• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.11a
• /
• pp.9-10
• /
• 2015

Waste Concrete Powder will be generated during the manufacture of construction waste as recycled aggregate Waste concrete. The main component of the waste concrete Powder is a silica-based composition 51% SiO₂, waste concrete cement-based composition Al₂O₃ 10%, CaO 26% component are contained. The material is silica sand of PHC piles should experiment by replacing the Waste Concrete Powder. The compressive strength results are as follows. 25% when the Silica was replaced 32.5Mpa, when 50% have replaced 43.4Mpa, when 75% have replaced 45.3Mpa was measured. Compared with the non-replaced test sample it appears that the strength increases. Therefore, it is determined that the practical use of the PHC piles by replacing silica via this experiment is possible.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.23-24
• /
• 2020

In this study, effect of surface modification of waste glass for fine aggregates on the mechanical properties and alkali silica reaction of mortar was analyzed. As a result, it was confirmed that the incorporation of waste glass fine aggregate decreases the mechanical properties of the mortar and increase the alkali silica reaction expansion. On the other hand, the surface modification of the waste glass fine aggregate is effective in improving this problem. However, unlike green and brown waste glass, it is judged that an additional experiment to determine the cause is necessary for white waste glass where alkali silica reactive expansion occurs extremely.

• Advances in concrete construction
• /
• v.11 no.3
• /
• pp.239-253
• /
• 2021

The behavior of concrete containing waste glass as a replacement of cement or aggregate was studied previously in the most of researches, but the present investigation focuses on the recycling of waste glass powder as a substitute for silica fume in high strength concrete (HSC). This endeavor deals with the efficiency of using waste glass powder, as an alternative for silica fume, in the flexural capacity of HSC beam. Thirteen members with dimensions of 0.3 m width, 0.15 m depth and 0.9 m span length were utilized in this work. A comparison study was performed considering HSC members and hybrid beams fabricated by HSC and conventional normal concrete (CC). In addition to the experiments on the influence of glass powder on flexural behavior, numerical analysis was implemented using nonlinear finite element approach to simulate the structural performance of the beams. Same constitutive relationships were selected to model the behavior of HSC with waste glass powder or silica fume to show the matching between the modeling outputs for beams made with these powders. The results showed that the loading capacity and ductility index of the HSC beams with waste glass powder demonstrated enhancing ultimate load and ductility compared with those of HSC specimens with silica fume. The study deduced that the recycled waste glass powder is a good alternative to the pozzolanic powder of silica fume.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.195-196
• /
• 2020

This study evaluated the mechanical properties and alkali silica reaction of mortar according to the mixing ratio of waste glass. As a result, as the mixing ratio of the waste glass increased, the compressive and flexible strength of the mortar decreased due to the slip of aggregate, and the alkali-silica reaction(ASR) increased. So, it is considered that research is needed to prevent slip and ASR of the waste glass aggregate in order to use the waste glass as a fine aggregate for concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.13-14
• /
• 2017

In this paper, research for use possibility as silica source of waste concrete powder discharged from direct and indirect carbonation has progressed. For the research, properties on the extruding panel using waste concrete powder with high silica content is evaluated. As the results, compressive strength of specimen is increased 24% compared to control specimen when waste concrete powder replaced 50%, that is discharged from carbonation process, as silica source.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.93-98
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of clear waste glass grading, and by-products(fly ash, blast-furnace slag) and by-products content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum grading can be found. Also, when the by-products are used with waste glass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass.

• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.1073-1078
• /
• 1999

The objectives of this study are to examine the applicability of waste slurry from soda ash manufacturing industries as a coagulant for the treatment of wastewater containing fine silica particles, and to reduce the cost of wastewater treatment containing silica. Acceptable water quality can be obtained with a little dosing of waste slurry by gelation before the coagulation process so it could be concluded that the waste slurry from soda ash can be used as a coagulant. Based on the results of experiments, the optimum pH of gelation for silica in wastewater was around five and the treatment process with the gelation of silica could reduce the chemical dosage and waste sludge after coagulation. Dewatering and settling characteristics of the floc after coagulation with the waste slurry are better than those of the floc after coagulation with the lime milk only.

• Journal of the Korea Concrete Institute
• /
• v.13 no.3
• /
• pp.213-220
• /
• 2001

Incorporation of wastes glass aggregate in mortar may cause crack and this may result in the strength reduction due to alkali-silica reaction(ASR) and expansion. The purposes of this study were to investigate the properties of alkali-silica expansion and strength loss through a series of experiments which had a main experimental variables such as waste glass aggregate contents, glass colors, fiber types, and fiber contents. The steel fibers and polypropylene fibers were used for constraining the ASR expansion and mortar cracking. From the result, green waste glass was more suitable than brown one because of low expansion. And in this accelerated ASTM C 1260 test of waste glass, pessimum content can not be found. Also, when used the fibers with waste glass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass. Specially, adding 1.5 vol.% of steel fiber to 20% of waste glass, the expansion ratio was reduced by 40% and flexural strength was developed by up to 110% comparing with only waste glass(80$\^{C}$ H$_2$O curing).

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.31-32
• /
• 2020

This study measured the mechanical performance and residual strength of high strength/normal strength mortar mixed with waste glass fine aggregate after alkali-silica reaction and alkali-silica reaction. As a result, the effect of improving the slip phenomenon of the waste glass fine aggregate in the high-strength mortar was not significant, but rather the amount of ASR was increased.

• International Journal of Concrete Structures and Materials
• /
• v.18 no.2E
• /
• pp.125-132
• /
• 2006

Waste glass has been increasingly used in industrial applications. One shortcoming in the utilization of waste glass for concrete production is that it can cause the concrete to be weakened and cracked due to its expansion by alkali-silica reaction(ASR). This study analyzed the ASR expansion and strength properties of concrete in terms of waste glass color(amber and emerald-green), and industrial by-products(ground granulated blast-furnace slag, fly ash). Specifically, the role of industrial by-products content in reducing the ASR expansion caused by waste glass was analyzed in detail. In addition, the feasibility of using ground glass for its pozzolanic property was also analyzed. The research result revealed that the pessimum size for waste glass was $2.5{\sim}1.2mm$ regardless of the color of waste glass. Moreover, it was found that the smaller the waste glass is than the size of $2.5{\sim}1.2mm$, the less expansion of ASR was. Additionally, the use of waste glass in combination with industrial by-products had an effect of reducing the expansion and strength loss caused by ASR between the alkali in the cement paste and the silica in the waste glass. Finally, ground glass less than 0.075 mm was deemed to be applicable as a pozzolanic material.