• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.182-185
• /
• 2003

Etching characteristics of (PB,Sr)$TiO_3$(PST) thin films Were investigated using inductively coupled chlorine based plasma system as functions of gas mixing ratio, RF power and DC bias voltage. It was found that increasing of Ar content in gas mixture' lead to sufficient increasing of etch rate and selectivity of PST to Pt. The maximum etch rate of PST film is 562 ${\AA}$/min and the selectivity of PST film to Pt is 0.8 at $Cl_2/(Cl_2+Ar)$ of 20 %. It was proposed that sputter etching is dominant etching mechanism while the contribution of chemical reaction is relatively low due to low volatility of etching products.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.3
• /
• pp.144-148
• /
• 2012

In this work, we investigated to the etching characteristics of $TiO_2$ thin film and the selectivity using the inductively coupled plasma system. The etch rate and the selectivity were obtained with various gas mixing ratios. The maximum etch rate of $TiO_2$ thin film was 61.6 nm/min. The selectivity of $TiO_2$ to TiN, and $TiO_2$ to $SiO_2$ were obtained as 2.13 and 1.39, respectively. The etching process conditions are 400 W for RF power, -150 V for DC-bias voltage, 2 Pa for the process pressure, and $40^{\circ}C$ for substrate temperature. The chemical states of the etched surfaces were investigated with X-ray photoelectron spectroscopy (XPS). Its analysis showed that the etching mechanism was based on the physical and chemical pathways in the ion-assisted physical reaction.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.314-318
• /
• 2002

The etching behaviors of the ferroelectric $YMnO_3$ thin films were studied by an inductively coupled plasma (ICP). The maximum etch rate of $YMnO_3$ thin film is 300 ${\AA}/min$ at Ar/$Cl_2$of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of $30^{\circ}C$. Addition of $CF_4$ gas decrease the etch rate of $YMnO_3$ thin film. From the results of XPS analysis, nonvolatile $YF_x$ compounds were found on the surface of $YMnO_3$ thin film which is etched in Ar/$Cl_2$/CF$_4$plasma. The etch profile of YMnO$_3$film is improved by addition of $CF_4$ gas into the Ar/$Cl_2$ plasma. These results suggest that YF$_{x}$ compound acts as a sidewall passivants which reduce the sticking coefficient of chlorine on $YMnO_3$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.232-232
• /
• 2010

정보화 산업의 발달은 DRAM, flash memory 등을 포함한 기존의 반도체 메모리 소자를 대체할 수 있는 차세대 메모리 소자에 대한 개발을 요구하고 있다. 특히 magnetic random access memory (MRAM)는 SRAM과 대등한 고속화 그리고 DRAM 보다 높은 기록 밀도가 가능하고 낮은 동작 전압과 소비전력 때문에 대표적인 차세대 비휘발성 메모리로 주목받고 있다. 또한 MRAM소자의 고집적화를 위해서 우수한 프로파일을 갖고 재증착이 없는 나노미터 크기의 magnetic tunnel junction (MTJ) stack의 건식 식각에 대한 연구가 선행되어야 한다. 본 연구에서는 고밀도 반응성 이온 식각법(Inductively coupled plasma reactive ion etching; ICPRIE)을 이용하여 재증착이 없이 우수한 식각 profile을 갖는 CoFeB과 IrMn 박막을 형성하고자 하였다. Photoresist(PR) 및 Ti 박막의 두 가지 마스크를 이용하여 HBr/Ar, HBr/$O_2$/Ar 식각 가스들의 농도를 변화시키면서 CoFeB과 IrMn 박막의 식각 특성들이 조사되었다. 자성 박막과 동일한 조건에 대하여 hard mask로서 Ti가 식각되었다. 좋은 조건을 얻기 위해 HBr/Ar 식각 가스를 이용 식각할 때 pressure, bias voltage, rf power를 변화시켰고 식각조건에서 Ti 하드마스크에 대한 자성 박막들의 selectivity를 조사하고 식각 profile을 관찰하였다. 식각 속도를 구하기 위해 alpha step(Tencor P-1)이 사용되었고 또한 field emission scanning electron microscopy(FESEM)를 이용하여 식각 profile을 관찰함으로써 최적의 식각 가스와 식각 조건을 찾고자 하였다.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.26 no.7
• /
• pp.675-678
• /
• 2015

