• Korean Journal of Materials Research
• /
• v.12 no.2
• /
• pp.129-134
• /
• 2002

The optimum condition for fabricating cordierite disc type filter element was deduced. Cordierite monolith was used as starting material for filter element because it has many advantages such as high thermal shock resistance and good catalytic activity compared with $TiO_2$and SiC. The contents of organic additives and foaming agent were optimized to control the porosity and mechanical strength of cordierite filter. Among the required properties to be adopted as filter elements, the pressure drop and NOx removal efficiency were investigated depending on processing variables. It was found that pressure drop depends on particle size distribution of cordierite monolith and organic additives added as forming agent. The pressure drop at 5cm/sec of face velocity was in the range of 15~655mm$H_2O$ at room temperature. The NOx removal efficiency of catalytic filter with $V_2O_5$ as catalyst was over 85% at $450^{\circ}C$.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2005.11b
• /
• pp.92-106
• /
• 2005

The head-end processes of spent TRISO fuel have been reviewed to understand the current status and the limitations of the reported processes. The main concerns in the TRISO treatment are to effectively breach and separate the carbon and SiC layers composing the TRISO particles. The crush-bum scheme which was considered in the early stages of the development has been replaced by the crush-leach or $CO_2$ burning and the succeeding CO decomposition process because of a sequestration problem of $CO_2$ containing $^{14}C$. However there are still many obstacles to overcome in the reported processes. Hence, innovative thermomechanical and pyrochemical concepts to breach the coating layers of the TRISO particle with a minimized amount of second waste are proposed in this paper and their principles are described in detail.

• Journal of the Mineralogical Society of Korea
• /
• v.30 no.4
• /
• pp.179-186
• /
• 2017

This study investigated the mineralogical characteristics of lime mortars used in pointing of Namhansanseon Yeojang from Joseon dynasty. Polarization microscopy revealed quartz, feldspar, mica, pyroxene and opaque minerals in the lime mortars. XRD analysis also confirmed clay minerals chlorite and kaolin. As a result of particle size analysis of lime mortars, the particle size distribution was wide and size was not uniform. 60% of samples were corresponded to the sand area. The chemical components detected from XRF analysis, 8.71-11.18 % of Ca as the main component of lime and $SiO_2$, $Al_2O_3$, and $Fe_2O_3$ in soil minerals were main components. The lime mortars showed an endothermic peak due to decarbonization reaction of $CaCO_3$ at $750^{\circ}C$ and weight reduction rate of 10%. The microstructures were agglomerated amorphous and observed rhombohedral calcite crystals by scanning electron microscope. It is considered that the pointing of Yeojang is a mortar mixed with lime and soil. In addition the Hanbongseong Yeojang was constructed using the same materials and construction technique because the minerals composition is not different according to the Yeojang location and use.

• Korean Chemical Engineering Research
• /
• v.43 no.4
• /
• pp.503-510
• /
• 2005

In this research, composite alumina was prepared to add the various promoters by sol-gel method and examined its thermal stability. After sintering at $1,200^{\circ}C$, the thermal stability resulted in following order, $Si{\fallingdotseq}La$ > Ti > $Ba{\fallingdotseq}Ce$ > Y > $Zr{\fallingdotseq}Mg$, in accordance with adding the promoters. Especially in case of silica-added alumina, a phase transformation temperature to ${\alpha}$-alumina increased about $150^{\circ}C$ and after sintering at $1,200^{\circ}C$, it showed to maintain in ${\gamma}$-form and ${\delta}$-form alumina phase. Also it showed an increase of surface area from $3m^2/g$ to $71m^2/g$ compared with pure ${\alpha}$-alumina. In the case of silicaadded alumina, the characterization change of this alumina particle resulted in a delay of phase transformation because Si-O-Al bond was increased when sintered at high temperature. In case of lanthanum-added alumina, there was a sintering delay phenomenon in inter-particles as $LaAlO_3$ structure existed. The existence of lanthanum structure was confirmed by XRD and XPS analysis. It appeared on the alumina surface as $La_2O_3$ structure when it was sintered under $1,000^{\circ}C$, as the perovskite structure of $LaAlO_3$ at above $1,000^{\circ}C$ and as the magneto-plumbite structure of $LaAl_{11}O_{18}$ at above $1,300^{\circ}C$.

