• Proceedings of the Membrane Society of Korea Conference
• /
• 2003.07a
• /
• pp.47-50
• /
• 2003

Carbon-silica membranes were Prepared by Pyrolyzing polyimide/silica composite obtained from ill-situ polymerization of alkoxy silanes via sol-gel reaction. In this study, effects of silica content and silica network in polyimide matrix were focused on the gas permeation and separation properties of the final carbon-silica membrane. The membranes prepared were characterized with a field emission scanning electron microscopy (FE-SEM), a solid state $^{29}$ Si nuclear magnetic resonance spectroscopy ($^{29}$ Si-NMR), an electron spectroscopy for chemical analysis (ESCA), a thermogravimetric analysis (TGA) and gas permeation tests.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2004.10a
• /
• pp.180-181
• /
• 2004

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.51-51
• /
• 2003

• Elastomers and Composites
• /
• v.32 no.3
• /
• pp.179-185
• /
• 1997

In solution and melting state, SiOD prepolymer was prepared by cured excess DDM with epoxy-terminated siloxane oligomers to control phase separation when DGEBA was blended with PDMS. DGEBA/SiOD prepolymer was also cured at $150^{\circ}C$ for 3hrs. Mechanical and thermal properties of the cured prepolymer specimen were investigated. DGEBA/SiOD60 specimen blended SiOD prepolymer had the best flexural strength, modulus and impact strength. To show crack-formation procedure to morphology, DGEBA/DDM neat specimen was flowed homogeneously in direction of crack energy, whereas DGEBA/SiOD$(30{\sim}60)$ specimen showed heterogeneously dispersed particles and scattered domain of crack energy, but DGEBA/SiOT specimen showed homogeneous phase.

• Journal of the Korean Ceramic Society
• /
• v.41 no.9
• /
• pp.637-641
• /
• 2004

We investigated the effects of SiH$_4$ gas on the surface of Hf-silicate films during the deposition of polycrystalline (poly) Si films and the thermal stability of sputtered Hf-silicate films in poly Si/Hf-silicate structure by using High Resolution Transmission Electron Microscopy (HR-TEM) and X-ray Photoelectron Spectroscopy (XPS). Hf-silicate films were deposited by using DC-mag-netron sputtering with Hf target and Si target and poly Si films were deposited at 600$^{\circ}C$ by using Low Pressure Chemical Vapor Deposition (LPCVD) with SiH$_4$ gas. After poly Si film deposition at 600$^{\circ}C$, Hf silicide layer was observed between poly Si and Hf-silicate films due to the reaction between active SiH$_4$ gas and Hf-silicate films. After annealing at 900$^{\circ}C$, Hf silicide, formed during the deposition of poly Si, changed to Hf-silicate and the phase separation of the silicate was not observed. In addition, the Hf-silicate films remain amorphous phase.

• Membrane and Water Treatment
• /
• v.10 no.5
• /
• pp.353-360
• /
• 2019

ZSM-5 membrane was prepared on tubular macroporous ${\alpha}$-alumina support using a different synthesis route. The effects of organic template agent and Si/Al ratio of the synthesis gel on morphology, structure, and separation performance of the ZSM-5 membrane used for dehydration of isopropanol were investigated. High water perm-selectivity ZSM-5 membrane with a thickness of about $3.0{\mu}m$ and a low Si/Al ratio of 10.1 was successfully prepared from organotemplate-free synthesis gel with a molar composition of $SiO_2$ : $0.050Al_2O_3$ : $0.21Na_2O$ : NaF : $51.6H_2O$ at $175^{\circ}C$ for 24 h. The ZSM-5 membrane exhibited high pervaporation performance with a flux of $3.92kg/(m^2{\cdot}h)$ and corresponding separation factor of higher than 10,000 for dehydration of 90 wt.% isopropanol/water mixture at $75^{\circ}C$.

