We produced cylindrical porous TiNi bodies by Self-propagating High-temperature Synthesis (SHS) process, varying the heating schedule prior to ignition of a loose preform compact made from (Ti+Ni) powder mixture. To investigate the effect of the heating schedule on the behaviour of combustion wave propagation and the structure of porous TiNi shape-memory alloy (SMA) body, change of temperature in the compact during SHS process was measured as a function of time and used for determining combustion temperature and combustion wave velocity. Microstructure of produced porous TiNi SMA body was observed and the results were discussed with the combustion characteristics. From the results it was concluded that the final average pore size could be controlled either by the combustion wave velocity or by the average temperature of the preform compact prior to ignition.

• 한국전기전자재료학회논문지
• /
• 제15권3호
• /
• pp.275-280
• /
• 2002

The peculiarities of using Self-propagating High-temperature Synthesis (SHS) and solid-stave chase synthesis for production of high temperature superconductor materials were discussed. Oxide superconductors with general formula of $ReBa_2Cu_3O_{7-x}$ (Re=Y, Sm) haute been made by using barium oxide initial powder instead of traditional barium carbonate. Phenomena observed during the grinding of the reactants mixture are presented. Mechano-chemical activation - as a pre-treatment of the reactants mixture - strongly influences the kinetic parameters, the reaction mechanism, and the composition and structure of the final product.

• 한국세라믹학회지
• /
• 제32권1호
• /
• pp.11-16
• /
• 1995

High reaction heat evolved from the oxidation of Al was used to synthesize SiC, which might be difficult to be formed by SHS. Al2O3-SiC composite powder was easily manufactured using KNO3 as an ignition and reaction catalyst. Unreacted Si and C were observed after reaction dependent upon the composition of starting powders, reaction atmosphere and relative densities of compacted bodies. The unreacted carbon could be removed by calcining at $600^{\circ}C$ and the remaining Si could be removed by dissolving in NaOH solution. The final powder particles were smaller than 1${\mu}{\textrm}{m}$ in size.

• 한국세라믹학회지
• /
• 제34권7호
• /
• pp.731-737
• /
• 1997

TixZr1-xC(0$0^{\circ}C$, 5.1 mm/sec respectively. The relative density, three point flexural strength, and the hardness of composites, which was sintered at 190$0^{\circ}C$ for 60 min by using hot-pressing under a pressure of 30 MPa, were 99%, 525 MPa and 24 GPa respectively.

• 한국세라믹학회지
• /
• 제40권1호
• /
• pp.18-23
• /
• 2003

정량의 B$_2$O$_3$/A1/C의 혼합분말을 화학노 대신 고압의 알곤 분위기를 사용하여 SHS 공정으로 B$_4$C-A1$_2$O$_3$ 복합분말을 제조하였다. 2B$_2$O$_3$+4A1+C=B$_4$C-2A1$_2$O$_3$의 반응식에 해당하는 B$_2$O$_3$(-100 메쉬), Al(-200 메쉬), C(-200 메쉬)의 분말을 2시간 건식 볼밀로 혼합한 후, 고온 고압의 SHS 반응기에 넣고 약 10기압의 알곤 분위기에서 점화하여 SHS을 일으켰다. 반응 생성물은 XRD 분석으로 안과 겉이 균일하게 반응이 일어났으며 반응 생성물로 화학노 사용시 동반되는 부산물 AlB$_{12}$C$_2$가 없는 B$_4$C-A1$_2$O$_3$ 복합 분말을 얻었다. 이 복합 분말은 SEM으로 보면 약 0.3~l $mu extrm{m}$ 크기의 결정이 모인 약 60~100$\mu\textrm{m}$ 크기이었다. 그러나 약 15기압을 사용하였을 때는 부분 소결이 일어나 15~25$\mu\textrm{m}$ B$_4$C 분말에 0.1~0.2$\mu\textrm{m}$의 알루미나가 분산되어 있는 고강도의 복합 분말이 생성되었다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2005년도 춘계학술강연 및 발표대회강연 및 발표논문 초록집
• /
• pp.52-52
• /
• 2005

