• 한국재료학회지
• /
• 제18권6호
• /
• pp.298-301
• /
• 2008

A preparation of $Ni_xMn_{1-x}Fe_2O_4$ nanoparticles produced via the reduction of Nickel nitrate hexahydrate, Manganese (II) nitrate hexahydrate and Iron nitrate nonahydrate with hydrazine in Igepal CO-520/cyclohexane reverse micelle solutions was investigated. Transmission Electron Microscope (TEM), X-ray Diffraction (XRD) and Vibration Sample Magnetometer (VSM) analyses showed that the resultant nanoparticles increased the molar ration of water to Igepal CO-520 as the concentrations of Nickel nitrate hexahyrate, Manganese (II) nitrate hexahydrate and Iron nitrate nonahydrate increased. The average size of the synthesized particles calcined at $600^{\circ}C$ for 2hrs was in the range of 20 nm to 30 nm, and the particle distribution was broadened. The phase of the synthesized particles was crystalline, and the magnetic behavior of the synthesized particles was superparamagnetism. The effect of the synthesis parameters of the molar ratio of water to surfactant and the calcination temperature was discussed.

• 한국생물공학회:학술대회논문집
• /
• 한국생물공학회 2000년도 춘계학술발표대회
• /
• pp.157-160
• /
• 2000

본 연구에서는 $20^{\circ}C$에서 음이온 계면활성제인 AOT와 isooctane으로부터 형성된 reverse micelle을 이용하여 수용액상에 녹아있는 BSA인 모델 단백질을 분리하는 실험을 행하였다. 염의 농도가 0.1M에서 최고 가용화 효율은 KCl, NaCl, $MgCl_2$ 그리고 $CaCl_2$의 경우 각각 pH=5, 5.5, 7, 5 근처임을 알 수 있었다. 또한 매우 낮은 염 농도에서는 가용화는 일어나지 못하고 계면이 혼탁한 현상을 보였다. 특히 $CaCl_2$의 경우에 염 농도에 대하여 최고의 가용화 효율을 보였다.

• 한국환경과학회지
• /
• 제11권9호
• /
• pp.987-992
• /
• 2002

Nanosized titania sol has been produced by the controlled hydrolysis of titanium tetraisopropoxide(TTIP) in sodium bis(2-ethylhexyl)sulfosuccinate(AOT) reverse micelles. The physical properties, such as crystallite size and crystallinity according to R ratio have been investigated by FT-IR, XRD and UV-DRS. In addition, the photocatalytic degradation of bromate has been studied by using batch reactor in the presence of UV light in order to compare the photocatalytic activity of prepared nanosized titania. It is shown that the anatase structure appears in the 300~$600^{\circ}C$ calcination temperature range and the formation of anatase into rutile starts above $700^{\circ}C$. The crystallite size increases with increasing R ratio. In the photocatalytic degradation of bromate, the photocatalytic decomposition of bromate shows the decomposition rate increases with decreasing initial concentration of bromate and with increasing intensity of light.

• 한국전기화학회:학술대회논문집
• /
• 한국전기화학회 2005년도 춘계총회 및 학술발표회
• /
• pp.23-23
• /
• 2005

• 공업화학
• /
• 제28권3호
• /
• pp.351-354
• /
• 2017

역미셀법을 이용하여 열적 안정성이 우수한 감마-알루미나의 합성 공정을 최적화하기 위하여 실험계획법을 사용하였다. 먼저 합성공정에 주 요소인 계면활성제, 물 및 오일의 비에 대한 최적의 실험조건을 설계하기 위하여 혼합물 실험법을 이용하여 12가지 실험조건을 도출하였다. 설계된 조건에서 역미셀법을 이용하여 합성한 입자를 $900^{\circ}C$에서 소성한 결과 입자의 크기에 차이는 있었지만 모두 감마-알루미나 결정구조를 가졌다. 도출된 실험결과를 이용하여 계산된 2차 회귀모델의 결정계수는 93.68%이었으며, P- 값이 0.002로서 유의하다고 할 수 있다. 다양한 입자크기를 가지는 감마-알루미나의 합성조건을 모든 범위에서 대하여 표면도와 등고선도를 이용하여 제시하였다. 그 결과 Surfactant/Water/Oil의 질량비가 0.3450/0.0729/0.5821인 조건에서 합성할 때 약 2.8 nm의 가장 작은 입자가 합성되는 것으로 계산되었다.

