• 마이크로전자및패키징학회지
• /
• 제12권4호통권37호
• /
• pp.339-343
• /
• 2005

Pt-$SrBi_2Nb_2O_9(SBN)-Pt-Y_2O_3-Si$ 게이트 전계효과 트랜지스터 (MFMISFETs)의 정보저장 특성향상을 위하여 SBN 박막을 산소 플라즈마 내에서 급속열처리 하였다. 그 결과 SBN 박막의 결정크기는 $700^{\circ}C$의 동일한 열처리조건에서 급속열처리한 SBN 결정립의 크기가 전기로 열처리에 의한 SBN 결정립보다 4배 이상 성장하였다. 또한 분극 특성을 비교한 결과 잔류분극은 2배이상 급속열처리 방법으로 제조된 SBN 박막을 이용한 MFMISFET의 메모리윈도우 (memory window)와 on/off상태의 정보저장특성(programming characteristics)은 월등히 향상되었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.723-727
• /
• 2003

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in $Ar/O_2$ atmosphere. SBN30 thin film of $1000{\AA}$ was pre-deposited as a seed layer on $Pt(100)/TiO_2/SiO_2/Si$ substrate followed by SBN60 deposition up to $3000{\AA}$ in thickness. As-deposited SBN60/SBN30 layer was heat-treated at different temperatures of 650, 700, 750, and $800^{\circ}C$ in air, respectively The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. There was no difference in the crystal structure with heat-treatment temperature, but the electric properties depended on the heating temperature and was the best at $750^{\circ}C$. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was $15{\mu}C/cm^2$, the coercive field (Ec) 75 kV/cm, and the dielectric constant 1075, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 제5회 영호남 학술대회 논문집
• /
• pp.85-88
• /
• 2003

$Sr_xBa_{1-x}Nb_2O_6$(SBN, $025{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in Ar/$O_2$ atmosphere. SBN30 thin film of 500 ${\AA}$ was pre-deposited as a seed layer on Pt(l00)/$TiO_2$/$SiO_2$/Si substrate followed by SBN60 deposition up to 4500 ${\AA}$ in thickness. SBN60/SBN30 layer was deposited at different Oxygen amount of 0, 8.1, 17, and 31.8 sccm, respectively. The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. The crystal structure and the electric properties depended on the Oxygen amount, heating temperature and was the best at O2 = 8.1 seem, $750^{\circ}C$. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was 13 ${\mu}C/cm^2$, the coercive field (Ec) 75 kV/cm, and the dielectric constant 1492, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 추계학술대회 논문집 Vol.16
• /
• pp.271-274
• /
• 2003

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in $Ar/O_2$ atmosphere. SBN30 thin films of different thickness were pre-deposited as a seed layer on $Pt(100)/TiO_2/SiO_2/Si$ substrate followed by SBN60 deposition up to $4500\;{\AA}$ in thickness. As-deposited SBN60/SBN30 layer was heat-treated at different temperatures of 650, 700, 750, and $800\;^{\circ}C$ in air, respectively, The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. There was difference in the crystal structure with heat-treatment temperature, and the electric properties depended on the heating temperature and the seed-layer thickness. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was $15\;{\mu}C/cm^2$, the coercive field (Ec) 65 kV/cm, and the dielectric constant 1492, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.382-383
• /
• 2006

The tungsten bronze type of strontium barium niobate(SBN) thin film was synthesized by metal organic decomposion method for SBN stock solution and the SBN thin film process were deposited by spin-coating process on Pt-deposited si-wafer(100) by magnetron sputtering system. The thickness of SBN thin film was 150~200 nm and were optimized for rpm of spin-coater system. The structural variation of SBN thin film was studied by TG-DTA and XRD. The deposited SBN stock solution on annealing at $400{\sim}800^{\circ}C$ a pure tungsten bronze SBN phase and the corresponding. average grain size about 500~1000 nm influenced by annealing temperature. The piezoelectric properties of prepared SBN thin film, the remanent polarization value(2Pr) and coercive field was $1.2{\mu}C/cm^2$ and 2.15V/cm, respectively.

