• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.98-105
• /
• 2017

In this study, the fiber blending ratio and strain rate effect on the tensile behavior of hybrid fiber reinforced cement composite was evaluated. Hooked steel fiber and polyvinyl alcohol fiber were used for reinforcing fiber. The fiber blending ratio of HSF+PVA were 1.5+0.5, 1.0+1.0 and 0.5+1.5vol.%. As a results, the tensile strength, strain capacity and fracture toughness of the hooked steel fiber reinforced cement composites were improved by the increase of the bond strength of the fiber and the matrix according to increase of strain rate. However, the tensile stress sharply decreased after the peak stress because of the decrease in the number of straightened pull-out fibers by micro cracks in the matrix around hooked steel fiber. On the other hand, PVA fiber showed cut-off fracture at strain rate $10^{-6}/s$ with multiple cracks. However, at the strain rate $10^1/s$, the multiple cracks and strain capacity were decreased because of the pull-out fracture of PVA fiber. The HSF1.5PVA0.5 shown the highest tensile strength because the PVA fiber suppressed the micro cracks in the matrix around the hooked steel fiber and improved the pull-out resistance of hooked steel fiber. Thus, DIF of strain capacity and fracture toughness of HSF1.5PVA were greatly improved. In addition, the synergistic response of fracture toughness was positive because the tensile stress was slowly decreased after the peak stress by improvement of the pull-out resistance of hooked steel fiber at strain rate $10^1/s$.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.271-278
• /
• 2019

The corrosion of reinforcements embedded in concrete causes severe deterioration in reinforced concrete structures. As a countermeasure, epoxy coated reinforcements are used to prevent corrosion of reinforcements. When epoxy coated bars are used, the resistance of corrosion is excellent, but epoxy coating on the bars have a disadvantage of reduction in bond capacity comparing to that of normal bars. Therefore, it is necessary to confirm the bond performance of epoxy coated reinforcements through experimental and analytical methods. Bond behaviors of epoxy coated bars for various diameters of 13 and 19mm and thicknesses of cover concrete of 3 types(ratio of cover to bar diameter) are examined. As the diameters of the epoxy coated bars increase, the difference of bond strength between epoxy coated and uncoated bars also increases and damage patterns showed pull out failure. In addition, finite element analysis was performed based on the bond-slip relationship obtained by direct pullout test and compared with the flexural test results. It is considered that flexural member test is more useful than pullout test for simulating the behavior of actual structure.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.16 no.1
• /
• pp.25-50
• /
• 2014

In order to identify a load transfer mechanism of ground anchors, the behavior of multi load transfer ground anchor systems was investigated and compared with those of compression type anchors and tension type anchors. Large scale model tests were performed and stress-strain relationships were obtained. The load transfer mechanism of ground anchors was also investigated in the field tests. Finally, numerical analyses to predict the load-displacement relationships of anchors were conducted. It is concluded that the load transfer characteristics of MLT anchors are mechanically much more superior in the pull-out resistance effect than those of existing compression and tension type anchors. From the results of research work, we could suggest that the max pull-out capacity of anchor capacity to each the soil condition. Also, the MLT anchors can be used to achieve both structural enhancement and economic construction in earth retaining or supporting structures.

• Geotechnical Engineering
• /
• v.10 no.4
• /
• pp.67-82
• /
• 1994

In this study, a reinforced clay model based on the limit equilibrium of forces under direct shear was proposed to predict shear strength increase in clays induced by the steel inclusion. The model accounted for the effects of orientation of inclusion, length, bonding stress between clay and indclusion and passive soil resistance 1 induced by the inclusion movement, on the behavior of reinforced clays. In order to compare with the theoretical predictions, direct shear tests were performed using a direct shear apparatus formed of an open shear box. Also pull-out tests were conducted to determine the bonding stress between the inclusion and clay. From the experimental results, the increase or decrease in shear strength of reinforced clay samples was found to depend on the orientation of inclusionas well as water content of clay samples. From the comparison of theoretical predictions and experimental results, it was found that the theore tical model predicted reasonably well the influence of orientation of the inclusion as well as passive soil resistance induced by the inclusion movement on the mechanical behavior of reinforced clays.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.9 no.2
• /
• pp.107-114
• /
• 1989

Model pile pull-out tests have been executed to investigate the characteristics of the critical relative displacement at which the critical pile skin resistance is mobilized. Test result shows that the critical relative displacement is neither constant nor pile size dependent, but it is the most closely related with the magnitude of the critical skin resistance. The empirical relationship between the two quantities has been established. Behavior of centrifuge physical models of skin-resistance-related problems has been investigated on a quantitative basis by a computational method. A pile downdrag problem has been employed as an example of the skin-resistance-related problems. A simple transfer function type method has been developed for the analysis of the downdrag. It is concluded from the analysis that centrifuge physical modeling of skin-resistance-related problems may lead to an erroneous result on an unconservative side, as may have been expected due to the violation of the similarity rule by the quantity of the critical relative displacement.

