• Tribology and Lubricants
• /
• v.16 no.6
• /
• pp.477-483
• /
• 2000

Rolling contact fatigue (RCF) tests were performed for two kinds of commercial silicon nitride balls using 4-Ball rolling contact fatigue life tester under EHL condition (Λ=8.9) and boundary lubrication condition (Λ=0.2). All the test balls were finished up to the dimensional accuracy of Grade 5 defined in KS B 2001 (Steel Balls for Ball Bearings) with a size of 8.731 mm. RCF tests were then conducted under the initial theoretical maximum contact stress 6.63 GPa and the spindle speed 10,000 rpm. All the test balls were not failed until 3.75 $\times$ 107 contact cycles and wear tracks of test balls were not conspicuous under EHL condition (Λ= 8.9). In the operations of low lambda regime (Λ= 0.2), all the test balls were surface damaged and high rolling wear resistance was achievable in fully densified using MgO 1 wt% and HIPed balls. Rolling wear of silicon nitride balls under boundary lubrication condition depend mainly on grain size and intergranular phase content of silicon nitride balls.

• International Journal of Railway
• /
• v.2 no.2
• /
• pp.43-49
• /
• 2009

Wear and rolling contact fatigue (RCF) defects are most important causes of rail damage, and often interaction competitive at present railway track. Head check is one of rolling contact fatigue (RCF) defects, and generally occurs in mild circular curves and transition curves that are set at both ends of sharp circular curves. Wear tends to limit the crack growth of head checks by removing the material from the RCF surface. In order to clarify the conditions of the occurrence and growth of head checks, the authors measured the interacting forces between wheels and rails and the angle of attack of wheelset, and carried out contact analyses using the actual profile data of wheels and rails. The effects of the lateral force, the contact geometry, and the wear rate at rail gauge comer on the formation of head checks were also analyzed by using the worn profiles of actual wheels and rails and the data obtained by a track inspection car. Some specific range of wear rate at the gauge comer was identified as having close relation with occurrence of head checks.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.8
• /
• pp.35-41
• /
• 2010

White Etching Layer(WEL) is a phenomenon that occurs on the surface of rail due to wheel/rail interactions such as excessive braking and acceleration. Rolling Contact Fatigue(RCF) cracks on the surface of rail have been found to be associated with WEL. In this study, we have investigated RCF damages of white etching layer using twin disc testing and fatigue analysis. These tests consist of wheel flat tests and rolling contact fatigue tests. WEL has been simulated by wheel flat test. It has been founded that the WEL with a bright featureless contrast is formed on the surface of specimen by etching. Rolling contact fatigue test was conducted by using flat specimens with the WEL generated by the wheel flat test. It has been observed that two types of cracks occur within the specimen. The contact fatigue test was simulated in 2D elastic-plastic FE simulations. Based on loading cycles obtained from the finite element analysis, the fatigue life analysis according to the thickness variation of WEL was carried out. The longest fatigue life was observed from the thickness of 20um.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.589-590
• /
• 2012

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.5
• /
• pp.355-359
• /
• 2000

Ion beam assisted deposition system was used to deposit CNx coatings with various thickness on the substrates of high-frequency induction hardened steels. Rolling contact fatigue tests were performed using Polymet RCF-1 machine with a constant supply of lubricant. Rolling contact fatigue life was substantially different in the steels with various thickness of CNx coatings. The optimum thickness of CNx coating was found to be $8.9{\mu}m$, showing the longest fatigue life, mainly caused by higher resistance to initiation of cracks and protective overcoat remaining to the surface failure during rolling contact fatigue. Cracks were initiated in the substrates under the surface of wear track and propagated to the surface, which eventually resulted in the failure. The reduction of fatigue life observed in the specimen with elimination of CNx coating during rolling contact fatigue was explained by the substrates deformation.

