• Electrical & Electronic Materials
• /
• v.16 no.9
• /
• pp.63.2-64
• /
• 2003

Epitaxial yttrium-stabilized HfO$_2$ thin films were deposited on p-type (100) Si substrates by pulsed laser deposition at a relatively lower substrate temperature of 550. Transmission electron microscopy observation revealed a fixed orientation relationship between the epitaxial film and Si; that is, (100)Si.(100)HfO$_2$ and [001]Si/[001]HfO$_2$. The film/Si interface is not atomically flat, suggesting possible interfacial reaction and diffusion, X-ray photoelectron spectrum analysis also revealed the interfacial reaction and diffusion evidenced by Hf silicate and Hf-Si bond formation at the interface. The epitaxial growth of the yttrium stabilized HfO$_2$ thin film on bare Si is via a direct growth mechanism without involoving the reaction between Hf atoms and SiO$_2$ layer. High-frequency capacitance-voltage measurement on an as-grown 40-A yttrium-stabilized HfO$_2$ epitaxial film yielded an dielectric constant of about 14 and equivalent oxide thickness to SiO$_2$ of 12 A. The leakage current density is 7.0${\times}$ 10e-2 A/$\textrm{cm}^2$ at 1V gate bias voltage.

• Korean Journal of Materials Research
• /
• v.9 no.5
• /
• pp.503-508
• /
• 1999

We have investigated the physical and diffusion barrier property of Ti-Si-N film for Cu metallization. The ternary compound was deposited by using reactive rf magnetron sputtering of a TiSi$_2$target in an Ar/$N_2$gas mixture. Resistivities of the films were in range of 358$\mu$$\Omega$-cm, to 307941$\mu$$\Omega$-cm, and tended to increase with increasing the $N_2$/Ar flow rate ratio. The crystallization of the Ti-Si-N compound started to occur at 100$0^{\circ}C$ with the phases of TiN and Si$_3$N$_4$identified by using XRD(X-ray Diffractometer). The degree of the crystallization was influenced by the $N_2$/Ar flow ratio. The diffusion barrier property of Ti-Si-N film for Cu metallization was determined by AES, XRD and etch pit by secco etching, revealing the failure temperature of 90$0^{\circ}C$ in 43~45at% of nitrogen content. In addition, the very thin compound (10nm) with 43~45at% nitrogen content remained stable up to $700^{\circ}C$. Furthermore, thermal treatment in vacuum at $600^{\circ}C$ improved the barrier property of the Ti-Si-N film deposited at the $N_2$(Ar+$N_2$) ratio of 0.05. The addition of Ti interlayer between Ti-Si-N films caused the drastic decrease of the resistivity with slight degradation of diffusion barrier properties of the compound.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.5
• /
• pp.237-241
• /
• 2004

Amorphous silicon (a-Si) films are used in a broad range of solar cell, flat panel display, and sensor. Because of the greater ease of deposition and lower processing temperature, thin films are widely used for thin film transistors (TFTs). However, they have lower stability under the exposure of visible light and because of their low field effect mobility ($\mu$$_{FE}$ ) , less than 1 c $m^2$/Vs, they require a driving IC in the external circuits. On the other hand, polycrystalline silicon (poly-Si) thin films have superiority in $\mu$$_{FE}$ and optical stability in comparison to a-Si film. Many researches have been done to obtain high performance poly-Si because conventional methods such as excimer laser annealing, solid phase crystallization and metal induced crystallization have several difficulties to crystallize. In this paper, a new crystallization process using a molybdenum substrate has been proposed. As we use a flexible substrate, high temperature treatment and roll-to-roll process are possible. We have used a high temperature process above 75$0^{\circ}C$ to obtain poly-Si films on molybdenum substrates by a rapid thermal annealing (RTA) of the amorphous silicon (a-Si) layers. The properties of high temperature crystallized poly-Si studied, and poly-Si has been used for the fabrication of TFT. By this method, we are able to achieve high crystal volume fraction as well as high field effect mobility.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.6
• /
• pp.520-526
• /
• 2007

In order to acquire fundamental informations to fabricate high precision thin film resistors, NiCr/NiCrSi alloy films were prepared using Ni and Cr targets. Effect of composition on the electrical properties of the NiCr/NiCrSi alloy film were then investigated. Considering the effect of Si doping on the electrical and material characteristics, the lower TCR (temperature coefficient of resistance) values could be achieved for samples with Ni/Cr ratio of $0.8{\sim}1.5$ (in a range of relative higher specific resistivity and Cr composition of $40\;wt%{\sim}55\;wt%$) and with Si doping. Consequently, the sample prepared using a DC power showed a good TCR of $-25\;ppm/^{\circ}C$, which implies that increase of specific resistivity and decrease of TCR would be achieved more efficiently not for Ni-Cr binary material but for Si doped Ni-Cr ternary material, and not using RF power but using DC power in the sputtering process.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2007.06a
• /
• pp.179-182
• /
• 2007

Polycrystaline (poly) 3C-SiC thin film on n-type and p-type Si were deposited by APCVD using HMDS, $H_2$, and Ar gas at $1180^{\circ}C$ for 3 hour. And then the schottky diode with Au/poly 3C-Sic/Si(n-type) structure was fabricated. Its threshold voltage ($V_d$), breakdown voltage, thickness of depletion layer, and doping concentration ($N_D$) value were measured as 0.84 V, over 140 V, 61nm, and $2.7{\times}10^{19}\;cm^3$, respectively. The p-n junction diode fabricated by poly 3C-SiC was obtained like characteristics of single 3C-SiC p-n junction diode. Therefore, its poly 3C-SiC thin films are suitable MEMS applications in conjuction with Si fabrication technology.

