• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.696-697
• /
• 2006

This paper presents the densification and microstructure evolution of bilayer components made from 316L stainless steel and M2 High speed steel during co-sintering process. The sintering was carried out at temperatures ranging from $1230-1320^{\circ}C$ in a reducing atmosphere. The addition of boron to 316L was examined in order to increase the densification rate and improve the sintering compatibility between the two layers. It was shown that the mismatch strain bettwen the two layers induces biaxial stresses during sintering, influencing the densification rate. The effect of boron addition was also found to be positive as it improves the bonding between the two layers.

• Journal of Powder Materials
• /
• v.22 no.5
• /
• pp.356-361
• /
• 2015

Fe-30 wt% TiC composite powders are fabricated by in situ reaction synthesis after planetary ball milling of (Fe, $TiH_2$, Carbon) powder mixture. Two sintering methods of a pressureless sintering and a spark-plasma sintering are tested to densify the Fe-30 wt% TiC composite powder compacts. Pressureless sintering is performed at 1100, 1200 and $1300^{\circ}C$ for 1-3 hours in a tube furnace under flowing argon gas atmosphere. Spark-plasma sintering is carried out under the following condition: sintering temperature of $1050^{\circ}C$, soaking time of 10 min, sintering pressure of 50 MPa, heating rate of $50^{\circ}C/min$, and in a vacuum of 0.1 Pa. The curves of shrinkage and its derivative (shrinkage rate) are obtained from the data stored automatically during sintering process. The densification behaviors are investigated from the observation of fracture surface and cross-section of the sintered compacts. The pressureless-sintered powder compacts are not densified even after sintering at $1300^{\circ}C$ for 3 h, which shows a relative denstiy of 66.9%. Spark-plasma sintering at $1050^{\circ}C$ for 10 min exhibits nearly full densification of 99.6% relative density under the sintering pressure of 50 MPa.

• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.13-22
• /
• 2010

The unique features of spark plasma sintering process are the possibilities of a very fast heating rate and a short holding time to obtain fully dense materials. $\beta$-SiC powder with 0, 2, 6, 10 wt% of $\alpha$-SiC particles (seeds) and 4 wt% of Al-B-C (sintering aids) were spark plasma sintered at $1700-1850^{\circ}C$ for 10 min. The heating rate, applied pressure and sintering atmosphere were kept at $100^{\circ}C/min$, 40 MPa and a flowing Ar gas (500 CC/min). Microstructural development of SiC as function of seed content and temperature during spark plasma sintering was investigated quantitatively and statistically using image analysis. Quantitative image analyses on the sintered SiC ceramics were conducted on the grain size, aspect ratio and grain size distribution of SiC. The microstructure of SiC sintered up to $1700^{\circ}C$ consisted of equiaxed grains. In contrast, the growth of large elongated SiC grains in small matrix grains was shown in sintered bodies at $1750^{\circ}C$ and the plate-like grains interlocking microstructure had been developed by increasing sintering temperature. The introduction of $\alpha$-SiC seeds into $\beta$-SiC accelerated the grain growth of elongated grains during sintering, resulting in the plate-like grains interlocking microstructure. In the $\alpha$-SiC seeds added in $\beta$-SiC, the rate of grain growth decreased with $\alpha$-SiC seed content, however, bulk density and aspect ratio of grains in sintered body increased.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.276-277
• /
• 2006

In order to accelerate the sintering of Al-Bronze powder covered with passive oxide film, we focused on the way to add Al-Ca fluoride consisting of $AlF_3$ and $CaF_2$, examined the effect of the $CaF_2$ mixing rate in Al-Ca fluoride, the amount of the added Al-Ca fluoride and the sintering temperature on sintering properties of Al-Bronze powder and considered the mechanism of the sintering acceleration. Al-Bronze powder was sintered most effectively by adding Al-Ca fluoride with the $CaF_2$ mixing rate of 20mass%. If the amount of added fluoride was over 0.05mass% and the sintering temperature was over 1123K, the sintering acceleration of the Al-Bronze powder appears. Regarding the mechanism of the sintering acceleration, it was presumed that $Al_2O_3$ film on the surface of the Al-Bronze particles was removed in the process of the formation of gaseous AlOF by the reaction with $AlF_3$, and the reaction was accelerated further by the presence of the liquid phase which is formed in Al-Ca fluoride.

