• Earthquakes and Structures
• /
• 제20권4호
• /
• pp.365-375
• /
• 2021

Rammed earth (RE) buildings have existed all over the world for thousands of years, and have gained increasing attention because of its sustainable advantages, however, the shrinkage cracks reduce its bearing capacity and seriously affect its durability and applicability. In this study, the shrinkage cracks test was carried out to investigate the effects of initial water content, proportion of sand and gravel, compaction degree, thickness and the additives (polypropylene fiber, cement and sodium silicate) of shrinkage cracks in RE buildings, ten groups of RE samples were prepared and dried outdoors to crack. Four quantitative parameters of geometrical structure of crack patterns were used to evaluate the development of cracks. The results show that the specimens cracking behavior and the geometrical structure of crack patterns are significantly influenced by these considered factors. The formation of crack can be accelerated with the increase of initial water content and thickness of specimen, while restricted with the increase of the compaction degree and the proportion of sand and gravel. Moreover, the addition of 1% polypropylene fiber, 10% cement and 0.5 volume ratio sodium silicate can significantly restrain the form and development of cracks. In RE construction, these factors should be considered comprehensively to prevent the harm caused by shrinkage cracks. Further works should be carried out to obtain the optimum dosage of the additives, which can benefit the construction of RE buildings in future.

• 한국구조물진단유지관리공학회 논문집
• /
• 제18권5호
• /
• pp.51-58
• /
• 2014

본 연구에서는 철근콘크리트 구조의 FRP를 이용한 보강에서 낮은 내화성능을 개선하기 위한 방안을 찾기 위하여, 보강된 FRP의 외부를 내화보강하는 방법에 대한 내화실험을 실시하였다. 특히 철근콘크리트 부재의 피복에 홈을 형성하여 FRP를 매입하는 보강 즉, NSM 보강을 대상으로 하였다. 실험에서의 주요 변수는 보강방법과 사용 내화재료로서, Perlite계 재료를 표면에 분사하여 보강하는 방법, Calcium silicate계 보드로 표면에 부착하는 방법, 그리고 추가로 홈내부에 Polymer mortar 또는 Calcium silicate조각을 삽입하여 보강하는 방법으로 보강한 뒤 가열로 내부의 온도변화에 따른 열전달을 관찰하였다. 실험결과, Perlite계 내화뿜칠로 표면을 보강하는 경우보다 Calcium Silicate계 내화보드로 표면을 보강하는 방법이 효과적인 것으로 나타났다. 홈 내부의 에폭시가 유리전이온도에 도달할 때의 외부 표면온도 $820^{\circ}C$까지 내화단열성능을 확보할 수 있는 것으로 나타났다.

• Advances in concrete construction
• /
• 제8권1호
• /
• pp.21-31
• /
• 2019

The rich recipe of ultra high performance concrete (UHPC) offers the higher mechanical, durability and dense microstructure property. The variable like cement/sand ratio, amount of supplementary cementitious material, water/binder ratio, amount of fiber etc. alters the UHPC hardened properties to any extent. Therefore, to understand the effects of these variables on the performance of UHPC, inevitably a stage-wise development is required. In the present experimental study, the effect of sand/cement ratio, the addition of finer material (fly ash and quartz powder) and, hybrid fiber on the fresh, compressive and microstructural property of UHPC is evaluated. The experiment is conducted in three phases; the first phase evaluates the flow value and strength attainment of ingredients, the second phase evaluates the efficiency of finer materials (fly ash and quartz powder) to develop the UHPC and the third phase evaluate the effect of hybrid fiber on the flow value and strength of ultra high performance hybrid fiber reinforced concrete (UHP-HFRC). It has been seen that the addition of fly ash improves the flow value and compressive strength of UHPC as compared to quartz powder. Further, the usage of hybrid fiber in fly ash contained matrix decreases the flow value and improves the strength of the UHP-HFRC matrix. The dense interface between matrix and fiber and, a higher amount of calcium silicate hydrate (CSH) in fly ash contained UHP-HFRC is revealed by SEM and XRD respectively. The dense interface (bond between the fiber and the UHPC matrix) and the higher CSH formation are the reason for the improvement in the compressive strength of fly ash based UHP-HFRC. The differential thermal analysis (DTA/TGA) shows the similar type of mass loss pattern, however, the amount of mass loss differs in fly ash and quartz powder contained UHP-HFRC.

