• Journal of Aerospace System Engineering
• /
• v.14 no.5
• /
• pp.73-82
• /
• 2020

Recently, there has been an increase in additive manufacturing for the fabrication of liquid rocket engines. This technology can innovate conventional fabrication methods to reduce the lead time and manufacturing cost and can enhance the performances such as weight reduction. In this study, a literature survey is presented that includes types, advantages, disadvantages, and foreign government-based projects of the technology related to liquid rocket engine manufacturing. The present survey focuses on the technology that has been applied to various components such as turbopumps and valves while much larger efforts are made for combustion chambers with regenerative cooling channels and diverging nozzles, as the advantages of the technology are maximized for the applications.

• Tribology and Lubricants
• /
• v.34 no.6
• /
• pp.270-278
• /
• 2018

STS 316L prepared by additive manufacturing (AM) exhibits deterioration of mechanical properties and wear resistance due to the presence of defects such as black-of-fusion defects, internal porosity, residual stress, and anisotropy. In addition, high surface roughness (integrity) of AM products remains an issue. This study aimed to apply ultrasonic nanocrystal surface modification (UNSM) technology to STS 316L prepared by AM to increase the surface hardness, to reduce the surface roughness, and to improve the friction and wear behavior to the level achieved by bulk material manufactured using traditional processes. Herein, the as-received and polished specimens were treated by UNSM technology and their resulting properties were compared and discussed. The results showed that UNSM technology increased the surface hardness and reduced the surface roughness of the as-received and polished specimens. These results can be attributed to grain size refinement and pore elimination from the surface. Moreover, the friction of the as-received and polished specimens after UNSM technology was lower compared to those of the as-received and polished specimens, but no significant differences in wear resistance were found.

• Korean Journal of Materials Research
• /
• v.28 no.11
• /
• pp.663-670
• /
• 2018

H13 tool steels are widely used as metallic mold materials due to their high hardness and thermal stability. Recently, many studies are undertaken to satisfy the demands for manufacturing the complex shape of the mold using a 3D printing technique. It is reported that the mechanical properties of 3D printed materials are lower than those of commercial forged alloys owing to micropores. In this study, we investigate the effect of microstructures and defects on mechanical properties in the 3D printed H13 tool steels. H13 tool steel is fabricated using a selective laser melting(SLM) process with a scan speed of 200 mm/s and a layer thickness of $25{\mu}m$. Microstructures are observed and porosities are measured by optical and scanning electron microscopy in the X-, Y-, and Z-directions with various the build heights. Tiny keyhole type pores are observed with a porosity of 0.4 %, which shows the lowest porosity in the center region. The measured Vickers hardness is around 550 HV and the yield and tensile strength are 1400 and 1700 MPa, respectively. The tensile properties are predicted using two empirical equations through the measured values of the Vickers hardness. The prediction of tensile strength has high accuracy with the experimental data of the 3D printed H13 tool steel. The effects of porosities and unmelted powders on mechanical properties are also elucidated by the metallic fractography analysis to understand tensile and fracture behavior.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.3
• /
• pp.211-218
• /
• 2019

Purpose: The purpose of the present study was to compare the accuracy of four different metal copings fabricated by CAD/CAM technology and to evaluate clinical effectiveness. Materials and methods: Composite resin tooth of the maxillary central incisor was prepared for a metal ceramic crown and duplicated metal die was fabricated. Then scan the metal die for 12 times to obtain STL files using a confocal microscopy type oral scanner. Metal copings with a thickness of 0.5 mm and a cement space of $50{\mu}m$ were designed on a CAD program. The Co-Cr metal copings were fabricated by the following four methods: Wax pattern milling & Casting (WM), Resin pattern 3D Printing & casting (RP), Milling & Sintering (MS), Selective laser melting (SLM). Silicone replica technique was used to measure marginal and internal discrepancies. The data was statistically analyzed with One-way analysis of variance and appropriate post hoc test (Scheffe test) (${\alpha}=.05$). Results: Mean marginal discrepancy was significantly smaller in the Group WM ($27.66{\pm}9.85{\mu}m$) and Group MS ($28.88{\pm}10.13{\mu}m$) than in the Group RP ($38.09{\pm}11.14{\mu}m$). Mean cervical discrepancy was significantly smaller in the Group MS than in the Group RP. Mean axial discrepancy was significantly smaller in the Group WM and Group MS then in the Group RP and Group SLM. Mean incisal discrepancies was significantly smaller in the Group RP than in all other groups. Conclusion: The marginal and axial discrepancies of the Co-Cr coping fabricated by the Wax pattern milling and Milling/Sintering method were better than those of the other groups. The marginal, cervical and axial fit of Co-Cr copings in all groups are within a clinically acceptable range.

• Journal of Powder Materials
• /
• v.24 no.3
• /
• pp.195-201
• /
• 2017

In this study, H13 tool steel sculptures are built by a metal 3D printing process at various laser scan speeds. The properties of commercial H13 tool steel powders are confirmed for the metal 3D printing process used: powder bed fusion (PBF), which is a selective laser melting (SLM) process. Commercial H13 powder has an excellent flowability of 16.68 s/50 g with a Hausner ratio of 1.25 and a density of $7.68g/cm^3$. The sculptures are built with dimensions of $10{\times}10{\times}10mm^3$ in size using commercial H13 tool steel powder. The density measured by the Archimedes method is $7.64g/cm^3$, similar to the powder density of $7.68g/cm^3$. The hardness is measured by Rockwell hardness equipment 5 times to obtain a mean value of 54.28 HRC. The optimum process conditions in order to build the sculptures are a laser power of 90 W, a layer thickness of $25{\mu}m$, an overlap of 30%, and a laser scan speed of 200 mm/s.