• The Journal of Korean Academy of Prosthodontics
• /
• v.32 no.3
• /
• pp.411-430
• /
• 1994

The denture may be fractured accidentally by an impact while outside the mouth, or may be cracked or broken while in service in the mouth. The latter is generally a fatigue failure caused by repeated flexure over a period of time. This investigation compared the flexural fatigue resistance, the impact force and the transverse strength of two denture base materials with and without the grid strengthener, the T300, the T800 and the Kevlar fiber to evaluate the fracture resistance. The distribution and behavior of fibers across fracture lines were examined by Hi-Scope Compact Microvision System. Through analyses of the data from this study, the following conclusions were obtained. 1. The flexural fatigue resistance, impact strength and transverse strength of high impact strength resin were higher than those of conventional heat polymerizing resin, but statistically there was no significant difference(p>0.05). 2. All specimens with and without the grid strengthener did not show significant differences in the flexural fatigue, the impact and the transverse strength test(p>0.05). 3. All specimens reinforced with the T300, the T800 and the Kevlar fiber showed significant increase of the fatigue resistance and the impact force(p<0.05). 4. All specimens reinforced with the T800 and the Kevlar fiber showed significant increase of the transverse strength(p<0.05). 5. All specimens reinforced with the T300, the T800 and the Kevlar fiber exhibited greenstick fractures. The fibers tended to remain enveloped in the resin, resisting pull-out.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.2 s.173
• /
• pp.438-448
• /
• 2000

Mechanical press joining technique has been used in sheet metal joining processes because of its simple process and possibility of joining dissimiliar metals, such as steel and aluminum. The static and cyclic behavior of single overlap AI-alloy and steel(SPCC) joints has been investigate. Relationships were developed to estimate the strength of the joint taking into consideration base metal strength properties and the geometry of the joint. Fatigue test results have shown that fatigue resistance of the SPCC mechanical press joints is almost equal to that of the spot weld at the life of $10^6$ cycles. Also, the dissimilar material jointed specimen with upper SPCC plate and button diameter corresponding to the nugget diameter of the spot welded specimen has almost same strength as the same material jointed specimen and as the spot welded specimen.

• Journal of the Korean Geotechnical Society
• /
• v.33 no.12
• /
• pp.107-113
• /
• 2017

Shear Connector should be used to fix the PHC pile with extension wall in order to utilize PHC-W retaining wall as permanent wall. The pullout behaviours on shear connectors anchored into PHC-W pile were observed as two modes. The first type behaviour showed that after reaching the maximum pullout resistance, the anchorage was broken and shear connector was pulled out abruptly. The second type behaviour showed that even after arriving the maximum pullout resistance, the anchorage was not destroyed and there was a progressive increase in pullout displacement. The maximum pullout resistance of the steel anchor shear connector is larger than that of deformed bar shear connector. The larger the diameter and the longer the embedment length of shear connector, the higher the maximum pullout resistance would be. The pullout displacements corresponding to the maximum pullout resistance of the shear connector showed various ranges regardless of the materials, the diameters and the anchoring lengths. A-D20 shear connectors showed a pull-out displacement of about 8~10 mm. A-D16, D-D19 and D-D16 shear connectors exhibited a pulling displacement of about 14~20 mm, but a pulling displacement of about 6~10 mm when the anchoring lengths were 50 and 80 mm.

• Journal of the Korea Concrete Institute
• /
• v.24 no.1
• /
• pp.79-86
• /
• 2012

Though steel reinforcing bars are the most widely used tensile reinforcement, corrosion problems are encountered due to the exposure to aggressive environments. As an alternative material to steel, the fiber reinforced polymers have been used as reinforcement in concrete structures. However, bond strength of FRP rebar is relatively low compared to steel rebar. It has been reported that fibers in matrix can resist crack growth, propagation and finally result in an increase of toughness. In this study, high-strength concrete reinforced with structural fibers was produced to enhance interfacial bond behavior between FRP rebar and concrete matrix. The interfacial bond-behaviors were investigated from a direct pullout test. The test variables were surface conditions of GFRP bars and fiber types. Total of 54 pullout specimens with three different types of bars were cast for bond strength tests. The bond strength-slip responses and resistance of the bond failure were evaluated. The test results showed that the bond strength and toughness increased according to the increased fiber volume.

• The Journal of Engineering Geology
• /
• v.27 no.1
• /
• pp.41-49
• /
• 2017

In this study, we tried to confirm the influence range in the ground due to Bulbed, Reinforcement change and ground conditions change through numerical analysis. By checking the increase width of the reinforcement effect accompanying the increase of Bulbed, grasping the trend accompanying the change of the ground conditions and deciding soil nail Reinforcement and Bulbed, so that economical construction will be carried out It can be judged that it can be utilized as basic material. In this paper, we analyzed the Displacement due to positional load of reinforcement by utilizing MIDAS GTS NX which is a universal numerical analysis program. In addition, it is necessary to ensure the diameter star economy of Bulbed size and Reinforcement by comparing / analyzing whether the Bulbed relaxation region of Reinforcement represents arbitrary characteristics in the ground in Sandy soil, Weathered granite soil ground due to soil nail pullout load Numerical analysis was conducted to select criteria that can be done.