• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.615-622
• /
• 1993

In order to increase chemical durability of thin films in binary system B2O3-SiO2 and Al2O3-SiO2 on the slide glass by the dip-coating technique from TEOS(Tetraethyl Orthosilicate) and boric acid or aluminum nitrate, phosphoric acid(5~20mol%) was added, respectively. Corrosion of acid and alkali of samples treated with 1N, HCl, NaOH and distilled water at 10$0^{\circ}C$ for 15 minute, were measured IR transmittance and variance of transmittance at visible range. Surface structure of thin film was investigated with SEM and formation of crystal phase according to additiion of phosphoric acid was measrued with XRD. In Al2O3-SiO2 system, change of remarkable characteristic was not obtained at the addition of P2O5 but transmittance of thin film was decreased with addition of P2O5 in B2O3-SiO2 system.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.325-326
• /
• 2006

Using $6wt%Y_2O_3-2wt%Al_2O_3$ as sintering additives and Si as a raw powder, the continuously porous in-situ $Si_2N_2O-Si_3N_4$ bodies were fabricated by multi-pass extrusion process and their microstructures were investigated depending on the addition of carbon (0-9wt%) in the mixture powder. The introduction of $Si_2N_2O$ fibers observed in the unidirectional continuous pores as well as in the pore-frame regions of the nitrided bodies can be an effective method in increasing the filtration efficiency. In the case of no carbon addition, the network type $Si_2N_2O$ fibers with high aspect ratio appeared in the continuous pores with diameters of 150-200 nm. However, in the case of 9wt% C addition, the fibers were found without any network type and had diameters of 200-250 nm.

• Journal of the Korean Ceramic Society
• /
• v.29 no.2
• /
• pp.127-135
• /
• 1992

It has been reported that natural petalite showed a low negative thermal coefficient and wide coefficient and wide coexisting region with liquid phase in Li2O-Al2O3-SiO2 system. Therefore, we investigated variation of microstructure and thermal and mechanical properties when the amount of SiO2 content in petalite compound and MgO addition to it compound were changed. As SiO2 content exceeded 80 wt%, crystal phases of $\beta$-cristobalite and $\beta$-spondumene solid solution were formed. Generally, the densification and bending strength were increased by the addition of MgO, but the positive thermal coefficient was found in the case of MgO 10 wt% addition because of second phase and glassy phase.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.237-241
• /
• 2000

The effects of Si addition on the precipitation processes of in Al-Cu-Si alloy films were studied by the transmission electron microscopy. Deposition of an Al-1.5Cu-1.5Si (wt. %) film at $305^{\circ}C$ resulted in formation of fine, uniformly distributed spherical $\theta$-phase particles due to the precipitation of the $\theta$ and Si phase particles during deposition. For deposition at $435^{\circ}C$, fine $\theta$-phase particles precipitated during wafer cooldown, while coarse Si nodules formed at the sublayer interface during deposition. The film susceptibility to corrosion is discussed in relation to the film microstructure and deposition temperature.

• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.15-20
• /
• 1994

The effect of SiC addition on sintering behaviors and microstructures of TiB2 ceramics were studied. The sintering of TiB2 was limited due to the surface diffusion and rapid grain growth at high temperature. However the addition of SiC to TiB2 ceramics improved the densification to above 99% of the theoretical density. The sintering of TiB2-SiC composite starts at 120$0^{\circ}C$ with the melting of the oxides in particle surface as impurities. After the reduction of the oxide by additional cabon at above 140$0^{\circ}C$, the grain boundary diffusion through the interface of TiB2-SiC play an important role. TEM observation showed neither chemical reactions nor other phases formed at the TiB2-SiC interfaces but the microcracks were observed due to the mismatch of thermal expansion between TiB2-SiC.

• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.668-676
• /
• 1997

Al2O3/SiC nanocomposites are fabricated through intensive ball milling to mix fine SiC particles uniformly with the Al2O3 powder. Another role of milling is to reduce particle sizes by crushing particles as well as agglomerates. However, balls are worn during ball milling and the sample powder mixtures pick up to weight loss of the balls. In this study, pressureless sintering was performed to obtain Al2O3/SiC nanocomposites. It was found that the wear rate of zirconia balls during milling was considerable, and the zirconia addition after even a few hours of ball milling could increase the sintering rates of the nanocomposites significantly. Thus, addition of ZrO2 changed the sintering behaviors as well as mechanical properties of Al2O3/SiC nanocomposites.

• Journal of Korea Foundry Society
• /
• v.25 no.3
• /
• pp.128-133
• /
• 2005

The effects of Mn and Cr on the crystallization behaviors of Fe-bearing intennetallics in A356 alloy were studied. Coarse and acicular ${\beta}-Al_{5}$FeSi phase in A356-0.20wt.%Fe alloy was modified into small ${\alpha}$-Al(Fe,Mn)Si and ${\alpha}$-Al(Fe,Cr)Si phases in response to Mn and Cr addition, respectively. Increasing of Mn addition amount elevates the crystallizing temperature of ${\alpha}$-Al(Fe,Mn)Si and the Mn/Fe ratio in the ${\alpha}$-Al(Fe,Mn)Si. Cr is more effective to modify ${\beta}-Al_{5}$FeSi in comparison with Mn. ${\alpha}$-Al(Fe,Mn)Si phase had BCC/SC dual structure.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.1
• /
• pp.3-11
• /
• 1994

Cyclic hot corrosion studies have been carried out on(82~94) wt. % Fe-(5, 10, 15) wt. % Cr alloys con-taining either (1, 3)wt. % of Si or Pt as minor alloying elements in molten salts of($Na_2SO_4$+NaCl) between 820 and $920^{\circ}C$. Si or Pt decreased corrosion rate with the most pronounced effect being observed for alloys having 15wt. %Cr. Especially, as Si or Pt contents are increased from 1 to 3 wt. %, improved corrosion resistance was obtained. The beneficial effect of Si addition is due to the presence of the Si-rich second phase along the grain boundaries as well as the formation of the protective $SiO_2$layer between substrates and oxide scale. The Pt addition also increased the corrosion resistance by enhancing the formation ($Cr_2O_3$+layers and by increasing the adherence of the oxide scale.

• Journal of the Korean Vacuum Society
• /
• v.11 no.1
• /
• pp.16-21
• /
• 2002

Selective epitaxial growth(SEG) of silicon were performed at low temperature under an ultraclean environment below $1000^{\circ}C$ using ultraclean $Si_2H_6$ and $H_2$ gases ambient in low pressure chemical vapor deposition(LPCVD). As a result of ultraclean processing, epitaxial Si layers with good quality were obtained for uniform and SEG wafer at temperatures range 600~$710^{\circ}C$ and an incubation period of Si deposition only on $SiO_2$ was found. Low-temperature Si selectivity deposition condition and epitaxy on Si were achieved without addition of HCl. The epitaxial layer was found to be thicker than the poly layer deposited over the oxide. Incubation period prolonged for 20~30 sec can be obtained by $O_2$addition. The surface morphologies & cross sections of the deposited films were observed with SEM, The structure of the Si films was evaluated XRD.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.1
• /
• pp.15-21
• /
• 2008

SiC has an excellent resistance to oxidation and corrosion, high temperature strength and good thermal conductivity. However, it is difficult to density because of its highly covalent bonding characteristics. Hot-press sintering process was applied to fabricate fully densified SiC ceramics with carbon and boron addition as a sintering additive. The addition of carbon improved the mechanical properties of SiC because it could induce a fine and homogeneous microstructure by the suppression of abnormal growth of SiC grain. Also, the addition of carbon could control the phase transformation of SiC. The phase transformation of 6H to 4H increased with sintering temperature but the addition of carbon decreased that kind of phase transformation.