• 설비공학논문집
• /
• 제25권8호
• /
• pp.438-442
• /
• 2013

The alternative refrigerant R436B is applied, to assess the application feasibility for a commercial cooling water system. The characteristic stability was verified by Sealed glass tube test and Autoclave test. R436B is chemically stable with the compressor material. The Oil miscibility test shows the usual compressor oil mixed well with R436B. Through the life acceleration test, the cooling performance is maintained. Though slight changes in oil and capillary tube diameter were found, they were within the permitted range. R436B should be applied to commercial cooling water systems as a simple replacement for the usual refrigerant.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.103-106
• /
• 1999

In this paper, we suggest the FED packaging technology that have 4mm thickness, using sodalime glass-to-sodalime glass electrostatic bonding. It based on conventional silicon-glass bonding. The silicon film was deposited an around the exhausting hole on FED backside panel. And then, the silicon film of panel was successfully bonded with capping(bare) glass in vacuum environment and the FED panel was vacuum-sealed. In this method, we could achieve more 153 times increased conductance and 200 times increased vacuum efficiency than conventional tube packaging method. The vacuum level in panel, by SRG test, was maintained about low 10$_{-4}$ Torr during above two months And, the light emission was observed to 0.7-inch tubeless packaged FED. Then anode current was 34 $\mu$ A. Emission stability was constantly measured for 10 days.

• Elastomers and Composites
• /
• 제42권1호
• /
• pp.20-31
• /
• 2007

고무의 안정성과 신뢰성 확보를 위해 재료 특성과 수명 평가는 매우 중요하다. 본 연구에서는 연료전지용 고무 가스켓으로 사용되는 황으로 가황한 NBR compound의 수명을 예측하였다. 5, 6, 7 vol% 황산농도에서 120, 140, $160^{\circ}C$ 온도로 각각 3시간에서 600시간까지 가속 노화시험을 하였다. 고무를 황산용액 안에 침지시키기 위해 pyrex glass tube를 사용하였다. 그리고 가열 시간 동안 용액의 증발을 막기 위하여 pyrex glass tube 양쪽 끝을 막았다. 연료전지용 가스켓인 NBR 고무의 수명을 예측하기 위하여 가속 산-열 노화시험 후 물성 실험을 하였으며 산-열 노화시험에서 물리적 특성의 영향을 연구하기 위하여 인장강도, 신장율, 경도, 가교밀도를 측정하였다. 인장강도는 황산농도와 온도가 증가함에 따라서 감소되었는데 이 결과로 Arrhenius 식을 유도하여 수명을 평가하였다.