• Journal of Conservation Science
• /
• v.37 no.5
• /
• pp.606-616
• /
• 2021

From the collection of the National Kimhae Museum, qualitative analyses using microscopic observation, SEM-EDS, Raman spectroscopy, FT-IR-ATR spectroscopy, and GC-MS were conducted on three burnished red potteries-Jeoksaekmaoyeonwa burnished red pottery (Neolithic age red pottery), Dandomaoyeonwan burnished red pottery(Bronze age red pottery) and Jeoksaekmaoyeongajimun burnished red pottery(Bronze age red pottery)-to investigate the components of the red pigments and the binder. After the layers of the primer were separated from the red surface, crystals of red pigment particles and minerals were found on the red surface. Through SEM-EDS, Raman estimates that the red pigment is Among soil pigments with iron oxide(Fe₂O₃) as the main color development source, Red Ocher(Fe₂O₃). A band characteristic of the Urushiol polymer was detected in the FTIR-ATRspectra(4000~600cm^-1), GC-MS analysis confirmed the presence of the benzenemethanol-2-prophenyl, 4-heptylphenol, 1-tetracecanol, heptafluorobutyric texidecane, all of which are the ingredients of the directional structure of the lacquer present in the red layer. Therefore, it seemed that the three burnished red pottery: Jeoksaekmaoyeonwan pottery(Neolithic age burnished red pottery), Dandomaoyeonwan pottery(bronze age burnished red pottery) and the Jeoksaekmaoyeongajimun pottery(bronze age burnished red pottery) made by mixing minerals and Red Ocher(Fe₂O₃), with lacquer.

• Korean Journal of Heritage: History & Science
• /
• v.53 no.4
• /
• pp.170-187
• /
• 2020

Dolmens bearing the burial layout and stone coffin tombs of the late Bronze Age were excavated from Samdeok-ri, Goseong, Gyeonsangnsamdo, and grave items such as red-burnished pottery, arrowheads, and stone swords were also discovered. In the case of the red-burnished pottery that was found, it retains a pigment layer with a thickness of about 50 to 160㎛, but with most of the other items, exfoliation and peeling-off of pigment layers can be observed on the surface. The raw materials of the red-burnished pottery contained moderately sorted minerals such as quartz, feldspar, and hornblende, and partly opaque iron oxide minerals were also identified. In particular, the raw materials of the red-burnished pottery from stone coffin tomb #6 were different from those of the other pottery, containing large amounts of hornblende and feldspar. The pottery's red pigment was identified as hematite and showed similar mineral content of raw materials such as fine grained quartz, feldspar, and hornblende. The firing temperature is estimated to have been approximately 900℃, based on their mineral phase. The possibility exists that the raw materials had been collected from the Samdeok-ri area, because diorite and granite diorite with dominant feldspar and hornblende have been identified within 3km of that area. During the pottery manufacturing process, it is estimated that the pigment was painted on the entire surface of the red-burnished pottery after it had been molded and then finished using the abrasion technique. In other words, the red-burnished pottery was made by the process of vessel forming - semi drying - coloring - polishing. The surface and cross-section of the pottery appears differently depending on the concentration of the pigment and the coloring method used after vessels were formed. Most of the excavated pottery features a distinct boundary between pigment and body fabric. However, in the case of pottery in which fine-grained pigments penetrate the body fabric so that layers cannot be distinguished, there is the possibility that the fine-grained pigment layer was applied at a low concentration or immediately after vessel forming. Many cracks can be seen on the surface pigments in thickly painted pottery items, and in many cases, only a small portion of the pigment layers remain due to surface exfoliation and abrasion in the burial environment. It is reported that pottery items may be more easily damaged by abrasion if coated with pigment and polished, so it is believed that the red-burnished pottery of the Samdeok-ri site suffered from weathering in the burial environment. This damage was more extensive in the potsherds that were scattered outside the tomb.