOS) 기술이 큰 주목을 받고 있다. 산화물 반도체는 기존의 a-Si에 비해 우수한 전기적인 특성과 낮은 구동전압 그리고 넓은 밴드 갭으로 인한 투명성의 장점들이 있다. 그리고 낮은 공정 온도에서도 제작이 가능하기 때문에 유리나 플라스틱과 같은 다양한 기판에서도 박막 증착이 가능하다. 하지만 기존의 furnace를 이용한 열처리 방식은 낮은 온도에서 우수한 전기적인 특성을 내기 어려우며, 공정 시간이 길어지는 단점들이 있다. 따라서 본 연구에서는 산화물 반도체중 In-Ga-Zn-O (IGZO)와 In-Sn-O(ITO)를 각각 채널 층과 게이트 전극으로 이용하였다. 또한 마이크로웨이브 열처리 기술을 이용하여 기존의 열처리 방식에 비해 에너지 전달 효율이 높고 짧은 시간동안 저온 공정이 가능하며 우수한 전기적인 특성을 가지는 투명 박막 트랜지스터를 구현 하였다. 본 실험은 glass 기판위에서 진행되었으며, RF sputter를 이용하여 ITO를 150 nm 증착한 후, photo-lithography 공정을 통하여 하부 게이트 전극을 형성하였다. 이후에 RF sputter를 이용하여 SiO2 와 IGZO 를 각각 300, 50 nm 증착하였고, patterning 과정을 통하여 채널 영역을 형성하였다. 또한 소자의 전기적인 특성 향상을 위해 마이크로웨이브 열처리를 1000 Watt로 2 분간 진행 하였고, 비교를 위하여 기존 방식인 furnace 를 이용하여 N2 분위기에서 $400^{\circ}C$로 30분간 진행한 소자도 병행하였다. 그 결과 마이크로웨이브를 통해 열처리한 소자는 공정 온도가 $100^{\circ}C$ 이하로 낮기 때문에 glass 기판에 영향을 주지 않고 기존 furnace 열처리 한 소자보다 전체적으로 전기적인 특성이 우수한 것을 확인 하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.292-292
• /
• 2012

현재 투명전극은 주로 ITO를 사용하고 있으며, ITO는 인듐산화물(In2O3)과 주석산화물(SnO2)이 9대 1의 비율로 혼합된 화합물로 인듐이 주성분이다. 따라서 ITO 사용량의 증가는 인듐의 수요 증가를 이끌어 2003년 이후 인듐 잉곳의 가격이 급등하였다. LCD에 응용되는 금속재료의 가격추이를 비교해보면, 인듐이 가장 큰 변화를 보이고 있으며, 2005년 인듐 가격은 2002년 대비 1,000% 이상 상승하였다가 2007년 이후 500%p 하락하여 2008년 2월 22일 기준으로 톤당 49만 달러에 거래되고 있다. 같은 기간 동안 알루미늄의 가격은 76.6% 상승하였으며 구리는 394%, 주석은 331% 상승하였다. 이러한 인듐의 가격 상승폭은 동일한 기간 동안 다른 금속 재료와 비해 매우 크며, 단위 질량당 가격도 20배 이상 높은 수준이다. ITO의 주성분인 인듐의 이러한 가격의 급등 및 향후 인듐의 Shortage 예상으로 인해 ITO 대체재 확보의 필요성이 증가되고 있다. 태양광 발전산업에서 현재 주류인 결정질 실리콘 태양전지의 변환효율은 꾸준히 향상되고 있으나, 태양전지의 가격이 매년 서서히 하강되고 있는 실정에서 결정질 실리콘 가격의 상승 등으로 고부가 가치 산업유지에 어려움이 있으며, 생산 원가를 낮출 수 있는 태양전지 제조기술로는 2세대 태양전지로 불리는 박막형이 현재의 대안으로 자리매김하고 있으며, 박막태양전지 산업분야가 현재의 정부정책 지원 없이 자생력을 갖추고 또한 시장 경쟁력을 확보하기 위해서는 박막태양전지 개발과 더불어 저가의 재료개발도 시급한 상황이다. 본 연구에서는 In-line magnetron sputtering system을 사용하여 소다라임 유리기판 위에 박막태양전지용 투명전도성 ZnO(Al) 박막을 제작하였고, 특히 이 박막은 n-형 반도체 특성을 가져야하기 때문에 홀이동도와 개리어농도의 상관관계 및 박막의 두께, 광투과율 특성, 온도 의존성을 조사하였고, 이를 논하고자 한다. (본 연구는 중소기업청의 기술혁신개발사업 연구지원금으로 이루어졌음).