• Journal of Magnetics
• /
• 제14권1호
• /
• pp.7-10
• /
• 2009

In this work, we studied the effects of Sn addition on the ordering temperature of FePt thin film. The coercivity of FePtSn film was about 1000 Oe greater than the coercivity of FePt film for an annealing temperature of $600^{\circ}C$. Therefore, Sn addition was effective in promoting the $L1_0$ ordering and in reducing the ordering temperature of the FePt film. From our X-ray diffraction results, we found that in the as-deposited film, the addition of Sn induced a lattice expansion in disordered FePt thin films. After the annealing process, the excess Sn diffuses out from the ordered FePt thin film because of the difference in the solid solubility of Sn between the disordered and ordered phases. The existence of precipitates of Sn from the FePt lattice was deduced by Curie temperature measurements of the FePt and FePtSn films. Therefore, the key role played by the addition of Sn to the FePt film can be explained by a reduction in the activation energy for the $L1_0$ order-disorder transformation of FePt which originates from the high internal stress in the disordered phase induced by the supersaturated Sn atoms.

• 한국세라믹학회지
• /
• 제34권12호
• /
• pp.1221-1226
• /
• 1997

The effects of sintering atmosphere and dopant addition on the behavior of densification and grain growth of SnO2 ceramics were investigated with consideration of defect chemistry. CoO and Nb2O5 were chosen as dopants, and oxygen and nitrogen were used for controlling of sintering atmospheres. With the decrease of oxygen partial pressure, densification was depressed due to evaporation of SnO2 ceramics. In the case of SnO2 sintering, the addition of CoO, which produced oxygen vacancy in SnO2 ceramics, led to acceleration of densification and grain growth. On the contrary, when Nb2O5 as a dopant producing Sn vacancy was added to SnO2 ceramics, densification and grain growth were simultaneously retarded. As results, it was conformed that diffusion of oxygen ions was rate determinant in densification and grain growth of SnO2 ceramics.

• 열처리공학회지
• /
• 제27권4호
• /
• pp.185-190
• /
• 2014

The influences of small amount of Sn addition on microstructure and creep resistance of AZ91-0.4%Ca alloy have been investigated. The microstructure of the AZ91-0.4%Ca alloy was characterized by ${\alpha}$-(Mg) dendrite cells surrounded by eutectic ${\beta}(Mg_{17}Al_{12})$ and $Al_2Ca$ phases. The 0.5%Sn addition resulted in the formation of rod-shaped CaMgSn particles with the extinction of $Al_2Ca$. The Sn-containing alloy exhibited better creep resistance below $175^{\circ}C$, but the tendency was reversed above $200^{\circ}C$. The reason was discussed in relation to the change in thermal stability of ${\beta}$ phase in response to the Sn addition.

• 한국주조공학회지
• /
• 제37권3호
• /
• pp.63-70
• /
• 2017

In the present study, effects of an addition of Sn on the microstructure and corrosion behavior were investigated in Mg-4%Zn-(0-3)%Sn casting alloys. With an increase in the Sn content, the ${\alpha}-(Mg)$ dendritic cell size was reduced, whereas the total amount of precipitates increased due to the formation of the $Mg_2Sn$ phase. It was found in immersion and electrochemical corrosion tests that the addition of Sn has a detrimental effect on the corrosion resistance of the Mg-4%Zn alloy. Microstructural examinations of the corrosion product and the corroded surface indicated that an accelerated micro-galvanic effect by the $Mg_2Sn-phase$ particles and a less protective corrosion product on the surface were responsible for the increased corrosion rate at a higher Sn content.

• 대한금속재료학회지
• /
• 제48권3호
• /
• pp.248-255
• /
• 2010

The effect of various alloying elements and melt treatment on the microstructural control of Al-Sn metallic bearing alloy was investigated. The thickness of tin film crystallized around primary aluminum decreased with the addition of 5% Cu in Al-Sn alloy, with tin particles being reduced in size by intervening the Ostwald ripening. With the addition of Si in Al-10%Sn alloy, the tin particles were crystallized with eutectic silicon, resulting in uniform distribution of tin particles. With the addition of Cu and Si in Al-Sn alloy, both the tensile strength and yield strength increased, with the increasing rate of yield strength being less than that of tensile strength. Although the Al-10%Sn-7%Si alloy has similar tensile strength compared with Al-10%Sn-5%Cu, the former showed superior abrasion resistance, resulting from preventing the tin particles from movement to the abrasion surface.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1171-1172
• /
• 2006

Addition of 2.0wt%$Dy_2O_3$ or 0.3wt%Sn proved to be very effective in improving the permanent magnetic properties of NdFeNbB magnets. $Dy_2O_3$ additions result in the increase in the Hci and temperature dependence due to formation of (NdDy)-rich phase and grain refinement of $\Phi$ phase. This improvement of the coercivity stability of the magnets from the addition of Sn is attributed to the smoothing effect of the Sn addition at the grain boundaries. The magnetic properties, the temperature dependence and Curie temperature of NdFeNbB with $Dy_2O_3$ and Sn combined addition were found to be considerably improved.