• Journal of the Korean Ceramic Society
• /
• v.35 no.3
• /
• pp.273-279
• /
• 1998

Unite cell of soid oxide fuel cell (SOFC) that consists of a dense yttria-stabilized zirconia(YSZ) electrolyte a porous nickel-YSZ cermet anode and a porous strontium- doped lanthanum manganate(LSM) cathod was fabricated from using pore former through co-firing technique. Initial sintering shrinkage rates of each layer were identified for fabricating SOFC. Heterogenous sintering was very effective in tailoring shrinkage rate for three layers. The powder tailoring necessary for shrinkage rate matching are as follows ; electrolyte of 60% TZ8YS/ 40% TZ8Y mixture anode of 51wt% NiO/49 wt% (70wt% TZ8YS/30 wt% UT ZrO2) mixture and cathode of 80% LSM/20% UT ZrO2 mixture . The overall sintering shrinkage rate differences of three layers using these compositions were maintained in a few percent.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1995.11a
• /
• pp.25-25
• /
• 1995

Liquid phase sintering of 90W-6Ni-4Mn alloy has been investigated as functions of sintering atmosphere, heating rate, and reduction temperature. The present work accounts for the thermodynamic oxidatiodreduction reactions of constituent powders of W, Ni and Mn. By discounting these reactions, the previous investigations would obtain only the alloy with large pores and the lowered relative sintered density, by the liquid phase sintering under a dry hydrogen atmosphere. the sintering cycle consisted of a rapid heating to reduction temperatures under high purity nitrogen atmosphere, and holding for 4 hours and sintering at $1260^{\circ}C$ for 1 hour under a dry hydrogen gas. The relative density of the sintered alloy increased with increasing heating rate. As the reduction temperature increased, the relative density increased to the lm theotical density at the duction temture above $1150^{\circ}C$. The mimsturcatre of sintered alloys has been analysed by a scanning election microscope. The sintered density was compared with those obtained from the other investigators. It was found that the reduction $1150^{\circ}C$ results in the lowered densification of 90W-6Ni-4Mn alloy. This is caused by the fact that reducing reactions of W and Ni oxides contained in W an Ni powders concomitantly leads to oxidizing reaction of Mn powder the oxidized Mn is hardly reduced at sintering temperature and thereby remains large pores in the alloy. It is concluded that the W-Ni-Mn alloy with full density can be obtained by the precise control of atmosphere, heating rate, and sintering temperature.

• Journal of the Korean Ceramic Society
• /
• v.29 no.4
• /
• pp.305-311
• /
• 1992

As compared with conventional sintering, rapid heating in microwave system could enhance sinterability and final properties of alumina with a very short sintering time. In this study microwave sintering was performed using zirconia brick as a reaction chamber which was positioned in a 2.45 GHz(700 W) multimode microwave cavity. Microwave-sintered alumina showed high density and smaller grain size than conventionally sintered alumina because the ratio of densification rate/grain growth rate was increased by rapid heating.

• Journal of the Korean Ceramic Society
• /
• v.49 no.2
• /
• pp.161-166
• /
• 2012

The temperature-rasing sintering method was used in this study to fabricate the aggregates of uniform pore size and distribution containing reject ash occurred in the thermal power plant. The spheric green aggregates made of reject ash were put into the box furnace of 800~$1000^{\circ}C$, heated with a heating rate of 5~$15^{\circ}C$/min to 1200~$1275^{\circ}C$, sintered for 10 min and then discharged out of the furnace to the room temperature. The input temperature, heating rate and sintering temperature increased the bloating phenomenon of the specimen, and the sintering temperature among them was the most effective factor. The aggregate manufactured at $1275^{\circ}C$ had the specific gravity of about 1.0 and water absorption of 1~2%, and the pores of 500~1,000 ${\mu}m$ were uniformly distributed across the whole specimen. Especially, the aggregates fabricated using the temperature-rasing sintering method in this study showed an excellent bloating properties and uniform microstructure without black core phenomenon which is typical for the bloated ceramics synthesized by direct sintering method.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.295-301
• /
• 2000

The effect of V2O5 addition on the low temperature sintering of Pb(Mn1/3Sb2/3)O3-PZT ceramics, which is known as a prominent material for piezoelectric transformer application was studied, and the densification behavior and piezoelectric characteristics of the samples as a function of heating rate were also examined. V2O5 led the system to liquid phase sintering by forming liquid phase during sintering, which accelerated densification through the particle rearrangement in the early stage of sintering. The liquid phase mostly existed at grain boundaries retarded the evaporation of PbO, while the densification temperature and the weight loss of V2O5-free samples were higher than those of samples with V2O5. Faster heating improved the densification of the samples regardless of V2O5 addition. The low temperature sintering at 100$0^{\circ}C$ was achieved in PMS-PZT ceramics with high density and reasonable dielectric and piezoelectric characteristics. This result revealed optimistic way to the development of multi-layered piezoelectric transformers.

• Journal of Advanced Marine Engineering and Technology
• /
• v.27 no.6
• /
• pp.783-789
• /
• 2003

An experimental method to investigate the fracture strength and fracture toughness for the silicon nitrides sintered at various sintering temperature is established. The erosion rate for these materials in the various concentration of NaOH solution is also investigated. In result, the fracture strength of Si3N4 is decreased with the increase of sintering temperature. On the other hand, the fracture toughness KIC is increased with the increase of sintering temperature. The erosion rate of silicon nitride in the NaOH solution depend largely on the grain size and the concentration of NaOH solution. The erosion rate of silicon nitride sintered at $1800^{\circ}C$ was much higher than that at $1950^{\circ}C$. These results are due to the unique columnar structure of silicon nitride.