• Korean Journal of Materials Research
• /
• v.9 no.8
• /
• pp.837-842
• /
• 1999

The Ta/TaN multilayer structure with repeating layers of a poly-crystalline Ta layer of high ductility and a TaN layer of high hardness is expected to exhibit toughness. This paper reports the results on the hardness and the adhesion strength of Ta/TaN multilayers and compositional gradient Ta/TaN layers deposited on the high speed steel substrate by reactive sputtering as a function of annealing temperature. The TaN film deposited with the $N_2$/Ar ratio of 0.4 in the reactive sputtering process exhibits the highest crystallinity, and the highest hardness and the results of scratch test of the Ta/TaN multilayers. The hardness and adhesion strength of the Ta/TaN multilayers becomes deteriorated with increasing the annealing temperature in the heat treatment right after depositing the layers. Therefore, post-annealing treatments are not desirable in the case of the Ta/TaN multilayers from the standpoint of mechanical properties. Also the hardness of Ta/TaN multilayers increases with decreasing the compositional modulation wavelength, but the adhesion property of the layers is nearly independent of the wavelength. On the other hand, the compositional gradient Ta/TaN film exhibits the highest hardness and the value of scratch test for the post-annealing temperatures of 20$0^{\circ}C$ and 40$0^{\circ}C$, respectively. This tendency of the compositional gradient Ta/TaN films differs from that of the Ta/TaN multilayers.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.17 no.2
• /
• pp.265-270
• /
• 2017

4H-SiC has attracted attention for high-power and high-temperature metal-oxide-semiconductor field-effect transistors (MOSFETs) for industrial and automotive applications. The gate oxide in the 4H-SiC MOS system is important for switching operations. Above $1000^{\circ}C$, thermal oxidation initiates $SiO_2$ layer formation on SiC; this is one advantage of 4H-SiC compared with other wide band-gap materials. However, if post-deposition annealing is not applied, thermally grown $SiO_2$ on 4H-SiC is limited by high oxide charges due to carbon clusters at the $SiC/SiO_2$ interface and near-interface states in $SiO_2$; this can be resolved via low-temperature deposition. In this study, low-temperature $SiO_2$ deposition on a Si substrate was optimized for $SiO_2/4H-SiC$ MOS capacitor fabrication; oxide formation proceeded without the need for post-deposition annealing. The $SiO_2/4H-SiC$ MOS capacitor samples demonstrated stable capacitance-voltage (C-V) characteristics, low voltage hysteresis, and a high breakdown field. Optimization of the treatment process is expected to further decrease the effective oxide charge density.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.29-33
• /
• 2003

Material and electrical properties of copper-based ohmic contacts on n-type 4H-SiC were investigated for the effects of the post-annealing and the metal covering conditions. The ohmic contacts were prepared by sequential sputtering of Cu and Si layers on SiC substrate. The post-annealing treatment was performed using RTP (rapid thermal process) in vacuum and reduction ambient. The specific contact resistivity ($p_{c}$), sheet resistance ($R_{s}$), contact resistance ($R_{c}$), transfer length ($L_{T}$), were calculated from resistance (RT) versus contact spacing (d) measurements obtained from TLM (transmission line method) structure. The best result of the specific contact resistivity was obtained for the sample annealed in the reduction ambient as $p_{c}= 1.0 \times 10^{-6}\Omega \textrm{cm}^2$. The material properties of the copper contacts were also examined by using XRD. The results showed that copper silicide was formed on SiC as a result of intermixing Cu and Si layer.

