• Journal of Power System Engineering
• /
• v.17 no.6
• /
• pp.122-129
• /
• 2013

The microstructure and deformation behavior in 22Cr-0.2N micro-duplex stainless steels with various Ni and Mn contents were compared using by OM, TEM, and XRD. The 22Cr-0.2N duplex stainless steel plates were fabricated and hot rolled, followed by annealing treatment at the temperature range of $1,000-1,100^{\circ}C$. All the samples showed the common strain hardening behaviour during the tensile test at a room temperature. The steels tested at the temperatures of $-30^{\circ}C$ or $-50^{\circ}C$ showed a distinct inflection point in the stress-strain curves, which should be resulted from the formation of strain-induced martensite(SIM) of austenite phase. This was confirmed by TEM observations. The onset strain of a inflection point in a stress-strain curve should be depended up the value of $M_d30$. With the decrease of the tensile test temperature, the inflection point appeared earlier, and the strength and fracture strain were higher. The tensile behaviour was discussed from the point of austenite stability of the micro-duplex stainless steels with the different Ni and Mn content.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.4
• /
• pp.200-205
• /
• 2015

Effects of austenite on the uniform corrosion in the solution of $1\;N\;H_2SO_4$ were investigated through the electrochemical polarization test. Two phases structures of martensite and austenite were obtained by annealing treatment at the range of $500^{\circ}C{\sim}700^{\circ}C$ for 10min. in 70% cold-rolled 202 stainless steel. Volume fraction of reversed austenite increased rapidly with an increase of annealing temperature. Uniform Corrosion was occur mainly on martensite phase in 202 austenitic stainless steel with two phase of austenite and martensite. Corrosion current density increased with an increase of volume fraction of austenite, therefore uniform corrosion was affected by volume fraction of austenite

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10a
• /
• pp.136-137
• /
• 2003

Recrystallization textures of ferritic stainless steel sheets of STS 430, the crystallographic texture was modified by means of cross rolling and subsequent annealing. The conventional normal rolling led to the formation of ｛334｝＜483＞ in the final recrystallization texture. Cross rolling in the present work was performed by a 45$^{\circ}$rotation of RD around ND. After recrystallization annealing the cross-rolled samples displayed stronger｛111｝//ND orientations. The cross rolled sample displayed a higher resistance against ridging.

• Nuclear Engineering and Technology
• /
• v.48 no.1
• /
• pp.164-168
• /
• 2016

Lean duplex stainless steels with 0.087 wt.% gadolinium (Gd) were inert arc-melted and cast in molds of size $10mm{\times}10mm{\times}20mm$. The micro-hardnesses of the rolling direction (RD), transverse direction (TD) and short transverse (ST) direction were $258.5H_V$, $292.3H_V$, and $314.7H_V$, respectively. A 33% cold rolled specimen had the crystallographic texture that (100) pole was mainly concentrated to the normal direction (ND) and (110) pole was concentrated in the center of ND and RD. The corrosion potential and corrosion rate in artificial seawater and $0.1M\;H_2SO_4$ solution were in the range of $105.6-221.6mV_{SHE}$, $0.59-1.06mA/cm^2$, and $4.75-8.25mV_{SHE}$, $0.69-1.68mA/cm^2$, respectively. The friction coefficient and wear loss of the 0.087 w/o Gd-lean duplex stainless steels in artificial seawater were about 67% and 65% lower than in air, whereas the wear efficiency was 22% higher. The corrosion and wear behaviors of the 0.087 w/o Gd-lean duplex stainless steels significantly depended on the Gd phases.

• Journal of Welding and Joining
• /
• v.31 no.2
• /
• pp.49-56
• /
• 2013

We have investigated traits of clad metals in hot-rolled clad steel plates, sensitization and mechanical properties of STS 316 steel plate and carbon steel(A516). Clad steel plates were butt-weld by SAW+SMAW, and with the time of heat treatment as the variable, heat treatment was conducted at $625^{\circ}C$, for 80, 160, 320, 640, 1280 minutes. As a way to evaluate it, sectioned weldments and external surfaces were investigated to reveal the degree of sensitization by mechanical property, etching and those of EPR test, results were compared with it. In short, the purpose of this study is suggesting some considerations in developing on-site techniques to evaluate the sensitization of stainless steels.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.99-101
• /
• 2008

At 21st century, material development concepts were changed to fulfill the environmental friendly demands. This study is to study the effect of pressurized nitrogen gas and manganese in high nitrogen austenitic stainless steel(HNS) in which N and Mn elements substitute the nickel element. 100kg HNS ingots were made by Pressurized Vacuum Induction Melting(P-VIM) and were forged according to free forging process. As forged HNS were hot and cold rolled by pilot scale rolling machine. Depending on the rolling condition, the mechanical properties of HNS were changed. The roll thrust and sheet folding showed asymmetry condition between work and drive side during cold and hot rolling. The purpose of this study are to improve workability the hot and cold rolling machine and to set the conditions for establishing the rolling process.

