• Progress in Superconductivity and Cryogenics
• /
• v.9 no.2
• /
• pp.11-14
• /
• 2007

The critical current, $I_c$, degradation behaviors with bending strain were investigated in a commercially available YBCO coated conductor tape. In particular, the strain reversibility of $I_c$ and the influence of repeated bending on $I_c$ have been studied. Also, repeated bending at 77 K was done in order to understand the Ie behavior under cyclic bending strains. A reversible behavior of $I_c$ has been found up to a high bending strain of 1.60% for the RABiTS/MOD processed CC sample with copper reinforcement. Under repeated bending, the Ie showed a 95% $I_c$ retention up to 100 cycles for bending strains of 1.0% or less. The n-value behavior showed a good agreement with the $I_c$ degradation behavior, representing that any cracking did not occur on the YBCO film resulting from the reinforcement provided by the copper stabilizers.

• Structural Engineering and Mechanics
• /
• v.47 no.6
• /
• pp.773-790
• /
• 2013

Bending behaviors of corroded reinforced concrete (RC) beams under repeated loading were investigated experimentally. A total of twenty test specimens, including four non-corrosion and sixteen corrosion reinforced concrete beams, were prepared and tested. A numerical model for flexural and cracking behaviors of the beam under repeated loading was also developed. Effects of steel corrosion on reinforced concrete beams regarding cracking, mid-span deflection, stiffness and bearing capacity of corroded beams were studied. The impact of corrosion on bond strength as the key factor was investigated to develop the computational model of flexural capacity. It was shown from the experimental results that the bond strength between reinforcement and concrete had increased for specimen of low corrosion levels, while this effect was changed when the corrosion level was higher. It was indicated that the bearing capacity of corrosion beam increased even at a corrosion level of about 5%.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.18 no.4
• /
• pp.362-368
• /
• 2009

In general, circuit board assemblies experience various mechanical loadings during assembly and in actual use. The repeated cyclic bending can cause electrical failures due to circuit board cracks, solder interconnects cracks, and the component cracks. In this paper, we report on the failure characteristics of semiconductor chips under the repeated cyclic bending. We first describe a new 4-point bending tester, which is developed according to JEDEC standard No. 22B113. The performance of the tester is then estimated through actual experiments. Test results reveal that the cracks first occur on the outer balls around 20,000 cycles and gradually propagate to the inner balls where cracks are found around 70,000 cycles.

• Electronic Materials Letters
• /
• v.14 no.6
• /
• pp.678-688
• /
• 2018

The repeated-bending properties of Sn-0.7Cu, Sn-0.3Ag-0.7Cu (SAC0307), and Sn-3.0Ag-0.5Cu (SAC305) solders mounted on flexible substrates were studied using highly accelerated stress testing (HAST), followed by repeated-bending testing. In the Sn-0.7Cu joints, the $Cu_6Sn_5$ intermetallic compound (IMC) coarsened as the HAST time increased. For the SAC0307 and SAC305 joints, the $Ag_3Sn$ and $Cu_6Sn_5$ IMCs coarsened mainly along the grain boundary as the HAST time increased. The Sn-0.7Cu solder had a high contact angle, compared to the SAC0307 and SAC305 solders; consequently, the SAC0307 and SAC305 solder joints displayed smoother fillet shapes than the Sn-0.7Cu solder joint. The repeated-bending for the Sn-0.7Cu solder produced the crack initiated from the interface between the Cu lead wire and the solder, and that for the SAC solders indicated the cracks initiated at the surface, but away from the interface between the Cu lead wire and the solder. Furthermore, the oxide layer was thickest for Sn-0.7Cu and thinnest for SAC305, regardless of the HAST time. For the SAC solders, the crack initiation rate increased as the oxide layer thickened and roughened. $Cu_6Sn_5$ precipitated and grew along the grain and subgrain boundaries as the HAST time increased, embrittling the grain boundary at the crack propagation site.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1995.10a
• /
• pp.1071-1074
• /
• 1995

This paper proposes two directional bending actator using three link, two shape memory alloys(SMA) of coil-type springs and two guide wires. By the heating of two SMA springs sequentially, the bending and stretching of the actuator is possible. Bending angle, force and repeated bending motion of actuator were measured and characterized. The performance of the actuator has been characterized for the possible application for catheter.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.483-486
• /
• 2004

Inner structured and bonded panel, or ISB Panel, as a kind of sandwich type panel, has metallic inner structures which have low relative density, because of their dimensional shape of metal between a pare of metal skin sheets or face sheets. In this work, ISB panels and inner structures formed as repeated pyramidal shapes are introduced. Pyramidal structures are formed easily with expanded metal sheet by the crimping process. Three kinds of pyramidal structures are made and used to fabricate test specimen. Through the multi-point electrical resistance welding, inner structures are bonded with skin sheet. 3-point bending tests are carried out to measure the bending stiffness of ISB panel and experimental results are discussed.

• Proceedings of the KOSOMBE Conference
• /
• v.1997 no.11
• /
• pp.497-500
• /
• 1997

In this paper, we proposes a bending actuator using shape memory alloy coil-type springs. By the heating of two shape memory alloy coil-type springs sequentially, the bending and stretching motion of the actuator is possible. We measure the bending angle and repeated bending motion with the various currents. Furthermore, we control the bending angle of the 1 directional bending actuator with sensors. The performance of the actuator has been characterized or the possible application for catheter.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.3 no.1
• /
• pp.176-182
• /
• 2000

$360^{\circ}$ bending of Ti-6Al-4V large-diameter seamless tube(62.37 mm $OD {\times} 4.40mm$ wall thickness) has been achieved at room temperature without heating. The bending process comprised two steps : the first step is $360^{\circ}$ bending by an uniquely designed rotary bender allowing spring back, which is subsequently eliminated by the second or finishing step which comprised repeated bending processes by powered three roll bender, In odor to prevent collapse of tube during bending, Cerro $Tru^{TM}$(Trade name of a non-ferrous low melting point alloy)has been employed as a filler metal. The resultant ovality(out of roundness) obtained was 1.28%, as compared with 6~8% without applying Cerro $Tru^{TM}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.298-299
• /
• 2005

Differently from the tensile, transverse compression and torsion cases, the bending test of HTS tapes requires a lot of time and efforts, since the sample should be mounted successively onto bent sample holders in the order of decreasing radius and measuring the $I_c$ at each step. The influence of repeated cooling and warming experienced during these processes on the $I_c$ degradation can not be ignored. As a result, in this study, particularly. a new one-body type sample holder which provides continuous bending strains at 77K was devised. And, $I_c$ degradation behavior of Bi-2223 tapes under easy bending condition was investigated and compared that with other cases using Goldacker-type bending tester or respective sample holder.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.627-630
• /
• 2004

This paper investigates a study on the bending behavior of beam strengthened with CFS under repeated loading. The test specimen consisted of 20cm in width, 40cm in depth, and 15cm in CFS width. We find the strength decrease under repeated loading test comparing with the monotonic incremental loading test.