We have investigated a glass-forming region of $V_2O_5-P_2O_5-ZnO$ glass and the effects of the addition of modifier oxides ($B_2O_3$) to the glass systems as a sealing material to improve the adhesion between the glass frits and a soda lime substrate. Thermal properties and coefficient of thermal expansion were measured using a differential scanning calorimetry, a dilatometer and a hot stage microscopy. Structural changes and interfacial reactions between the glass substrate and the glass frit after sintering (at $400^{\circ}C$ for 1 h) were measured by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and scanning electron microscope. The results showed that the adhesion strength increases as the content of $B_2O_3$ at 5 mol% increases because of changes in the structural properties. It seems that the glass structures change with $B_2O_3$, and the $Si^{4+}$ ions from the substrate are diffused to the sealing glass. From these results, we could understand the mechanism of strengthening of the adhesion of soda lime silica substrate by ion-diffusion from the substrate to the glass.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.258-258
• /
• 2016

최근 디스플레이 산업의 발전에 따라 고성능 디스플레이가 요구되며, 디스플레이의 백플레인 (backplane) TFT (thin film transistor) 구동속도를 증가시키기 위한 연구가 활발히 진행되고 있다. 트랜지스터의 구동속도를 증가시키기 위해 높은 이동도는 중요한 요소 중 하나이다. 그러나, 기존 백플레인 TFT에 주로 사용된 amorphous silicon (a-Si)은 대면적화가 용이하며 가격이 저렴하지만, 이동도가 낮다는 (< $1cm2/V{\cdot}s$) 단점이 있다. 따라서 전기적 특성이 우수한 산화물 반도체가 기존의 a-Si의 대체 물질로써 각광받고 있다. 산화물 반도체는 비정질 상태임에도 불구하고 a-Si에 비해 이동도 (> $10cm2/V{\cdot}s$)가 높고, 가시광 영역에서 투명하며 저온에서 공정이 가능하다는 장점이 있다. 하지만, 차세대 디스플레이 백플레인에서는 더 높은 이동도 (> $30cm2/V{\cdot}s$)를 가지는 TFT가 요구된다. 따라서, 본 연구에서는 차세대 디스플레이에서 요구되는 높은 이동도를 갖는 TFT를 제작하기 위하여, amorphous In-Ga-Zn-O (a-IGZO) 채널하부에 화학적으로 안정하고 전도성이 뛰어난 SnO2 채널을 얇게 형성하여 TFT를 제작하였다. 표준 RCA 세정을 통하여 p-type Si 기판을 세정한 후, 열산화 공정을 거쳐서 두께 100 nm의 SiO2 게이트 절연막을 형성하였다. 본 연구에서 제안된 적층된 채널을 형성하기 위하여 5 nm 두계의 SnO2 층을 RF 스퍼터를 이용하여 증착하였으며, 순차적으로 a-IGZO 층을 65 nm의 두께로 증착하였다. 그 후, 소스/드레인 영역은 e-beam evaporator를 이용하여 Ti와 Al을 각각 5 nm와 120 nm의 두께로 증착하였다. 후속 열처리는 퍼니스로 N2 분위기에서 $600^{\circ}C$의 온도로 30 분 동안 실시하였다. 제작된 소자에 대하여 TFT의 전달 및 출력 특성을 비교한 결과, SnO2 층을 형성한 TFT에서 더 뛰어난 전달 및 출력 특성을 나타내었으며 이동도는 $8.7cm2/V{\cdot}s$에서 $70cm2/V{\cdot}s$로 크게 향상되는 것을 확인하였다. 결과적으로, 채널층 하부에 SnO2 층을 형성하는 방법은 추후 높은 이동도를 요구하는 디스플레이 백플레인 TFT 제작에 적용이 가능할 것으로 기대된다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.3
• /
• pp.211-215
• /
• 2010

