• Journal of Powder Materials
• /
• v.5 no.4
• /
• pp.312-318
• /
• 1998

The effect of the mechanical alloying of elemental Mo and Si powders on the combustion densification behavior of MoSi$_2$ was investigated. The ignition temperature of the combustion reaction of the mechanically alloyed powder was measured to be significantly lower than that of the powder mixture prepared by the low energy ball milling process. The densification of the products after the combustion reaction under compressive pressure from the mechanically alloyed powders, however, was found to be poorer than that of the products from the ball milled powder.

• Journal of Powder Materials
• /
• v.9 no.6
• /
• pp.441-448
• /
• 2002

Dispersions of non-soluble ceramic particles in a metallic matrix can enhance the strength and heat resistance of materials. With the advent of mechanical alloying it became possible to put the theoretical concept into practice by incorporating very fine particles in a flirty uniform distribution into often oxidation- and corrosion- resistant metal matrices. e.g. superalloys. The present paper will give an overview about the mechanical alloying technique as a dry, high energy ball milling process for producing composite metal powders with a fine controlled microstructure. The common way is milling of a mixture of metallic and nonmetallic powders (e.g. oxides. carbides, nitrides, borides) in a high energy ball mill. The heavy mechanical deformation during milling causes also fracture of the ceramic particles to be distributed homogeneously by further milling. The mechanisms of the process are described. To obtain a homogeneous distribution of nano-sized dispersoids in a more ductile matrix (e.g. aluminium-or copper based alloys) a reaction milling is suitable. Dispersoid can be formed in a solid state reaction by introducing materials that react with the matrix either during milling or during a subsequent heat treatment. The pre-conditions for obtaining high quality materials, which require a homogeneous distribution of small dis-persoids, are: milling behaviour of the ductile phase (Al, Cu) will be improved by the additives (e.g. graphite), homogeneous introduction of the additives into the granules is possible and the additive reacts with the matrix or an alloying element to form hard particles that are inert with respect to the matrix also at elevated temperatures. The mechanism of the in-situ formation of dispersoids is described using copper-based alloys as an example. A comparison between the in-situ formation of dispersoids (TiC) in the copper matrix and the milling of Cu-TiC mixtures is given with respect to the microstructure and properties, obtained.

• Journal of Powder Materials
• /
• v.27 no.1
• /
• pp.37-43
• /
• 2020

The Fe-22wt.%Cr-6wt.%Al foams were fabricated via the powder alloying process in this study. The structural characteristics, microstructure, and mechanical properties of Fe-Cr-Al foams with different average pore sizes were investigated. Result of the structural analysis shows that the average pore sizes were measured as 474 ㎛ (450 foam) and 1220 ㎛ (1200 foam). Regardless of the pore size, Fe-Cr-Al foams had a Weaire-Phelan bubble structure, and α-ferrite was the major constituent phase. Tensile and compressive tests were conducted with an initial strain rate of 10^-3/s. Tensile yield strengths were 3.4 MPa (450 foam) and 1.4 MPa (1200 foam). Note that the total elongation of 1200 foam was higher than that of 450 foam. Furthermore, their compressive yield strengths were 2.5 MPa (450 foam) and 1.1 MPa (1200 foam), respectively. Different compressive deformation behaviors according to the pore sizes of the Fe-Cr-Al foams were characterized: strain hardening for the 450 foam and constant flow stress after a slight stress drop for the 1200 foam. The effect of structural characteristics on the mechanical properties was also discussed.

• Korean Journal of Materials Research
• /
• v.13 no.1
• /
• pp.24-30
• /
• 2003

The Raney Ni catalyst was fabricated by mechanochemically process(MC process) in the Al-Ni system. Intermetallic compound obtained by mechanical alloying was leached in an alkaline solution. The characteristics of the mechanically alloyed powder and Raney Ni catalyst were analyzed by XRD, ICP-AES and EXAFS. In Al-50wt.%Ni, the metastable intermetallic compound phase close to AlNi phase was obtained by mechanical alloying unlike Al-Ni equilibrium phase diagram. The metastable intermetallic compound was transformed into $Al_3$$Ni_2$phase via the annealing at $750^{\circ}C$. The microstructure of Raney Ni fabricated by MC process was mainly bcc Ni including fcc Ni.

