• Korean Journal of Materials Research
• /
• v.25 no.10
• /
• pp.537-542
• /
• 2015

One-dimensional (1D) silver nanostructures, which possess the highest conductivity among all room-temperature materials, moderate flexibility and high transmittance, are one of the most promising candidate materials to replace conventional indium tin oxide transparent electrodes. However, the short length and large diameter of 1D silver nanostructures cause a substantial decrease in the optical transparency or an increase in the sheet resistance. In this work, ultra-long silver nanofiber networks were synthesized with a low-cost and scalable electrospinning process, and the diameter of the nanofibers were finetuned to achieve a higher aspect ratio. The decrease in the diameter of the nanofibers resulted in a higher optical transparency at a lower sheet resistance: 87 % at $300{\Omega}/sq$, respectively. It is expected that an electrospun silver nanofiber based transparent electrode can be used as a key component in various optoelectronic applications.

• Macromolecular Research
• /
• v.17 no.9
• /
• pp.688-696
• /
• 2009

In this study, a new class of polyurethane (PU) nanofibers containing silver (Ag) nanoparticles (NPs) was synthesized by electrospinning. A simple method that did not depending on additional foreign chemicals was used to self synthesize the silver NPs in/on PU nanofibers. The synthesis of silver NPs was carried out by exploiting the reduction ability of N,N-dimethylformamide (DMF), which is used mainly to decompose silver nitrate to silver NPs. Typically, a sol-gel consisting of $AgNO_3$/PU was electrospun and aged for one week. Silver NPs were created in/on PU nanofibers. SEM confirmed the well oriented nanofibers and good dispersion of pure silver NPs. TEM indicated that the Ag NPs were 5 to 20 nm in diameter. XRD demonstrated the good crystalline features of silver metal. The mechanical properties of the nanofiber mats showed improvement with increasing silver NPs content. The fixedness of the silver NPs obtained on PU nanofibers was examined by harsh successive washing of the as-prepared mats using a large amount of water. The results confirmed the good stability of the synthesized nanofiber mats. Two model organisms, E. coli and S. typhimurium, were used to check the antimicrobial influence of these nanofiber mats. Subsequently, antimicrobial tests indicated that the prepared nanofibers have a high bactericidal effect. Accordingly, these results highlight the potential use of these nanofiber mats as antimicrobial agents.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.4
• /
• pp.777-781
• /
• 2008

In this work, silver nanoparticles-containing polyacrylonitrile (PAN) solutions in N,N-dimethylformamide (DMF) were electrospun to be webs consisting of nanofibers. The inputted voltage and PAN content in the solution were fixed at 15 kV and 10 wt.% in DMF with 10 cm of tip-to-collector distance (TCD). The PAN/Ag nanofiber webs were stabilized by oxidation at 250 ${^{\circ}C}$ for 2 h in air and carbonized at 1000 ${^{\circ}C}$ for 2 h in $N_2$. The resultant diameter distribution and morphologies of the nanofibers were evaluated by scanning electron microscope analysis. The electrochemical behaviors of the nanofiber webs were also observed by cyclic voltammetry tests. It was found that the presence of silver nanoparticles in carbon nanofiber webs led to the increase of specific capacitance and the decrease of fiber diameters.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.4
• /
• pp.238-243
• /
• 2018

A nanofiber was fabricated with carbon nanotubes for transparent electrodes. It was prepared with a composite solution of bio-molecules polycaprolactone (PCL) and multiwalled carbon nanotubes (MWCNTs) by electrospinning on a glass substrate, following which its electrical characteristics were investigated. The content of MWCNTs was varied during electrospinning, while that of PCL was fixed. Further, a nanometer-thick thin film of silver was deposited on the nanofiber layer using a thermal evaporator to improve the electrical characteristics; the sheet resistance significantly reduced after this deposition. The results showed that this carbon nanotube nanofiber has potential applications in biotechnology and as a flexible transparent display material.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1501-1502
• /
• 2013

• Polymer(Korea)
• /
• v.33 no.5
• /
• pp.429-434
• /
• 2009

In this study, electro spinning conditions for PMMA were studied. Namely, the ratio of DMF and THF and its maximum concentration were examined. Conductivity of the polymer solution containing silver nanoparticles and its effect on fiber diameter were also studied. As the results, the maximum concentration for the electro spinning of PMMA was found at 18 wt%, and the ratio of DMF/THF was 7:3. The diameter of nanofibers obtained was 100-400 nm when the PMMA solution containing 1000 ppm silver was electrospun. It was found, from TEM results, that silver nanoparticles were distributed on the edge of fibers and the resulting nanofiber mats showed a good antibacterial activity.