In this paper, we proposed a multi-function conversion block for microwave receiver. The proposed multi-function conversion block is composed of a broadband voltage controlled oscillator and a dual-mode mixer. Depending on whether the bias voltage is supplied, the first IF(Intermediate Frequency) output frequency(4,595 MHz/6,045 MHz) needed in microwave receiver is converted to 720 MHz and the another IF output frequency(720 MHz) for receiving Ku-band has the multi-functional operations of the dual mode that are bypass and attenuation without frequency conversion. Implementation and measurement results show that each intermediate frequency has conversion loss characteristic according to the LO power. The LO power conversion loss of 4,595 MHz at the LO levels from 2 dBm to 4 dBm is 13 dB, another of 6,035 MHz is 12 dB and the other of 720 MHz is 7.0 dB.

• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.754-762
• /
• 1995

Strontium titanate(SrTiO$_3$) thin film was prepared on Si substrates by RF magnetron sputtering for a high capacitance density required for the next generation of LSTs. The optimum deposition conditions for SrTiO$_3$thin film were investigated by controlling the deposition parameters. The crystallinity of films and the interface reactions between SrTO$_3$film and Si substrate were characterized by XRD and AES respectively. High quality films were obtained by using the mixed gas of Ar and $O_2$for sputtering. The films were deposited at various bias voltages to obtain the optimum conditions for a high quality file. The best crystallinity was obtained at film thickness of 300nm with the sputtering gas of Ar+20% $O_2$and the bias voltage of 100V. The barrier layer of Pt(100nm)/Ti(50nm) was very effective in avoiding the formation of SiO$_2$layer at the interface between SrTiO$_3$film and Si substrate. The capacitor with Au/SrTiO$_3$/Pt/Ti/SiO$_2$/Si structure was prepared to measure the electric and the dielectric properties. The highest capacitance and the lowest leakage current density were obtained by annealing at $600^{\circ}C$ for 2hrs. The typical specific capacitance was 6.4fF/$\textrm{cm}^2$, the relative dielectric constant was 217, and the leakage current density was about 2.0$\times$10$^{-8}$ A/$\textrm{cm}^2$ at the SrTiO$_3$film with the thickness of 300nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.104-104
• /
• 2009

Critical dimensions has rapidly shrunk to increase the degree of integration and to reduce the power consumption. However, it is accompanied with several problems like direct tunneling through the gate insulator layer and the low conductivity characteristic of poly-silicon. To cover these faults, the study of new materials is urgently needed. Recently, high dielectric materials like $Al_2O_3$, $ZrO_2$ and $HfO_2$ are being studied for equivalent oxide thickness (EOT). However, poly-silicon gate is not compatible with high-k materials for gate-insulator. To integrate high-k gate dielectric materials in nano-scale devices, metal gate electrodes are expected to be used in the future. Currently, metal gate electrode materials like TiN, TaN, and WN are being widely studied for next-generation nano-scale devices. The TaN gate electrode for metal/high-k gate stack is compatible with high-k materials. According to this trend, the study about dry etching technology of the TaN film is needed. In this study, we investigated the etch mechanism of the TaN thin film in an inductively coupled plasma (ICP) system with $O_2/BCl_3/Ar$ gas chemistry. The etch rates and selectivities of TaN thin films were investigated in terms of the gas mixing ratio, the RF power, the DC-bias voltage, and the process pressure. The characteristics of the plasma were estimated using optical emission spectroscopy (OES). The surface reactions after etching were investigated using X-ray photoelectron spectroscopy (XPS) and auger electron spectroscopy (AES).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.10
• /
• pp.785-791
• /
• 2001

