• Journal of Korea Foundry Society
• /
• v.17 no.1
• /
• pp.28-35
• /
• 1997

SiC whisker and $Al_2O_3-SiO_2$ short fiber reinforced AC8A, AC8B and AC8B(J) marix composites were fabricated by squeeze casting method. Preform deformation, change of reinforcement volumefraction and formation of macro-segregation in two composites were investigated by using micro Vickers hardness test, analysis of macro and micro structures with OM, SEM and EDAX. $Al_2O_3-SiO_2$ short fiber preform manufactured with 5% $SiO_2$ binder in this study was considerably deformed and cracked, nevertheless, the short fibers were distributed homogeneously in the composites. In SiC whisker reinforced composites, on the other hand, preform deforming and cracking were not occurred, however, macro segregation zone formed along the infiltration routes by interface reaction during infiltration of molten metal into the preform was observed at center-low area in the composites. The decrease of hardness in the macro segregation zone resulted from the depletion of Si and Mg atoms.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.375-380
• /
• 1994

Matrices retaining electrolyte in phosphoric acid fuel cell were prepared with SiC to SiC whisker mixing ratios of 1:0.5, 1:1, 1:1.5, 1:2, 1:3 by tape casting method. When viscosity of the slurry was 5.9 poise and the SiC to SiC whisker mixing ratios were 1:1, 1:1.5, 1:2, the ranges of porosity, acid absorbency and bubble pressure were 80~90%, 2.5~6 and 700~2200 mmH2O, respectively. Those ranges are acceptable for a practical electrolyte-retaining matrix. With increasing the mixing ratio of SiC whisker to SiC, the porosity and the vol.% of large pores in the main pore size distribution which is between 1 and 10 ${\mu}{\textrm}{m}$, increased rapidly. Impedance spectroscopy was measured to know characteristics of matrix inside and contact region of matrix to catalyst layer. When the SiC to SiC whisker mixing ratio was 1:2, hydrogen ions were transported in the matrix most effectively because of high ionic conductivity and low activation energy due to high acid absorbency in spite of high interfacial resistance. The cell current density of the cell made using the matrix was 220 mA/$\textrm{cm}^2$ at 0.7 V.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1513-1520
• /
• 1994

Mechanical properties of hot-pressed SiC whisker/Al2O3 composites were strongly dependent on the granular characteristics of mixed powder, which were controlled by co-dispersion condition, the existence of steric barrier on whisker surface, and granulating method, etc. Heat-treatment of SiC whiskers at $700^{\circ}C$ for 1 hr in air was very effective both for achieving dispersion stability of whiskers with PVA adsorption and for obtaining excellent mechanical properties of resulting composites. It is believed from the fractography of composites prepared with various whisker dispersion conditions that the most common fracture origin of Al2O3 agglomerate could be attributed to whisker clusters arising due to flocculation. Further improvement of mechanical properties of composites were achieved by hot pressing green tapes prepared by Doctor-blade process, which promoted two-dimensional random alignment of whiskers.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1039-1043
• /
• 2000

$\alpha$-Si$_3$N$_4$가 20vol% 혼합된 SiC/Si$_3$N$_4$혼합물에서 $\alpha$-SiC의 일부를 SiC whisker로 치환하여 첨가한 후 180$0^{\circ}C$, 25MPa의 압력으로 hot pressing하여 SiC/Si$_3$N$_4$/SiCw 복합체를 제조하였다. SiC whisker의 첨가 함량이 증가할수록 상대밀도, 꺽임강도, 마모 저항성은 감소되었으나, 파괴인성은 크게 향상되었다. $\alpha$-SiC의 일부를 SiC whisker로의 치환은 치밀화를 억제하였으나 파괴인성의 증가는 마모 저항성을 향상시키지 않았다.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.165.1-165
• /
• 2000

• Proceedings of the Korean Ceranic Society Conference
• /
• 2004.04b
• /
• pp.48.3-48.3
• /
• 2004

• Journal of Korea Foundry Society
• /
• v.16 no.2
• /
• pp.132-140
• /
• 1996

Both cast and extruded composites of SiC whisker reinforced 6061 Al alloy matrix were fabricated by high pressure infiltration of the alloy melt into the SiC preform and subsequent hot extrusion of the composite ingots. The micro structures, age hardening behavior and mechanical properties have been examined on the both cast and extruded composites of SiCw/6061. The cast composites of SiCw/6061 were obtained in which SiC whiskers were randomly oriented. Hot extrusion of these cast composites lead to alignment of the whisker in the direction of extrusion. Strengthening effect of whisker in the extruded composites is lower than that of the cast composites. The cast composites of SiCw/6061 showed higher thensile strength and lower elongation than extruded composites of SiCw/6061 at all testing temperatures. Lower tensile strength and higher elongation of the extruded composites were attributable to fine grain structures in which grain boundary sliding occruued preferentially at elevated temperatures.

• Journal of the Korean Ceramic Society
• /
• v.36 no.2
• /
• pp.193-202
• /
• 1999

Al powder, AlN powder, SiC whisker and sintering aids were wet-mixed, and then the specimens prepared with mixed powder were reacted by nitridation at 600∼1400$^{\circ}C$ for 5 hrs. It was cleat that the higher nitridation and the more SiC whisker content were, the better bending strength was. The specimen of Al50/AlN50 reacted at 1400$^{\circ}C$ for 5hrs had the nitridation percent of 97%, the shrinkage under 2%, and the relative density of 78%. And the maximum bending strength of reaction-bonded specimen was 250 MPa. The specimens completely nitrided were post-sintered at 1700, 1800 and 1900$^{\circ}C$ for 2hrs. The post-sintered body had the shrinkage under 6% and the relative density of 86%. Because of the formation of solid solution between AlN and SiC whisker over 1800$^{\circ}C$, the promotion of mechanical properties according to SiC whisker addition was not observed. The post-sintered body had the maximum bending strength of 195 MPa.

• Journal of the Korean Ceramic Society
• /
• v.23 no.6
• /
• pp.59-65
• /
• 1986

Flexural strength fracture toughness and strengthening mechanisms of cordierite ceramics reinforced by SiC whiskers up to 40vol% were investigated. The specimens were hot pressed at Ar atmosphere. The porosity increased with the SiC whisker content. Flexural strength and single edge notch beam fracture toughness were measured up to 1,000$^{\circ}C$. Extrapolating to zero porosity the reinforced composites exhibited in-creasings in flexural strength and fracture toughness with the SiC whisker content. The composites were strengthened mainly by load transfer crack impediment and partially by crack deflection mechanisms. Impurities played an important role in determining the mechanical properties of the composites.

• Korean Journal of Materials Research
• /
• v.3 no.6
• /
• pp.606-613
• /
• 1993

This was studied about aging characteristic of AC4A/$SiC_{w}$ 10-30v/o reinforced composite. Aging hardenability was decreased $SiC_{w}$ 30% > 10% > 20%. Aging hardening of T6 treatmented composite was higher absolute value than AC4A I/M material. And this results indicated initial hardening phenomenon according to increase $SiC_{w}$ volume fraction. Reinforced effect by pressure was the same effect as before aging treatment and the best condition pressure at 75MPa. Similar to reinforced effect according to $SiC_{w}$ volume fraction was 30 % > 10 % > 20 %. In case of pressure is low, whisker is not break the same time press with base metal after wetting. After it is wetting with base metal, a part transformed or wetting part break and whisker maintain original shape or a part transformed on the otherhand, in case of pressure is high, whisker is break in same time it was not against pressure and whisker's shape is near a polygon or spherical shape.