• Resources Recycling
• /
• v.2 no.2
• /
• pp.27-38
• /
• 1993

In this study, we investigated the grinding and sedimentation(elutriation) process of the dusts for the effective separation of high purity iron and iron oxides. For characterization of the dust, particle size distribution and chemical composition, were examined. The results obtained in this study may be summarized as follows : 1. The converter CF(clarifier) dust of the Pohang 1st, 2nd steel making factory and EC(Evaporation Cooler), EP(Eltrostatic precititator) dust of the Kwangyang 2nd steel making factory are composed $\alpha$-Fe(21~50%), FeO(wustite)$Fe_3$$O_4$(magnetite), $Fe_2$$O_3$, CaO, $Al_2$$O_3$, $SiO_2$, and etc. 2. Pure iron has ductile characteristic in nature, particle size of the pure iron increase by increasing the grinding time. On the other hand, it is conformed that bo고 particles of hematite and magnetite become less than 325 mesh after 10 minutes grinding. 3. By applying the elutriation technique for the EC dust of the Kwangyang 2nd steel making factory, the iron powder of high content more than 99.17% of pure Fe was recovered with 37.8% yield at grinding time for 40 minutes. 4. By applying the elutriation technique for the CF dust of the Pohang 2nd steel making factory, the iron powder of high content more than 98.38% of pure Fe was recovered with 44.42% yield at grinding time for 40 minutes. 5. When magnetic separation was performed using plastic bonding magnet of 70 gauss, more than 98% Fe grade of iron powder was recovered in the size range +65 -200 mesh but the recovery of it was low.

• Korean Journal of Materials Research
• /
• v.12 no.7
• /
• pp.573-579
• /
• 2002

Stoichiometric mullite ($3Al_2$$O_3$. $2SiO_2$) precursor sol has been prepared by sol-gel method. The effects of the precursor pH and sintering temperature on the synthesizing behavior and morphology of mullite have been studied. Mullite precursor sol was prepared by dissolution of aluminum nitrate enneahydrate (Al($NO_3$)$_3$.9H$_2O) into the mixture of silica sol. Precursor pH of the sols was controlled to acidic condition ($PH\leq$ 1~1.5) and to basic condition ($pH\geq$8.5~9). The synthesized aluminosilicate sols were formed under 20 MPa pressure after drying at $150^{\circ}C$ for 24 hours, and then sintered for 3hours in the temperature range of $1100~1600^{\circ}C$. From TGA/DTA analysis, total weight loss in the aluminosilicate gel of the acidic sample was (equation omitted) 56% and that of the basic sample was (equation omitted) 85%, indicating that the synthesizing temperature of mullite phase for acidic and basic samples was above $1200^{\circ}C$ and $1300^{\circ}C$, respectively. The morphologies of the synthesized mullite were fine and needle-like (or rod-like) for acidic sample, and granular for basic sample that has been sintered above $1300^{\circ}C$. It was found that the morphology of mullite particle was predominantly governed by precursor pH and sintering temperature.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2006.06a
• /
• pp.61-66
• /
• 2006