• 한국응용과학기술학회지
• /
• 제33권3호
• /
• pp.441-448
• /
• 2016

본 연구는 구리 아연 금속합금의 산화 환원 반응과 합성 알루미늄 실리케이트의 흡착 반응을 이용한 폐수 중 중금속 처리에 관한 연구이다. 극세사 형태로 제조된 구리 아연 금속합금이 수용액 중에서 산화 환원반응에 의해 아연보다 이온화 경향이 작은 중금속은 환원 처리되고, 이온화 된 아연 및 미반응 중금속은 흡착 처리하여 제거하는 연구이다. 극세사 형태로 제조된 금속합금 물질은 표면적이 커서 1회 처리만으로도 반응 평형에 도달하게 하여 효율이 높은 것으로 나타났다. 크롬($Cr^{+3}$)은 redox 반응 1회 처리만으로도 100.0 % 제거 되었으며, 수은은 98.0 %, 주석 92.0 %, 구리는 91.4 % 정도 제거되었다. 카드뮴, 니켈, 납도 각각 40.0 %, 50.0 %, 58.0 %가 제거 되었다. 크롬($Cr^{+3}$)은 아연과 이온화 경향 차이가 거의 없지만 제거 효율이 높은 것으로 나타났는데 이는 3가 크롬은 이온 상태로 존재하면 redox 반응에서 발생한 $OH^-$ 이온과 결합하여 수산화물 침전을 형성하는 것으로 판단된다. Redox 반응 후 증가한 아연 및 미반응 중금속 농도를 알루미늄실리케이트를 1회 통과하여 거의 100.0 % 제거할 수 있었다. 이는 합성 알루미늄 실리케이트의 비표면적이 크고 금속 이온의 흡착능력이 우수한 것으로 나타났으며, 반응 후 알루미늄 이온은 증가하지 않는 것으로 보아 이온 교환이 아닌 흡착으로 아연 및 중금속 이온들을 제거할 수 있는 것으로 나타났다.

• 한국농공학회논문집
• /
• 제62권4호
• /
• pp.23-31
• /
• 2020

Recently, meteorological disasters have been increasing by climate change, excessive rainfall, and landslide. The purpose is to develop new fabric concrete that can prevent and recover from damages because some of areas are vulnerable to meteorological disaster. Specifically, this technology can minimize time and space constraint when repairing the concrete structure and installing a formwork. The structure of fabric concrete is a mixture of fabric concrete and a high-speed hardened cement, Silica sand, wollastonite mineral fiber, fabric material and waterproof PVC fabric. In this study, the ratio of mechanical properties and durability of the fabric concrete mixture was evaluated by deriving the binder: silica sand mix ratio of the fabric concrete mixture and substituting part of the cement amount with wollastonite mineral fiber. Best binder in performance evaluation: Silica sand mix ratio is 6: 4 and the target mechanical performance and durability are the best when over 15% wollastonite binder is replaced by silicate mineral fiber.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.481-486
• /
• 2014

Environmental barrier coatings (EBCs) are used to protect SiC-based ceramics or composites from oxidation and corrosion due to reaction with oxygen and water vapour at high temperatures above $1000^{\circ}C$. Mullite ceramics have been studied for environmental barrier coatings for Si-based ceramics. More recently, rare earth silicate ceramics have been identified as more water vapour-resistant materials than mullite for environmental barrier coatings. In this study, we fabricate mullite and yttrium silicate ceramics by an atmospheric plasma spray coating method using spherical granules fabricated by spray drying. As a result, EBCs with thicknesses in the range of $200-300{\mu}m$ are successfully fabricated without any macroscopic cracks or interfacial delamination. Phase and microstructure analysis are conducted, and the basic mechanical properties, such as hardness and indentation load-displacement curves are evaluated.

