• 한국태양에너지학회 논문집
• /
• 제26권1호
• /
• pp.57-64
• /
• 2006

Cr-CrO cermet solar selective coatings with a double cermets layer film structure were prepared using a special direct current (dc) magnetron sputtering technology. The typical films structures from surface to bottom substrate were measured to be an $Al_2O_3$ anti-reflection layer on a double Cr-CrO cermet layer on an Al metal infrared reflection layer. Optical properties of optimized Cr-CrO cermet solar selective coating were absorptance (${\alpha}$) = 0.95 and emittance (${\varepsilon}$) = 0.10 ($100^{\circ}C$). Atomic force microscopy (AFM) image showed that Cr-CrO cermet film was very smooth and their grain size was also very small The results of thermal stability test showed that the Cr-CrO cermet solar selective coatings were stable for use at temperature of $400^{\circ}C$.

• 한국광학회지
• /
• 제26권5호
• /
• pp.275-282
• /
• 2015

단축이방성 박막들과 등방성 박막들이 코팅되어 있는 시료에 비스듬히 입사한 빛의 유효반사계수 표현들을 유도하였다. 단축 이방성 박막 내에서의 다중반사 효과를 반영하여 여러 층의 등방성 박막들과 이방성 박막들이 섞여 있는 시료의 유효반사계수 표현들과 타원상수 표현들을 제시함으로써 시료면에 수직한 방향으로 균일하지 않은 단축이방성 분포를 가진 시료의 광학이방성을 여러 개의 단축이방성 박막으로 나누어 분석할 수 있도록 하였다.

• 한국광학회지
• /
• 제5권2호
• /
• pp.225-230
• /
• 1994

홀로그래피 HUD의 제작에 필요한 주요 파라미터를 살펴보고 이들 값을 결정하기 위한 관계식을 유도하여 설계 값을 설정하였다. 기록 방법으로는 간섭무늬에 의한 잡음을 최소화할 수 있는 공기층 반사 기록방법을 제시하였다. 특히, DCG필름을 처리한 후에 생기는 중심파장의 이동을 보정하기 위한 새로운 방법을 소개하였다.

• Journal of Magnetics
• /
• 제5권1호
• /
• pp.1-3
• /
• 2000

We have theoretically investigated changes in reflection coefficients induced by misfit strain located near the interface between an iron-yttrium garnet magnetic film and a nonmagnetic gadolinium-gallium garnet substrate in a transverse magneto-optical configuration.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1995년도 추계 학술발표 강연 및 논문개요집
• /
• pp.68-68
• /
• 1995

• 한국광학회지
• /
• 제6권4호
• /
• pp.259-265
• /
• 1995

국내 민수용으로 유통되고 있는 20여종의 무반사 안경렌즈들을 선정하여 광학적 특성을 분석하였다. 분광광도계를 사용하여 측정한 반사특성과 투과특성을 렌즈의 굴절력, 각 무반사층들 및 렌즈기층에 의한 영향과 연결시켜 분석하였다. 흡수단 근방에서의 겉보기 흡수스펙트럼은 기층물질에 따라 결정되며 400-700nm의 파장대역에서 대부분의 시료들의 겉보기 흡수스펙트럼과 반사스펙트럼은 강한 양의 상관관계를 보여준다. 예외적으로 기층에 의한 흡수가 큰 렌즈들은 상관관계가 약해지며 이와 같은 기층에 의한 흡수는 무반사 특성에 부정적인 효과를 가진다. 또한 국내에서 제작되는 $SiO_2/TiO_2/SiO_2/ZrO_2/Cr$ 다층박막층을 c-Si 기층위에 성장시키면서 각 단계별로 ex-situ 분광타원해석법으로 분석하여 $TiO_2$ 박막과 $ZrO_2$ 박막의 조밀도가 80% 정도에 불과하며 박막이 두꺼원 짐에 따라 박막에 수직한 방향으로 균일하지 않음을 확인하였다. 마지막으로 실시간, in-suti 측정을 바탕으로하여 엄밀한 사양이 요구되는 다층박막, 초격자박막 등을 재현성있게 성장시킬 수 있는 가능성에 대해 토의하였다.

