• Journal of the Korean Association of Oral and Maxillofacial Surgeons
• /
• v.39 no.4
• /
• pp.188-192
• /
• 2013

Post-traumatic anterior open bite can occur as a result of broken balance among the masticatory muscles. The superior hyoid muscle group retracts the mandible downward and contributes to the anterior open bite. Denervation of the digastric muscle by injection of botulinum toxin type A (BTX-A) can reduce the power of the digastric muscle and help to resolve the post-traumatic anterior open bite. A patient with a bilateral angle fracture had an anterior open bite even after undergoing three operations under general anesthesia and rubber traction. Although the open bite showed some improvement by the repeated operation, the occlusion was still unstable six weeks after the initial treatment. To eliminate the residual anterior open bite, BTX-A was injected into the anterior belly of the digastric muscle. Following injection of BTX-A, the anterior open bite showed immediate improvement. Complication and relapse were not observed during follow-up. Long-standing post-traumatic open bite could be successfully corrected by injection of BTX-A into the anterior belly of the digastric muscle without complication.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.4 s.97
• /
• pp.110-115
• /
• 1999

The surface gloss of an injection molded part is one of the most significant point for evaluating the quality of products appearance. The effects of process condition on the gloss of ABS(Acrylonitrile-Butadiene-Styrene) molded part were investigated in this work. The measurements of gloss and morphology on the surface of molded part were carried out with different melt temperature, mold temperature, mold surface roughness, injection pressure and holding pressure. Gloss had a maximum value with melt temperature in the range of 210 to 220 ${^\circ}C$ and with mold temperature 40 to 50${^\circ}C$ and with injection pressure 80~90 MPa, respectively. Melt temperature was shown to have the largest effect on gloss in our work. Gloss was not improved in the region of melt temperature 240${^\circ}C$ above and of mold temperature 60${^\circ}C$ above. It was concluded that the variation of gloss was mainly caused by rubber particles migration under shear stress not by their aggregation or necklace.

• Elastomers and Composites
• /
• v.44 no.4
• /
• pp.373-377
• /
• 2009

Most of the plastics products are being manufactured by injection molding. Warpage in injection molded affects the product dimension and it causes assembling problem. In this study, warpages in the injection molded part been studied. Specimens are rectangular flat shapes with and without ribs. Amorphous polymers (PC and ABS) and crystalline polymers (PP and PA66) were used for material. Flat shape with ribs showed higher warpage than flat shape without ribs by 6 to 9%. The specimens with ribs that are located parallel to the flow direction has higher warpage than specimens with ribs that are located perpendicular to the flow direction by 25 to 39%. Crystalline polymers have higher warpage than amorphous polymers by 23 to 67%. Warpage decreases as packing time increases and it increases as injection temperature increases.

• Korean Chemical Engineering Research
• /
• v.49 no.1
• /
• pp.47-55
• /
• 2011

The optimum mold design and the optimum process condition were constructed upon executing process simulation of rubber injection molding with the commercial CAE program of MOLDFLOW (Ver. 5.2) in order to solve the process-problems of K company relating to cracks, which occurs at the inner cavity wall of C. V. joint boots. As a result it was confirmed that the real cracks occurs at the exactly same position of the cavity as exhibits the defects of weld and meld line and unsatisfactory curing according to the result of simulation. In order to prevent the occurrence of weld and meld line at the defect-position, the location of gate was altered to the optimum position of the cavity. Consequently the filling pattern was established to minimize the degree of the melt-fronts confronting or the melt-flows melding to prevent the occurrence of weld and meld line at the defect-position. It was observed that both gate-positions to maximize the degree of the formation of weld and meld line and air traps are located, respectively, in opposite direction each other with reference to the optimum gate position. In addition, the temperature of mold was raised by $10^{\circ}C$ and maintained at $170^{\circ}C$ for satisfactory curing.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.5
• /
• pp.61-68
• /
• 2020

In this study, the international standard ISO TS 16774 Part 3 Test Method for Water (wash out) Resistance and KS F 4935 ｢Sealant Injection type for water leakage maintenance of adhesive flexible rubber asphalt series｣, which are standardized as a quality control method of injection type repair materials used for water leakage cracks in underground concrete structures, are currently used in Korea. As a result, considering the performance criteria of "mass change rate -0.1%" stipulated in KS F 4935, the remaining 13 types repair materials, excluding RG-2 of synthetic rubber and UG-1 of urethane, need to be reviewed for stabilization of the loss resistance due to the flow of ground water. The results of this study are determined to be available as a basic indicator for the selection of repair materials used for cracks in concrete structures. In addition, it is expected that the results of this study can be utilized as reference data that can be reflected in the improvement of the quality of repair materials that will be researched and developed later.

