• 한국압력기기공학회 논문집
• /
• 제11권1호
• /
• pp.25-32
• /
• 2015

Many crack flaws have been detected at tubing seal weld zone in Steam Generator with Alloy600 material tubes. it is very difficult to discriminate the signal from parent material and that from weld zone because weld zone gives complicated ECT signal due to manufacturing processes. ECT signal analysis in the seal weld zone is very important since the tubes with crack in this area shall be out of service by plugging. The purpose of this paper is to distinguish between Parent material and Weld Zone ECT signal in the seal weld zone through the demonstration test of Steam Generator seal weld mock-up.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.273-275
• /
• 2005

Variation of hardness and corrosion potential of welding zone was investigated when cold arc welding of cast iron was carried out with a parameter of Ni electrode. Hardness of HAZ was the highest compared to other welding zone. And corrosion potential of HAZ was also more negative value than other welding zone. However there was not a proportional relation between hardness and corrosion potential. Local corrosion of HAZ was clearly appeared than other welding zone by small anode and large cathode in seal water solution.

• 한국압력기기공학회 논문집
• /
• 제11권1호
• /
• pp.20-24
• /
• 2015

Steam generator(S/G) tubes in pressurized water reactor (PWR's) are subject to several types of degradation. This degradation includes denting, pitting, intergranular attack(IGA), intergranular stress corrosion cracking(IGSCC), fatigue, fretting and wear. Degradation can be derived from either the primary side(inside) or the secondary side(outside) of the tube. Recent issue for tube degradation in domestic steam generator is the tube end cracking on seal weld region. The seal weld region at the tube end and tube itself is regarded as a pressure boundary between the primary side and the secondary side. One of the Westinghouse Model-F S/G has experienced tube end cracking and its number of plugging approximately becomes to the operating limit up to 5% due to tube end cracking which was reported as SAI/MAI(single/multiple axial indication) or SCI/MCI(Single/multiple circumferential indication) from the results of eddy current testing. Eddy current mock-up test was carried out to determine the origin of cracking whether it is from weld zone area or parent tube. This result was helpful to analyze crack location on ECT data. Correct action on this problem was the installation of tube-end sleeve. Last year, after removing 340 installed plugs from tubes, selected 269 tubes took tube-end sleeve installation. Tube-end sleeve brought pressure boundary from parent tube to installed sleeve tube. Tube-end sleeve has the benefit of reducing outage period and increasing more revenue than replacing S/G. This paper is provided to assist interest parties in effectively understanding this issue.