Waste Concrete Powder will be generated during the manufacture of construction waste as recycled aggregate Waste concrete. The main component of the waste concrete Powder is a silica-based composition 51% SiO₂, waste concrete cement-based composition Al₂O₃ 10%, CaO 26% component are contained. The material is silica sand of PHC piles should experiment by replacing the Waste Concrete Powder. The compressive strength results are as follows. 25% when the Silica was replaced 32.5Mpa, when 50% have replaced 43.4Mpa, when 75% have replaced 45.3Mpa was measured. Compared with the non-replaced test sample it appears that the strength increases. Therefore, it is determined that the practical use of the PHC piles by replacing silica via this experiment is possible.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 가을 학술논문 발표대회
• /
• pp.23-24
• /
• 2020

In this study, effect of surface modification of waste glass for fine aggregates on the mechanical properties and alkali silica reaction of mortar was analyzed. As a result, it was confirmed that the incorporation of waste glass fine aggregate decreases the mechanical properties of the mortar and increase the alkali silica reaction expansion. On the other hand, the surface modification of the waste glass fine aggregate is effective in improving this problem. However, unlike green and brown waste glass, it is judged that an additional experiment to determine the cause is necessary for white waste glass where alkali silica reactive expansion occurs extremely.

• Advances in concrete construction
• /
• 제11권3호
• /
• pp.239-253
• /
• 2021

The behavior of concrete containing waste glass as a replacement of cement or aggregate was studied previously in the most of researches, but the present investigation focuses on the recycling of waste glass powder as a substitute for silica fume in high strength concrete (HSC). This endeavor deals with the efficiency of using waste glass powder, as an alternative for silica fume, in the flexural capacity of HSC beam. Thirteen members with dimensions of 0.3 m width, 0.15 m depth and 0.9 m span length were utilized in this work. A comparison study was performed considering HSC members and hybrid beams fabricated by HSC and conventional normal concrete (CC). In addition to the experiments on the influence of glass powder on flexural behavior, numerical analysis was implemented using nonlinear finite element approach to simulate the structural performance of the beams. Same constitutive relationships were selected to model the behavior of HSC with waste glass powder or silica fume to show the matching between the modeling outputs for beams made with these powders. The results showed that the loading capacity and ductility index of the HSC beams with waste glass powder demonstrated enhancing ultimate load and ductility compared with those of HSC specimens with silica fume. The study deduced that the recycled waste glass powder is a good alternative to the pozzolanic powder of silica fume.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 봄 학술논문 발표대회
• /
• pp.195-196
• /
• 2020

This study evaluated the mechanical properties and alkali silica reaction of mortar according to the mixing ratio of waste glass. As a result, as the mixing ratio of the waste glass increased, the compressive and flexible strength of the mortar decreased due to the slip of aggregate, and the alkali-silica reaction(ASR) increased. So, it is considered that research is needed to prevent slip and ASR of the waste glass aggregate in order to use the waste glass as a fine aggregate for concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 춘계 학술논문 발표대회
• /
• pp.13-14
• /
• 2017

In this paper, research for use possibility as silica source of waste concrete powder discharged from direct and indirect carbonation has progressed. For the research, properties on the extruding panel using waste concrete powder with high silica content is evaluated. As the results, compressive strength of specimen is increased 24% compared to control specimen when waste concrete powder replaced 50%, that is discharged from carbonation process, as silica source.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.93-98
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of clear waste glass grading, and by-products(fly ash, blast-furnace slag) and by-products content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum grading can be found. Also, when the by-products are used with waste glass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass.

