• 에너지공학
• /
• 제13권4호
• /
• pp.267-274
• /
• 2004

스크린 메쉬윅 및 소결윅 히트파이프의 열수송 한계를 예측하기 위한 이론적 해석을 수행하였다. 히트파이프의 직경은 8mm이고 작동유체는 물을 사용하였다 250메쉬 조건에서, 각각의 유효 모세관 반경(r$_{c}$ ), 기공률($\varepsilon$), 투과율(K)을 토대로 작동온도와 윅 두께 그러고 경사각에 따른 모세관압력과 열 수송 한계, 열 저항을 분석하였다. 작동온도가 높고 윅 두께가 증가할수록 모세관한계가 높아졌으며, 대체로 소결윅이 스크린적보다 높은 열수송 한계를 나타냈다. 스크린윅의 열저항이 소결윅보다 높았으며, 두 가지 모두 윅 두께가 증가함에 따라 열저항이 선형적으로 상승하였다.

• 한국군사과학기술학회지
• /
• 제21권2호
• /
• pp.195-203
• /
• 2018

Among the techniques of reducing the drag to increase the speed of underwater moving bodies, we studied on the drag reduction method by gas injection. Researches on gas injection method have been paid much attention to reduce the drag of vessels or pipe inner walls. In this study, we used a sintered metal mesh that can uniformly distribute fine bubbles by gas injection method, and applied it to a cylindrical underwater moving body. Using the KRISO medium-sized cavitation tunnel, we measured both the bubble size on the surface of the sintered mesh and the bubble distribution in the boundary layer. Then, drag reduction tests were performed on the cylinder type underwater moving models with cylindrical or round type tail shape. Experiments were carried out based on the presence or absence of tail jet injection. In the experiments, we changed the gas injection amount using the sintered mesh gas injector, and changed flow rate accordingly. As a result of the test, we observed increased bubbles around the body and confirmed the drag reduction as air injection flow rate increased.

• 한국분말재료학회지
• /
• 제17권5호
• /
• pp.365-372
• /
• 2010

The evolution of sinterability, microstructure and mechanical properties for the spark plasma sintered(SPS) Ti from commercial pure titanium(CP-Ti) was studied. The densification of titanium with 200 mesh and 400 mesh pass powder was achieved by SPS at $750{\sim}1100^{\circ}C$ under 10 MPa pressure and the flowing $H_2$+Ar mixed gas atmosphere. The microstructure of Ti sintered up to $800^{\circ}C$ consisted of equiaxed grains. In contrast, the growth of large elongated grains was shown in sintered bodies at $900^{\circ}C$ with the 400 mesh pass powder and the lamella grains microstructure had been developed by increasing sintering temperature. The Vickers hardness of 240~270 HV and biaxial strength of 320~340 MPa were found for the specimen prepared at $950^{\circ}C$.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.611-612
• /
• 2006

In a manufacturing technique of the sintered filter, pressureless sintering method has good permeability, it is not need the binder and lubricant used on compacting process, so it has little contamination and it is easy to control the pore size and shape but the mechanical strength is low relatively and it is difficult that parts of complicate form are manufactured. In the case of manufacturing the filter by press and sintering method, in order to be satisfactory characteristic of un-pressed filter, in this study sintered metal filter fabricated by using 30-40mesh stainless steel 316L powder and additive agents. Porosity and structure of pores, permeability and mechanical strength of the sintered filter were investigated with the variation sintering conditions. Porosity was nearly constant about $60{\sim}70%$, density, permeability and mechanical strength were changed markedly with quantity of additive materials and sintering conditions.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1996년도 추계학술대회논문집
• /
• pp.20-28
• /
• 1996

An Eulerian finite element method for the analysis of steady state rolling/extrusion of sintered powder metals is presented. Initial guess of the porosity distribution in an Eulerian mesh is obtained from the velocity and scaled pressure field computed by the Consistent Penalty finite element formulations-the standard one and the consistent penalty type one-are invoked for the analysis of strain hardening, dilatant viscoplastic deformation of porous metals. Comparisons of the predicted distributions of porosity to those by a Lagrangian finite element method and by experiments reported in the articles prove the effectiveness and validity of the proposed method.

• 한국기계가공학회지
• /
• 제18권8호
• /
• pp.82-90
• /
• 2019

We propose an equivalent model of a sintered metal mesh filter calculated by Ergun's equation and polynomial regression for the CFD analysis of breakaway devices at a hydrogen fueling station. CFD analysis of filters that cause high pressure loss is essential because breakaway devices in high-pressure hydrogen conditions require low pressure loss. A differential pressure experiment with a filter was performed in a low-pressure air condition considering similarities. An equivalent model was developed by deriving the resistance value by the polynomial regression using the experimental results. The results of CFD analysis using the equivalent model show that there was almost no error in the operating condition of the breakaway device compared to the experimental results. Through this work, we believe that the proposed equivalent model of a filter can be applied to the analysis of breakaway devices in hydrogen fueling stations. We will study how to optimize the shape and position of the filter in breakaway devices using the developed equivalent model.

