• Elastomers and Composites
• /
• v.59 no.1
• /
• pp.17-21
• /
• 2024

Solution styrene-butadiene rubber (S-SBR) is used to improve the wet grip and rolling resistance properties of tire treads. As blending of SBRs can improve the physical properties of tire treads, we investigated the effects of SBR type and blending ratio on the physical properties. Twelve SBR/SBR biblend composites were prepared using four SBRs with different microstructures. The glass transition temperature (T_g), tanδ at 0℃ (wet grip predictor), and tanδ at 60℃ (rolling resistance predictor) were obtained from dynamic mechanical analysis, and were compared to the expected values obtained from the results of single SBR samples. Most of the SBR/SBR biblend composites exhibited crosslink densities lower than the expected values. The tanδ values at 0℃ and 60℃ of the SBR/SBR blend composites deviated from the expected values, with many of the deviations being disadvantageous. Of the twelve composites, six samples had higher 0℃ tanδ values than the corresponding expected values, and four exhibited superior wet grip properties to those of the SBR single samples. In addition, two of the twelve samples exhibited improved rolling resistance properties as compared with the single SBR samples. Finally, four samples exhibited lower T_g values than expected, and the T_g of one composite was lower than those of the single SBR samples.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.08a
• /
• pp.307-316
• /
• 2004

This study examined the cause of the wrinkle defect which is frequently encountered in wire rod rolling of low carbon steel$(C0.08\~0.13wt.\%)$. Even a small defect on the surface of rolled bars can easily develop into fatal cracks during cold heading process of low carbon steel, and it is therefore necessary to minimize inherent defects on the surface of hot rolled bars. Hot rolling process of low carbon steel was analyzed to identify the cause of the wrinkle defect in conjunction with FE analysis. The integrated analysis revealed that the wrinkle defect initiated in the first stage of rolling, and it was at the billet edge where severe deformation and drastic temperature drop were present. To elucidate the micro-mechanical mechanism of the wrinkle defect, hot compression tests were carried out at various temperatures and strain rates using Gleeble-3800. The surface profile of the each other compressed specimens was compared, and rough surface lines were observed at relatively low temperatures. Those surface defects can develop into wrinkles during multi-pass rolling. To control the wrinkle defect in rolling, it is necessary to design an adequate caliber which can minimize the loss of ductility, and thereby prevent flow localization. To use the result of this study fur other steels, the quantitative measure of the wrinkle defect and flow localization parameter should be proposed.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.13-18
• /
• 2003

Reduced activation ferritic steel, JLF-1 steel (Fe-9Cr-2W-V-Ta), is one of the promising candidate materials for fusion reactor applications. Fracture toughness ($J_IC$) and tensile tests were carried out at room temperature and elevated temperature ($400^{\circ}C$). Two types of CT specimen were prepared to examine the effect of rolling direction on the fracture toughness of JLF-1 steel. Four types of tensile specimen were also prepared to investigate the property by the rolling direction and welding. The Micro Vickers hardness was measured at various distances of a cross section of the TIG joints of JLF-1 steel according to the heating history of each position. Finally, the fracture surface was observed by scanning electron microscopy (SEM).

• Journal of Korea Foundry Society
• /
• v.10 no.5
• /
• pp.435-443
• /
• 1990

By using the centrifugal atomization, which is one of the rapid solidification processes, Al-5,10wt%Pb alloys which are monotectic alloys were melted at 150K over two liquid phase line in the phase diagram. The melted alloy was poured on the rotating disk, being made into atomized powders, and then the solidified microstructure and morphology of the powder were investigated. This study converted the produced powders into strips by strained powder rolling. According to sintering temperature, the microstructure and hardness were investigated. The solidified structure of the powders were almost cellular dendritic structure. Pb particles ($2.0-3.0{\mu}m$) were fairl distributed in the Al matrix. Powder shapes were irregular. Rolling property and the compacting was good, respectively, because of increasing mechanical interlocking and surface area in the small size powders. With increasing temperature, the boundarys of powders were in porous form due to the diffusion. Pb particles which were surrounding the pores were inverse-segregated at the surface of the powders. With increasing of sintering temperature, the hardness of the powders and the strips decreased. In particular rolling-strip, the hardness abruptly decreased due to the release of work-hardening.

• Korean Journal of Materials Research
• /
• v.30 no.5
• /
• pp.246-251
• /
• 2020

The annealing characteristics of cold-rolled Al-6.5Mg-1.5Zn-0.5Fe-0.5Mn alloy, newly designed as an automobile material, are investigated in detail, and compared with those of other aluminum alloys. Using multi-pass rolling at room temperature, the ingot aluminum alloy is cut to a thickness of 4 mm, width of 30 mm, and length of 100 mm to reduce the thickness to 1 mm (r = 75 %). Annealing after rolling is performed at various temperatures ranging from 200 to 500 ℃ for 1 hour. The specimens annealed at temperatures up to 300 ℃ show a deformation structure; however, from 350 ℃ they have a recrystallization structure consisting of almost equiaxed grains. The hardness distribution in the thickness direction of the annealed specimens is homogeneous at all annealing temperatures, and their average hardness decreases with increasing annealing temperature. The tensile strength of the as-rolled specimen shows a high value of 496 MPa; however, this value decreases with increasing annealing temperature and becomes 338 MPa after annealing at 400 ℃. These mechanical properties of the specimens are compared with those of other aluminum alloys, including commercial 5xxx system alloys.

