• Transactions on Electrical and Electronic Materials
• /
• v.14 no.6
• /
• pp.308-311
• /
• 2013

The effect of an electric field on the ac electrical treeing in various epoxy/reactive diluent systems was studied in a needle-plate electrode geometry. Diglycidyl ether of bisphenol A (DGEBA) type epoxy was used as a base resin, and 1,4-butanediol diglycidyl ether (BDGE) or polyglycol (PG) as a reactive diluent was introduced to the DGEBA system, in order to decrease the viscosity of the DGEBA epoxy system. BDGE was acted as a chain extender, and PG acted as a flexibilizer, after the curing reaction. To measure the treeing initiation time and the propagation rate, three constant alternating currents (ac) of 10, 13 and 15 kV/4.2 mm (60 Hz) were applied to the specimen, in a needle-plate electrode arrangement, at $30^{\circ}C$ of insulating oil bath. When 10 kV/4.2 mm (60 Hz) was applied, the treeing initiation time and the propagation rate in the DGEBA system were 356 min and $1.10{\times}10^{-3}$ mm/min, respectively, those in the DGEBA/BDGE system were 150 min and $1.14{\times}10^{-3}$ mm/min, respectively. Those in the DGEBA/PG system were 469 min and $1.05{\times}10^{-3}$ mm/min, respectively. As 15 kV/4.2 mm (60 Hz) was applied, the propagation rate in the DGEBA system was $5.41{\times}10^{-3}$ mm/min, and that in the DGEBA/PG system was $1.42{\times}10^{-3}$ mm/min. These values meant that PG could be used as a reactive diluent in the DGEBA system, without the deterioration of the insulation breakdown property.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.2
• /
• pp.77-80
• /
• 2014

The effect of reactive diluents on the ac electrical treeing in epoxy/nanosilicate systems was studied, in a needle-plate electrode geometry. Diglycidyl ether of bisphenol A (DGEBA) type epoxy was used as a base resin, and layered silicate was used as a nano-sized filler. Polyglycol (PG) or 1,4-butanediol diglycidyl ether (BDGE) was introduced as a reactive diluent to the DGEBA/nanosilicate system, in order to decrease the viscosity of the nanocomposite system. PG acted as a flexibilizer, and BDGE acted as a chain extender, after the curing reaction. To measure the treeing propagation rate, a constant alternating current (ac) of 10 kV/4.2 mm (60 Hz) was applied to the specimen, in a needle-plate electrode arrangement, at $30^{\circ}C$ of insulating oil bath. When 10 kV/4.2 mm (60 Hz) was applied, the treeing propagate rate in the DGEBA system was $1.10{\times}10^{-3}$ mm/min, and that in the DGEBA/PG system was $1.05{\times}10^{-3}$ mm/min. As 1.5 wt% of nanosilicate was added to the DGEGA/PG system, the propagation rate was $0.33{\times}10^{-3}$ mm/min. This meant that the nano-sized layered silicates would act as good barriers to treeing propagation. The effect of chlorine content was also studied, and it was found that chlorine had a bad effect on the electrical insulation property of the epoxy system.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.2
• /
• pp.87-90
• /
• 2014

The effects of electric field frequency on the ac electrical treeing phenomena in an epoxy/reactive diluent/layered silicate (1.5 wt%) were carried out, in needle-plate electrode arrangement. A layered silicate was exfoliated in an epoxy base resin, by using our ac electric field apparatus. To measure the treeing propagation rate, constant alternating current (AC) of 10 kV with three different electric field frequencies (60, 500 and 1,000 Hz) was applied to the specimen, in needle-plate electrode arrangement, at $30^{\circ}C$ of insulating oil bath. As the electric field frequency increased, the treeing propagation rate increased. At 500 Hz, the treeing propagation rate of the epoxy/PG/nanosilicate system was $0.41{\times}10^{-3}$ mm/min, which was 3.4 times slower than that of the epoxy/PG system. The electrical treeing morphology was dense bush type at 60 Hz; however, as the frequency increased, the bush type was changed to branch type, having few branches, with very slow propagation rate.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.6
• /
• pp.317-320
• /
• 2013

Partial discharge resistance for the epoxy systems with two diluents was investigated in the rod-plane electrodes arrangement, and the effect of electric frequency on the partial discharge resistance was also studied. Diglycidyl ether of bisphenol A (DGEBA) type epoxy was used as a base resin, and 1,4-butanediol diglycidyl ether (BDGE) or polyglycol (PG) as a reactive diluent was introduced to the DGEBA system, in order to decrease the viscosity of the DGEBA epoxy system. BDGE was acted as a chain extender, and PG acted as a flexibilizer, after the curing reaction. To measure the partial discharge resistance, 5 kV alternating current (ac) with three different frequencies (60, 500 and 1,000 Hz) was applied to the specimen in a rod-plane electrode arrangement, at $30^{\circ}C$. PG had a good effect, while BDGE had a bad effect on the partial discharge resistance of the DGEBA system, regardless of the electric frequency.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.12 no.1
• /
• pp.69-79
• /
• 1994

For the vehicle of UV ink formulated with prepolymer and/or reactive diluent, according to change photoinitiator concentration, we measured viscoelasticity of films of bisphenol A diacrylate cured by UV irrdiation, investigated dynamic characteristics and structural changes.

