• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.6
• /
• pp.487-490
• /
• 2010

This paper describes the elecrtical and optical characteristics of $N_2$ doped porous 3C-SiC films. Polycrystalline 3C-SiC thin films are anodized by $HF+C_2H_5OH$ solution with UV-LED exposure. The growth of in-situ doped 3C-SiC thin films on p-type Si (100) wafers is carried out by using APCVD (atmospheric pressure chemical vapor deposition) with a single-precursor of HMDS (hexamethyildisilane: $Si_2(CH_3)_6)$. 0 ~ 40 sccm $N_2$ was used for doping. After the growth of doped 3C-SiC, porous 3C-SiC is formed by anodization with $7.1\;mA/cm^2$ current density for anodization time of 60 sec. The average pore diameter is about 30 nm, and etched area is increased with $N_2$ doping rate. These results are attributed to the decrease of crystallinity by $N_2$ doping. Mobility is dramatically decreased in porous 3C-SiC. The band gaps of polycrystalline 3C-SiC films and doped porous 3C-SiC are 2.5 eV and 2.7 eV, respectively.

• Journal of Sensor Science and Technology
• /
• v.18 no.3
• /
• pp.207-209
• /
• 2009

This paper describes the characteristics of poly 3C-SiC micro resonators with $3{\times}10^{17}{\sim}1{\times}10^{19}cm^{-3}$ doping concentrations. The 1.2 ${\mu}m$ thick cantilever and the 0.4 ${\mu}m$ thick doubly clamped beam resonators with different lengths were fabricated using poly 3C-SiC thin films. The characteristics of poly 3C-SiC micro resonators were evaluated by quartz and a laser vibrometer in vacuum at room temperature. The resonant frequencies of micro resonators decreased with doping concentrations owing to reduction in the Young's modulus of poly 3C-SiC thin films. It was confirmed that the resonant frequencies of poly 3C-SiC resonators are controllable by doping concentrations. Therefore, poly 3C-SiC resonators could be applied to MEMS devices and bio/chemical sensor applications.

• Journal of Sensor Science and Technology
• /
• v.17 no.4
• /
• pp.256-260
• /
• 2008

This paper describes the mechanical properties of poly(polycrystalline) 3C-SiC thin films with various doping concentration, in which poly 3C-SiC thin fil's mechanical properties according to the n-doping concentration 1($9.2{\times}10^{15}cm^{-3}$), 3($5.2{\times}10^{17}cm^{-3}$), and 5%($6.8{\times}10^{17}cm^{-3}$) respectively were measured by nano indentation. In the case of $9.2{\times}10^{15}cm^{-3}n$-doping concentration, Young's modulus and hardness were obtained as 270 and 30 GPa, respectively. When the surface roughness according to n-doping concentrations was investigated by AFM(atomic force microscope), the roughness of poly 3C-SiC thin films doped by 5% concentration was 15 nm, which is also the best of them.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.131-131
• /
• 2009

This paper describes the fabrication and characteristics of polycrystalline (poly) 3C-SiC microresonators with $3{\times}10^{17}{\sim}1{\times}10^{19}cm^{-3}$ in-situ N-doping concentrations. In this work, the crystallinity, carrier concentration and surface morphology of the grown thin films were evaluated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The 1.2 ${\mu}m$ thick cantilvers and the 0.4 ${\mu}m$ thick doubly-clamped beam microresonators with various lengths were implemented using in-situ doping poly 3C-SiC thin films. The characteristics of the poly 3C-SiC microresonators were evaluated using quartz and a laser vibrometer under vacuum at room temperature. The resonant frequencies of the SiC microresonators decreased with doping concentrations owing to the reduction of the Young's modulus of the poly 3C-SiC thin films. It was confirmed that the resonant frequencies of the poly 3C-SiC microresonators are controllable by adjusting the doping concentrations.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.6
• /
• pp.245-248
• /
• 2005

The physical and electrical properties of polycrystalline $\beta$-SiC were studied according to different nitrogen doping concentration. Nitrogen-doped SiC films were deposited by LPCVD(1ow pressure chemical vapor deposition) at $900^{\circ}C$ and 2 torr using $100\%\;H_2SiCl_2$ (35 sccm) and $5 \%\;C_2H_2$ in $H_2$(180 sccm) as the Si and C precursors, and $1\%\;NH_3$ in $H_2$(20-100 sccm) as the dopant source gas. The resistivity of SiC films decreased from $1.466{\Omega}{\cdot}cm$ with $NH_3$ of 20 sccm to $0.0358{\Omega}{\cdot}cm$ with 100 sccm. The surface roughness and crystalline structure of $\beta$-SiC did not depend upon the dopant concentration. The average surface roughness for each sample 19-21 nm and the average surface grain size is 165 nm. The peaks of SiC(111), SiC(220), SiC(311) and SiC(222) appeared in polycrystalline $\beta$-SiC films deposited on $Si/SiO_2$ substrate in XRD(X-ray diffraction) analysis. Resistance of nitrogen-doped SiC films decreased with increasing temperature. The variation of resistance ratio is much bigger in low doping, but the linearity of temperature dependent resistance variation is better in high doping. In case of SiC films deposited with 20 sccm and 100 sccm of $1\%\;NH_3$, the average of TCR(temperature coefficient of resistance) is -3456.1 ppm/$^{\circ}C$ and -1171.5 ppm/$^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.368-369
• /
• 2008