• Nuclear Engineering and Technology
• /
• v.40 no.4
• /
• pp.305-310
• /
• 2008

Based on a composition of 99.4 wt% AISI 316L stainless steel, 0.3wt% Ti and 0.3 wt% $Y_2O_3$, an austenitic ODS steel was fabricated by a process of mechanical alloying, hot isostatic pressing and rolling. Fine oxide particles were observed in the matrix, and their chemical formulations were determined to be $Y_2Si_2O_7$ and TiO. Heat treatment of the cold-rolled sample at $1200^{\circ}C$ induced an isotropic tensile behavior at room temperature and at $700^{\circ}C$. This result would be mainly attributed to the equiaxed grains that form as a result of the heat treatment for recrystallization.

• Journal of Welding and Joining
• /
• v.32 no.2
• /
• pp.29-36
• /
• 2014

Recently, in order to enhance the function and usefulness of products, cladding of dissimilar materials that maximizes the performance of the material is being widely used in all areas of industry as an important process. Clad steel plate, produced by cladding stainless steel plate, an anticorrosive material, on carbon steel plate, is being used to produce pressure vessels. Stainless steel plate has good corrosion resistance, and carbon steel plate has good rigidity and strength; clad steel can satisfy all of these qualities at once. This study aims to find the ${\delta}$-ferrite behavior, mechanical properties, structure change, integrity and reliability of clad steel weld on hot rolled steel plates. For this purpose, multi-layer welding, repair welding and post weld heat treatment were implemented according to welding procedure specifications (WPS). In order to observe the mechanical properties and toughness of clad steel weld zone, post weld heat treatment was carried out according to ASME Sec. VIII Div.1 UW-40 procedure for post weld heat treatment. With heat treatment at $625^{\circ}C$, the hold time was used as the process variable, increased by intervals that were doubled each time, from 80 to 1,280 min. The structure of weld part was typical cast structure; localized primary austenite areas appeared near central vermicular ferrite and fusion line. The heat affected zone showed rough austenite structure created by the weld heat input. Due to annealing effects of heat treatment, the mechanical properties (tensile strength, hardness, impact value) of the heat affected area tended to decrease. From the results of this study, it is possible to conclude the integrity of clad steel welds is not affected much in field welding, repair welding, multi-layer welding, post weld heat treatment, etc.

• Journal of Welding and Joining
• /
• v.31 no.5
• /
• pp.47-53
• /
• 2013

We have investigated the traits of clad metals in hot-rolled clad steel plates, including the sensitization and mechanical properties of STS 316 steel plate and carbon steel (A516), under various specific circumstances regarding post heat treatment, multilayered welds, and thick or repeated welds for repair. For evaluations, sectioned weldments and external surfaces were investigated to reveal the degree of sensitization by micro vickers hardness, tensile, and etching tests the results were compared with those of EPR tests. The clad steel plates were butt-welded using FCAW and SAW with the time of heat treatment as the variable, a that was conducted at $625^{\circ}C$, for 80, 160, 320, 640, and 1280 min. Then, the change in corrosion resistance was evaluated in these specimens. With carbon steel (A516), as the heat treatment time increased, the annealing effect caused the tensile strength to decrease. The micro-hardness gradually increased and decreased after 640 min. The elongation and contraction of the area also increased gradually. The oxalic acid etch test and EPR test on STS316 and the clad metal showed STEP structure and no sensitization. From the test results on multi-layered and repair welds, it could be concluded that there is no effect on the corrosion resistance of clad metals. The purpose of this study was to suggest some considerations for developing on-site techniques to evaluate the sensitization of stainless steels.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.212-212
• /
• 2014

0.04% Gd-duplex stainless steels (Gd-DSTSs) for neutron absorbing materials were inert arc-melted and poured into a Y-shape block with the size of $100{\times}100{\times}20[mm]$. The Gd-DSTS was hot rolled at $1200^{\circ}C$ followed by cold rolling to have 33% reduction. The average grain sizes of the rolling (RD), transverse (TD) and short transverse (ST) directions were 6, 7, $11{\mu}m$, respectively. The micro-hardnesses of the RD, TD and ST directions were 258.5, 292.3, 314.7 $H_V$, respectively. Corrosion potential and corrosion rate of the cold rolled Gd-duplex stainless steel in aerated artificial sea water and 0.1M $H_2SO_4$ solution were $0.2216V_{SHE}$, $0.0106A/cm^2$, $-0.0825V_{SHE}$, $0.0168A/cm^2$ for RD, $0.2210V_{SHE}$, $0.0077A/cm^2$, $0.0817V_{SHE}$, $0.0092A/cm^2$ for TD, $0.1056V_{SHE}$, $0.0059A/cm^2$, $0.0475V_{SHE}$, $0.0069A/cm^2$ for ST, respectively. The corrosion behavior depended on the texture, which were due to mainly grain boundary and minorly crystallographic texture. Friction coefficient and wear resistance were 2.07 and 0.48 mm, respectively.