• 공업화학
• /
• 제10권7호
• /
• pp.1073-1078
• /
• 1999

본 연구의 목적은 소오다회 제조 공장에서 발생하는 폐슬러리를 미세 실리카가 함유된 공장 폐수의 응집제로 이용 가능한 지를 확인하고 이로부터 폐수 처리비용을 절감하고자 수행되었다. 실리카 함유 폐수를 처리하는 경우 단순히 응집 처리하는 기존의 방법과는 달리 수중에 미립자로 존재하는 실리카를 먼저 겔화(gellation)시킨 후 응집 처리하는 방법을 사용한 경우, 적은 양의 폐슬러리를 사용하여도 양호한 처리수질을 얻을 수 있어 소오다회 폐슬러리를 실리카 함유 폐수 처리를 위한 응집제로 재이용이 가능함을 확인할 수 있다. 폐수 중 실리카의 겔화를 위한 적정 pH는 5정도였으며 겔화에 의한 응집 처리시 약품 사용량의 감소와 응집 수 발생되는 슬러지 양을 감소시킬 수 있었다. 소오다회 폐슬러리로 응집시킨 플럭의 탈수성과 침강성 역시 양호한 결과를 얻을 수 있었다.

• 콘크리트학회논문집
• /
• 제13권3호
• /
• pp.213-220
• /
• 2001

콘크리트에 폐유리의 사용은 알칼리 실리카 반응(ASR)의 팽창으로 균열과 강도저하를 일으킬 수 있다. 본 연구에서는 폐유리의 혼입률과 색상(갈색, 녹색) 및 폐유리로 인해 발생되는 ASR팽창을 저감시키기 위해 섬유의 종류(강섬유, 폴리프로필렌섬유)와 섬유혼입률에 따른 ASR팽창과 강도특성을 분석하였다. 연구결과 녹색의 폐유리가 팽창량이 비교적 작기 때문에 갈색의 폐유리보다 더욱 유용하며, ASTNM C 1260의 시험에 있어서 폐유리의 혼입으로 인한 퍼시멈(pessimum)량은 발견되지 않았다. 또한, 폐유리와 함께 섬유의 혼입은 폐유리의 실리카와 시멘트 페이스트의 알칼리 사이의 ASR로 인한 팽창과 강도 저하를 저감시키는데 효과적인 것으로 나타났다. 특히 폐유리 혼입률 20%에 대해서 강섬유를 1.5vol.% 혼입하였을 경우 팽창은 40%까지 감소하였으며 휨강도는 폐유리만을 혼입한 것(8$0^{\circ}C$ $H_2O$ 양생)에 비해 110%의 강도발현을 나타내었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 가을 학술논문 발표대회
• /
• pp.31-32
• /
• 2020

This study measured the mechanical performance and residual strength of high strength/normal strength mortar mixed with waste glass fine aggregate after alkali-silica reaction and alkali-silica reaction. As a result, the effect of improving the slip phenomenon of the waste glass fine aggregate in the high-strength mortar was not significant, but rather the amount of ASR was increased.

• International Journal of Concrete Structures and Materials
• /
• 제18권2E호
• /
• pp.125-132
• /
• 2006

Waste glass has been increasingly used in industrial applications. One shortcoming in the utilization of waste glass for concrete production is that it can cause the concrete to be weakened and cracked due to its expansion by alkali-silica reaction(ASR). This study analyzed the ASR expansion and strength properties of concrete in terms of waste glass color(amber and emerald-green), and industrial by-products(ground granulated blast-furnace slag, fly ash). Specifically, the role of industrial by-products content in reducing the ASR expansion caused by waste glass was analyzed in detail. In addition, the feasibility of using ground glass for its pozzolanic property was also analyzed. The research result revealed that the pessimum size for waste glass was $2.5{\sim}1.2mm$ regardless of the color of waste glass. Moreover, it was found that the smaller the waste glass is than the size of $2.5{\sim}1.2mm$, the less expansion of ASR was. Additionally, the use of waste glass in combination with industrial by-products had an effect of reducing the expansion and strength loss caused by ASR between the alkali in the cement paste and the silica in the waste glass. Finally, ground glass less than 0.075 mm was deemed to be applicable as a pozzolanic material.