• Nuclear Engineering and Technology
• /
• v.33 no.4
• /
• pp.375-385
• /
• 2001

The total burnup in the spent U$_3$Si/Al fuel samples from Hanaro reactor was determined by destructive methods using $^{148}$ Nd, the sum of $^{143}$ Nd and $^{144}$ Nd, the sum of $^{145}$ Nd and $^{146}$ Nd, and the sum of total Nd isotopes($^{143}$ Nd, $^{144}$ Nd, $^{145}$ Nd, $^{146}$ Nd, $^{148}$ Nd and $^{150}$ Nd) monitors. The fractional($^{235}$ U) turnup in the spent fuel samples was also determined by U and Pu mass spectrometric method. The samples were dissolved in a mixture of 4 M HCI and 10 M HNO$_3$ without any catalyst. The separation of U, Pu and Nd from the spiked and unspiked sample solutions was achieved by two sequential anion exchange separation methods. The isotope compositions of these elements, after their separation from the fuel samples were measured by mass spectrometry. The contents of the elements in the spent fuel samples were determined by isotope dilution mass spectrometric method(IDMS) using $^{233}$ U, $^{242}$ Pu and $^{150}$ Nd as spikes. The effective fission yield was calculated from the weighted fission yields averaged over the irradiation period. The difference between total turnup values determined by various Nd monitors were in the range of 1.8%.

• Journal of the Korean Ceramic Society
• /
• v.25 no.3
• /
• pp.251-260
• /
• 1988

Ion-exchange porous glasses were prepared by heat treatment and subsequently hydro thermalor acid leaching treatment $10Li_2O$.$(90-x)B_2O_3$.$xSiO_2$ base glasses containing various amount of $Al_2O_3$ or $MoO_3$. It was investigated how the phase separation and the cation exchange capacity(CEC) were affected by the addition of $Al_2O_3$ or $MoO_3$. The optimum condition of phase separation in these glasses was about 48$0^{\circ}C$ for 10 hrs. The degree of phase separation was rapidly suppressed by the addition of $Al_2O_3$ up to 10 mol% and thereafter suppression effect was decreased. The maximum value of CEC, about 252meq/100g, was observed with the $1OLi_2O$.$45B_2O_3$.$45SiO_2＋7.5Al_2O_3$ porous glass prepared by hydrothermal treatment and its mean pore radius was about 16.3A. The addition of $MoO_3$ accelerated phase separation and leaching rate. Looking at the remakable increment of pore diameter and pore volume of these porous glasses by the addition of $MoO_3$, the effect of $MoO_3$ may be ascribed to the lowering of silica concentration in the borate phase and to the forming of water-soluble complex with silica during the leaching treatment.

• Membrane Journal
• /
• v.18 no.1
• /
• pp.103-107
• /
• 2008

Membrane process has been focused as an alternative separation process because not only it exhibits a high selectivity compared with a traditional distillation process, but also it is known to be an energy saving separation process. Inorganic membrane, especially zeolite membrane, has been studied since it can be operated in severe conditions compared to the organic membranes. Recently, new zeolite materials are tested as an inorganic membrane material to overcome disadvantages of existing zeolite membranes. Kalsilite can be used as an inorganic membrane material for gas separation and selective water separation from water/organic mixtures because it is expected to be hydrophilic resulted from Si/Al ratio of 1 like zeolite 4A and has a narrow pore size of 0.36 nm. In this study, kalsilite was synthesized by a new economical hydrothermal process using Si : Al : K : $H_2O$ mole ratio of 1 : 1 : 8 : 60. The synthesized kalsilite powder was confirmed by XRD and has a mean diameter of $2.73{\mu}m$. The vapor adsorption test showed the synthesized kalsilite is hydrophilic.

• Journal of the Korean Chemical Society
• /
• v.39 no.7
• /
• pp.524-529
• /
• 1995

The separation efficiency of metal ions by using silica gel bonded 15-crown-5 (SGBM) has been determined by column chromatography in aqueous solution at pH 1. Bindinng constants and separation factors for several SGBM-Metal interactions were measured in aqueous solution. The order of these binding constants and separation factors with metal ions was Li(Ⅰ) < Sr(Ⅱ) < Na(Ⅰ) < Cu(Ⅱ) < Mg(Ⅱ) < K(Ⅰ) < Ca(Ⅱ) < Bi(Ⅲ) < Sb(Ⅲ). These results were explained in terms of the size effect and electron density effect. This experimental results showed good efficiency for separation of $Sb^{3+}$ from mixtures of alkali, alkaline earth metal ions, and $Cu^{2+}$ in aqueous solution.