• Electrical & Electronic Materials
• /
• v.9 no.7
• /
• pp.668-673
• /
• 1996

In this paper, (P $b_{1-x}$ L $a_{x}$)(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ (X=0-13[at%]) thin film were prepared by the Sol-Gel method, Multiple PLZT thin films were spin-coated on the Pt/Ti/ $SiO_{2}$Si substrate. The electrical properties of the films were investigated for varying the annealing temperature. In the PLZT(11/52/48) specimens, the dielectric ocnstant of 1236 and the polarization reversal time of 460[nm] were obtained and the breakdown of the film did not occur up to 1*10$^{10}$ cycles at the voltage of 7[V] by the bipolar acceleration. The remanent polarization and coercive field decreased with increasing the content of La in the range of 0-13[at%] and thin film of the PLZT(11/52/48) showed the value of 2.56[.mu.C/c $m^{2}$] and 21.1[kV/cm], respectively.ly.y.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.191-191
• /
• 2009

$Bi_4Ti_3O_{12}$ (BiT) thin films were well developed on the Pt/Ti/$SiO_2/Si$ substrate by a metal organic decomposition (MOD) method. Oxygen was effective on the crystallization of the BiT thin films during a rapid thermal annealing process. The electrical properties of the BiT films dependant on the oxygen partial pressure were investigated. No crystalline phase was observed for the BiT film annealed at $700^{\circ}C$ under oxygen free atmosphere. However, its crystallinity was significantly evolutionned with increasing oxygen partial pressure. In addition, its dielectric and piezoelectric properties were enhanced with increasing oxygen partial pressure to 10 torr. Especially, the BiT film, annealed at $700^{\circ}C$ and 10 torr oxygen pressure, showed good dielectric properties: dielectric constant of 51 and dielectric loss of 0.2 % at 100 kHz. Its leakage current and piezoelectric constant ($d_{33}$) was also considerably improved, being as 0.62 nA/$cm^2$ at 1 V and approximately 51 pm/V, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.4
• /
• pp.290-296
• /
• 2009

$Bi_{4}Ti_{3}O_{12}$ (BiT) thin films were grown on the Pt/Ti/$SiO_2$/si substrate using a metal organic decomposition (MOD) method. Effects of oxygen annealing on the structural properties and dielectric properties of the BiT thin films were investigated. The BiT films were well developed when rapid thermal annealed at $>500^{\circ}C$ in oxygen ambient. For the film annealed at $700^{\circ}C$, no crystalline phase was observed under oxygen free annealing atmosphere while its crystallinity was significantly enhanced as the oxygen pressure increased. The BiT film also exhibited a smooth surface with defect free grains. A high dielectric constant and a low dielectric loss were achieved satisfactory in the frequency range from 75 kHz to 1 MHz. Especially, the BiT film, annealed at $700^{\circ}C$ and 10 torr oxygen pressure, showed good dielectric properties: dielectric constant of 51 and dielectric loss of 0.2 % at 100 kHz. Its leakage current was also considerably improved, being as $0.62\;nA/cm^2$ at 1 V. Therefore, it is considered that the oxygen annealing has effects on an enhancement of crystallinity and dielectric properties of the BiT films.

• Applied Chemistry for Engineering
• /
• v.17 no.5
• /
• pp.471-475
• /
• 2006

$VO_x$ thin films with the thickness of 450 nm were prepared on a $Pt/Ti/SiO_{2}/Si$ substrate at room temperature by a reactive radio frequency (rf) magnetron sputtering method. The deposition rates of $VO_x$ thin films were investigated as a function of $O_{2}$ concentration and rf power. As the $O_{2}$ concentration in a $O_{2}/Ar$ mixture increased, the deposition rate decreased. However, the deposition rate increased with increasing rf power. The deposited $VO_x$ thin films were annealed at $450^{\circ}C$ for 2, 4, and 6 h in $O_{2}$ and $N_{2}$ ambient. After annealing, the phase changes of $VO_x$ thin films were investigated using X-ray diffraction analysis. The plane and cross-sectional views of $VO_x$ thin films before and after annealing were observed by field emission scanning electron microscopy. The metal-insulator transition (MIT) properties of $VO_x$ thin films were measured using current-voltage measurement. The excellent MIT properties were observed in $VO_x$ thin films annealed in $O_{2}$ ambient.

• Korean Journal of Materials Research
• /
• v.11 no.11
• /
• pp.960-964
• /
• 2001

$Bi_{3.99}Ti_{2.97}V_{0.03}O_{12}$ (BTV) thin films with 3 mol% vanadium doping were Prepared on $Pt/Ti/SiO_2/Si$ substrate by sol-gel method. X-ray diffraction analysis indicated that single-phase layered perovskite were obtained and preferred orientation was not observed. Under the annealing temperature at $600^{\circ}C$, the surface morphology of the BTV thin films had fine-rounded particles and then changed plate-like at $650^{\circ}C$ and $700^{\circ}C$. The remanent polarization $(2P_r)$ and coercive field $(2E_c)$ of $700^{\circ}C$ annealed BTV thin film were 25 $\mu$C/cm$^2$ and 116 kV/cm, respectively. In addition, BTV thin film showed little polarization fatigue during $10_9$ switching cycles. These improved ferroelectric properties were attributed to the increased rattling space and reduced oxygen vacancies by substitution $Ti^{4+}$ ion (68 pm) with smaller $V^{5+}$ ion (59 pm). The dielectric constant and loss were measured 130 and 0.03 at 10 kHz, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.869-873
• /
• 2004