• Journal of Adhesion and Interface
• /
• v.17 no.2
• /
• pp.67-71
• /
• 2016

In this study, low-viscosity polyurethane hot-melt were synthesized with polyether polyol / polyester polyol, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), 2-butanone oxime (MEKO) to improve the properties and peel strength. The properties of the synthesized low-viscosity polyurethane hot-melt was evaluated through FT-IR, viscosity meter and UTM. When the content of the reactive diluent increases and the NCO-blocked prepolymer decreases, the viscosity of low-viscosity polyurethane hot-melt adhesive was increased. When the ratio of OH-terminated oligomer, NCO-blocked prepolymer and content of reactive diluent is 1 : 0.5 : 0.5, low-viscosity polyurethane hot-melt showed 1.1 kgf/cm peel strength.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.4
• /
• pp.199-202
• /
• 2013

In order to study the effect of reactive diluents on the electrical insulation breakdown strength and mechanical properties of, a polyglycol and an aliphatic epoxy were individually introduced to an epoxy system. Reactive diluents were used in order to decrease the viscosity of the epoxy system; polyglycol acted as a flexibilizer and 1,4-butanediol diglycidyl ether (BDGE) acted as an aliphatic epoxy, which then acted as a chain extender after curing reaction. The ac electrical breakdown strength was estimated in sphere-to-sphere electrodes and the electrical breakdown strength was estimated by Weibull statistical analysis. The scale parameters of the electrical breakdown strengths for the epoxy resin, epoxy-polyglycol, and epoxy-BDGE were 45.0, 46.2, and 45.1 kV/mm, respectively. The flexural and tensile strengths for epoxy-BDGE were lower than those of the epoxy resin and those for epoxy-polyglycol were lower than those of the epoxy resin.

• Applied Chemistry for Engineering
• /
• v.5 no.6
• /
• pp.1030-1035
• /
• 1994

Curing behavior and glass transition temperatures of epoxy resins into which reactive diluents were added to control processability were investigated. Heat of cure generated of the epoxy resin was reduced with butyl glycidyl ether(BGE) and phenyl glycidyl ether(PGE) contents. $T_g$ of the resin was decreased with the amount of reactive diluents and it was attributed to increased molecular weight between crosslink points. Cure kinetics of the resins was studied employing autocatalytic reaction model and found that reaction constants decreased as the contents of reactive diluent was increased.

• Polymer(Korea)
• /
• v.37 no.1
• /
• pp.121-126
• /
• 2013

UV-curable high refractive index di-functional epoxy acrylate, 4,4'-thiodibenzenethiol diglycidyl ether diacrylate, was synthesized from acrylic acid and 4,4'-thiodibenzenethiol diglycidyl ether that was obtained by reacting 4,4'-thiodibenzenethiol and epichlorohydrin using a direct method (Taffy process). Its chemical structure was identified by $^1H$ NMR and FTIR. After its dilution with a reactive diluent, 2-phenoxythiol ethyl acrylate as 5, 10, 15, 20, and 30 wt% content, the relationship between their viscosity and refractive index was investigated. Their degree of cure decreased with increasing the amount of reactive diluent, and the refractive index of UV-cured film increased with increasing the degree of cure.

• Journal of Powder Materials
• /
• v.10 no.5
• /
• pp.344-347
• /
• 2003

Pure tantalum powder has been produced by combining Na as a reducing agent, $K_2$TaF$_{7}$ as feed material, KCl and KF as a diluent in a stainless steel (SUS) bomb, using the method of metallothermic reduction. And we examined various types of after-treatment that affect the high purification of powder. A significant amount of impurities contained in recovered powder was removed in various conditions of acid washing. In particular, 20% (HCl + HNO$_3$) was effective in removing heavy metal impurities such as Fe, Cr and Ni, 8% H$_2$SO$_4$ + 8% $Al_2$(SO$_4$)$_3$ in removing fluorides such as K and F from non-reactive feed material, and 2% $H_2O$$_2$ + 1 % HF in removing oxides that formed during reaction. Significant amounts of oxygen and part of light metal impurities could be removed through deoxidation and heat treatment process. On the other hand, because it is difficult to remove completely heavy metal impurities such as Fe, Cr, and Ni through acid washing or heat treatment process if their contents are too high, it is considered desirable to inhibit these impurities from being mixed during the reduction process as much as possible.