• Proceedings of the KIEE Conference
• /
• 2004.11a
• /
• pp.75-78
• /
• 2004

$Bi_{3.25}Eu_{0.75}Ti_3O_{12}$ (BET) thin films were deposited on the $LaNiO_3$ (LNO (100))/Si and Pt/Ti/$SiO_2$/Si substrates by the metal-organic decomposition method. Structural and dielectric properties of BLT thin films for the applications in nonvolatile ferroelectric random access memories were investigated. Both the structure and morphology of the films were analyzed by x-ray diffraction (XRD) and atomic force microscope (AFM). Even at low temperatures $650^{\circ}C$, the BET thinfilms were successfully deposited on LNO bottom electrode and exhibited (001) and (117) orientation. Compared with the Pt electrode films, the BET thin films on the LNO electrode annealed at $650^{\circ}C$ showed better dielectric constantsand remanent polarization. The BET thin films on the LNO electrode for the annealing temperature of $650^{\circ}C$, the remanent polarization Pr and coercive field were $45.6\;C/cm^2$ and 171 kV/cm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1992.11a
• /
• pp.22-27
• /
• 1992

Phosphorus doped hydrogenated microcrystalline silicon (${\mu}c$-Si:H) thin films were deposited by PECVD (Plasma Enhanced Chemical Vapour Deposition) method using 10.2% $SiH_4$ gas (diluted in Ar) and 308ppm $PH_3$ gas (diluted in Ar). The structural, optical and electrical properties of the films were investigated as a function of substrate temperature(15 to $400^{\circ}C$) and RF power(10 to 120W). The thin film deposited by varing substrate temperature had columnar structure and microcrystalline phase. The volume fraction of microcrystalline phase in the films deposited at RF power of 80W, increased with increasing substrate temperature up to $200^{\circ}C$, and then decreased with further increasing substrate temperature. Volume fraction of microcrystalline phase increased monotonously with increasing RF power at substrate temperature of $250^{\circ}C$. With increasing volume fraction of microcrystalline, electrical resistivity of films decreased to 0.274 ${\Omega}cm$.

• Korean Journal of Materials Research
• /
• v.19 no.2
• /
• pp.102-107
• /
• 2009

The effect of annealing under argon atmosphere on hydrogenated amorphous silicon (a-Si:H) thin films deposited at room temperature and $300^{\circ}C$ using Radio Frequency (RF) magnetron sputtering has been investigated. For the films deposited at room temperature, there was not any increase in hydrogen content and optical band gap of the films, and as a result, quality of the films was not improved under any annealing conditions. For the films deposited at $300^{\circ}C$, on the other hand, significant increases in hydrogen content and optical band gap were observed, whereas values of microstructure parameter and dark conductivity were decreased upon annealing below $300^{\circ}C$. In this study, it was proposed that the Si-HX bonding strength is closely related to deposition temperature. Also, the improvement in optical, electrical and structural properties of the films deposited at $300^{\circ}C$ was originated from thermally activated hydrogen bubbles, which were initially trapped at microvoids in the films.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.4
• /
• pp.543-548
• /
• 2018

Ferroelectric $Bi_4Ti_3O_{12}$ films were deposited on $SrTiO_3(100)$ and Si(100) substrate by using conductive $SrRuO_3$ films as underlayer, and their ferroelectric and electrical properties were investigated depending on crystal structure and orientation. C-axis oriented $Bi_4Ti_3O_{12}$ films were grown on well lattice-matched pseudo-cubic $SrRuO_3$ films deposited on $SrTiO_3(100)$ substrate, while random-oriented polycrystalline $Bi_4Ti_3O_{12}$ films were grown on $SrRuO_3$ films deposited on Si(100) substrate. The random-oriented polycrystalline film showed a good ferroelectric hysteresis property with remanent polarization ($P_r$) of $9.4{\mu}C/cm^2$ and coercive field ($E_c$) of 84.9 kV/cm, while the c-axis oriented film showed $P_r=0.64{\mu}C/cm^2$ and $E_c=47kV/cm$ in polarizaion vs electric field curve. The c-axis oriented $Bi_4Ti_3O_{12}$ film showed a dielectric constant of about 150 and lower thickness dependence in dielectric constant compared to the random-oriented film. Furthermore, the c-axis oriented $Bi_4Ti_3O_{12}$ film showed leakage current lower than that of the polycrystalline film. The difference of ferroelectric properties in two films was explained from the viewpoint of depolarization effect due to orientation of spontaneous polarization and layered crystal structure of bismuth-base ferroelectric oxide.

