• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.247-255
• /
• 2000

Silicon carbide with sialon was prepared by hot pressing and transient liquid-phase sintering, and the effects of sintering atmosphere and starting phases on their microstructural characteristics were investigated. The sintered SiC with Sialon composition(Y2O3, AlN, Si3N4) in argon atmosphere had high sintered density and large aspect ratio. But sintered specimens in nitrogen atmosphere showed low aspect ratio and small grian size, becuase of the retardation of phase transformation and grain growth. Addition of Y-Sialon powder to SiC also retarded the phase transformation to ${\alpha}$-SiC from ${\beta}$-SiC and densification. The SiC specimen prepared from the starting ${\beta}$-SiC powder with Sialon composition(Y2O3, AlN, Si3N4) showed the highest fracture toughness about 6.0 MPa$.$m1/2.

• Journal of Powder Materials
• /
• v.1 no.2
• /
• pp.135-144
• /
• 1994

Silicon carbide powder was prepared from mixtures of Sangdong silica sand and carbon black by SHS (Self propagating High temperature Synthesis) method which utilizes magnesiothermic reduction of silica. In the powder preparation process, the reacted powder was leached by chloric acid to remove the magnesium oxide and was subsequently roasted to remove free carbon. The impurities were mostly eliminated by hot acid treatment. The resultant SiC powder showed the mean particle size of 0.22 ${\mu}{\textrm}{m}$ and the specific surface area of $66.55 m^2/g$. The SiC powder was mixed with 1 wt% of boron and of carbon to increase densification rate. The mixed powder was pressed and sintered pressurelessly at $2100^{\circ}C$ for 30 min in argon gas. The sintered body showed the hardness of $2550 kg{\cdot}f/mm^2$ and the fracture toughness, KIC of $3.47 MN/m^{3/2}$.

• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.413-418
• /
• 1995

The (B.Si)C composite was prepared form the mixture of metal boron, silicon, and carbon powders in Ar atmosphere by Self-propagating High-temperature Synthesis Chemical Furnace. The characterization of synthesized power and sintered body were investigated. The microstructure of sintered body suggested that SiC boundary was made between B4C grains. The most excellent mechanical properties, the relative density of 95% oftheoretical value, 3 point flexural strength of 360MPa, and fracture toughness of 3.6MN/m3/2 could be obtained in 80wt% B4C-20 wt% SiC composite were obtained.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.234-238
• /
• 2008

The efficiency of fiber reinforced CMC(ceramic matrix composite) on the SiC materials have been investigated, in conjunction with the fabrication process by liquid phase sintering and the characterization. LPS-$SiC_f$/SiC composites was studied with the detailed analysis such as the microstructure, sintered density, flexural strength and fracture behavior. The applicability of carbon interfacial layer has been also investigated in the LPS process. Submicron SiC powder with the constant total amount and composition ratio of $Al_2O_3,\;Y_2O_3$ as sintering additives was used in order to promote the performance of the SiC matrix material. LPS-$SiC_f$/SiC composites were fabricated with hot press under the sintering temperature and applied pressure of $1820^{\circ}C$ and 20MPa for 1hr. The typical property of monolithic LPS-SiC materials was compared with LPS-$SiC_f$/SiC composites.

• The Korean Journal of Ceramics
• /
• v.2 no.4
• /
• pp.231-237
• /
• 1996

Mullite ceramics can be sintered by rf plasma sintering to densities as high as 97% compared to the theoretical density of the mullite, while SiC whisker-reinforced mullite matrix ceramic composites were not sintered by plasma sintering. Decomposition of mullite occurs in a superficial regins at the outside surface of the specimen by volatilization of SiO at elevated temperature by plasma. SiC whiskers were destroyed, and the matrix was converted to alumina from SiC-whisker reinforced mullite matrix ceramic composites during the plasma sintering. Accelerated volatilization from the SiC whisker in the mullite prevents sintering. The volatile species are mainly SiC and CO gas species. The effects of plasma on mullite and SiC-whisker reinforced mullite matrix composites are interpreted by thermodynamic simulation of the volatile species in the plasma environment. The thermodynamic results show that the decomposition will not occur during hot pressing.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.40 no.7
• /
• pp.684-689
• /
• 1991

Magnetic properties of sintered Fe-Si-P alloys have been investigated as a function of sintering condition and composition. Sintering was carried in the temperature range from 1100ø C to 1400ø C in vacuum. As the sintering temperature increases, the magnetic properties of specimens were improved mainly due to the easy movement of domain wall because large pores and large grains were formed during the sintering process at high temperature. When sintered at 1400ø C, Fe-2w/o Si-0.5w/o P compact had the best mgnetic properties, but more phosphorus addition degraded magnetic properties. It appears that the degradation was caused by the formation of non-magnetic compounds such as Si P, Fe3P in the compacts with high phosphorus contents.