• 한국광학회지
• /
• 제20권1호
• /
• pp.57-60
• /
• 2009

CMOS 이미지 센서의 수광 효율을 높이기 위해서 픽셀의 광 통로 벽에 광학 박막의 도입을 제안하고자 한다. Essential Macleod를 이용하여 시뮬레이션해 본 결과, 전반사가 일어나는 범위가 현저히 증가하였다. 특히 공기 박막을 도입할 경우에, 그 효과가 가장 현저하여, 광 통로 벽에서의 전반사 임계각이 50도로까지 확대되었다.

• 한국전기전자재료학회논문지
• /
• 제28권12호
• /
• pp.821-825
• /
• 2015

Anti-reflective (AR) thin film was fabricated on a glass substrate by sol-gel method. The coating solution was synthesized with TEOS (tetraethlyorthosilicate) and poly ethylene glycol (PEG, 4.0 wt%). As the withdrawal speed of coating was changed from 0.1 mm/sec to 0.3 mm/sec, the thickness and refractive index of prepared thin films were changed. The reflectance and transmittance of coating glass fabricated by the withdrawal speed of 0.1 mm/sec were 0.62% and 95.0% in visible light range. The refractive index and thickness of single layer thin film were n= 1.29 and ca. 99.0 nm.

• 한국광학회지
• /
• 제8권5호
• /
• pp.395-402
• /
• 1997

$\1.55mu\textrm{m}$ InGaAsP MQW FP 반도체 레이저 단면의 무반사 코팅 두께를 앞면에 무반사 코팅하는 동안 뒷면의 출력을 실시간으로 측정하여 결정하였다. 굴절률 1.85인 $SiO_x$ 박막의 최적 두께는 188 nm이고, 무반사 코팅 전, 후의 문턱전류비로 계산한 단면의 반사율은 약 2 $\times$ $10^{-4}$이었다. 무반사 코팅 후 주입전류 60 mA일 때 출력이 87%, 기울기 효율이 3.4배, 문턱전류가 2.64배 증가하였다. 또한 실시간으로 $Si/SiO_2$ 박막의 고반사 코팅을 뒷면에 한 후 코팅 전보다 출력이 약 160% 향상되었고, 기울기 효율이 3.8배 증가하였으며, 문턱전류는 1.07배로 코팅 전과 거의 비슷하여, 무반사 및 고반사 코팅 후 반도체 레이저의 출력특성이 크게 향상되었다.

• 한국초전도ㆍ저온공학회논문지
• /
• 제10권2호
• /
• pp.20-23
• /
• 2008

[ $La_2Zr_2O_7$] (LZO) buffer layers were deposited on biaxially textured Ni-W substrates by chemical solution deposition method (CSD). In this study, the effect of $B_2O_3$ addition on texture and surface roughness of LZO films was investigated. The alkoxide-based precursor solution was employed to synthesize the precursor solution of LZO and the solution was coated on biaxially textured Ni-W substrates and subsequently annealed at $900^{\circ}C$ for crystallization. The pure LZO film without $B_2O_3$ addition showed a (222) reflection in the X-ray diffraction (XRD) profile. The intensity of (222) reflection was enhanced and more rough surface was obtained after further repetition of coating. Contrary to this, the LZO film prepared by $B_2O_3$ added precursor solution shows well-developed (400) reflection peak in the XRD profile and excellent biaxial texture (${\Delta}{\theta}=4.3^{\circ}$, ${\Delta}{\phi}=6.8^{\circ}$). The surface roughness of LZO films were also improved by addition of $B_2O_3$ even after multicoating ($R_{rms}{\sim}3.1nm$). It was shown that the LZO film with smooth surface and biaxial texture was grown on the biaxially textured Ni-W substrates with addition of $B_2O_3$ in the precursor solution.