• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.257-259
• /
• 2007

For this study, SM45C steel rods using generally for power transmission shafts and machine components was selected and welded by Butt-GMAW method. and then it was studied about estimation of fatigue strength and the region of infinite life. From this result, it is demanded that the stress for safety design of machine components using SM45C butt-welded steel rods must be selected in the region of the lowest infinite life of heat affected zone.

• Proceedings of the KWS Conference
• /
• 2000.04a
• /
• pp.161-163
• /
• 2000

• Journal of the korean Society of Automotive Engineers
• /
• v.13 no.2
• /
• pp.103-111
• /
• 1991

To determine the effects of microstructure on the fatigue crack propagation behavior in SM45C steel, experimental investigations have been carried out with the specimens of different grain sizes and different spacings between the Fe$_{3}$C particles. Fatigue and tensile tests were conducted and the quantitative analysis of the relations between the threshold stress intensity range and grain size, interparticle spacing and yield stress were carried out. Some of the conclusions obtained are as follows; (1) .DELTA.K$_{th}$ was observed to increase with grain size and the spacing between the Fe3C particles. (2) In both pearlite and spheroidite microstructures, .DELTA.K$_{th}$ was increased when yield stress was decreased.sed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.3
• /
• pp.219-224
• /
• 2017

A study on dissimilar friction-welded joints was performed for cam shaft applications using solid bar samples, 20mm in diameter, of forging steel(SF45) and carbon steel(SM45C). The main parameters of friction welding such as tensile tests, Vickers hardness surveys of the bond of area, the heat affected zone (HAZ), and the observation of microstructure were investigated to ensure a good quality of friction welding through visual observations. The specimens were tested as-welded and post weld heat treatment(PWHT). This paper deals with optimizing the welding conditions and analyzing various rotary bending fatigue test(RBFT) properties about heat-treated base metal(BM), as-welded and PWHT. Consequently, two materials for friction welding are strongly mixed with a well-combined structure of micro-particles without any molten material, particle growth, or any defect. Moreover, the fatigue limit of BM(SF45) and PWHT for the RBFT were observed as 180MPa and 250MPa, respectively. It was confirmed that the PWHT causes approximately 40％ improvement in the fatigue limit when compared to the BM(SF45).

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.8 no.5
• /
• pp.47-53
• /
• 1999

The purpose of this study was to determine the effects of various cutting condition on the cutting resistance and surface roughness of material in turning operation using a coated carbide tool. The workpiece materials were the carbon steel SM20C and SM45C The results of this study are summarized as follows: The cutting force decreases as the feedee amount and the cutting depth decrease and the cutting speed increases. In order to obtain a proper surface roughness to each material it is desirable to set the feeding amount as 0.059mm.rev, the cutting depth as 0.4mm and the cutting speed as 270m/min for SM20C, while setting the feeding as 0.059mm/rev the cutting depth as 0.6mm and the cutting speed as 270m/min for SM45C.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.17 no.1
• /
• pp.50-58
• /
• 2008

The SM45C metallic coupons have been tested under static tensile loading with acoustic emission (AE) as the load-deflection curve mainly. In this study, we used AE to detect the yielding of material and AE techniques was applied to rapidly estimate the mechanical characteristics of a material. First, coupons without an artificial defect were tested at different cross-head speed. For all cases in this analysis, yielding point of SM45C coupons did not appear definitely compared to mild steel, whereas coupons start to generate AE counts upon yielding. So all cases are normalized to know the possibility of accelerated life test of a material. And next, coupons with different from sizes of circular hole defects were tested at the same cross-head speed of 5 mm/min. Results were classified into 3 classes and analyzed by AE amplitude & signal strength as a function of time. Summarizing the specific conclusions, we need to additional research considering plate with width-ratio in order to estimate the fracture mechanism.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.6
• /
• pp.932-937
• /
• 2012

In the presented study, SM45C carbon steel parts were joined by friction welding. The welding process was carried out under optimized conditions using statistical approach. The study of SM45C is conducted with various combinations of process parameters. Parameter optimization, microstructure and mechanical property correlation are the major contribution of the study. The welded joints were produced by varying spindle revolution speed, friction pressure, upset pressure and burn-off length. Tension tests were applied to welded parts to obtain the strength of the joints. Fracturs properties were additionally obtained experimentally under fluctuated tensile loads. Microstructures using microphotographs were examined in the weld interface and weld region and heat affected zone and base metal and flash zone of welded parts. Finally, Hardness variations in welding zone and base metal were also obtained. Through these tests, the optimum conditions of parameters for ${\phi}20$ SM45C in friction welding were obtained when the friction spindle revolution was 1,950 rpm, the friction pressures was 30 MPs, upset pressures was 50 MPs.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.3
• /
• pp.451-460
• /
• 1989

This paper dealt with the effect of the ratios N2 to H2 gas on the corrosion fatigue failure behavior of ion-nitrided SM45C steel specimens. The specimens were water cooled after ion-nitriding at 500.deg. C for 3hrs in 5 Torr, 0.8N$_{2}$ and 0.5N$_{2}$ atmospheres. As the nitrogen concentration increases, the higher compressive residual stresses developed in the surface layer and the depth of nitrided layer increased, which in turn gave rise to increases in fatigue strength and corrosion fatigue life. In the region less than 1.5 * 10$^{5}$ cycles, fatigue failure initiated at the brittle nitrided case, whereas in the region higher than 1.5 * 10$^{5}$ cycles crack initiated from the non-metallic inclusions in the subsurface. The initiation of corrosion fatigue failure was mainly attributed to pitting of case hardened surface layer.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2006.06a
• /
• pp.235-236
• /
• 2006

• Proceedings of the Safety Management and Science Conference
• /
• 2009.11a
• /
• pp.471-481
• /
• 2009

This study is deal with the high frequency induction hardening (HF at $850^{\circ}C$, 120kHz & 50kW condition) SM45C steel. (1) The HF specimen which was tempered at $150^{\circ}C$, did not appear any tempering effect. A brittle fracture occurred at rounded area of the tensile specimen. AE amplitude distribution showed between 45~60dB. (2) The HF specimen which was tempered at $300^{\circ}C$, slip and fracture occurred at the hole area of the tensile specimen. As it passes the yield point, the AE energy increased intermittently and AE amplitude distribution showed between 70~85dB. In addition, after the maximum tensile load, it showed high amplitude and energy distribution. The AE amplitude showed between 45~70dB. (3) The HF specimen which was tempered at $450^{\circ}C$, a brittle fracture occurred as if it is torn in the direction of $45^{\circ}$ on parallel area over the both sides of the tensile specimen, which led to several peak to be appeared in AE energy. It was found that the AE amplitude was relatively low and the AE energy was high.