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient, piezoelectric, and a photo refractive properties. In this study, SBN60(x=0.6) thin film was manufactured by ion beam sputtering technique. Using the prepared SBN60 target in $Ar/O_2$ atmosphere as-deposited SBN60 thin film on Pt(100)/$TiO_2/SiO_2/Si$ substrate crystallization and orientation behavior as well as electric properties of SBN60 thin film were examined. SBN60 deposition up to $3000{\AA}$ in thickness, SBN60 thin film was heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation was shown primarily along (001) plane from XRD pattern where working pressure was $4.3{\times}10^{-4}$ torr. The deposited layer was uniform, preferred orientatin and crystallization behavior resulted in the change of $O_2$ ratio was observed. In electric propertie of Pt/SBN60/Pt thin film capacitor remnant polarization (2Pr) value was $10{\mu}C/cm^2$, the coercive filed (Ec) 50 kV/cm, and the dielectric constant 615, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.08a
• /
• pp.85-88
• /
• 2003

$Sr_xBa_{1-x}Nb_2O_6$(SBN, $025{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in Ar/$O_2$ atmosphere. SBN30 thin film of 500 ${\AA}$ was pre-deposited as a seed layer on Pt(l00)/$TiO_2$/$SiO_2$/Si substrate followed by SBN60 deposition up to 4500 ${\AA}$ in thickness. SBN60/SBN30 layer was deposited at different Oxygen amount of 0, 8.1, 17, and 31.8 sccm, respectively. The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. The crystal structure and the electric properties depended on the Oxygen amount, heating temperature and was the best at O2 = 8.1 seem, $750^{\circ}C$. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was 13 ${\mu}C/cm^2$, the coercive field (Ec) 75 kV/cm, and the dielectric constant 1492, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.623-626
• /
• 2004

[ $Ba_{0.6}Sr_{0.4}TiO_3$ ] (BST) dielectric thin films doped by Cr were prepared using an alkoxide-based sol-gel method on the Pt/Ti/SiO2/Si substrate. Atomic force microscopy and x-ray diffraction analysis showed that increasing the Cr doping ratio causes increased grain size while the surface remains smooth and crack-free. It was also found that compared with undoped films the increase of Cr content in BST improves the dielectric constant and the leakage-current characteristics. The figure of merit reached the maximum value of 72.3 at the 5 mol % of Cr doping. This composition showed the dielectric constant of 426, the loss factor of 0.0065, tenability of 47.7%, and leakage-current density (at the electric field of 100 kV/cm) of $5.31{\times}10^{-8}A/cm^2$. The results show that the Cr-doped BST thin films are prospective candidates for applications in tunable devices.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.32A no.8
• /
• pp.78-85
• /
• 1995

We fabricated the Pb$_{1-0.28{\alpha}}La_{0.28}TiO_{3}$ (PLT(28)) thin film successfully by using the sol-gel method and characterized it to evaluate its potential for being utilized as the capacitor dielectrics of ULSI DRAMs. In our sol-gel process, the acetates were used as the starting materials. Through the TGA-DTA analysis, we established the excellent fabrication conditions of the sol-gel method for the PLT(28) thin film. We obtained the dense and crack-free PLT(28) thin film of 100% perovskite phase by drying at 350$^{\circ}C$ after each coating and final annealing at 650$^{\circ}C$. Its electrical properties were measured from the planar capacitors fabricated on the Pt/Ti/SiO$_{2}$/Si substrate. By the P-E hysteresis measurement, its paraelectric phase was identified and its dielectric constant and leakage current density were measured as 936 and 1.1${\mu}A/cm^{2}$, respectively. Those electrical values indicate that the PLT(28) thin film is the most successful candidate for the capacitor dielectrics of ULSI DRAMs at the present.

• Proceedings of the KIEE Conference
• /
• 1997.11a
• /
• pp.291-293
• /
• 1997

In this study, Sol-Gel derived $(Ba_{0.7}Sr_{0.3})TiO_3$ thin films were fabricated and investigated. The stock solution was synthesized and spin-coated on Pt/Ti/$SiO_2$/Si substrate at 4000(rpm] and then, annealed at $650{\sim}750[^{\circ}C]$. Crystallization condition, microstructural properties and interfacial structure were observed by XRD, AFM, SEM and TEM. It was found that the BST thin films were completely crystallized at 750[$^{\circ}C$] and showed nano-sized grains. The dielectric constant and loss of the BST thin films were 220, 0.01 at 1[kHz] respectively. Increasing the temperature, the dielectric constant and loss characteristics were not varied widely. At the applied voltage of 1.5[V], the leakage current density was under the $10^{-9}[A/cm^2]$.