• Elastomers and Composites
• /
• 제33권1호
• /
• pp.44-51
• /
• 1998

The purpose of this experiments were investigated on the physical properties of rubber com-pounds containing two types carbon black. Bound rubber and interaction coefficient for com-pounds with pure carbon black were higher than those for the compounds with dual phase carbon black. Slightly higher values in 300% modulus and tensile strength indicated that the ratio of rubber-filler bound to rubber-rubber bound of pure carbon black were higher than those of com-pounds with dual phase carbon black. It was founded that dynamic properties, that is rebound, heat build-up, 0 & $60^{\circ}C$ tan $\delta$, and cut and chip loss of compounds with dual phase carbon black were better than those of compounds with pure carbon black, but abrasion property of dual phase carbon black was lower than those of pure carbon black because of low reinforcing ability.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 가을 학술발표회 논문집
• /
• pp.51-57
• /
• 1996

The purpose of this study is to improve the properties by increasing of the adhesion strength of styrene-butadiene rubber(SBR) latex coated powdered rubber in cement mortar. SBR-modified mortar using powdered rubber is also tested as the same method. From the test results, the cement mortar using SBR latex coated powdered rubber have a good mechanical properties compared with that using uncoated powdered rubber. The mechanical properties of SBR-modified mortar using powdered rubber with polymer-cement ratios of 10% are also improved.

• Elastomers and Composites
• /
• 제46권4호
• /
• pp.318-323
• /
• 2011

폐타이어고무분말을 재활용하기 위하여 방수시트용 고무분말 복합체를 제조하였으며, 수지 종류와 가교제의 함량이 복합체의 기계적 특성에 미치는 영향을 고찰하였다. EPDM이 부가됨에 따라 고무분말 PE 복합체의 신장율이 3배 이상 증가하는 현상을 나타내었다. 고무분말 충전 복합체에 가교제의 농도가 증가함에 따라 복합체의 강도가 증가하였으며, 특히 재생 폴리프로필렌을 사용한 경우 3배 이상 인장강도가 현저하게 높게 나타났다. 따라서 폴리프로필렌 블렌드물로 고무분말 복합체를 제조하는 경우 신재 폴리프로필렌을 사용하는 것 보다 재생 폴리프로필렌을 사용하는 것이 기계적 특성면에서 효과적인 것으로 나타났다.

• Composites Research
• /
• 제12권6호
• /
• pp.83-89
• /
• 1999

고무/폴리머 복합재료의 충격강도와 파괴 기구를 기지재의 체인 유연성을 나타내는 특성비 $C_{\infty}$와 강화고무의 입자 크기의 두 가지 관점에서 연구하였다. 본 연구에서 특성비는 PPO와 PS폴리머의 조성비에 의하여 조절하였다. 아이조드 충격 시험과 주사전자현미경에 의한 파단면 관찰을 수행하였다. 전단항복과 크래이징으로 대별되는 소성 변형 기구의 이해를 넓히기 위해 유한요소해석을 수행하였다. 전단항복은 폴리머의 유연성이 상대적으로 낮거나 고무의 입자 크기가 작은 경우에 잘 나타났다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2007년도 추계학술대회 논문집
• /
• pp.47-51
• /
• 2007

The present paper reports the life time prediction of Acrylonitrile-Butadiene rubber (NBR) fuel cell gasket materials as a function of operational variables like acid concentration, ageing time and temperature. Both material and accelerated acid-heat aging tests were carried out to predict the useful life of the NBR rubber gasket for use as a fuel cell stack. The acid ageing of the gasket compounds has been investigated at 120, 140 and $160^{\circ}C$, with aging times from 3 to 600 h and increasing acid ($H_2SO_4$) concentrations of 5, 6, 7 and 10 vol%. Material characteristics the gas compound such as cross-link density, tensile strength and elongation at break were studied. The hardness of the NBR rubber was found to decrease with decreasing acid concentration at both 120 and $140^{\circ}C$, but at $160^{\circ}C$ interestingly the hardness of the NBR rubber increased abruptly in a very short time at different acid concentrations. The tensile strength and elongation at break were found to decrease with increase in both the acid concentrate ion & temperature. The life time of the compounds were evaluated using the Arrhenius equation.