This paper describes the mechanical properties of poly(polycrystalline) 3C-SiC thin film with various doping concentration, in which poly 3C-SiC thin film's mechanical properties according to the n-doping concentration 1%$(9.2\times10^{15}cm^{-3})$, 3%$(5.2\times10^{17}cm^{-3})$, and 5%$(6.8\times10^{17}cm^{-3})$ respectively was measured by nano indentation. In the case of $9.2\times10^{15}^{-3}$ n-doping concentration, Young's Modulus and hardness were obtained as 270 GPa and 30 GPa, respectively. When the surface roughness according to n-doping concentrations was investigated by AFM(atomic force microscope), the roughness of poly 3C-SiC thin film doped by 5% concentration was 15 nm, which is also the best of them.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.194-194
• /
• 2009

3C-SiC thin films are widely used in extreme environments, radio frequency (RF) environments, and bio-materials for micro/nano electronic mechanical systems (M/NEMS). The mechanical properties of 3C-SiC thin films need to be considered when designing M/NEMS, so Young's Modulus and the hardness need to be accurately measured. Young's Modulus and the hardness are influenced by N-doping. In this paper, we show that the mechanical properties of poly (polycrystalline) 3C-SiC thin films are influenced by the N-doping concentration. Furthermore, we measure the mechanical properties of 3C-SiC thin films for N-doping concentrations of 1%, 3%, and 5%, by using nanoindentation. For films deposited using a 1% N-doping concentration, Young's Modulus and the hardness were measured as 270 GPa and 30 GPa, respectively. When the surface roughness of the thin films was investigated by using atomic force microscopy (AFM), the roughness of the 5% N-doped 3C-SiC thin film was the lowest of all the films, at 15 nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.10
• /
• pp.799-802
• /
• 2011

In this study, SiC single-crystal ingots were prepared on two seed crystals with different doping level by using the physical vapor transport (PVT) technique; then, SiC crystal wafers sliced from the grown SiC ingot were systematically investigated to find the effect of seed doping level on the doping concentration and crystal quality of the SiC. To exclude extra effects induced by adjustment of the process parameters, we simultaneously grew the SiC crystals on two seed crystals with different level, which were fabricated from previous two SiC crystal ingots.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.199-200
• /
• 2009

This paper describes the electrical properties of polycrystalline (poly) 3C-SiC thin films with different nitrogen doping concentrations. The in-situ-doped poly 3C-SiC thin films were deposited by using atmospheric-pressure chemical vapor deposition (APCVD) at $1200^{\circ}C$ with hexamethyldisilane (HMDS: $Si_2$ $(CH_3)_6)$ as a single precursor and 0 ~ 100 sccm of $N_2$ as the dopant source gas. The peaks of the SiC (111) and the Si-C bonding were observed for the poly 3C-SiC thin films grown on $SiO_2/Si$ substrates by using X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) analyses, respectively. The resistivity of the poly 3C-SiC thin films decreased from $8.35\;{\Omega}{\cdot}cm$ for $N_2$ of 0 sccm to $0.014\;{\Omega}{\cdot}cm$ with $N_2$ of 100 sccm. The carrier concentration of the poly 3C-SiC films increased with doping from $3.0819\;{\times}\;10^{17}$ to $2.2994\;{\times}\;10^{19}\;cm^{-3}$, and their electronic mobilities increased from 2.433 to $29.299\;cm^2/V{\cdot}S$.

• Journal of Sensor Science and Technology
• /
• v.17 no.5
• /
• pp.325-328
• /
• 2008

This paper describes the electrical properties of poly (polycrystalline) 3C-SiC thin films with different nitrogen doping concentrations. In-situ doped poly 3C-SiC thin films were deposited by APCVD at $1200^{\circ}C$ using HMDS (hexamethyildisilane: $Si_2(CH_3)_6)$) as Si and C precursor, and $0{\sim}100$ sccm $N_2$ as the dopant source gas. The peak of SiC is appeared in poly 3C-SiC thin films grown on $SiO_2/Si$ substrates in XRD(X-ray diffraction) and FT-IR(Fourier transform infrared spectroscopy) analyses. The resistivity of poly 3C-SiC thin films decreased from $8.35{\Omega}{\cdot}cm$ with $N_2$ of 0 sccm to $0.014{\Omega}{\cdot}cm$ with 100 sccm. The carrier concentration of poly 3C-SiC films increased with doping from $3.0819{\times}10^{17}$ to $2.2994{\times}10^{19}cm^{-3}$ and their electronic mobilities increased from 2.433 to $29.299cm^2/V{\cdot}S$, respectively.