• Transactions of Materials Processing
• /
• v.13 no.2
• /
• pp.137-141
• /
• 2004

The large deformation at cryogenic temperature is expected as one of the effective methods to produce large bulk ultrafine grained materials. The effects of annealing temperature, 150∼$300^{\circ}C$, on microstructures and mechanical properties of the sheets received 85% reduction at cryogenic temperature were investigated, in comparison with those at room temperature. Annealing of 5083 Al alloy deformed 85%, at $200^{\circ}C$ for an hour,. resulted in the considerable increase of tensile elongation without the great loss of strength and the occurrence of equiaxed grains less than 300nm in diameter.

• Transactions of Materials Processing
• /
• v.6 no.2
• /
• pp.102-109
• /
• 1997

The multistage deformation and stress relaxation were carried out to investigate the strain induced precipitation by torsion tests in the range of 1000~80$0^{\circ}C$, 0.05~5/sec for V-microalloyed steel. The starting temperature and time for the initiation of precipitation were determined by stress relaxation tests. The distribution of precipitates increased, as the strain rate increased and the mean size of precipitates was found to be about 10~30nm. The precipitation starting time$(P_s)$ decreased with increasing strain rate and the amount of pre-strain. The effect of deformation conditions on the no-recrystallization temperature$(T_nr)$ was also determined in the multistage deformation. $T_nr$ Tnr decreased with increasing the strain and strain rate. In the controlled rolling simulation, grain refinement and precipitation hardening effects could be achieved by the alternative large pass strain at the latter half pass stage under the condition of low temperature and high strain rate.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.08a
• /
• pp.233-239
• /
• 2004

The effect of annealing temperature on microstructures and mechanical properties of the sheets received $88\%$ reduction at cryogenic temperature was investigated for the annealing temperature of $150\~300^{\circ}C$, in comparison with those at room temperature. The presence of equiaxed grains, whose size is about 200nm in a diameter, was observed in 5052 Al alloy deformed $88\%$ and annealed $200^{\circ}C$ for an hour. When compared with the deformation at room temperature, the deformation at cryogenic temperature showed the higher strengths and equivalent elongation after annealing at the annealing temperature below $200^{\circ}C$. However, for annealing above $250^{\circ}C$ materials deformed at cryogenic temperature showed the lower strength than those deformed at room temperature. This behavior might be attributed to the higher rate of recrystallization and growth in materials deformed at cryogenic temperature during annealing, due to the lager density of dislocations accumulated during the deformation.

• 연구논문집
• /
• s.22
• /
• pp.115-125
• /
• 1992

Mechanical properties and microstructure were investigated on vacuum induction melted $Fe_3A1$base alloys of $DO_3$ structure. Specal emphasis were put on the effect of alloy chemistry, grain size and process(rolling, directional solidification) on mechanical properties of Fe-22.5-39at.%Al at elevated temperature between room temperature and $800^{\circ}C$. grain size of as-cast alloys is refined by rolling from 1mm to $80\mum$. Tensile strength of Fe-24.lat.%AI was about 404MPa at the critical ordering temperature, and the fracture strain of the alloy was 1-2% at room temperature. An inverse temperature dependence of the strength is noticed as-cast $Fe_3A1$. The presence of Cr and Zr do not affect the room temperature ductility and high temperature strength. Fracture strain of directionally solidified(DS) $Fe_3A1$ is about 1%at room temperature, but is about 60%at. $T_C$(550^{\circ}C)$. Tensile strength of DS alloy is lower than that of as-cast alloy at $530^{\circ}C$ and $430^{\circ}C$. Failure mode at room temperature varies from transgranular fracture to intergranular fracture with the addition of Al. the failure mode also varies from mixed(transgranular+ intergranular) mode between room temperature and $500^{\circ}C$ to intergranular mode above $550^{\circ}C$

• Journal of Powder Materials
• /
• v.10 no.2
• /
• pp.103-107
• /
• 2003

Aluminum-based $Al/Al_2O_3$ composites were fabricated by a powder-in sheath rolling method. A stainless steel tube with outer diameter of 12 mm and wall thickness of 1 mm was used as a sheath. A mixture of aluminum powder and $Al_2O_3$ particles of which volume content was varied from 5 to 20%, was filled in the tube by tap filling and then rolled by 75% reduction in thickness at ambient temperature. The rolled specimen was then sintered at 56$0^{\circ}C$ for 0.5 h. The mixture of Al powders and $Al_2O_3$ particles was successfully consolidated by the sheath rolling. The $Al/Al_2O_3$ composite fabricated by the sheath rolling showed a recrystallized structure, while unreinforced Al powder compact fabricated by the same procedure showed a deformed structure. The unreinforced Al powder compact was characterized by a deformation (rolling) texture of which main component is {112}<111>, while the $Al/Al_2O_3$ composite showed a mixed texture oi deformation and recrystallization. The sintering resulted in recrystallization in Al powder compact and grain growth in the composite.