• Journal of the Korean Ceramic Society
• /
• v.45 no.8
• /
• pp.486-492
• /
• 2008

Reaction bonded silicon carbide(RBSC) composite for heat-exchanger was fabricated by molten Si infiltration method. The raw materials with variable particle sizes were used in this experience. The finer the particle size in sintered silicon carbide was the more increasing 3-point bending strength and fracture toughness. As the adaptable particle sizes had been occupied interstice arising from packing sample, the mechanical properties were increased. In the PCS1-1 sample, the 3-point bending strength and fracture toughness were 323MPa and $4.9\;MPa{\cdot}m^{1/2}$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.948-954
• /
• 2002

Porous reaction bonded SiC with high fracture strength was developed using Si melt infiltration method for use of the support layer in high temperature gas filter that is essential to develop the next generation power system such as integrated gasification combined cycle system. The porosity and pore size of porous RBSC developed in this study were in the range of 32∼36% and 37∼90 ${\mu}m$ respectively and the maximum fracture strength of porous RBSC fabricated was 120 MPa. The fracture strength and thermal shock resistance of porous RBSC fabricated by Si melt infiltration were much improved compared to those of commercially available porous clay bonded SiC due to the formation of the strong SiC/Si interface between SiC particles. The characteristics of pore structure of porous RBSC was varied depending on the amounts of residual Si as Well as the size of SiC particle used in green body.

• Journal of the Korean Society of Safety
• /
• v.33 no.1
• /
• pp.1-6
• /
• 2018

The effects of the fiber direction, specimen size and temperature on the compressive strength of carbon fiber reinforced silicon carbide composite (C/SiC composite) manufactured by liquid silicon infiltration(LSI) is investigated. Tests were conducted in accordance with ASTM C 695 at room temperature and elevated temperatures. Experiments are conducted with two different specimens considering grain direction. With grain (W/G) specimens have a carbon fibers parallel to the load direction, but across grain (A/G) specimens have a perpendicular carbon fibers. To verify the specimen size effect of C/SiC composite, two types of specimens are manufactured. One has a one to two ratio of diameter to height and the other has a one to one ratio. The compressive strength of C/SiC composite increased as temperature rise. As specimens are larger, compressive strength of A/G specimens increased, however compressive strength of W/G decreased.

• Journal of Powder Materials
• /
• v.28 no.1
• /
• pp.51-58
• /
• 2021

The conversion of carbon preforms to dense SiC by liquid infiltration is a prospectively low-cost and reliable method of forming SiC-Si composites with complex shapes and high densities. Si powder was coated on top of a 2.0wt.% Y2O3-added carbon preform, and reaction bonded silicon carbide (RBSC) was prepared by infiltrating molten Si at 1,450℃ for 1-8 h. Reactive sintering of the Y2O3-free carbon preform caused Si to be pushed to one side, thereby forming cracking defects. However, when prepared from the Y2O3-added carbon preform, a SiC-Si composite in which Si is homogeneously distributed in the SiC matrix without cracking can be produced. Using the Si + C → SiC reaction at 1,450℃, 3C and 6H SiC phases, crystalline Si, and Y2O3 were generated based on XRD analysis, without the appearance of graphite. The RBSC prepared from the Y2O3-added carbon preform was densified by increasing the density and decreasing the porosity as the holding time increased at 1,450℃. Dense RBSC, which was reaction sintered at 1,450℃ for 4 h from the 2.0wt.% Y2O3-added carbon preform, had an apparent porosity of 0.11% and a relative density of 96.8%.

• Korean Journal of Materials Research
• /
• v.31 no.5
• /
• pp.301-311
• /
• 2021

The conversion of all carbon preforms to dense SiC by liquid infiltration can become a low-cost and reliable method to form SiC-Si composites of complex shape and high density. Reactive sintered silicon carbide (RBSC) is prepared by covering Si powder on top of 0.5-5.0 wt% Y₂O₃-added carbon preforms at 1,450 and 1,500℃ for 2 hours; samples are analyzed to determine densification. Reactive sintering from the Y₂O₃-free carbon preform causes Si to be pushed to one side and cracking defects occur. However, when prepared from the Y₂O₃-added carbon preform, an SiC-Si composite in which Si is homogeneously distributed in the SiC matrix without cracking can be produced. Using the Si + C = SiC reaction, 3C and 6H of SiC, crystalline Si, and Y₂O₃ phases are detected by XRD analysis without the appearance of graphite. As the content of Y₂O₃ in the carbon preform increases, the prepared RBSC accelerates the SiC conversion reaction, increasing the density and decreasing the pores, resulting in densification. The dense RBSC obtained by reaction sintering at 1,500 ℃ for 2 hours from a carbon preform with 2.0 wt% Y₂O₃ added has 0.20 % apparent porosity and 96.9 % relative density.