• Journal of the Korean Vacuum Society
• /
• v.20 no.3
• /
• pp.182-188
• /
• 2011

Polysilazane and polymethylsilazane based precursor films were deposited on Si-substrate by spin-coating, subsequently annealed at $150{\sim}850^{\circ}C$, and characterized. Structural analysis, shrink, compositional change, etch rate, and gap-filling were observed. Annealing the precursor films led to formation of spin-on dielectric films. C-containing precursor films showed that less loss of N, H, and C while less gain of O than that of C-free precursor films at $400^{\circ}C$, but more loss of N, H, and C while more gain of O at $850^{\circ}C$. Thus polysilazane based precursor films exhibited less reduction in thickness of 14.5% than silazane based one of 15.6% at $400^{\circ}C$ but more 37.4% than 19.4% at $850^{\circ}C$. FTIR indicated that C induced smaller amount of Si-O bond, non-uniform property, and lower resistance to chemical etching.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.29A no.3
• /
• pp.87-95
• /
• 1992

The electrical characteristics of Al/TaS12TOS15T/SiOS12T/Si metal insulator-semiconductor (MIS) capacitors were studied. Tantalum pentoxide thin films on SiOS12T/p-Si substrate have been prepared by thermal oxidation at 450-$600^{\circ}C$ of sputter deposited tantalum films. Composition and structures of the tantalum oxide films were examined by AES and XRD. From the C-V analysis, dielectric constant of TaS12TOS15T which were oxidized at 55$0^{\circ}C$ for 1h in OS12T were 18-23, the value depending on the oxidation and annealing temperature. The leakage current density was found to be about 10S0-10T-10S0-9T A/cmS02T at an applied electric field of 1 MV/cm. The dielectric breakdown strength of the tantalum oxide films annealed at 100$0^{\circ}C$ were in the range from 2.5MV/cm to 2.8 MV/cm.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.26-26
• /
• 2000

High quality epitaxial Y2O3 thin films were prepared on Si(111) and (001) substaretes by using ion beam assisted deposition. As a substrate, clean and chemically oxidized Si wafers were used and the effects of surface state on the film crystallinity were investigated. The crystalline quality of the films were estimated by x-ray scattering, rutherford backscattering spectroscopy/channeling, and high-resolution transmission electron microscopy (HRTEM). The interaction between Y and Si atoms interfere the nucleation of Y2O3 at the initial growth stage, it could be suppressed by the interface SiO2 layer. Therefore, SiO2 layer of the 4-6 layers, which have been known for hindering the crystal growth, could rather enhance the nucleation of the Y2O3 , and the high quality epitaxial film could be grown successfully. Electrical properties of Y2O3 films on Si(001) were measured by C-V and I-V, which revealed that the oxide trap charge density of the film was 1.8$\times$10-8C/$\textrm{cm}^2$ and the breakdown field strength was about 10MV/cm.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.1
• /
• pp.36-40
• /
• 2003

The diamond-like nanocomposite (DLN) thin films were deposited on Si substrates using $CH_4/(C_2H_5O)_4Si/H_2$/Ar gas mixtures as source gases by the plasma enhanced chemical vapor deposition (PECVD). The chemical structure and microstructure of grown films were investigated and their tribological properties were evaluated by a ball-on-plate type tribometer. The deposited DLN films mainly consisted of diamond-like a-C:H and quartz-like a-Si:O networks. The DLN films had a good agreement with tribological coating applications due to their extremely low friction coefficients and low wear rates.

• Journal of Sensor Science and Technology
• /
• v.15 no.6
• /
• pp.386-390
• /
• 2006

This paper describes the ohmic contact formation of polycrystalline 3C-SiC films deposited on thermally grown Si wafers. In this work, a TiW (titanium tungsten) film as a contact material was deposited by RF magnetron sputter and annealed with the vacuum process. The specific contact resistance (${\rho}_{c}$) of the TiW contact was measured by using the C-TLM (circular transmission line method). The contact phase and interfacial reaction between TiW and 3C-SiC at high-temperature as also analyzed by XRD (X-ray diffraction) and SEM (scanning electron microscope). All of the samples didn't show cracks of the TiW film and any interfacial reaction after annealing. Especially, when the sample was annealed at $800^{\circ}$ for 30 min., the lowest contact resistivity of $2.90{\times}10{\Omega}cm^{2}$ was obtained due to the improved interfacial adhesion. Therefore, the good ohmic contact of polycrystalline 3C-SiC films using the TiW film is very suitable for high-temperature MEMS applications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.54-54
• /
• 2011

The demand for low-friction, wear and corrosion resistant components, which operate under severe conditions, has directed attentions to advanced surface engineering technologies. The Filtered Vacuum Arc Cathode Deposition (FVACD) process has demonstrated atomically smooth surface at relatively high deposition rates over large surface areas. Preparation of Ti-Si-C-N nanocomposite coatings on (100) Si and stainless steel substrates with tetramethylsilane (TMS) gas pressures to optimize the film preparation conditions. Ti-S-C-N coatings were characterized using X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, nanoindentation, Rockwell C indentation and ball-on-disk wear tests. The XRD results have confirmed phase formation information of TiSiCN coatings, which shows mixing of TiN and TiC structure, corresponding to (111), (200) and (220) planes of TiCN. The chemical composition of the film was investigated by XPS core level spectra. The binding energy of the elements present in the films was estimated using XPS measurements and it shows present of elemental information corresponding to Ti2p, N1s, Si 2p and C1. Film hardness and elastic modulus were measured with a nano-indenter, and film hardness reached 40 GPa. Tribological behaviors of the films were evaluated using a ball-on-disk tribometer, and the films demonstrated properties of low-friction and good wear resistance.