• Journal of Conservation Science
• /
• v.30 no.1
• /
• pp.95-101
• /
• 2014

Silver objects tarnish with black from reaction with sulfurous acid or hydrogen sulfide of atmospheric. Blackening of silver objects results from formation of silver sulfide($Ag_2O$) on the surface. Silver sulfide usually is usually removed by conservation treatment. There are several cleaning methods such as chemical, electrochemical and micro-abrasion cleaning, but all of them consume silver. This study investigated the safe and effective parameter of laser cleaning by test on silver coupons. Laser cleaning is a selective process for the removal of specific substances. At first, laser cleaning applied to plain silver coupons, which were not corroded, to find out the safe range of laser energy density. From results, plain silver coupons were not changed at 1064nm below $4.00J/cm^2$ and at 532nm below $2.39J/cm^2$. The corrosion layer(silver sulfide) of artifical corroded silver coupons was removed at 1064nm with $2.39J/cm^2$ by 5~10 pulses and at 532nm with $1.19J/cm^2$ by 5~10 pulses. The removal thickness of corrosion layer was about 13-25nm per a laser pulse using AES analysis. In addition, laser cleaning tested the tarnish silver rings based on the results of silver coupons. As a result of test, the black surface were clean successfully and gave luster of silver, which showed the application possibility of laser cleaning for silver objects.

• Conservation Science in Museum
• /
• v.1
• /
• pp.15-26
• /
• 1999

More than 200 objects selected for the newly-opened Kimhae National Museum were treated for conservation. The objects which represent ancient Kaya culture, were mainly composed of metallic such as gilt bronze, silver, copper alloy and iron. The corrosion products on gilt bronze and copper alloy objects were preserved or removed according to their stability. Minimum treatment was done for preserving the original state of the objects. For silver objects and iron objects with silver-plate decorations, silver surfaces were revealed after treatment of corrosion products and treatments to prevent corrosion of silver and iron were done emphatically. For iron objects, which were stabilized, the original shape of objects was restored and acrylic coating was applied to prevent further corrosion. For the objects which were being corroded, 2-step de-chloride treatments were undertaken. The first step was immersing the objects in a solution of 0.3M sodium hydroxide and the second was the pressure de-chloride treatment using borax-distilled water. The main purpose of those treatments was to get rid of the causes of corrosion. Besides, conservation treatments for potteries, making of special mounting board for exhibition and amendment of various modeling were done too.

• Journal of Surface Science and Engineering
• /
• v.8 no.1
• /
• pp.1-9
• /
• 1975

The crorosion film of gilt bronz, silver and iron objects, which were excaved from Ancient Tomb of Silla Dynasty, was removed by the electrolytic reduction process. These metallic objects were mainly investigated for microstructure, designs and gilting film etc. Most iron objects might be made by hot forging process. The cold extrusion technique might be used for gold and silver objects, in addition to an amalgam method might be applied for the gilting Au film on Cu-alloy surface. For the gilting on glass surface, first, a Cu alloy was cladded on glass , next, Au-film was obtained on the Cu-ally by the amagum method.

• Journal of Conservation Science
• /
• v.30 no.2
• /
• pp.157-168
• /
• 2014

This study, by selecting 3 kinds(Polish T, H, C) of metal polish being frequently used for silver archival objects treatment at present, a polish having excellent conservative property that minimizes damage of silver surface while effectively removing its yellow discolored layer by each using tool was intended to be discovered by comparing performance of tarnish inhibitor, corrosion inhibitor contained in each polish. As a result of analysis, it was confirmed that specimen that was cleaned with cotton swab and lint-free wipe by using Polish C provides not only uniformed surface expression and minimum damage but also removal function of corrosion layer. In addition, even though tarnish inhibition film should be formed after polish treatment, discolored phenomenon is unable to be prevented but among those polishes, Polish C was represented to be most stable against UV and yellowing and it showed relatively better features than that of Polish H and T in terms of hydrophobic, dispersive property. Through this, it is confirmed that Polish C would show the most excellent performance among polishes being used for conserving silver archival objects.

• Korean Journal of Heritage: History & Science
• /
• v.52 no.3
• /
• pp.160-171
• /
• 2019

The sword with a ring pommel, which was excavated from the first stone chamber of the ancient tombs of Jeongchon Village in Naju, is a sword with a pentagon undecorated ring pommel consisting of a mother sword and two child swords. The sword with an undecorated ring pommel of Jeongchon comprises a ring pommel, a hilt, a knife, and a knife end decoration. This sword was coated with lacquer. The ring pommel is an iron frame covered with silver plate; however the silver tarnished into a light purple due to silver chloride corrosion, and iron corrosion originated from the inside is visible on the surface. Silver chloride corrosion is produced when silver objects are exposed to water, dissolved salts, and dissolved chloride ions when in a buried state. It changes objects into powder, making it difficult to preserve original shapes. The other silver artifacts found in the Jeongchon ancient tombs show similar signs of corrosion. The results of X-ray irradiation and a CT analysis showed that the sword had a ring at the end of the handle, a T-shaped hilt, and was probably connected to the handle end of a knife. If the shape of the mother sword can be inferred from the child swords, the mother sword had a ring pommel, decorations of the handle, covered with silver plate, and a gold ring and a silver line wound around the handle. It is assumed that the ring pommel was connected to the knife by welding because no holes were observed. The end decoration of the knife was made by using an iron plate formed into a shape, half covered by silk, and the other half decorated with silver plate and a gold ring. The sword with an undecorated ring pommel excavated from the ancient tombs of Jeongchon Village comprises the metals of gold, silver, and iron, and includes features of Baekje, Silla, and Gaya, which highlights the influence of surrounding historic sites and various cultures.