• 한국재료학회지
• /
• 제25권2호
• /
• pp.95-99
• /
• 2015

$NiAl_2O_4$ nanoparticle was synthesized by a reverse micelle processing for inorganic pigment. $Ni(NO_3)_2{\cdot}6H_2O$ and $Al(NO_3)_3{\cdot}9H_2O$ were used for the precursor in order to synthesize $NiAl_2O_4$ nanoparticles. The aqueous solution, which consisted of a mixing molar ratio of Ni/Al, was 1:2 and heat treated at $800{\sim}1100^{\circ}C$ for 2h. The average size and distribution of synthesized $NiAl_2O_4$ powders are in the range of 10-20 nm and narrow, respectively. The average size of the synthesized $NiAl_2O_4$ powders increased with an increasing water-to-surfactant molar ratio and heating temperature. The crystallinity of synthesized $NiAl_2O_4$ powder increased with an increasing heating temperature. The synthesized $NiAl_2O_4$ powders were characterized by X-ray diffraction analysis(XRD), a field emission scanning electron microscopy(FE-SEM), and a color spectrophotometer. The properties of synthesized powders were affected as a function such as a molar ratio and heating temperature. Results indicate that synthesis using a reverse miclle processing is a favorable process to obtain $NiAl_2O_4$ spinels at low temperatures. The procedure performed suggests that this new synthesis route for producing these oxides has the advantage of being fast and simple. Colorimetric coordinates indicate that the pigments obtained exhibit blue colors.

• 공업화학
• /
• 제35권2호
• /
• pp.115-121
• /
• 2024

본 연구는 W1/O/W2 이중유화법을 통한 마이크로 캡슐화 공정을 최적화하기 위해 역미셀(reverse micelle), salt 농도 등의 열역학적 변수와 유체의 점도, 계면장력 등 계면의 유동에 영향을 미치는 공정변수들의 영향성을 분석하였다. 아스코르브산의 PLA (polylactic acid) 미립자 내부로의 캡슐화 효율에 가장 큰 영향을 미치는 변수는 W1과 W2상의 삼투압의 차이로 W2상의 salt 농도를 높이거나, W1상의 아스코르브산 농도를 줄이면 캡슐화 효율이 높아짐을 관찰하였다. 또한, 삼투압의 차이가 클수록 미립자 표면의 손상이 심해짐을 확인할 수 있었다. 캡슐화 효율을 높일 것으로 예상되었던 역미셀 도입은 그 기여도가 낮거나 오히려 캡슐화 효율을 낮추었다. 마이크로캡슐의 수율은 공정 조건, 용액 조성 등과 상관없는 universal 함수로 표현하였는데, Ca > 20에서는 더 이상의 수율 증가가 관찰되지 않았다.

• KSBB Journal
• /
• 제7권1호
• /
• pp.51-58
• /
• 1992

역미셀을 이용하여 세포나 효소와 같은 생촉매제를 용해, 추출할 수 있으며 이 생촉매제는 bioreactor로써 여러가지 기질물질을 bioconversion시킬 수 있다. 역미셀을 이용하여 지금까지 할 수 없었던 많은 연구를 가능하게 할 수 있으며 효소를 의약춤 함성, 약품분석, 의료진단에 더욱 용이하게 이용할 수 있다.

• 한국결정성장학회지
• /
• 제11권2호
• /
• pp.67-70
• /
• 2001

Nanosize $SiO_2$composite particles have been synthesized within reverse micelle via metal alkoxide hydrolysis and condensation. The size of the particles can be controlled by manipulating the relative rates of the hydrolysis and condensation reactions of tetraethoxysilane (TEOS) within the microemulsion. The average size of synthesized particles was about in the size range 14~30nm. The effects of synthesis parameters, such as the molar ratio of water to TEOS, the molar ratio of water to surfactant, and the amount of base catalyst, are discussed.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.85.2-85
• /
• 2000