• Journal of the Korean Vacuum Society
• /
• v.16 no.5
• /
• pp.348-352
• /
• 2007

In submicron processes, the feature size of ULSI devices is critical, and it is necessary both to reduce the RC time delay for device speed performance and to enable higher current densities without electromigration. In case of contacts between semiconductor and metal in semiconductor devices, it may be very unstable during the thermal annealing process. To prevent these problems, we deposited tungsten carbon nitride (W-C-N) ternary compound thin film as a diffusion barrier for preventing the interdiffusion between metal and semiconductor. The thickness of W-C-N thin film is $1,000{\AA}$ and the process pressure is 7mTorr during the deposition of thin film. In this work we studied the interface effects W-C-N diffusion barrier using the XRD and 4-point probe.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.11
• /
• pp.526-530
• /
• 2002

The $(Sr_{0.9}Ca_{0.1})TiO_3(SCT)$ thin films were deposited on Pt-coated electrode (Pt/TiN/$SiO_2$/Si) using RF sputtering method. The composition of SCT thin film deposited on Si substrate at room temperature is close to stoichiometry(1.081 in A/B ratio). The maximum dielectric constant of SCT thin film was obtained by ammealing at $600^{\cric}C$. The temperature dependence of dielectric loss showed a value within 0.02 in temperature ranges of -80 ${\sim}$ +90$^{\circ}C$. The capacitance characteristics showed a stable value within ${\pm}$4%. The drastic decrease of dielectric constant and increase of dielectric loss in SCT thin films was observed at the frequency above 200kHz.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.52 no.2
• /
• pp.56-60
• /
• 2003

In this work, we have fabricated thin film resistors using the DC/RF magnetron sputter of 51wt%Ni-41wt%Cr-8wt%Si alloy target and studied the effect of the process parameters on the electrical properties. In fabrication process, sputtering power, substrate temperature and annealing temperature have been varied as controllable parameters. TCR decreases with increasing the substrate temperature, but TCR increases over 300 [$^{\circ}C$]. The films are annealed to 400 [$^{\circ}C$] in air atmosphere, TCR increases with increasing the annealing temperature. The resistivity was 172 [${\mu}{\Omega}{\cdot}cm$] and 209 [${\mu}{\Omega}{\cdot}cm$] for the RF and DC as a sputtering power sources, respectively. Also, TCR was -52 [$ppm/^{\circ}C$] and -25 [$ppm/^{\circ}C$]. As a results of them, it is suggested that the sheet resistance and TCR of thin films can be controlled by variation of sputter process parameter and annealing of thin film.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.44 no.11
• /
• pp.20-25
• /
• 2007

In this paper, It was reported the dielectric constant in organic inorganic hybrid silica material such as SiOC film modeling of bond structure by annealing in organic properties. The organic inorganic hybrid silica material were deposited using bis-trimethylsilymethane (BTMSM, [(CH3)3Si]2CH2) and oxygen gas precursor by a plasma chemical vapor deposition (CVD). The organic inorganic hybrid silica material have three types according to the deposition condition. The dielectric constant of the films were performed MIS(Al/Si-O-C film/p-Si) structure. The C 1s spectra in organin inorganic silica materials with the flow rate ratio of O2/BTMSM=1.5 was organometallic carbon with the peak 282.9 eV by XPS. It means that organometallic carbon component is the cross-link bonding structure with good stability. The dielectric constant was the lowest at annealed films with cross-link bonding structure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.196-196
• /
• 2008

We have investigated that the effect of post annealing on the structural and electrical properties of $Ba_{0.5}Sr_{0.5}TiO_3$ thin films. The BST thin films were deposited on n-type 4H-silicon carbide(SiC) using pulsed laser deposition (PLD). The deposition was carried out in oxygen ambient 100mTorr for 5 minutes, which results in about 300nm-thick BST films. For the BST/4H-SiC, 200nm thick silver was deposited on the BST films bye-beam evaporation. The X-ray diffraction patterns of the BST films revealed that the crystalline structure of BST thin films has been improved after post-annealing at $850^{\circ}C$ for 1 hour. The root mean square (RMS) surface roughness of the BST film measured by using a AFM was increased after post-annealing from 5.69nm to 11.49nm. The electrical properties of BST thin film were investigated by measuring the capacitance-voltage characteristics of a silver/BST/4H-SiC structure. After the post-annealing, dielectric constant of the film was increased from 159.67 to 355.33, which can be ascribed to the enhancement of the crystallinity of BST thin films.