The role of excess Pb about the crystallization behavior and electrical properties in b(Zr$\sub$0.52/Ti$\sub$0.48/)O3(PZT) thin films has not been precisely defined. In this work, the effect of excess Pb content on the ferroelectric properties of these films was investigated. To analyze the effect, PZT films containing various amounts of excess Pb were Prepared. PZT thin films were deposited on the Pt/Ti bottom electrode by rf magnetron sputtering method and then they were crystallized by rapid thermal annealing (RTA). The experiment showed that all PZT films indicated perovskite polycrystalline structure with preferred orientation (111) and no pyrochlore phase was observed. As higher excess Pb was included, the films showed that value of leakage current shift from 2.03${\times}$10$\^$-6/ to 6.63 ${\times}$ 10$\^$-8/A/cm$^2$ at 100kV/cm, and value of remanent polarization shift from 8.587 ${\mu}$C /cm$^2$ to 4.256 ${\mu}$C/ cm$^2$. Electrical properties of PZT thin film affected by Pb excess content of target were explained to be caused of defect among space charges and defect grain boundaries.

• 한국결정성장학회지
• /
• 제19권2호
• /
• pp.70-74
• /
• 2009

Sol-gel 법으로 제조한 $Pb(Sc_{1/2}Nb_{1/2})O_3$(이하 PSN) sol을 이용하여 스핀 코팅법으로 Pt(111)/Ti/$SiO_2$/Si 기판위에 제조한 박막의 제조 공정에 따른 영향을 연구하였다. Pt 기판위에 PSN sol을 증착, 건조한 후에 $370^{\circ}C$에서 5분간 열처리를 행한 후 $10^{\circ}C/sec$의 급속 가열로 $600{\sim}700^{\circ}C$에서 최종 열처리한 경우에 박막은 (111)면으로 우선 배향하는 것으로 나타났다. 그러나 중간 열처리를 거치지 않고, 급속가열에 의한 최종 열처리만을 행한 경우에는 (100)면으로 우선 배향하는 것으로 나타났다. 한편, 중간 열처리 후 $4^{\circ}C/min$의 승온속도로 관상로에서 최종 열처리를 행한 경우에는 (111)면과 (100)면이 동시에 나타나는 것으로 나타났다. 동일한 조건하에서 박막의 두께는 모두 300로 중간 열처리 공정이 어떠한 영향도 미치지 않는 것으로 나타났다.