Abstract
This was studied about aging characteristic of AC4A/$SiC_{w}$ 10-30v/o reinforced composite. Aging hardenability was decreased $SiC_{w}$ 30% > 10% > 20%. Aging hardening of T6 treatmented composite was higher absolute value than AC4A I/M material. And this results indicated initial hardening phenomenon according to increase $SiC_{w}$ volume fraction. Reinforced effect by pressure was the same effect as before aging treatment and the best condition pressure at 75MPa. Similar to reinforced effect according to $SiC_{w}$ volume fraction was 30 % > 10 % > 20 %. In case of pressure is low, whisker is not break the same time press with base metal after wetting. After it is wetting with base metal, a part transformed or wetting part break and whisker maintain original shape or a part transformed on the otherhand, in case of pressure is high, whisker is break in same time it was not against pressure and whisker's shape is near a polygon or spherical shape.
자동차용 부품재 및 일반산업용 재료로 사용되고 있는 AC4A Al합금에 $SiC_{w}$ preform을 용탕단조법으로 강화시킨 복합재료의 시효 경화능은 SiC/aub w/30%> 10%> 20%의 순이며, 이는 $100^{\circ}C$-$400^{\circ}C$까지의 등시시효에서도 같은 결과를 나타낸다. 복합재의 T6처리재가 AC4A I/M재 보다도 시효경화능이 크고 절대값이 높았으며 $SiC_{w}$체적분율 증가에 따라 초기경화 현상을 나타내었다. 가압력에 의한 강화효과는 미시효때와 같이 가압력 75MPa일때 가장 좋았으며, $SiC_{w}$는 30%> 10%>20%순이었다. 가압력이 낮을경우 가입과 동시에 휘스커는 파단되지 않고 원래의 형상을 유지하거나 기지금속과 wetting으로 일부 변형된 다음 가압이 진행되면서 이부부의 응력 집중으로 wetting부가 파단하게 되어 가압력을 이기지 못하고 파단하게 되어 휘스커 모양도 다각형이거나 구형에 가깝게 되며 가압이 진행됨에따라 재차 파단되므로써 길이도 짧게 된다. 한편 가압력 75 MPa일 경우 휘스커의 형상은 일부 변형된 것과 잘게 파손된 것이 고르게 공존하고 있어 강화효과가 가장 우수한 것으로 사료된다.