• Journal of the Korean Vacuum Society
• /
• v.17 no.2
• /
• pp.156-159
• /
• 2008

The electrical characteristic of SiGe-on-SOI (SGOI) wafer with different Ge concentration were evaluated by pseudo-MOSFET. Epitaxial SiGe layers was grown directly on top of SOI with Ge concentrations of 16.2, 29.7, 34.3 and 56.5 at.%. As Ge concentration increased, leakage current increased and threshold voltage shifted from 3 V to 7 V in nMOSFET, from -7 V to -6 V in pMOSFET. The interface states between buried oxide and top of Si was significantly increased by the rapid thermal annealing (RTA) process, and so the electrical characteristic of SGOI wafer degraded. On the other hand, additional post RTA　annealing (PRA) showed that it was effective in decreasing the interface states generated by RTA processes and the electrical characteristic of SGOI wafer enhanced higher than initial state.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.558-561
• /
• 2001

Vanadium oxide ($VO_x$) thin films are very good candidate material for uncooled infrared (IR) detectors due to their high temperature coefficient of resistance (TCR) at room temperature. But, the deposition of $VO_x$ thin films showing good electrical properties is very difficult in micro bolometer fabrication process using sacrificial layer removal because of its low process temperature and thickness of thin films less than $1000{\AA}$. This paper presents a new fabrication process of $VO_x$ thin films having high TCR and low resistance. Through sandwich structure of $VO_{x}(100{\AA})/V(80{\AA})/VO_{x}(500{\AA})$ by sputter method and post-annealing at oxygen ambient, we have achieved high TCR more than $-2%/^{\circ}C$ and low resistance less than $10K\Omega$ at room temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.558-561
• /
• 2001

Vanadium oxide ($VO_{x}$) thin films are very good candidate material for uncooked infrared (IR) detectors due to their high temperature coefficient of resistance (TCR) at room temperature. But, the deposition of $VO_{x}$ thin films showing good electrical properties is very difficult in micro bolometer fabrication process using sacrificial layer removal because of its low process temperature and thickness of thin films less than 1000${\AA}$. This paper presents a new fabrication process of $VO_{x}$ thin films having high TCR and low resistance. Through sandwich structure of $VO_{x}$(100${\AA}$)/V(80${\AA}$)/$VO_{x}$(500${\AA}$) by sputter method and post-annealing at oxygen ambient, we have achieved high TCR more than -2%/$^{\circ}C$ and low resistance less than $10K\Omega$ at room temperature.

• Korean Journal of Materials Research
• /
• v.22 no.1
• /
• pp.24-28
• /
• 2012

$In_2O_3$ films were deposited by RF magnetron sputtering on a glass substrate and then the effect of post deposition annealing in nitrogen atmosphere on the structural, optical and electrical properties of the films was investigated. After deposition, the annealing process was conducted for 30 minutes at 200 and $400^{\circ}C$. XRD pattern analysis showed that the as deposited films were amorphous. When the annealing temperature reached 200-$400^{\circ}C$, the intensities of the $In_2O_3$ (222) major peak increased and the full width at half maximum (FWHM) of the $In_2O_3$ (222) peak decreased due to the crystallization. The films annealed at $400^{\circ}C$ showed a grain size of 28 nm, which was larger than that of the as deposited amorphous films. The optical transmittance in the visible wavelength region also increased, while the electrical sheet resistance decreased. In this study, the films annealed at $400^{\circ}C$ showed the highest optical transmittance of 76% and also showed the lowest sheet resistance of $89{\Omega}/\Box$. The figure of merit reached a maximum of $7.2{\times}10^{-4}{\Omega}^{-1}$ for the films annealed at $400^{\circ}C$. The effect of the annealing on the work-function of $In_2O_3$ films was considered. The work-function obtained from annealed films at $400^{\circ}C$ was 7.0eV. Thus, the annealed $In_2O_3$ films are an alternative to ITO films for use as transparent anodes in OLEDs.