• Proceedings of the KSR Conference
• /
• 2005.11a
• /
• pp.1109-1114
• /
• 2005

The rolling contact fatigue of wheels for high speed trains is a matter of increasing importance. The wheel damages from fatigue crack makes noise up and safety down. RCF-casued accidents cause traffic congestion and economical costs as well as personal injuries. In this study, we examine the rolling contact fatigue of wheels for power car running at 300km/h. Using the results of multi-body dynamic analysis and the proposed procedure of Ekberg, we calculate the fatigue index of surface-initiated fatigue, subsurface-initiated fatigue and fatigue initiated at deep material defects. As a result. the fatigue index shows us whether fatigue will appear and in which form. In addition, we present Shakedown map on surface-initiated fatigue.

• Journal of the Korean Society of Safety
• /
• v.32 no.1
• /
• pp.15-20
• /
• 2017

A large amount of research has been performed on the rolling contact fatigue(RCF) life of bearings, since it directly affects the safety and reliability of mechanical systems. It is well known that rolling contact fatigue life is influenced by several parameters including contact pressure, oil contamination by water or metal particles, and the surface conditions of bearings. However, the detailed damage mechanisms involved in rolling contact fatigue have not been clearly identified yet. In this paper the effects of water contamination of the lubricant and surface roughness of bearing steel on the rolling contact fatigue life were investigated. Two types of specimens with different surface roughness values were prepared through turning and lapping operations. They were tested under two different lubrication conditions, i.e. oil lubricant with 100% of oil and the water contaminated condition with 80% of oil and 20% of water using the rolling contact fatigue testing machine. The surface damage induced by the rolling contact fatigue was observed by using atomic force microscope(AFM). Experimental results show that the rolling contact fatigue life, $L_{10}$ was reduced by 24 to 33% depending on the lubrication condition. The reduction of fatigue life in the range of 53 to 57% was also observed at different surface roughness conditions.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1583-1584
• /
• 2013

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.2115-2124
• /
• 2011

The rail surface defects which are generated on repeated rolling contact fatigue are getting increased according to high speed, high density, and minimum weight. In addition, Increasing noise and vibration are affected by these also impact load generated as well. Because of this phenomenon, more serious and critical damages were occurred. In fact, in order to control them, the rail grinding were conducted. However, there are not enough researches to make an criteria of generating optimal rail grinding amount in Korea. This study evaluated how depth of hardening on rail surface is formed and suggested optimal rail grinding amount by RCF(rolling contact fatigue) test with generated contact pressure between KTX wheel and UIC60 rail by applying FEM analysis. Therefore, the amount was generated approximately 0.2mm/20MGT to maintain integrity of rail surface by getting rid of depth of hardening on rail according to rail accumulated passing tonnage.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.1
• /
• pp.10-19
• /
• 2008

To investigate the effect of ultrasonic nano-crystalline surface modification (UNSM) treatment on rolling contact fatigue and residual stress properties of bearing steels, this paper carried out a rolling contact fatigue test, measured residual stress and retained austenite, performed a wear test, observed microstructure, measured micro hardness, and analyzed surface topology. After the UNSM treatment, it was found that the surface became minute by over $100{\mu}m$. The micro surface hardness was changed from Hv730~740 of base material to Hv850~880 with about 20% improvement, and hardening depth was about 1.3 mm. The compressive residual stress was measured as high as -700~-900 MPa, and the quantity of retained austenite was reduced to 27% from 34%. The polymet RCF-6 ball type rolling contact fatigue test showed over 4 times longer fatigue lifetime after the UNSM treatment under 551 kgf load and 8,000 rpm. In addition, this paper observed the samples, which went through the rolling contact fatigue test, with OM and SEM, and it was found that the samples had a spalling phenomenon (the race way is decentralized) after the UNSM treatment. However, before the treatment, the samples had excessive spalling and complete exploration. Comparison of the test samples before and after the UNSM treatment showed a big difference in the fatigue lifetime, which seems to result from the complicated effects of micro particles, compressive residual stress, retained austenite, and surface topology.