• 보존과학연구
• /
• s.20
• /
• pp.81-90
• /
• 1999

We performed the non-destructive analysis of objects excavated at the Tomb of Mich’un-ri in Ch’ung-won. We analysed components using of Energy Dispersive X-Ray Micro-Fluorescence Analyzer. Glass bead inlaid with silver was classified as K2O-CaO-SiO2 type of glass. Purity of silver inlaid in the surface was verified above 97%.All small ear-ring were made by rolling up gold broad to a bronze wick. The composition ratio of Au : Ag has significantly higher 87 : 11 than bigear-ring. As a result of composition analysis of a welded part with big ear-ring, it contained the more Cu, Hg contents and the less Au, Ag contents than the surface of big ear-ring.

• Journal of Conservation Science
• /
• v.27 no.1
• /
• pp.1-11
• /
• 2011

For the silver artifacts in the Koryo Dynasty excavated from Neungnae-ri Ganghwa island, the metallographic section analysis and hardness and chemical analysis were conducted. After making samples in the similar ratio of the composition concentration, the changes of the microstructure were checked according to the working method and temperature. The results show that those silver artifacts are Au-Cu alloys with 2 to 6 % of Cu. From the results it is judged that Cu was artificially alloyed with them to keep the proper hardness and identified that they were gilded by the amalgamation process seeing that mercury was included at the guilt layer. Also the porous texture on the surface of them could be formed at over $400^{\circ}C$, therefore, it is assumed the hot working or heat treatment at over $400^{\circ}C$ were performed. In silver artifacts made by the relief and repousse, they have the similar composition analysis to other 7 artifacts but the hardness is lower than pure silver. Consequently from differences in the hardness, it can be inferred that the low hardness of silver artifacts is concerned with manufacturing techniques.

• Proceedings of the Korea Contents Association Conference
• /
• 2008.05a
• /
• pp.270-273
• /
• 2008

The point of the meaning, this study selects population which is aged over 65 and new silver generation who is aged between 55 to 64. The objects were selected by purposeful sampling method and the 933 objects who participated in leisure sports age over 55 were used for this thesis's analysis. The results of the study were as follow; First, the weekly participation frequency was physical psychological burden, facilities, information technology, interpersonal relations, concern lack, time lack, bear. there was statistically significant difference. Second, the daily workout time was physical psychological burden, facilities, information technology, interpersonal relations, concern lack, time lack, bear. there was statistically significant difference. Third, the participant experience was physical psychological burden, facilities, information technology, interpersonal relations, concern lack, time lack, bear. there was statistically significant difference.

• Journal of Conservation Science
• /
• v.37 no.2
• /
• pp.179-189
• /
• 2021

In this study, the research objects are gilt plated silver-iron nails excavated from the west of the tombs in Neungsan-ri, Buyeo. A gilt plated silver-iron nail was fabricated by combining silver and iron via heating and then gilding amalgam on top of this combination, demonstrating that this ancient artifact that can be replicated using current technology. Since the metal (Au, Ag) surface of these gilt plated artifacts are covered with iron oxide, which slips into the cracks and scratches of the artifacts as well, desalination is essential. Based on the results of the preliminary experiment, the research objects were classified into grades A, B, and C, according to the degree of corrosion and then desalinated using an alkali solution (NaOH, Sodium Sesquicarbonate of 0.1 M) at 60℃. The results demonstrate that the more serious is the degree of corrosion, the more is the amount of Cl^- detected. Further, more Cl^- was released when NaOH was used than when sodium sesquicarbonate was used, for all grades except Grade A. Furthermore, the more serious is the degree of corrosion, the longer is the desalination period and the reaction with NaOH for all grades except Grade A. A comparison of the Fe composition of the surface before and after desalination shows that Fe composition is the use of NaOH resulted in a smaller increase compared with the use of sodium sesquicarbonate, for all grades except Grade B. However, four of the nails were damaged owing to NaOH (Grade B 3ea, Grade C 1ea) during desalination. Thus, Cl^- ions are more stably released when sodium sesquicarbonate is used than when NaOH is used.

• International Journal of Internet, Broadcasting and Communication
• /
• v.7 no.2
• /
• pp.16-27
• /
• 2015

Holography technology which was developed by Dennis Gabor (1900~1979) in 1948 is a technology to record wave planes of actual 3D objects. It is known as the only technology which can express 3D information most perfectly close to human-friendly. Holography technology is widely used in advertisement, architecture and arts as well as science technology areas. Especially, digital holographic print which is an applied area is greatly used in military map, architecture map and cultural asset restoration by printing and reproducing 3D information. Holography is realized by recording and reproducing the amplitude and phase information on high resolution film using coherent light like laser. Recording materials for digital holographic printer are silver halide, photoresist and photopolymer. Because the materials have different diffraction efficiency according to film characteristics of each manufacturer, appropriate guide lines should be suggested through efficiency analysis of each film. This paper suggests appropriate guide lines through the diffraction efficiency measurement of silver halide which is a holographic printer recording medium. And the objective of this study is to suggest appropriate guide lines through diffraction efficiency analysis of Ultimate 08-C and PFG-03C which are commercially used. The experiment was prepared by self-diffraction efficiency system which measures the strength with the defector by penetrating RGB recording medium and concentrating diffracted beams through collimating lens. The experiment showed Geola's PFG-03C which is a silver halide for full color has price/performance advantage in optical hologram recording, but recording angles and reproduction angles are irregular for digital holographic printer recording. Ultimate's Ultimate08-C for full color shows its diffraction efficiency is relatively stable and high according to recording angles and laser wavelength.