• Membrane Journal
• /
• v.17 no.1
• /
• pp.44-53
• /
• 2007

The primary objective of this study is to increase the extent of water flux and fouling resistance of nano-filtration or reverse osmosis membranes. This study was performed to investigate the effect of surface characteristics of silane coated membranes on modified fouling index. Commercial polyamide composite RO membrane (RE1812-LP) and NF membrane (ESNA4040-LF) were treated with silane coupling agents in ethanol at five different concentrations. The silane coupling reagent, aminopropylmethoxydiethoxysilane, contains one aminoalkyl and three alkoxy groups. The hydrophilic effect of aminoalkyl group of APMDES on the permeability and fouling resistance of the modified membrane was examined. The surfaces of the modified membranes were characterized by FE-SEM, contact angle analyzer, and zeta potentiometer in order to confirm successful sol-gel methods. The modified NF membranes showed significantly enhanced water flux and fouling resistance without a decrease in salt rejection in divalent ionic feed solution.

• Proceedings of the Korean Fiber Society Conference
• /
• 1995.10a
• /
• pp.127-127
• /
• 1995

• Applied Chemistry for Engineering
• /
• v.9 no.4
• /
• pp.608-613
• /
• 1998

The purpose of this experiment was the physical properties of rubber compounds with DPCB and pure carbon black. Si-O peak in the silcia surface was observed at the range of wavenumber from 1,100 to 1,200 in the DPCB by FT-IR analysis. Cure rate of rubber compounds containing DPCB and organic silane coupling agent were (Si69) delayed compared with those containing pure carbon black. 300% modulus and interaction coefficient of DPCB with silane coupling agent were higher than those of pure carbon black and PICO weight loss amount showed constant value. It was found that $0^{\circ}C$ tan$\delta$ of rubber compounds with DPCB was larger than those of pure carbon black at 2.0% silane coupling agent based on 50 phr DPCB and $60^{\circ}C$ tan$\delta$ of rubber compounds with DPCB decreased as increasing the usage coupling agent. Consequently, it is postulated that DPCB is strong candidate material for lowering rolling resistance under constant abrasion resistance.

• Journal of the Korean Applied Science and Technology
• /
• v.27 no.3
• /
• pp.300-309
• /
• 2010

Melamincyanurate(MC), as an non halogen flame retardant are used as the polymer and plastic materials. In this study, melamine and cyanuric acid were used for the synthesis of MC. The optimum condition of synthetic MC were controlled by different molar ratio of melamine to cyanuric acid. MC was modified by coupling reaction with four different agents. The influences of modified MC were based on the coupling agent types. Preparation methods are available to offer the prospect of improved morphology control deposit stability in polyol. The results reveal that glycidoxypropyltrimethoxysilane(GDS) has the best storage stability. The best properties were obtained with melamine and cyanuric acid from 1:1 molar ratio. Modification of MC through coupling agent can efficiently enhanced the deposit stability in polyol up to 30 %.

• Polymer(Korea)
• /
• v.25 no.6
• /
• pp.774-781
• /
• 2001

In order to reuse the waste matters, the polyester hybrid composites were fabricated with the waste stone (WSP) and waste tire (WTC). Before mixing, the waste fillers were treated with the silane coupling agent [${\gamma}$-methacryloxy propyl trimethoxy silane(${\gamma}$-MPS)] for enhancing the dispersion of the fillers and interfacial bonding with polymer matrix. Mechanical properties and morphologies of the resulted hybrid composites were investigated with the filler content. The hybrid composites containing surface treated fillers have high initial thermal decomposition temperature and low weight loss compared to the untreated one. The highest mechanical properties of composites were obtained with the ${\gamma}$-MPS (2 wt%) treated fillers. The porosity of composite increased with the content of organic filler which can be reduced by the silane surface treatment of fillers. The pore size distribution of the composites varied with the waste filler content.