• 한국재료학회지
• /
• 제12권4호
• /
• pp.248-253
• /
• 2002

Effect of Sn addition on the fatigue properties of Al-Cu-Mn cast alloy was investigated by low and high cycle fatigue tests. Fatigue life showed the maximum value of 5450cycles in the Al-Cu-Mn alloy containing 0.10%Sn, but decreased rapidly beyond 0.20% of Sn additions. It was found that the fatigue strength was 132MPa and fatigue ratio was 0.31 in the alloy containing 0.10%Sn. Metallographic observation revealed that the fatigue crack initiated at the surface and propagated along the grain boundary. This propagation path was attributed to the presence of PFZ along the grain boundary. The tensile strength increased from 330MPa in 7he Sn-free Al-Cu-Mn cast alloy to 429MPa in the alloy containing 0.10%Sn. But above 0.20%Sn additions, tensile strength was decreased by the segregation of Sn.

• 한국재료학회지
• /
• 제8권11호
• /
• pp.1011-1019
• /
• 1998

Pb의 환경오염 문제를 발생하지 않는 저농도 Pb 솔도합금을 개발하기 위하여, 새로운 Sn-5%Pb-1.5%Ag-x%In계 합금 조성을 설계하고, 이 합금의 융점, 젖음성, 상분석, 경도, 인장강도, 드로스성을 평가하여, Sn-37%Pb 솔더오 대체 가능성을 타진하였다. Sn-37%Pb 솔도 합금의 Pbdldhs 용출농도는 국제규제치인 3ppm보다 훨씬 적은 0.46ppm이었고, 환경문제를 유발하지 않는 것으로 확인되었다. 이 합금계의 융점은 $183-192^{\circ}C$이고, 응고온도범위도 $5^{\circ}C$내외로 매우 좁았다. 젖음성은 In의 첨가양에 따라 큰 차이가 거의 없었으며, Sn-375Pb와 비슷하였다. 융점 및 젖음성 측면에서 Sn-37%Pb와 대체 가능한 것으로 판단되었다. 경도는 Sn-37%Pb의 약 1.5배이고, 인장강도는 Sn-37%Pb의 것보다 높고, In의 첨가량에 따라 증가하였지만, 연신율은 감소하였다. In이 1% 첨가된 합금에서는 수지 상정 경계에 Ag3Sn과 Pb가 정출되고, 3% 이상에서는 $Ag_3Sn$과 $Ag_3In$ 및 Pb가 정출되었다. 드로스 생성속도는 Sn-37%Pb 합금이 Sn-5%Pb-1.5%Ag 합금보다 빠르고, In을 첨가할수록 느리고 2%의 In을 첨가한 합금은 180분에서도 거의 드로스가 발생하지 않았다.

• 한국재료학회지
• /
• 제12권6호
• /
• pp.436-441
• /
• 2002

Effect of Sn addition on the stress corrosion cracking(SCC) resistance of the Al-Cu-Mn cast alley was investigated by C-ring teat and electrical conductivity measurement, The electrical conductivity and SCC resistance increased by Sn addition. The alley containing 0,10%Sn showed maximum electrical conductivity and the best SCC resistance. At the same composition, the electrical conductivity and SCC resistance increased from peak aged condition to ever aged condition. The PFZ and coarse precipitates along the grain boundary were observed from TEM micrographs. The fracture mode of the alloy was confirmed as intergranular type and showed brittle fracture surface. The SCC mechanism of the alloy was concluded as the anodic dissolution model, The maximum hardness was increased from 130Hv in the Sn-free alloy to 156Hv in the 0.10%Sn added alloy.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.496-499
• /
• 2000

In order to investigate the effect of Ge addition to the Cu Matrix on the microstructure and the critical current density, four kinds of internal tin processed Nb$_3$Sn strands with pure Cu and Cu 0.2, 0.4, 0.6 wt％ Ge alloy were drawn to 0.8 mm diameter. The microstructure and critical current of internal tin processed Nb$_3$Sn wires that were heat treated at temperatures ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$ for 240 h were investigated. The Ge addition to the matrix did not make workability worse. A Ge rich layer in the Cu-Ge matrix suppressed the growth of the Nb$_3$Sn layer and promoted grain coarsening. The greater the Ge content in the matrix, the lower the net Jc result after Nb$_3$Sn reaction heat treatment. There was no significant variation in Jc observed with heat treatment temperature ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$.