• Journal of Powder Materials
• /
• v.6 no.4
• /
• pp.286-293
• /
• 1999

This study was to analyse the relationship between process parameters of the sintered composite and plasma nitriding properties with pulsed DC plasma. Fe-40at%$SiC_p$ composites of full density were fabricated by hot pressing at 1100~$1150^{\circ}C$. Sintered Fe-40at%Al and Fe-40at%$Al/SiC_p$ alloys were nitrided under pulsed DC plasma. Excellent surface hardness in the FeAl alloys could be obtained by plasma nitriding. ($H_v$ :100gf, diffusion layer : 1100~$1450kg/mm^2$, matrix : 330~$360kg/mm^2$) The wear resistance of $FeAl/SiC_p$ composites were improved about by 4~6times than FeAl and nitrided $FeAl/SiC_p$ were improved about 2 times than $FeAl/SiC_p$ matrix.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.1027-1032
• /
• 1995

SiC had been widely applied for mechanical sealing as a sealing material. SiC sintering is commonly made of reaction sintering, presureless sintering, and hot isostatic pressing (HIP) sintering. In this investigation, however, clay bonded sintering was used to avoide any complications of the special sintering methods as mentioned above. In order to prevent harmful SiC oxidation in the clay bonded sintering, clay and frit were used to form the SiC oxidation protecting layer and graphite was added to provide high solid lubricity. As a result, the material with 6% clay (clay 5.4% and frit 0.6%) and 2~4% graphite (45 mesh) sintered at 140$0^{\circ}C$ for 3 hours, showed the following physical properties; porosity 6%, static friction coefficient 0.15, kinematic coefficient 0.1,. and specific wear rate 4.8$\times$10-8 $\textrm{mm}^2$kgf-1. On the other hand, the flexural strength was 900kgf/$\textrm{cm}^2$. This tribological characteristic properties were similar to those of the reaction sintered SiC except the flexural strength.

• Journal of the Korean Ceramic Society
• /
• v.32 no.11
• /
• pp.1308-1314
• /
• 1995

Changes in phase and microstructure were investigated in the SiC-AlN ceramics prepared by pressureless sintering using yttrium aluminum garnet (YAG) as a sintering aid at 200$0^{\circ}C$ and 210$0^{\circ}C$. The SiC/AlN ratio made a remarkable difference in densification, phase relations and the morphology of grains. In the AlN-rich composition, major phase was 2H and microstructure was composed of the densified equiaxed grains irrespective of the sintering temperatures. While those sintered at 200$0^{\circ}C$ were porous with major phase being 3C, the rod-like and the equiaxed grains were coexisted when sintered at 210$0^{\circ}C$ in the SiC-rich composition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.118-122
• /
• 2001

The ${\beta}-SiC+TiB_2$ ceramic electroconductive composites were pressureless-sintered and annealed by adding 12wt% $Al_2O_3+Y_2O_3$(6 : 4wt%) powder as a function of sintering temperature. The relative density is over 78.83% of the theoretical density and increased with increasing sintering temperature. The phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H), $TiB_2$, $Al_5Y_2O_{12}$ and $\beta$-SiC(15R). Flexural strength showed the highest of 140 MPa for composites sintered at $1900^{\circ}C$. The vicker's hardness increased with increasing sintering temperature and showed the highest of 4.07 GPa at $1900^{\circ}C$. Owing to YAG, the fracture toughness showed the highest of 4.07 $MPa{\cdot}m^{1/2}$ for composites at $1900^{\circ}C$. The electrical resistivity was measured by the Pauw method from $25^{\circ}C$ to $700^{\circ}C$. The electrical resistivity of the composites showed the PTCR(Positive Temperature Coefficient Resistivity).