The $SiO_2$ membranes for polymer electrolyte membrane fuel cell (PEMFC) are preapared by electrospinning method. It leads to high porosity and surface area of membrane to accommodate the proton conducting materials. The composite membrane was prepared by impregnating of Nafion ionomer into the pores of electrospun $SiO_2$ membranes. The $SiO_2$:heteropolyacid (HPA) nano-particles as a inorganic proton conductor were prepared by microemulsion process and the particles are added to the Nafion ionomer. The characterization of the membranes was confirmed by field emission scanning electron microscope (FE-SEM), thermogravimetry analysis (TGA), and single cell performance test for PEMFC. The Nafion impregnated electrospun $SiO_2$ membrane showed good thermal stability, satisfactory mechanical properties and high proton conductivity. The addition of the $SiO_2$:HPA nano-particle improved proton conductivity of the composite membrane, which allow further extension for operation temperature in low humidity environments. The composite membrane exhibited a promising properties for the application in high temperature PEMFC.

• Membrane Journal
• /
• v.17 no.4
• /
• pp.311-317
• /
• 2007

Proton conducting crosslinked membranes have been prepared by polymer blending, which consist of poly(vinyl alcohol-co-ethylene) (PVA-co-PE) and poly(styrene sulfonic acid-co-maleic acid) (PSSA-co-PMA) at 50 : 50 wt ratio. Two kinds of PSSA-co-PMA copolymer with 3 : 1 and 1 : 1 the molar ratio of PSSA to PMA wereused as a proton conducting source. The ethylene content of PVA-co-PE was also changed as 0, 27 and 44 mol%. The membranes were thermally crosslinked via the esterification reaction between -OH of PVA and -COOH of PMA, as demonstrated by FT-IR spectroscopy (PVA-co-PE)/(PSSA-co-PMA) membranes with 3 : 1 the molar ratio of PSSA to PMA showed higher ion exchange capacity (IEC), lower water uptake and higher proton conductivity than those with 1 : 1 molar ratio. As the PE concentration increased, the IEC values, water uptake and proton conductivities decreased continuously. These properties were elucidated in terms of competitive effect between the concentration of sulfonic acid, hydrophilicity and the crosslinked structure of membranes.

• Journal of the Korean Ceramic Society
• /
• v.42 no.2 s.273
• /
• pp.77-80
• /
• 2005

A series of proton conductive composite membranes based on poly(vinyl alcohol) and phosphosilicate gels powders were successfully prepared. The proton conductivity of these composite was attributed to the phosphosilicate gel, which derived from tetraethoxysilane and phosphoric acid by sol-gel process at a molar ratio of P/Si = 1.5. The proton conductivity increased with increasing both the content of phosphosilicate gel and relative humidity. Temperature dependence of conductivity showed a Vogel-Tamman-Fulcher type behavior, indicating that proton was transferred through a liquidlike phase formed in micropores of phosphosilicate gel. The high conductivity of 0.065 S/cm with a membrane containing 60 wt$\%$ of the gel was obtained at $60^{\circ}C$ at $90\%$ relative humidity.

• Membrane Journal
• /
• v.18 no.3
• /
• pp.234-240
• /
• 2008

This work demonstrates the preparation of proton conducting crosslinked polymer electrolyte membranes by blending polystrene-b-poly(hydroxyethyl acrylate) (PS-b-PHEA) and poly(vinyl alcohol) (PVA) at 1 : 1 wt ratio. The PHEA block of the diblock copolymer was crosslinked with PVA using sulfosuccinic acid (SA) via the esterification reaction between -OH of membrane and -COOH of SA, as confirmed by FT-IR spectroscopy. Ion exchange capacity (IEC) continuously increased from 0.14 to 0.91 meq/g with increasing concentrations of SA, due to the increasing portion of charged groups in the membrane. In contrast, the water uptake increased up to 20.0 wt% of SA concentration above which it decreased monotonically. The membrane also exhibited a maximum proton conductivity of 0.024 S/cm at 20.0 wt% of SA concentration. The maximum behavior of water uptake and proton conductivity is considered to be due to competitive effect between the increase of ionic sites and the crosslinking reaction according to the SA concentration.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.3
• /
• pp.245-250
• /
• 2009

