• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.415-420
• /
• 2002

This study is intended to investigate the influence of mineral admixtures on the autogenous and drying shrinkage of high performance concrete. According to results, drying shrinkage increases with increase of fly ash content, and it does not show difference with replacement of blast furnace slag powder. It increases when incorporating silica fume or fly ash and silica fume together. The autogenous shrinkage shows increasing tendency with increase of silica fume and blast furnace slag powder content, and incorporating of silica fume or fly ash and silica fume together has effects on reducing autogenous shrinkage. Therefore, it is considered that application of both silica fume and fly ash can reduce the cracks caused by autogenous shrinkage, including enhancement in strength and placeability of high performance concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.7 no.2
• /
• pp.159-167
• /
• 2003

Cracks in reinforced concrete structures reduce overall durability by allowing the penetration of water and aggressive agents, thereby accelerating the deterioration of the reinforcing steel. Highway pavement and bridge decks are especially susceptible to this type of deterioration since these structures exhibit high rates of shrinkage and are frequently exposed to aggressive environmental conditions. The objectives of this investigation included the development of experimental procedures for assessing shrinkage cracking potential of recycled aggregate concrete, the evaluation of mix composition on shrinkage cracking potential, and the development of theoretical models to simulate early-age cracking behavior. Specifically, the influences of shrinkage-reducing admixture(SRA) and recycled aggregate concrete were investigated. The shrinkage-reducing admixture substantially reduces free shrinkage and restrains shrinkage cracking while providing similar mechanical properties. A fracture mechanics modeling approach was developed to predict the behavior of a variety of restrained concrete specimens. This modeling approach was used to successfully explain experimental results from a variety of mixture compositions. The model was used to demonstrate the influence of material and structural properties on the potential for cracking.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.216-217
• /
• 2017

Slag cement or ternary blended cement is mainly used for non-structural lean concrete for the purpose of foundation work or protection of the waterproof layer on the roof of buildings. However, such non-structural lean concrete has a lot of drying shrinkage cracks, which makes it difficult to maintain the quality of the structure. Therefore, in this study, the compressive strength and the drying shrinkage of ternary blended cement(blended of portland cement, blast furnace slag, fly ash from combined heat and power Plant) for non-structural lean concrete were examined. As a result, it was confirmed that this non-structural lean concrete reduced drying shrinkage compared to the conventional ternary blended cement using fly ash from power plant.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.285-288
• /
• 2004

Generally, the autogenous shrinkage of high performance concrete is important in that it can lead the early cracks in concrete structures. In the previous study, The. autogenous shrinakge of HPC was found to decrease with incresing expansive additive and shrinakge reduction agent. In case of combined use, the autogenous shrinakge was more reduction than in case separate use. The purpose of this study is to derive a realistic equation to estimate the autogenous shrinakge model of high performance concrete with exapnsive agent and shrinakge reduction agent. investigated the durability of high performance concrete using expansive additive and shrinkage reducing agent. The proposed equation showed reasonably good correlation with test data on autogenous shrinakge of high performance concrete with material for shrinkage reduction.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.321-326
• /
• 2003

The nonlinear humidity distribution occurs due to the moisture diffusion when a concrete is exposed to an ambient air. These nonlinear humidity distribution induces shrinkage cracks on surfaces of the concrete. Because shrinkage cracks largely affect the durability and serviceability of concrete structures, the moisture diffusion in concrete must be investigated. The purpose of this paper is to propose a model of the moisture diffusion coefficient that governs moisture diffusion within concrete structures. To propose the model, numerical analysis were performed based on several experiments. Because the moisture diffusion coefficient is changed with aging, especially at early ages, the proposed model includes aging effect by terms of the porosity as well as the humidity of concrete.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.11
• /
• pp.416-424
• /
• 2019

In Korea, press concrete in basements is mainly applied using plain concrete. This system has undesirable defects such as cracks caused by plastic shrinkage and irregular temperature distribution. To solve this problem, metal lath and fibers have been used in the past. However, they have not been effective in controlling cracks. This study analyzed the reduction of plastic shrinkage cracking for press concrete using various admixtures in a basement has been. In the air contents test, the specimens with various admixtures showed air contents similar to plain concrete (4.5±1.5%). The specimens using silica fume, super plasticizer agent, and SBR showed higher compressive strength by about 10-15% than plain concrete. Cracking decreased when the MC, super plasticizer, and SBR were added. When MC was used in the concrete, the plastic shrinkage did not occur.

• Magazine of the Korea Concrete Institute
• /
• v.11 no.1
• /
• pp.141-148
• /
• 1999

Recently, high performance concrete developed has a good quality at fresh and hardened state, but high binder contents results in spending much money on manufacturing and many cracks by drying and autogenous shrinkage, Therefore, in this paper, not only prevention of cracks caused by drying and autogenous shrinkage, but improvement of quality and accomplishment of economy by applying F.A(fly ash), S.F(silica fume) and CSA(calcium sulfa aluminate) expansive additives as an inorganic admixtures in W/B 35% are discussed. According to the experimental results, when 5% of CSA expansive additives and 15:5(F.A:S.F)are replaced at unit cement content, high performance concrete with both good fluidity at fresh state and high compressive strength, compensation of drying and autogenous shrinkage at hardened state are accomplished.

• Journal of the Korea Concrete Institute
• /
• v.24 no.3
• /
• pp.233-240
• /
• 2012

Hybrid SHCC is being researched actively for its excellent performance in controlling macro and micro cracks using macro and micro fibers, respectively. However, a significant autogenous shrinkage of SHCC is expected since it possesses high unit cement volume in its mix proportion, resulting in autogenous shrinkage cracks. Therefore, this study was performed to evaluate mechanical property of shrinkage-reducing type hybrid SHCC mixed together with steel fiber and PE fiber with excellent micro/macro crack controlling performance. In order to evaluate mechanical property of shrinkage-reducing type hybrid SHCC, replacement ratios of 0% and 10% of expansive admixture and water to binder ratios of 0.45, 0.3, and 0.2 were considered as variables. Then, shrinkage, compressive, flexural, and direct tensile tests were performed. The test results showed that mix proportion with W/B 0.3 significantly improved mechanical performance by using 10% replacement of expansive admixture.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.731-736
• /
• 2001

In this thesis, the study on controlling of cracks of concrete box culvert in early ages is presented. The optimum construction method and economical analysis were proposed also through the experiment of the material and field test. As a result of the experiment of the material, using fly ash, CSA expansive agent and BELITE cement(type IV) showed good result in the control of cracks induced by heat of hydration and shrinkage. As a result of construction test analysis, the maintenance time of form system did not show a big difference in controlling of cracks. Control of distribution of reinforcement, spacing of expansion joint and use of BELITE cement showed big differences in the control of cracks in early ages. As a result of economical analysis, control of construction variables before construction can make it possible to reduce the repair expense.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10b
• /
• pp.1095-1100
• /
• 2000

Concrete structure often exhibit cracks due to the combination of material construction and design error. Minor crack can be tolerated depending on exposure condition, but major cracks are aesthetically unpleasant and affect the durability and safety of the structure. All of the reinforced concrete structure have many inevitable cracks for various reason such as drying shrinkage, heat liberation of cement and over loads. Epoxy resin injection widely used for repairing cracks in concrete is too sensitive to high temperature. Besides, the problem in the epoxy resin injection is the difficulty of quality control after execution. Whereas, Ultra Fine Cement is similar in coefficient of thermal expansion and modulus of elasticity to concrete. The objective of the study is to find out that it is possible for Ultra Fine Cement to be used for repairing cracks in reinforced concrete.