• Journal of the Korean Ceramic Society
• /
• v.44 no.7
• /
• pp.381-386
• /
• 2007

A porous reaction bonded silicon carbide (RBSC) was fabricated by a molten Si infiltration method. The porosity and flexural strength of porous RBSC fabricated in this study were dependent upon the amount of carbon source used in the SiC/carbon preform as well as the amount of Si infiltrated into the SiC/carbon preform. The porosity and flexural strength of porous RBSC were in the range of $20 vo1.{\sim}49 vo1.%$ and $38{\sim}61 MPa$, respectively. With increase of carbon contents and molten Si for infiltration, volume fraction of the pores was gradually decreased, and flexural strength was increased. The porous RBSCs fabricated with the same amount of molten Si show less residual Si around neck with increase of carbon source, as well as a new SiC was formed around neck which resulted in the decreased porosity and improvement of the flexural strength. In addition, decrease of the porosity and increase of the flexural strength were also obtained by increase of the amount of molten Si with the same amount of carbon source. However, it was found that the flexural strength of porous RBSC depends on the porosity rather than the amount of the newly formed SiC in neck phase between SiC particles used as a starting material.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.11a
• /
• pp.446-461
• /
• 2005

본 연구에서는 반응소결 탄화규소 다공질 지지체 개발을 위하여 SiC/C로 이루어진 성형체를 사용한 Si melt infiltration 공정 및 SiC/C/Si으로 이루어진 성형체를 사용하는 Si embedding 공정 개발이 이루어졌다. 개발된 반응소결 탄화규소 다공질 지지체의 기공률은 38% 이상이었으며 평균기공은 130 ${\mu}m$ 크기이었다. Si melt infiltration 방법으로 제조된 반응소결 탄화규소 다공질 지지체의 파괴강도는 상용 반응소결 탄화규소 지지체의 파괴강도보다 최대 200% 이상 높게 나타났다. 본 연구에서는 용융 Si의 침윤공정을 이용하여 반응소결 탄화규소 여과층을 갖는 반응소결 탄화규소 필터 및 그 제조공정이 개발되었다. 개발된 반응소결 탄화규소 필터의 필터 특성은 상용 탄화규소 필터의 필터 특성과 대체적으로 대등한 것으로 조사되었다.

• Composites Research
• /
• v.30 no.2
• /
• pp.108-115
• /
• 2017

Among several fabrication processes of $SiC_f/SiC$ composites, the chemical vapor infiltration (CVI) process has attractive advantages in manufacturing complex net-or near-net-shape components at relatively low temperatures, easily controlling the microstructure of the matrix and obtaining the highest SiC purity level. However, it has disadvantages in that the ratio of residual pores in matrix is higher than other processes and processing time is relatively long. To reduce the residual porosity, the whisker-growing-assisted CVI process, which is composed of whisker growth and matrix filling steps has been developed. The whiskers grown before matrix filling may serve to divide the large natural pores between the fibers or bundles so that the matrix can be effectively filled into the finely divided pores. In this paper, the fundamentals of the CVI process for preparation of $SiC_f/SiC$ composites and some experimental results prepared by CVI and whisker-growing-assisted CVI processes are briefly introduced.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1114-1118
• /
• 2000

Ti 및 C 입자로 이루어진 다공질 성형체에 용융 Si의 침윤 및 반응으로 새로운 Ti$_3$SiC$_2$합성공정이 개발되었다. 용융 Si 침윤에 의한 Ti$_3$SiC$_2$합성공정에서는 이제까지 연구된 합성방법 보다 넓은 조성 범위에서 Ti$_3$SiC$_2$의 합성이 이루어졌다. 용융 Si을 활성 매질로 사용한 Ti$_3$SiC$_2$의 합성에서는 성형체 조성, 원료 입자 크기 및 침윤되는 용융 Si의 양에 따라 합성되는 상 및 각 합성상의 양이 다르게 나타났다. Ti:Si:C=3:1:6 조성을 제외한 모든 조성의 시편에서 Ti$_3$SiC$_2$상이 합성되었으며, 일부 조성을 제외한 모든 조성의 시편에서 Ti$_3$SiC$_2$, TiC 및 SiC가 함께 합성되었다. 작은 Ti 입자로 이루어진 성형체를 사용하여 합성한 시편에서 Ti$_3$SiC$_2$상의 합성이 용이하게 이루어졌으며, 성형체 조성 및 침윤되는 Si의 양이 화학양론적으로 Ti$_3$SiC$_2$에 근접한 조성을 갖는 시편에서 Ti$_3$SiC$_2$를 높은 수율로 합성할 수 있었다.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.430-434
• /
• 2014

$SiC_f$/SiC composites were prepared using the hybrid process of chemical vapor infiltration (CVI) and polymer impregnation and pyrolysis (PIP). Before the application of PIP, partially matrix-filled preform composites with different densities were fabricated by control of chemical vapor infiltration time and temperature. The changes of the final density of the $SiC_f$/SiC composites had a tendency similar to that of preform composites partially filled by CVI. Composites with lower density after the CVI process had a larger increment of density during the PIP process. Three types of microstructures were observed on the fractured surface of the composite: 1) well pulled-out fibers and lower density, 2) slightly pulled-out fibers and higher density, and 3) only bulk SiC. The different fractions and distributions of the microstructures could have an effect on the mechanical properties of the composites. In this study, $SiC_f$/SiC composites prepared using a hybrid process of CVI and PIP had density values in the range of $1.05{\sim}1.44g/cm^3$, tensile strength values in the range of 76.4 ~ 130.7 MPa, and fracture toughness values in the range of $11.2{\sim}13.5MPa{\cdot}m^{1/2}$.