• Korean Journal of Materials Research
• /
• v.22 no.10
• /
• pp.562-568
• /
• 2012

Metal nanowires can be coated on various substrates to create transparent conducting films that can potentially replace the dominant transparent conductor, indium tin oxide, in displays, solar cells, organic light-emitting diodes, and electrochromic windows. One issue with these metal nanowire based transparent conductive films is that the resistance between the nanowires is still high because of their low aspect ratio. Here, we demonstrate high-performance transparent conductive films with silver nanofiber networks synthesized by a low-cost and scalable electrospinning process followed by two-step sequential thermal treatments. First, the PVP/$AgNO_3$ precursor nanofibers, which have an average diameter of 208 nm and are several thousands of micrometers in length, were synthesized by the electrospinning process. The thermal behavior and the phase and morphology evolution in the thermal treatment processes were systematically investigated to determine the thermal treatment atmosphere and temperature. PVP/$AgNO_3$ nanofibers were transformed stepwise into PVP/Ag and Ag nanofibers by two-step sequential thermal treatments (i.e., $150^{\circ}C$ in $H_2$ for 0.5 h and $300^{\circ}C$ in Ar for 3 h); however, the fibrous shape was perfectly maintained. The silver nanofibers have ultrahigh aspect ratios of up to 10000 and a small average diameter of 142 nm; they also have fused crossing points with ultra-low junction resistances, which result in high transmittance at low sheet resistance.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.6
• /
• pp.1553-1560
• /
• 2021

We have confirmed that optimized transmittance and surface resistance by electrospinning time, also the fabricated transparent electrode composed of silver nanofiber with excellent electrical, optical and mechanical performances is showed applicability to next generation flexible displays such as solar cells, displays, and touch screens. → We have confirmed the optimized transmittance and surface resistance by electrospinning time Also the fabricated transparent electrode composed of silver nanofiber with excellent electrical, optical and mechanical performances showed applicability to next generation flexible displays such as solar cells, displays, and touch screens.

• Applied Chemistry for Engineering
• /
• v.24 no.4
• /
• pp.416-422
• /
• 2013

In order to incorporate silver ions into the alginate, silver-alginate was prepared with aqueous solutions of silver nitrate. In the study, the silver-alginate was prepared by blending with poly vinylpyrrolidone solutions and the electrospinning was performed by using this blend solution. Antibacterial properties of silver-alginate/PVP solutions were estimated for Escherichia coli and Staphylococcus aureus by the colony counting test. Electrospinning conditions of silver-alginate/PVP solution were the tip-to-collector distance of 22 cm, the flow rate of the solution at 0.01 mL/min, and the voltage at 26 kV. The form and size of silver-alginate/PVP nanofibers were estimated by SEM and Image J. The average diameter of the electrospun SA5P15 fibers was 124 nm and showed a narrow diameter distribution. The reduction of bacteria for SA5P15 exhibited 99.9% after 24 h.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.47 no.3
• /
• pp.577-592
• /
• 2023

In this study, nanofiber-based textile sensors were developed for motion detection and monitoring. Poly(vinylidene fluoride) (PVDF) nanofibers containing zinc oxide (ZnO) nanoparticles and silver nanowires (AgNW) were fabricated using electrospinning. PVDF was chosen as a piezoelectric polymer, zinc oxide as a piezoelectric ceramic, and AgNW as a metal to improve electric conductivity. The PVDF/ZnO/AgNW nanocomposite fibers were used to develop a textile sensor, which was then incorporated into an elbow band to develop a wearable smart band. Changes in the output voltage and peak-to-peak voltage (V_p-p) generated by the joint's flexion and extension were investigated using a dummy elbow. The β-phase crystallinity of pure PVDF nanofibers was 58% when analyzed using Fourier transform infrared spectroscopy; however, the β-phase crystallinity increased to 70% in PVDF nanofibers containing ZnO and to 78% in PVDF nanocomposite fibers containing both ZnO and AgNW. The textile sensor's output voltage values varied with joint-bending angle; upon increasing the joint angle from 45° to 90° to 150°, the V_p-p value increased from 0.321 V_p-p to 0.542 V_p-p to 0.660 V_p-p respectively. This suggests that the textile sensor can be used to detect and monitor body movements.