• 한국분말재료학회지
• /
• 제16권4호
• /
• pp.268-274
• /
• 2009

For the purpose of obtaining basic information on the development of lead-free materials, a high density composites (a) W-Cu, (b) W-Sn (c)W-Cu-Sn and (d) W-Cu-Ni were fabricated by the P/M method. The particle size of used metal powders were under 325 mesh, inner size of compaction mould was $\phi8$ mm, and compaction pressure was 400 MPa. A High density composite samples were sintered at a temperature between $140^{\circ}C$ and $1050^{\circ}C$ for 1 hour under Ar atmosphere. The microstructure, phase transformation and physical properties of the sintered samples were investigated. As the results, the highest relative density of 95.86% (10.87 g/$cm^3$) was obtained particularly in the sintered W-Cu-Sn ternary system sample sintered at 450 for 1hr. And, Rockwell hardness (HRB) of 70.0 was obtained in this system.

• 대한금속재료학회지
• /
• 제49권9호
• /
• pp.678-685
• /
• 2011

The aim of this study was to determine the effect of applied pressure and sintering temperature on the microstructure and mechanical properties for spark plasma sintering (SPS) from commercial pure titanium (CP-Ti) powders. Spark plasma sintering is a relatively new sintering technique in powder metallurgy which is capable of sintering metal and ceramic powers quickly to full density at a fairly low temperature due to its unique features. SPS of -200 mesh or -400 mesh CP-Ti powders was carried out in an $Ar+H_2$ mixed gas flowing atmosphere between $650^{\circ}C$ and $750^{\circ}C$ under 10 to 80 MPa pressure. When SPS was carried out at relatively low temperatures ($650^{\circ}C$ to $750^{\circ}C$), the high (>60 MPa) pressure had a marked effect on densification and grain growth suppression. The full density of titanium was achieved at temperatures and pressures above $700^{\circ}C$ and 60 MPa by spark plasma sintering. The crystalline phase and microstructure of titanium sintered up to $700^{\circ}C$ consisted of ${\alpha}$-Ti and equiaxed grains. Vickers hardness ranging from 293 to 362 Hv and strength ranging from 304 to 410 MPa were achieved for spark plasma sintered titanium.

• 한국세라믹학회지
• /
• 제32권9호
• /
• pp.1027-1032
• /
• 1995

SiC had been widely applied for mechanical sealing as a sealing material. SiC sintering is commonly made of reaction sintering, presureless sintering, and hot isostatic pressing (HIP) sintering. In this investigation, however, clay bonded sintering was used to avoide any complications of the special sintering methods as mentioned above. In order to prevent harmful SiC oxidation in the clay bonded sintering, clay and frit were used to form the SiC oxidation protecting layer and graphite was added to provide high solid lubricity. As a result, the material with 6% clay (clay 5.4% and frit 0.6%) and 2~4% graphite (45 mesh) sintered at 140$0^{\circ}C$ for 3 hours, showed the following physical properties; porosity 6%, static friction coefficient 0.15, kinematic coefficient 0.1,. and specific wear rate 4.8$\times$10-8 $\textrm{mm}^2$kgf-1. On the other hand, the flexural strength was 900kgf/$\textrm{cm}^2$. This tribological characteristic properties were similar to those of the reaction sintered SiC except the flexural strength.

• 한국수소및신에너지학회논문집
• /
• 제7권2호
• /
• pp.157-164
• /
• 1996

The AB5-type metal hydride electrodes using $(LM)Ni_{4.49}Co_{0.1}Mn_{0.205}Al_{0.205}$(LM : Lanthaniumrich Mischmetal) alloy powders(${\leq}200$mesh) which were coated with 25wt% copper in an acidic bath were prepared with or without addition of 10wt% PTFE as a binder. Prior to electrochemical measurements, the electrodes were sintered at $40^{\circ}C$ for 1 and 2hrs in vacuum with Mm(mischmetal) and sponge type Ti getters. The properties such as maximum capacity, cycle life and mechanical strength of the negative electrode have been investigated. The surface analysis of the electrode was also obtained before and after charge-discharge cycling using scanning electron microscope(SEM). From the observations of electrochemical behavior, it was found that the sintered electrode shows a lower maximum discharge capacity compared with non-sintered electrode but it shows a better cycle life. For the both electrodes with or without addition of PTFE binder, the values of mechanical strength were obtained, and their values increased with increasing sintering time. However, there is little difference of discharge capacity for both electrodes.