• 한국분말재료학회지
• /
• 제11권4호
• /
• pp.294-300
• /
• 2004

This study for preparation of aluminum nitride (AlN) with high purity was carried out by self-propagating high-temperature synthesis method in two different systems, $Al-N_{2}$ and $Al-N_{2}$-AlN, with the change of nitrogen gas pressure and dilution factor. On the occasion of $Al-N_{2}$ system, unreacted aluminum was detected in the product in spite of high nitrogen pressure, 10 MPa, This may be caused by obstructing nitrogen gas flow to inner part of molten and agglomerate of aluminum, formed in pre-heating zone. In $Al-N_{2}$-AlN system, AlN with a purity of 95% or ever can be prepared in the condition of $f_{Dil}\geq0.5$, $P_{N_{2}}\geq$ 1 MPa, and the purity can be elevated to 98% over in the condition of $f_{Dil}$ = 0.7 and $P_{N_{2}}$ = 10 MPa.

• 자원리싸이클링
• /
• 제12권4호
• /
• pp.51-57
• /
• 2003

케퍼시터용 Ta 분말제조공정에서 발생하는 waste 분말을 이용하여 TaC 분말을 자전고온합성법에 의하여 합성하였다. waste TA는 합성반응의 활성 및 산화방지를 위하여 전처리공정에서 미분쇄 및 탈산처리가 필요하였다. 합성반응에서는 TaC 단일상은 6∼7wt.％C의 조성범위에서 얻을 수 있었다. 또한 반응온도는 시료의 압축력에 영향을 받으며, 압축력 1600psi에서 최고반응온도를 나타냈다.

• 대한금속재료학회지
• /
• 제50권6호
• /
• pp.439-443
• /
• 2012

YAG:Ce phosphor were prepared in a self-propagating high-temperature synthesis (SHS) using a $1.5Y_2O_3+2.5Al_2O_3+0.116CeO_2+3.0KClO_3+kCO(NH_2)_2+m(C_2F_4)_n$ precursor mixture. The heat for the combustion propagation was provided by the reaction of a $KClO_3+CO(NH_2)_2+(C_2F_4)n$ mixture. Pure-phase YAG phosphor was synthesized at the combustion temperature of $1210^{\circ}C$ from k=3.6 mole and m=0.3 mole. The as-prepared YAG:Ce phosphor had a particle size of $2-10{\mu}m$. The addition of Teflon to the precursor mixture increased the YAG particle size and its luminescent intensity. The emission peak of the YAG phosphor was blue-shifted with an increase of Teflon concentration.

• 한국세라믹학회지
• /
• 제42권1호
• /
• pp.69-75
• /
• 2005

고온자전연소법에 의한 질화알루미늄 합성에 있어서, 반응물(Al) 형상과 희석제(AlN) 입도 등의 형상학적 조건이 반응생성물에 미치는 영향을 조사하였다. 평균 입경(34$\mu$m)이 같은 두 종류의 Al 분말(입상, 편상)과 평균입경이 다른 4종류의 AM분말을 희석제로 사웅하여 반응 성형체를 준비하였다. 반응성형체의 충진밀도는 이론밀도의 $35\%로 고정하였고, 초기 질소압은 $1\~10MPa$, 희석을은 $0.4\~0.7$로 변화시키면서 반응을 실시하였다. 반응물과 희석제의 입도를 비슷하게 조절함으로써, 상대적으로 질소압이 낮은 1MPa의 조건에서도 순도 $98\% 이상, 입경 수십 $\mu$m의 AlN 합성이 가능함을 확인하였다. 이러한 고순도, 고입경화는 연소파 진행 후, 성형체 내부로 질소가스 투입 용이성의 차이에 의한 현상이라고 판단된다.