Pulsed laser deposition is a very efficient technique for fabricating thin films of complex compounds. In the present work, $Bi_2O_3$-MgO-ZnO-$Nb_2O_5$ (BMZN) pyrochlore thin films were deposited on platinized Si substrates at various temperatures by using pulsed laser deposition technique. These films have been characterized by X-ray diffractometer (XRD), atomic force microscopy (AFM) to investigate their structural, morphological properties. MIM structure was manufactured to analyze di-electrical properties of BMZN thin films. XRD results reveal the thin films deposited at less than $400^{\circ}C$ show only amorphous phase, the crystallized thin films was observed when the thin films were prepared temperature at above $500^{\circ}C$. From AFM, it was known that the thin film grown at $400^{\circ}C$ is the densest. Dielectric constant increased with increasing temperature up to $400^{\circ}C$ at 100 kHz and dramatically decreased at the higher temperature. A aspect of dissipation factor was the exact opposite of dielectric constant. BMZN thin films grown at $400^{\circ}C$ exhibited a high dielectric constant of 60.9, a low dissipation factor of 0.007 at 100 kHz.

• Corrosion Science and Technology
• /
• v.12 no.6
• /
• pp.295-303
• /
• 2013

Silane surface treatments have been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. The silane performance is comparable to, or in some cases better than, that of chromate layers. Based on the tetra-ethylorthosilicate(TEOS) and methlyl trieethoxysilane(MTES), inorganic sol was synthesized and formed hybrid networks with $SiO_2$ nano particle and polypropylene glycol(PPG) on Zn alloyed steel surface. According to SST results, addition of 10nm and 50nm $SiO_2$ nanoparticle in synthesized solution improved anti-corrosion property by its shear stress relaxation effect during curing process. Also, SST results were shown that anti-corrosive property was affected by the amounts of organic compounds.

• Journal of the Korean Vacuum Society
• /
• v.19 no.4
• /
• pp.293-299
• /
• 2010

Vertically aligned ZnO nanorods on Si (111) substrate were prepared by hydrothermal method. The ZnO nanorods on spin-coated seed layer were synthesized at $140^{\circ}C$ for 6 hours in autoclave and were thermally annealed in argon atmosphere for 20 minutes at temperature of 300, 500, $700^{\circ}C$. The effects of the thermal annealing on the structural and optical properties of the grown on ZnO nanorods were investigated by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), photoluminescence (PL). All the ZnO nanorods show a strong ZnO (002) and weak (004) diffraction peak, indicating c-axis preferred orientation. The residual stress of the ZnO nanorods is changed from compressive to tensile by increasing annealing temperature. The hexagonal shaped ZnO nanorods are observed. The PL spectra of the ZnO nanorods show a sharp near-band-edge emission (NBE) at 3.2 eV, which is generated by the free-exciton recombination and a broad deep-level emission (DLE) at about 2.12~1.96 eV, which is caused by the defects in the ZnO nanorods. The intensity of the NBE peak is decreased and the DLE peak is red-shifted due to oxygen-related defects by thermal annealing.

• Journal of Conservation Science
• /
• v.35 no.4
• /
• pp.373-383
• /
• 2019

We characterized the smelting process and smelting furnace through scanning electron microscopy-energy dispersive spectroscopy, wavelength dispersive X-ray fluorescence, X-ray diffraction, and raman micro-spectroscopy with 13 relics including slags and furnace walls excavated from square-shaped building sites and pits of the Three Kingdoms site at the Ungyo site section I. Our results revealed that the principal components were FeO and SiO₂; and CuO, PbO, and ZnO were contained in small quantities. Furthermore, fayalite, magnetite, augite, copper, and cuprite were found. High contents of FeO or SiO₂ components seem to have been added to form fayalite to remove gangue in the smelting process. The relatively low content of S detected in the copper prills suggests that roasting was performed well. Cristobalite and mullite, which are minerals that indicate high-temperature found in the furnace wall, show that the smelting temperature was higher than 1,250℃. The findings of this study show a high possibility that the Wanju Ungyo site is smelting remains of copper ores, which are nonferrous metals, rather than iron. Various smelting byproducts excavated in this area in the future will help us better understand the copper smelting process that may have been performed since ancient times.

