• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.5
• /
• pp.218-224
• /
• 2015

Recently, removing methods of red tide has been attempted by filtering the organisms using the ceramic porous bodies. However, the marine biofouling could be developed on the surfaces of porous ceramic body after use for more than one month, and it might decrease the function of the specimen. In this paper, a method of inhibiting marine biofouling by changing the physical properties or surface-modification of ceramic porous body was studied. After experiment with six different ceramic porous bodies, it was found that the specimen of lower porosity and water absorption showed the least amount of biofouling. In addition, by increasing the surface roughness with silica particles bonded to the surface of specimen, the amount of biofouling caused by large marine life such as barnacle and mussel could be decreased. On the other hand, when the surface of specimen was coated and fused by glass powder, the amount of biofouling was rather increased. This might be due to eluted inorganic ions from the glass which can promote the growth of the microorganism. In conclusion, the environmental-friendly methods to reduce the amount of marine biofouling, such as controlling the physical properties and the surface roughness of the porous ceramics, can be possible without the use of dangerous substances. So it is expected for the results obtained to be applicable to a marine structure.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.5
• /
• pp.94-104
• /
• 2013

Experiments were divided into two parts; one part is to understand the basic properties of high flowable VA/VeoVa-modified cement mortar with different polymer cement ratio (P/C) and the weight ratio of fine aggregate to cement (C:F) and the other part is to investigate the effect of surface water spread on the concrete substrate on adhesion in tension. To understand the basic performance, the specimens were prepared with proportionally mixing VA/VeoVa redispersible powder, ordinary portland cement, silica sand, superplasticizer and viscosity enhancing agent. Here, P/C were 10, 20, 30, 50 and 75% and C:F were 1:1 and 1:3. As the change of P/C and C:F unit weight, flow test, crack resistance and adhesion in tension were measured. Three specimens with good adhesion properties were selected among specimens with different P/C and C:F. The effect of surface water evenly sprayed on concrete substrate on adhesive strength is investigated. The results show that surface water on concrete substrate increases the adhesion in tension of high flowable VA/VeoVa-modified cement mortar and additionally improves the flowability compared to the non-sprayed case.

• Journal of Conservation Science
• /
• v.34 no.1
• /
• pp.1-9
• /
• 2018

The analysis of ancient DNA extracted from archaeological bones has become an important research tool in palaeogenetics and anthropology. Eight human skeletal remains of the Joseon dynasty, excavated from Hwamyeong-dong, were used in this study. DNA was extracted from bone powder using a silica-based protocol. The isolated DNA was analyzed by the sequencing variation of hyper-variable region of the mitochondrial DNA. In the present study, 3 human remains were identified into mtDNA haplogroups including the A 5a, D4a, and M4"67+16311 groups, using HaploGrep 2 program. The identified haplotypes of the 3 samples have been confirmed that the specimens in the tombs were not related by the maternal line. This is the first analysis of human skeletal remains of the Joseon dynasty excavated in Busan. Date from the analysis of human remains from the Joseon dynasty are considered as the basis for understanding the genetic relationship between modern and ancient humans of the Korean peninsula.

• Clean Technology
• /
• v.25 no.2
• /
• pp.101-106
• /
• 2019

The aim of this study is to investigate the feasibility of an Ni-SA catalyst, which was prepared from nickel, kieselguhr, and alumina, for the hydrogenation of triglyceride in a bench-scale reactor. Ni-SA powders were prepared by precipitating nickel precursors on a silica and alumina support. The powder was reduced in a hydrogen flow, mixed with a saturated palm oil, and then cooled to prepare an Ni-SA catalyst tablet. The sizes of NiO crystals of a commercial Pricat catalyst and the Ni-SA catalyst prepared in this study were $35{\AA}$ and $38{\AA}$, respectively. The pore volume and pore size of the Ni-SA catalyst was much larger than the pore volume and pore size of the Pricat catalyst. In addition, the average particle size of the Ni-SA catalyst was much smaller than that of the Pricat catalyst. The triglyceride hydrogenation reaction was carried out in a semi-batch reactor using catalysts impregnated with oil and molded into tablets. It was found that the Ni-SA catalyst was superior to the commercial Pricat catalyst in triglyceride hydrogenation, which could be ascribed to the raw material and the products being less influenced by the diffusion resistance in the pores of the Ni-SA catalyst. The Ni-SA catalyst prepared in this study has the potential to replace the Pricat catalyst as a catalyst for use in the commercial process for hydrogenation of triglyceride.