• ETRI Journal
• /
• 제42권2호
• /
• pp.282-291
• /
• 2020

The study reports on the design and performance of two air-filled and two partial ethanol-filled photonic crystal fiber (PCF) structures with a tetra core for supercontinuum generation. The PCFs are nonlinear with ultra-flattened zero dispersion. Holes with smaller areas are used to create a tetra-core PCF structure. Ethanol is filled in the holes of smaller area while the larger holes of cladding region are airfilled. Optical properties including dispersion, effective mode area, confinement loss, normalized frequency, and nonlinear coefficient of the designed PCF structures are investigated via full vector finite difference time domain (FDTD) method. A PCF structure with lead silicate as wafer exhibits significantly better results than a PCF structure with silica as wafer. However, both structures report dispersion at a telecommunication wavelength corresponding to 1.55 ㎛. Furthermore, the PCF structure with lead silicate as wafer exhibits a very high nonlinear coefficient corresponding to 1375 W^-1 km^-1 at the same wavelength. This scheme can be used for optical communication systems and in optical devices by exploiting the principle of nonlinearity.

• 한국건설순환자원학회논문집
• /
• 제5권1호
• /
• pp.29-36
• /
• 2017

이 연구의 목적은 알칼리 활성화제의 종류와 양생방법에 따라 나타나는 고로슬래그 기반 섬유보강 복합재료의 압축강도 및 인장거동에 대해 실험적으로 조사하는 것이다. 이를 위하여 알칼리 활성화제 2종류의 배합과 2가지 양생방법을 결정하였고, 밀도 실험, 압축강도 실험과 일축인장 실험을 수행하였다. 실험 결과, 규산나트륨을 사용한 경우 수산화칼슘과 탄산나트륨을 혼합하여 사용한 경우에 비하여 강도, 인장변형성능, 인성 측면에서 우수한 것으로 나타났으며, 활성화제 종류에 따라 양생방법에 의한 영향이 다르게 나타나는 것을 확인하였다.

• The Korean Journal of Ceramics
• /
• 제5권3호
• /
• pp.284-287
• /
• 1999

CuO catalyst-coated alumino-silicate fiber filters were prepared for the simultaneous removal of particulate matter and gaseous contaminants such as NOx and SOx. Hot gas cleaning experiments similar to Shell UOP process other than the catalyst supporting materials were carried out between 300 and $500^{\circ}C$ for the evaluation of the gas removal efficiency of the catalytic filter. Experimental results showed that removel efficiency for $SO_2$ was greater than 99% in the temperature range 450~$500^{\circ}C$ and more than 90% of NO was collected between 350 and $370^{\circ}C$. It was found that the higher the CuO content, the higher the removal efficiency for $SO_2$. Removal efficiency for NO was more affected by the gas cleaning temperature than by the CuO content in the catalyst-filter.

• 한국세라믹학회지
• /
• 제53권4호
• /
• pp.386-392
• /
• 2016

Heat insulation plates of fumed silica were prepared by mixing fumed silica, SiC powder and chopped glass fiber by a high speed mixer followed by pressing of the mixture powder in a stainless steel mold of $100{\times}100mm$. Composition of the plates, particle size of SiC, and type of inorganic binder were varied for observation of their contribution to heat insulation of the plate. The plate was installed on the upper portion of an electric furnace the inside temperature of which was maintained at $400^{\circ}C$ and $600^{\circ}C$, for investigation of heat transfer through the plate from inside of the electric furnace to outside atmosphere. Surface temperatures were measured in real time using a thermographic camera. The particle size of SiC was varied in the range of $1.3{\sim}17.5{\mu}m$ and the insulation was found to be most excellent when SiC of $2.2{\mu}m$ was incorporated. When the size of SiC was smaller or larger than $2.2{\mu}m$, the heat insulation effect was decreased. Inorganic binders of alkali silicate and phosphate were tested and the phosphate was found to maintain the heat insulation property while increasing mechanical properties.