• Journal of Powder Materials
• /
• v.23 no.2
• /
• pp.120-125
• /
• 2016

P-type ternary $Bi_{0.5}Sb_{1.5}Te_3$ alloys are fabricated via mechanical alloying (MA) and spark plasma sintering (SPS). Different ball sizes are used in the MA process, and their effect on the microstructure; hardness, and thermoelectric properties of the p-type BiSbTe alloys are investigated. The phases of milled powders and bulks are identified using an X-ray diffraction technique. The morphology of milled powders and fracture surface of compacted samples are examined using scanning electron microscopy. The morphology, phase, and grain structures of the samples are not altered by the use of different ball sizes in the MA process. Measurements of the thermoelectric (TE) transport properties including the electrical conductivity, Seebeck coefficient, and power factor are measured at temperatures of 300-400 K for samples treated by SPS. The TE properties do not depend on the ball size used in the MA process.

• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.36-43
• /
• 2010

In present work, amorphous TiCuNi powders were fabricated by mechanical alloying process. Amorphization and crystallization behaviors of the TiCuNi powders during high-energy ball milling and subsequent microstructure changes were studied by X-ray diffraction and transmission electron microscope. TEM samples were prepared by the focused ion beam technique. The morphology of powders prepared with different milling times was observed by field-emission scanning electron microscope and optical microscope. The powders developed a fine, layered, homogeneous structure with milling times. The crystallization behavior showed that glass transition, $T_g$, onset crystallization, $T_x$, and super cooled liquid range ${\Delta}T=T_x-T_g$ were 628, 755 and 127K, respectively. The as-prepared amorphous TiCuNi powders were consolidated by spark plasma sintering process. Full densified TiCuNi samples were successfully produced by the spark plasma sintering process. Crystallization of the MA powders happened during sintering at 733K.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1033-1034
• /
• 2006

Metallic compound of ternary Al-B-C system was prepared by mechanical alloying (MA) using Al, boron and graphite powders as starting materials. MA was carried out using Spex 8000 mixer/mill for 50 hours in an argon atmosphere without process control reagent such as methyl alcohol. The MA powders obtained were heat-treated in vacuum at the temperature of 873 and 1273 K for 5 hour. Pure ternary Al-B-C compound was obtained in the chemical content of Al:B:C=55:27:18. The ternary compound obtained in this study has a new phase whose crystal structure is not identified yet.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.164-167
• /
• 2003

The mechanical alloying effect has been studied on the three Cu-based alloy systems with a positive heat of mixing. The extended bcc solid solution has been formed in the Cu-V system and an amorphous phase in the Cu-Ta system. However, it is round that a mixture of nanocrystalline Cu and Mo Is formed in the Cu-Mo system. The neutron diffraction has been employed at a main tool to characterize the detailed amorphization process. The formation of an amorphous phase in Cu-Ta system can be understood by assuming that the smaller Cu atoms preferentially enter into the bcc Ta lattice during ball milling.

• Journal of Powder Materials
• /
• v.24 no.5
• /
• pp.357-363
• /
• 2017

In this study, Bi-Sb-Te thermoelectric materials are produced by mechanical alloying (MA) and spark plasma sintering (SPS). To examine the influence of the milling atmosphere on the microstructure and thermo-electric (TE) properties, a p-type Bi-Sb-Te composite powder is mechanically alloyed in the presence of argon and air atmospheres. The oxygen content increases to 55% when the powder is milled in the air atmosphere, compared with argon. All grains are similar in size and uniformly, distributed in both atmospheric sintered samples. The Seebeck coefficient is higher, while the electrical conductivity is lower in the MA (Air) sample due to a low carrier concentration compared to the MA (Ar) sintered sample. The maximum figure of merit (ZT) is 0.91 and 0.82 at 350 K for the MA (Ar) and MA (Air) sintered samples, respectively. The slight enhancement in the ZT value is due to the decrease in the oxygen content during the MA (Ar) process. Moreover, the combination of mechanical alloying and SPS process shows a higher hardness and density values for the sintered samples.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2005.04a
• /
• pp.21-22
• /
• 2005