• Korean Journal of Materials Research
• /
• v.9 no.2
• /
• pp.168-172
• /
• 1999

We have studied the formation of Co/Ti bilayer silicide with low resistivity and good thermal stability on the heavily boron doped $\textrm{p}^{+}$-Si region. In this paper, Co/Ti bilayer silicides were fabricated by depositing Co($150\AA$)/Ti($50\AA$) films on the clean $\textrm{p}^{+}$-Si substrates in an E-beam evaporator and performing the two step RTA process (first annealing: 650$50^{\circ}C$/20sec, second annealing: $800^{\circ}C$/20sec) in a $N_2$ambient with the pressure of $\textrm{10}^{-1}$atm. Co/Ti bilayer silicides obtained from our experiments exhibited the low resistivity of about $18\mu\Omega$-cm and the uniform thickness of about $500\AA$ without change of sheet resistance and agglomeration under the long post0annealing time up to $1000^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.03a
• /
• pp.21-21
• /
• 2010

(Ba,Sr)$TiO_3$ (BST) thin film with a perovskite structure has potential for the practical application in various functional devices such as nonvolatile-memory components, capacitor, gate insulator of thin-film transistors, and electro-optic devices for display. Normally, the BST thin films derived from sol-gel and sputtering are amorphous or partially crystalline when processed below $600^{\circ}C$. For the purpose of integrating BST thin film directly into a Si-based read-out integrated circuit (ROIC), it is necessary to process the BST film below $400^{\circ}C$. The microstructural and electrical properties of low-temperature crystallized BST film were studied. The BST thin films have been fabricated at $350^{\circ}C$ by UV-assisted rapidly thermal annealing (RTA). The BST films are in a single perovskite phase and have well-defined electrical properties such as high dielectric constant, low dielectric loss, low leakage current density, and high breakdown voltage. Photoexcitation of the organics contained in the sol-gel-derived films by high-intensity UV irradiation facilitates elimination of the organics and formation of the single-crystalline phase films at low temperatures. The amorphous BST thin film was transformed to a highly (h00)-oriented perovskite structure by high oxygen pressure processing (HOPP) at as low as $350^{\circ}C$. The dielectric properties of BST film were comparable to (or even better than) those of the conventionally processed BST films prepared by sputtering or post-annealing at temperature above $600^{\circ}C$. When external pressure was applied to the well-known contractive BST system during annealing, the nucleation energy barrier was reduced; correspondingly, the crystallization temperature decreased. The UV-assisted RTA and HOPP, as compatible with existing MOS technology, let the BST films be integrated into radio-frequency circuit and mixed-signal integrated circuit below the critical temperature of $400^{\circ}C$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.29.1-29.1
• /
• 2009

Fabrication of good quality P-type GaN remained as a challenge for many years which hindered the III-V nitrides from yielding visible light emitting devices. Firstly Amano et al succeeded in obtaining P-type GaN films using Mg doping and post Low Energy Electron Beam Irradiation (LEEBI) treatment. However only few region of the P-GaN was activated by LEEBI treatment. Later Nakamura et al succeeded in producing good quality P-GaN by thermal annealing method in which the as deposited P-GaN samples were annealed in N2 ambient at temperatures above $600^{\circ}C$. The carrier concentration of N type and P-type GaN differs by one order which have a major effect in AlGaN based deep UV-LED fabrication. So increasing the P-type GaN concentration becomes necessary. In this study we have proposed a novel method of activating P-type GaN by electrochemical potentiostatic method. Hydrogen bond in the Mg-H complexes of the P-type GaN is removed by electrochemical reaction using KOH solution as an electrolyte solution. Full structure LED sample grown by MOCVD serves as anode and platinum electrode serves as cathode. Experiments are performed by varying KOH concentration, process time and applied voltage. Secondary Ion Mass Spectroscopy (SIMS) analysis is performed to determine the hydrogen concentration in the P-GaN sample activated by annealing and electrochemical method. Results suggest that the hydrogen concentration is lesser in P-GaN sample activated by electrochemical method than conventional annealing method. The output power of the LED is also enhanced for full structure samples with electrochemical activated P-GaN. Thus we propose an efficient method for P-GaN activation by electrochemical reaction. 30% improvement in light output is obtained by electrochemical activation method.