• Membrane Journal
• /
• v.16 no.2
• /
• pp.106-114
• /
• 2006

This study is concerned with preparation of chlorine resistant (CR) thin layer composite (TFC) membranes. The novel method for making CR membranes from commercially available RO membranes is based on sol-gel condensation of trialkoxyalkylsilane derivatives. The silane coupling agents used in this study have different number of alkyl carbon chain group (methyltriethoxysilane; METES and octyltriethoxysilane; OCTES). The OCTES composite membranes have a significant tolerance to chlorine compared to commercial polyamide RO membrane or METES composite membranes. The surface properties of membranes were examined to explain a significant difference of chlorine tolerance between OCTES composite membrane and the other two membranes. In this study, we tried several surface analyses to explain difference of chlorine tolerance. The element composition results of surface analysis by EDX confirmed that both silane fixed on polyamide firmly, The surface roughness and contact angle results showed long chain alkyl group of OCTES enhancing hydrophobicity considerably than METES. The hydrophobicity plays an important role in chlorine resistance of membrane.

• Membrane Journal
• /
• v.15 no.4
• /
• pp.320-329
• /
• 2005

Polyamide membrane degradation by chlorine has been studied to improve membrane durability. In this study, it was found that the salt rejection was reduced rapidly and flux of the membrane was increased slowly far membrane treated under chlorine condition. In order to improve resistance to chlorine of the polyamide reverse osmosis membrane, fluorine-containing silane coupling agent (FSCA) was introduced to surface modification. Surface properties and chlorine resistance of silane modified membrane were compared with virgin membrane. It was found that the surface of silane modified membrane has dense structure according to FSCA concentration increasing. The results of surface analysis suggest that FSCA retrieved a severe change in the hydrophobicity and surface roughness. In addition, it appears that FSCA can enhance chlorine resistance due to the interaction of such substance with free radical chlorine.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.105-108
• /
• 2002

Polyimide-epoxysilane (coupling agent) composites were reacted with oligomeric PDMS, a condensation product of difunctional silane, by a sol-gel process and were then dried into films. And then, the surface, mechanical, and electric properties were measured. The study showed that PDMS existed in the polyimlde matrix by the use of FT-IR. In the mechanical properties, the maximum elongation and toughness was increased in the polyimide with silane-groups. But the maximum tensile strength was slightly decreased. And the intensive dispersion of the silane-groups on the surface of polyimide was ascertained through XPS measurement. In the electric properties, AC break down voltage was increased by increasing the amount of difunctional silane. This experiment showed that PDMS added polyimide had better mechanical and electric properties than classical materials.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.26-29
• /
• 2002

Polyimide-epoxysilane (coupling agent) composites were reacted with oligomeric PDMS, a condensation product of difunctional silane, by a sol-gel process and were then dried into films. And then, the surface, mechanical, and electric properties were measured. The study showed that PDMS existed in the polymide matrix by the use of FT-IR. In the mechanical properties, the maximum elongation and toughness was increased in the polyimide with silane-groups. But the maximum tensile strength was slightly decreased. And the intensive dispersion of the silane-groups on the surface of polyimide was ascertained through XPS measurement. In the electric properties. AC break down voltage was increased by increasing the amount of difunctional silane. This experiment showed that PDMS added polyimide had better mechanical and electric properties than classical materials.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.61 no.10
• /
• pp.1454-1460
• /
• 2012

In order to develop an new electric insulation material for heavy electric equipments, epoxy/micro/nano composite (EMNC) was prepared by mixing micro-silica with nano layered silicate, where the nano layered silicate was synthesized by our electric field dispersion method, EMNSC was prepared by treating the EMNC with a silane coupling agent. Thermal properties such as glass transition temperature (Tg) and thermal expansion coefficient, and DMA characteristics were studied, and mechanicla properties such as tensile and flexural tests were performed. AC electrical insulation strength was also tested. All properties of EMNSC were modified by treating EMNC with silane coupling agent and it was confirmed that our new developed composites could be used in the heavy electric equipments.