Crosslinked membrane based on sulfonated polyimide was prepared by the introduction of crosslinkable monomer in polymerization process and crosslinking during membrane casting. Crosslinked membranes showed different properties from non-crosslinked membranes. Crosslinking decreased methanol crossover and therefore unit cell using crosslinked membrane showed increased open circuit voltage, 0.81 V, in comparison with unit cell using noncrosslinked membrane, 0.71 V. In addition, water uptake of crosslinked membrane, 40.5%, was lower than that of non-crosslinked membrane, 57.0%, and this resulted in improved dimensional stability. However, proton conductivity of crosslinked membranes showed rather low relative to non-crosslinked membrane due to reduced water uptake.

• Journal of the Korean Electrochemical Society
• /
• v.15 no.1
• /
• pp.35-40
• /
• 2012

The composite membranes using Nafion as matrix and 1-ethyl-3-methylimidazolium tetracyanoborate (EMITCB) as ion-conducting medium in replacement of water were prepared and characterized. The amount of EMITCB in Nafion varied from 30 to 50wt%. The composite membranes are characterized by ion conductivity, thermogravitational analyses (TGA) and small-angle X-ray scattering (SAXS). The composite membranes containing EMITCB of 40wt% showed the maximum ionic conductivity which was ~0.0146 S $cm^{-1}$ at 423.15 K. It is inferred that the decrease in ionic conductivity of all the composite membranes might be due to the decomposition of a tetracyanoboric acid formed in the composite membranes. The results of SAXS indicated that the ionic clusters to conduct proton in the composite membranes were successfully formed. In accordance with the results of ionic conductivity as a function of a reciprocal temperature, SAXS showed a proportional decrease in scattering maximum $q_{max}$ as the amount of EMITCB increases in the composite membranes, which results in the increase in ionomer cluster size. The TGA showed no significant decomposition of the ionic liquid as well as the composite membranes in the range of operating temperature ($120-150^{\circ}C$) of high temperature proton exchange membrane fuel cells (HTPEMFC). As a result, EMITCB is able to play an important role in transferring proton in the composite membranes at elevated temperatures with no external humidification for proton exchange membrane fuel cells.

• Membrane Journal
• /
• v.19 no.4
• /
• pp.291-301
• /
• 2009

Double-layered polymer electrolyte membranes were prepared from two different sulfonated poly(aryl ether sulfone) copolymers by the two-step solution casting method for direct methanol fuel cells (DMFC). Sulfonation degrees were adjusted 10% (SPAES-10) and 50% (SPAES-50) by controlling monomer ratios, and the weight ratios of SPAES-10 copolymer were varied in the range of 5~20% to investigate the effect of thickness of coating layers on the membranes. Proton conducting layers were fabricated from SPAES-50 solutions of N-methyl-2-pyrrolidone (NMP) by a solution casting technique, and coating layers formed on the semiliquid surface of the conducting layer by pouring of SPAES-10-NMP solutions onto. It was found that double-layered polymer electrolyte membrane could significantly reduce the methanol crossover through the membrane and maintain high proton conductivities being comparable to single-layered SPAES-50 membrane. The maximum power density of membrane-electrolyte assembly (MEA) at the condition of $60^{\circ}C$ and 2 M methanol-air was $134.01\;mW/cm^2$ for the membrane prepared in the 5 wt-% of SPAES-10 copolymer, and it was corresponding to the 105.5% of the performance of the commercial Nafion 115 membrane.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2008.05a
• /
• pp.147-150
• /
• 2008

• Proceedings of the Membrane Society of Korea Conference
• /
• 2008.05a
• /
• pp.154-157
• /
• 2008

• Proceedings of the Membrane Society of Korea Conference
• /
• 2003.07a
• /
• pp.139-140
• /
• 2003

No Abstract, See Full Text