Over the past 20 years there has been a revolution involving the use of nano or macro size particles as drainage and retention systems during the manufacture of paper. More recently a group of patented technologies called Synthetic Mineral Microparticles (SMM) has been invented and developed. This system has potential to further promote the drainage of water and retention of fine particles during papermaking. Prior research, as well as our on preliminary research showed that the SMM system has advantages in both of drainage and retention compared with montmorillonite (bentonite), which one of the most popular materials presently used in this kind of application. In spite of the demonstrated advantages of this SMM system, the properties and activity of SMM particles in the aqueous state have not been elucidated yet. Streaming current titrations with highly charged polyelectrolytes were used to measure the charge properties of SMM and to understand the interactions among SMM particles, fibers, fiber fines, and cationic polyacrylamide (cPAM) as a retention aid. It was found that pH profoundly affects the charge properties of SMM, due to the influence of Al-ions and the Si-containing particle surface. SEM pictures, characterizing the morphology, geometry and size distribution of SMM, showed an broad distribution of primary particle size. Dilution of SMM mixturee appeared to wash out particles smaller than 100 nm from the surface of larger particles, which themselves appeared to be composed of fused primary particles. DSC thermoporometry was used to measure the size distribution of nanopores within SMM particles.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.2
• /
• pp.291-297
• /
• 2008

The solid particle erosion behaviour of unidirectional carbon fiber reinforced plastic (CFRP) composites was investigated. The erosive wear of these composites was evaluated at different impingement angles ($30^{\circ}$, $45^{\circ}$, $60^{\circ}$, $90^{\circ}$), different impact velocities (40, 55, 60, 70m/s) and at three different fiber orientations ($0^{\circ}$, $45^{\circ}$, $90^{\circ}$). The erodent was SiC sand with the size $50-100{\mu}m$ of irregula. shapes. The result showed ductile erosion behaviour with maximum erosion rate at $30^{\circ}$ impingement angle. The fiber orientations had a significant influence on erosion. The erosion rate was strongly dependent on impact velocity which followed power law $E{\propto}\;V^n$. Based on impact velocity (V), impact angle (${\alpha}$) and fiber orientation angle (${\beta}$), a method was proposed to predict the erosion rate of unidirectional fiber reinforced composites.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.2
• /
• pp.131-136
• /
• 2008

Using ultrasonic standing waves, micro particles submerged or flowing in fluid can be manipulated. Due to acoustic radiation force of ultrasound, particles are forced to move to pressure nodal or antinodal lines. In this work, we propose a method to control the position of micro particle in a flow by adjusting the frequency of the standing wave. To this end, standing wave field generation system including a few millimeter thick micro channel was established using an immersible ultrasonic transducer. The present generation system works valid in a frequency range between 2.0 MHz and 2.5 MHz. We observed the SiC particles in water moved to pressure nodal lines by the standing wave. The effect of the channel thickness and operating frequency was also investigated. Interestingly, it was shown that the operating frequency have a close relation with the location of the pressure nodal line. Consequently, it fan be said that the position of particle movement rail be controlled by adjusting the ultrasound frequency. The maximum range of the controllable position was about 261 micrometers under the given condition. The resulted observations reveal the possibility of various applications of the ultrasonic standing wave to the manipulation of particles submerged in a fluid.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.428-436
• /
• 1997

Hexacelsian ($BaO{\cdot}Al_2O_3{\cdot}2SiO_2$) powder was prepared by a solution-polymerization route employing PVA solution as a polymeric carrier. A fine amorphous-type hexacelsian powder with an average particle size of 0.8 $\mu \textrm{m}$ and a BET specific surface area of $63 \textrm{m}^2$/g was made by a ball-milling the powder precursor for 12 h after calcination at $800^{\circ}C$ for :1 h. A densified hexacelsian was obtained through sintering at $1550^{\circ}C$ for 2 h under an air atmosphere. The $\alpha\longleftrightarrow\beta$ and $\beta\longleftrightarrow\gamma$ displacive phase transformation in polycrystalline hexacelsia,n was examined by using dilatometry and differential scanning calorimtry. The reconstructive transformation between hexacelsian and celsian was obtained by annealing at $1600^{\circ}C$ for 72h. Volume contraction of 5.6% was accompanied by the reconstructive transformation.