• Elastomers and Composites
• /
• v.34 no.3
• /
• pp.229-238
• /
• 1999

In this study, double bond, unsaturated group was introduced to the main chain of EVA by chemically treating EVA, nondiene polymer. Benzene sulfonic acid, ENB and DCPD were used as a third element. Also, from blending CR and SBR, conventional synthetic rubber we prepared vulcanizates and examined their physical properties. The datum lead to the following conclusion that some problems were modified; limited temperature in use and mechanical properties like hardness, tensile strength, tensile stress, and elongation rate of thermoplastic EVA, keeping the following advantages of original EVA; green strength, injection molding by Pressure, adhesion, tackiness, dimensional stability, and ozone resistance, etc. It is expected that continuous research of the modification between nondiene and diene polymer will improve what were shown disadvantages in synthetic polymer; processing, oxidation resistance, and adhesion. In addition, it will be possible to continue process of rubber products by utilizing possible fluidity for fusion of EVA.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.2 no.3
• /
• pp.107-115
• /
• 1998

This paper deals with the study on injection with EPDM(Ethylene propylene dien ter polymer) the gap which narrow, long, and tubular between an ablative composite tube and a steel motor case. Small size motor assembly was designed and manufactured for man-portable air defense propulsion system. Motor assembly is consisted with steel tube, ablative composite tube and insulation rubber. Ablative composite tube was made of carbon/phenolic prepreg by rolling process and insulation rubber was made of EPDM by TPM(Trans-power molding) process. To select the insulation rubber material, we tested ablative insulation property and degradation property at first and we tested fluidity, adhesive property and hardness of EPDM rubber. Finally we designed TPM process to manufacture motor case assembly and the motor case assembly was examined by non-destructive test(X-ray).

• Journal of Adhesion and Interface
• /
• v.2 no.4
• /
• pp.24-31
• /
• 2001

Polypropylenes(PP) with different melt index values were mixed with ethylene-propylene rubber(EPR) or ethylene-propylene diene monomer rubber(EPDM) and an ethylene copolymer containing carboxylic acid group in a twin screw extruder. Then test specimens were prepared from the pellets of the blends with an injection molding machine. The mechanical properties and morphology of fractured surfaces were measured. Relative peak intensities of carboxylic acid group on the specimen surface were measured with an attennuated total reflection infrared spectrometer (ATR-IR) and compared with each other. The blend specimens were found to have the gradient morphology of rubber domains in PP matrix in the core region and PP skin layer. The blends containing PP of higher melt index showed greater content of ethylene copolymer containing carboxylic acid on the surface when the relative peak intensities of ATR-IR for carboxylic acid were compared. As the melt index values were increased, the decrease tendency in mechanical propeties such as tensile strength and impact strength was more significant for PP/EPR blends than PP/EPDM blends.

• Elastomers and Composites
• /
• v.48 no.4
• /
• pp.300-305
• /
• 2013

Part shrinkage in injection molding is inevitable phenomenon. Thus, it is necessary not only study on the reducing part shrinkage but characterization of part shrinkage. In this study, part shrinkage in injection molded 2.5 dimensional annular shaped specimens has been studied using glass fiber reinforced PC. Annular shaped specimens were designed with various sizes of outer diameter and thickness. Injection temperature, packing time and packing pressure were selected for operational conditions. Profile variations of outer and inner diameters of molded specimens for various operational conditions were investigated. Sizes of outer and inner diameters of injection molded specimens were smaller than the sizes of mold. Part shrinkage decreased as outer diameter and thickness increased. Part shrinkage showed anisotropic behavior and it depended upon gate location. Subsequently, molded specimens were not circular but oval in shape, and showed the largest shrinkage in the direction of gate. It was realized that the mold design such as gate design is important to control the shape of molded products.

• Elastomers and Composites
• /
• v.39 no.4
• /
• pp.286-293
• /
• 2004

Ester- and ether-based thermoplastic polyurethanes of different hardness were injection molded at different mold temperatures and effects of mold temperature on the physical properties of TPUs were investigated. Glass transition temperatures of soft segments of TPUs were hardly changed by mold temperatures. The phase separation of soft and hard segments of injection molded TPUs were affected little by mold temperatures. However, crystallinity of hard segments, temperature range of rubbery plateau, and tensile strength of injection molded TPUs decreased with increasing mold temperatures for TPUs of high hardness. However, injection molded TPUs of low hardness showed increases of crystallinity of hard segments, temperature range of rubbery plateau, and tensile strength with increasing mold temperatures. Different physical properties of injection molded TPUs depending on mold temperatures were attributed to different crystallization and physical crosslinking effects of hard segments.