• Clean Technology
• /
• v.26 no.4
• /
• pp.263-269
• /
• 2020

Zeolite was synthesized hydrothermally using the water-treatment sludge, and the effects of various synthesis parameters like reaction temperature, reaction time, and Na2O/SiO2 molar ratio on the crystallization of zeolite were investigated. Crystal structure, physical property, and thermal stability of zeolite crystals were characterized by X-ray powder diffraction, FTIR spectroscopy, BET nitrogen adsorption, and TGA measurements. The removal efficiencies of nitrogen in ammonia, heavy metal ions, and TOC were calculated to evaluate zeolite's adsorption capacity. The primary chemical composition of water-treatment sludge was 28.79% Al2O3 and 27.06% SiO2. The zeolites were synthesized by merely employing the water-treatment sludge as silica and alumina sources without additional chemicals. Zeolite crystals synthesized through the water-treatment sludge were confirmed as an A-type zeolite structure. Zeolite A had the highest crystallinity obtained from a gel with the molar composition 2.1Na2O-Al2O3-1.6SiO2-65H2O after 5 h at a temperature of 90 ℃. The specific surface area of zeolite obtained was 55 ㎡ g-1, which was higher than commercial zeolite A. The removal efficiency of nitrogen in ammonia was 68% after 3 h of reaction time, while the removal efficiencies of Pb2+ and Cd2+ ions were 99.1% and 99.3%, respectively. These results indicate active ion exchange between Pb2+ or Cd2+ ion and Na+ ion in the zeolite framework. The adsorption experiments on the different zeolite addition conditions were performed for 3 h with 300 ppm humic acid. Based on the results, TOC's highest efficiency was 83% when 5 g of zeolite was added.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.44 no.3
• /
• pp.211-218
• /
• 2018

Instant face lifting cosmetics contain various film forming agents for stretching the wrinkles on the skin surface. But, most of the film-forming polymers have sticky feels. And they are easily scrubbed out when skin is rubbed on. In this study, we focused on the influence of sodium silicate that has rapid film forming effect on skin surface and immediate wrinkle reducing effect. Sodium silicate, also known as water glass or soluble glass, is a compound containing sodium oxide and silica. Sodium silicate is a white powder that is readily soluble in water, producing an alkaline solution. Sodium silicate is stable in neutral and alkaline solutions. The sodium silicate solution hardens by drying in air and rapidly forms a thin film. When the solution is applied to the skin, the fine membrane coating is formed by water evaporation and ionic bond re-formation. It also makes the strong siloxane (Si-O) bonding on the skin surface. When these fixation properties are applied to cosmetics, they can give remarkable skin tightening effect. The sodium silicate solution can provide the lifting effect by forming a film on skin at a proper concentration. But, skin irritation may be caused with too high concentration of sodium silicate. We studied a desirable range of the sodium silicate concentration and combination with other fixatives for skin care formulation that has no sticky feels and no scrubbing out phenomenon. Immediate lifting gel was developed by using sodium silicate and various thickening systems. Among of the various thickeners, aluminum magnesium silicate showed the best compatibility with sodium silicate for rapid lifting effect. This instant physical lifting gel was confirmed as a low stimulating formula by skin clinical test.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.30 no.2
• /
• pp.181-187
• /
• 2004

Preparations of mesoporous materials using various templates and their applicability have been intensively investigated for many years. We studied on synthesizing mesoporous Ti02 with pores in which sensitive compounds having weak physico-chemical properties such as thermal or UV irradiation and low solubility in solvent are trapped. Prior to trapping OMC in the pores of mesoporous titania, OMC was nano-emulsified in O/W system using Lecithin. Thereafter the OMC was trapped in the pores of mesoporous titania using sol-gel method. Main focus of this work is to prepare OMC-trapped mesoporous titania and to trace the stability and solubility of nano-emulsified OMC in the pores of mesoporous titania, and compared with that of mesoporous silica. OMC-trapped mesoporous Inorganic-Organic hybrid titania showed higher factors in sun protecting and a skin penetration phenomenon was reduced.