High dielectric (Ba, Sr) TiO$_3$ thin films were etched in an inductively coupled plasma (ICP) as a function of Cl$_2$/Ar mixing ration. Under Cl$_2$(20)/Ar(80), the maximum etch rate of the BST films was 400 $\AA$/mim and selectivities of BST to Pt and PR were obtained 0.4 and 0.2, respectively. Etching products were redeposited on the surface of BST and resulted in varying the nature of crystallinity. Therefore, we investigated the etched surface of BST by x-ray photoelectron spectroscopy (XPS) atomic force microscopy (AFM) and x-ray diffraction (XRD). From the result of XPS analysis, we found that residues of Ba-Cl and Ti-Cl bonds remained on the surface of the etched BST for high boiling point. The morphology of the etched surfact was analyzed by AFM. A smoothsurface(roughness ~2.8nm) ws observed under Cl$_2$(20)/Ar(80), rf power of 600 W, dc bias voltage of -250 V and pressure of 10 mTorr. This changed the nature of the crystallinity of BST. From the result of XRD analysis, the crystallinities of the etched BST film under Ar only and Cl$_2$(20)/Ar(80) were maintained as similar to as-deposited BST. However, intensity of BST(100) orientation under Cl$_2$ only plasma was abruptly decreased. This indicated that CI compounds were redeposited on the etched BST surface and resulted in changed of the crystallinity of BST during the etch process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.93-98
• /
• 2001

YMnO$_3$ films are excellent gate dielectric materials of ferroelectric random access memories (FRAMs) with MFSFET (metal -ferroelectric-semiconductor field effect transistor) structure because YMnO$_3$ films can be deposited directly on Si substrate and have a relatively low permittivity. Although the patterning of YMnO$_3$ thin films is the requisite for the fabrication of FRAMs, the etch mechanism of YMnO$_3$ thin films has not been reported. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ film is 285$\AA$/min under Cl$_2$/(Cl$_2$+Ar) of 1.0, RF power of 600 W, dc-bias voltage of -200V, chamber pressure of 15 mTorr and substrate temperature of $25^{\circ}C$. The selectivities of YMnO$_3$ over CeO$_2$ and $Y_2$O$_3$ are 2.85, 1.72, respectively. The selectivities of YMnO$_3$ over PR and Pt are quite low. Chemical reaction in surface of the etched YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy (XPS) surface of the selected YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy(XPS) and secondary ion mass spectrometry (SIMS). The etch profile was also investigated by scaning electron microscopy(SEM)

• Proceedings of the IEEK Conference
• /
• 2003.07b
• /
• pp.771-774
• /
• 2003

Passivation Ledge's device is taken possession on one-side to the Emitter in this Paper. contact used in this paper Pt as Passivation Ledge of device to use Schottky Diode which has leitmotif, It is accomplished Current Modulation that we wish to do purpose using this device. Space Charge acts as single device which is becoming Passivation to know this phenomenon. This device becomes floating as well as Punched-through. V$_{L}$ (Voltage for Ledge) = - 0.5V ~ 0.5V variable values , PD(Partially Depleted ; Λ＞0), as seeing FD(Fully Depleted ; A = 0) maximum electric current gains and Gummel Plot of I-V characteristics (V$_{L}$ = 0.1/ V$_{L}$ = -0.1 ). Becomming Degradation under more than V$_{L}$ = 0.1 , less than V$_{L}$ =-0.05 and Maximum Gain(=98.617076 A/A) value in the condition V$_{L}$ = 0.1. A Change of Modulation is electric current gains by using Schottky Diode and Extrinsic Base PN Diode of Passivation Ledge to Emitter Depletion Layer in HBT of Gummel-Poon I-V characteristics and the RF wide-band electric current gains change the Modulation of CE(Common-Emitter) amplifier description, and it had accomplished Current Gain Modulation by Ledge Bias that change in high frequency and wide bands. wide bands.s.