• 한국염색가공학회지
• /
• 제29권3호
• /
• pp.155-161
• /
• 2017

In CPB(Cold-Pad-Batch) dyeing, the rubber of the padder roll is influenced by the heat, chemical and mechanical influences and thus aging of the padder roll rubber occurs. This study presents an accelerated thermal aging test of the CPB padder roll rubber with strong alkali conditions. Using Arrhenius formula of the various property values for the various aging temperatures($80^{\circ}C$, $90^{\circ}C$, $100^{\circ}C$) of the padder roll, the accelerated life predictions could be calculated. The threshold value of the property was set at different values. The hardness was set at the point where 5% degradation occurs based on the actual use conditions, and the tensile strength was set at the point where 50% degradation occurs based on the general life prediction standards. From the results of the different physical properties at differing temperatures, the Arrhenius plot could be obtained. Through the usage of the Arrhenius Equation, significant duration expectation could be predicted, and the chemical aging behavior of the CPB padder roll could be found at the arbitrary and actual temperatures.

• Steel and Composite Structures
• /
• 제41권5호
• /
• pp.649-661
• /
• 2021

This paper presents experimental and analytical studies to understand the behavior of crumb rubber concrete (CRC)-filled fiber reinforced polymer (FRP) and steel tube double skin column (DSC) and beam (DSB) members under cyclic loading. The main test variable was the percentage of rubber which ranged from 0 to 40%. For column members, different heights corresponding to different aspect ratios were examined to understand the to understand the effect of DSCs' slenderness on the cyclic response of the columns. the. The behavior of the specimens in terms of failure mode, strain development, energy dissipation, load-displacement response were presented and compared. The ability of the current provisions of the Australian codes to predict the capacity of such double skin members was also evaluated based on the test results. This study concluded that the reduction in the concrete strength was more severe at the material level compared to structural level. Also, as the load changed from axial compression in columns to pure moment in beams the negative effect of rubber percentage on the strength became less significant.

• Elastomers and Composites
• /
• 제8권1호
• /
• pp.33-51
• /
• 1973

We have studied the blending effects of Diene NF 35 R and Alfin 1530 at various blending ratios, 100/0, 70/30, 50/50, 30/70, 0/100, and of carbon black HAF-HS and ISAF-HS at various compounding ratios of 45 PHR, 55 PHR, 65 PHR, for tyre tread rubber. As the results, it was found that; 1. For tyre tread rubber, as the blending ratio, AR 1530/Diene NF 35R, indicated 70/30, the physical properties we examined were most excellent. 2. Excellent result was obtained in the case of carbon black compounding ratio of 55 PHR. The compounding of ISAF-HS made better result than that of HAF-HS for tensile strength, but the compounding of HAF-HS made better result than that of ISAF-HS for tearing strength and best result for abrasion quantity. 3. Heat buildup obtained from compounding carbon black HAF-HS indicated low temperature than that from compounding carbon black HAP-HS. As the compounding amount of carbon black increased, and as the blending amount of AR 1530 decreased, the heat buildup increased. 4. Carbon black was more efficient to AR 1630 than io Diene NF 35 R. 5. In the physical properties, mooney viscosity and mooney scorch time, as the compounding amount of carbon black increased, the values of mooney viscosity increased, but that of mooney scorch time had a max. point at the compoundiug amount of carbon black, 55 PHR.

• Elastomers and Composites
• /
• 제36권4호
• /
• pp.262-267
• /
• 2001

내전압 특성과 항균성을 갖는 절연 고무장갑을 제조하기 위해 천연고무 라텍스 (NRL)와 수분산성 폴리우레탄 (PU) 그리고 4급 아민 키토산 (4N-chitosan)을 배합하여 침지법으로 제조하였다. 절연 고무장갑의 기계적인 특성은 폴리우레탄 함량이 증가할수록 인장강도는 증가하였으나 신장율은 저하되었으며, 노화후 인장강도 및 신장율의 잔존율은 폴리우레탄 함량 증가에 따라 증가하였다. 또한, 리칭시간이 증가할수록 내전압 특성이 증가하였으며, 3시간의 리칭시간에서 10000V의 내전압 성능을 나타내었다. 고무장갑에 4N-chitosan을 첨가한 결과 균이 거의 생존하지 않았다.

• 폴리머
• /
• 제39권1호
• /
• pp.107-113
• /
• 2015

클로로부틸(CIIR) 방진고무 복합소재 내에서 실리카-실란이 기계적 물성과 점탄성에 미치는 영향을 평가하였다. 실리카-실란이 첨가된 경우, 방진고무의 핵심물성 중 하나인 인열강도는 13%, 파단 신장률은 14%씩 각각 증가하였다. 그 외 인장강도 및 경도 등은 비슷한 값을 보였다. 점탄성 관찰로부터 인열강도 및 파단 신장률의 증가는 실리카-실란의 첨가에 의한 복합소재 내 실리카와 클로로부틸간 3차원 사슬구조의 형성에 따른 것으로 판단되었다. 인열강도 및 파단 신장률의 향상에 관한 메커니즘을 논의하였다.