• Proceedings of the KIEE Conference
• /
• 1999.07e
• /
• pp.2361-2363
• /
• 1999

The conventional SiC-type of lightning arresters in distribution systems has been replaced by ZnO-type because the ZnO-type has characteristics such as outstanding non linearity, high energy absorption capability, surge suppressing performance, and excellent response to abrupt wave. Out of the various types of lightning arrester failures, some which have been often reported could be prevented in advance. Therefore, the preventive countermeasures which can cope with the failures are strongly required. This paper summed up and analyzed the lightning arrester failures which occurred, from 1983 to 1992, in distribution systems in order to provide fundamental data, classified by year, to make countermeasures.

• Korean Journal of Materials Research
• /
• v.32 no.12
• /
• pp.560-564
• /
• 2022

In this study, lanthanum boron silicate glasses were prepared with a composition of x Li₂O-(60-x)B₂O₃-5CaO-5BaO-7ZnO-10SiO₂-10La₂O₃-3Y₂O₃ where x = 1,3,5,7, and 9 mol%. Each composition was melted in a platinum crucible under atmospheric conditions at 1,400 ℃ for 2 h. Clear glasses with a transmittance exceeding 85 % were fabricated. Their optical, thermal, and physical properties, such as refractive index, Abbe number, density, glass transition (T_g) and Knoop hardness were studied. The results demonstrated that refractive index was between 1.6859 and 1.6953 at 589.3 nm. The Abbe number was calculated using an equation for 589.3 nm (nd), 656.3 nm (nf) and 486.1 nm (nc) and was observed to be in the range from 57.5 to 62.6. As the Li₂O content increased, the glass transition temperature of the optical glass decreased from 608 ℃ to 564 ℃. If glass mold pressing is performed using a material with a low transition temperature and high mechanical strength, then the optical glasses developed in this study can be completely commercialized.

• Economic and Environmental Geology
• /
• v.42 no.6
• /
• pp.549-559
• /
• 2009

The objectives of this study are to investigate the biomineralization of goethite and lepidocrocite formed on the twisted-stalk and the sheathed-filament structure that is suggest microbe origin, and heavy metal in the yellow Fe-hydroxide. On the ratio of Cl and the Cl/Br ratios that are a pollution and non-pollution of groundwaters, it is indicated that the groundwater in this areas were relatively contaminated by human activity. The composition of the yellow Fe-hydroxide consisted mainly of $Fe_2O_3$ and $SiO_2$. The content of $Fe_2O_3$ ranges from 58.57 wt.% to 75.7 3wt.%, and $SiO_2$ content ranges from 5.8 wt.% to 16.17 wt.%. Heavy metal elements such as Zn(max. 6,160 mg/kg), Pb(max. 377 mg/kg), U(max. 503 mg/kg), Cr(max. 203 mg/kg), Cu(max. 77 mg/kg), V(max. 162 mg/kg), Ni(max. 105 mg/kg) were observed to be rich in those yellow Fe-hydroxide. The lath and platy crystals and needle-shaped crystals were clearly observed on the twisted-stalks and sheathed-filaments structure. The goethite, gypsum, and lepidocrocite were identified in the yellow Fe-hydroxide by x-ray powder diffraction.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.905-908
• /
• 2001

The microstructure and the magnetic properties of Mn-Zn ferrite, which were power loss and saturation magnetic flux density, were investigated as the function of the process before firing. The highest initial permeability and the lowest power loss were attained to the specimen with CaO 400 ppm as a resulted from the highest solubility to SiO$_2$and the creation of liquid phase which improved sintering. The biggest grain size, the highest saturation magnetic flux density and the lowest power loss, which was resulted from that the eddy current loss increased as grain size increased but the hysteresis loss much more decreased and the hysteresis loss strongly influenced on the total power loss rather than the eddy current loss, were obtained to the Mn-Zn ferrite added 2wt% PVA. The power loss was lowest and the saturation magnetic flux density was highest in case of 1 ton/$\textrm{cm}^2$ and the grain size was not influenced.