• 한국세라믹학회지
• /
• 제38권12호
• /
• pp.1167-1173
• /
• 2001

텅스텐브론즈 구조를 가지는 Sr$_{x}Ba_{1-x}Nb_{2}O_{6}$(SBN) (0.3$\le$x$\ge$0.7) 세라믹스를 고상반응법으로 합성하고 Sr/Ba의 비에 따른 유전특성을 조사하였다. SBN 세라믹스는 Sr/Ba의 비가 증가함에 따라 상전이 온도는 낮아지고 상전이 온도에서의 최대 유전율은 증가하였다. 또한 SBN 세라믹스는 Sr 함량에 따른 relaxor 거동을 정량화하여 평가하였는데, Sr/Ba의 비가 증가할수록 유전율은 더욱 완만해지는 것을 관찰할 수 있었다. 이러한 실험 결과를 텅스텐브론지 구조를 가진 SBN 세라믹스의 결정구조 관점에서 해석하였다.

• 한국전기전자재료학회논문지
• /
• 제22권8호
• /
• pp.671-676
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various deposition conditions. We investigated the effect of deposition condition on the surface morphology and dielectric properties of SBN thin films. The optimum of the rougness showed about 4.33 nm in 70/30 of Ar/$O_2$ ratio. The crystallinity and rougness of SBN thin films were increased with the increase of rf power. Also, Deposition rate of SBN thin films was about 4.17 nm/min in 70 W of rf power. The capacitance of SBN thin films were increased with the increase of Ar/$O_2$ ratio, rf power and deposition temperature respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.393-394
• /
• 2005

SBN25 박막을 씨앗층으로 사용하여 이온빔으로 증착한 SBN60/SBN25 다층박막에 대하여 결정화 및 배향 특성을 고찰하였다. 기판은 Pt(111)/TiO2/SiO2/Si(100) 웨이퍼 (Pt 두께 200nm)를 사용하였으며, 약 3000${\AA}$으로 증착한후 650~$750^{\circ}C$에서 후열처리를 하였다. 제작된 박막의 증착조건 및 열처리 조건에 따른 결정화특성 변화에 대하여 연구하였으며, SBN 박막을 MFM 구조의 박막커패시터로 제조하여 강유전특성을 측정하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.90-90
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode($Pt/Ti.SiO_2/Si$) using RF sputtering method. The dielectric constant of SBN thin films were increased with the increase of annealing temperature. The maximum dielectric constant of SBN thin film is obtained by annealing at 700[$^{\circ}C$]. The dielectric constant and dielectric loss had a stable value within -5~+5[V].

• 한국재료학회지
• /
• 제11권4호
• /
• pp.290-293
• /
• 2001

세라믹 타겟인 Sr$_2$Nb$_2$O$_{7}$ (SNO)과 Bi$_2$O$_3$을 장착한 RF-마그네트론 스퍼터링을 이용하여 SrBi$_2$Nb$_2$O$_{9}$ (SBN) 박막을 p-type Si(100) 기판 위에 증착하였다. 증착시 두 타겟의 파워비를 조절하여 조성의 변화에 따른 SBN 박막의 구조적 및 전기적 특성을 조사하였다. 증착된 SBN 박막은 $700^{\circ}C$의 산소분위기에서 1시간 동안 열처리를 하였으며 상부전극으로 Pt를 증착한 후 산소분위기에서 30분 동안 $700^{\circ}C$에서 전극 후열처리를 실시하였다. 증착된 SBN 박막은 $700^{\circ}C$ 열터리 후에 페로브스카이트 상을 나타냈으며 SNO 타겟과 Bi$_2$O$_3$타겟의 파워가 120 W/100 W 일 때 가장 좋은 전기적 특성을 나타내었다. 이때의 조성은 EPMA(Electron Probe X-ray Micro Analyzer) 분석을 통하여 확인하였으며 Sr:Bi:Nb의 비가 약 1:3:2임을 나타내었다. 이러한 과잉의 Bi조성을 가진 SBN 박막은 3-9 V의 인가전압에서 1.8 V-6.3 V의 우수한 메모리 윈도우 값을 나타내었으며 누설전류 값은 인가전압 5 V에서 1.54$\times$$10^{-7}$ A/$\textrm{cm}^2$였다.